• Journal of Ocean Engineering and Technology
• /
• v.10 no.2
• /
• pp.77-87
• /
• 1996

The estimation of the remaining life for the aged components in power plant as well as chemical and peroleum plants has been recently coberned. The raw materials used in this syudy are the 1Cr-1Mo-0.25V rotor steel which intensified P and S compositions along with the nominal compositions of ASTM A470 standard. Five kinds of specimens with the different degradation levels were prepared by isothermal aging teat treatment at $630^{\circ}C$ The mechanical properties and fatigue strength of virgin and aged 1Cr-1Mo-0.25V rotor steel have been inbestigated through the hardness, tensile, fatigue test, SEM fractograph and EDS analysis at room temperature. Thus, the data of aged specimens were compared with those of virgin specimen to evaluate the aging effects. The main results obtained in this study are as follows; The decrease of the hardness due to degradation was distinguished until 50, 000hrs simulated service time. And is was confirmed that the considerable amount of P, Mn, Cr and S was precipitated at the grain boundary of aged material through the SEM and EDS analysis. The fatigue strength of 25, 000, 50, 000, 75, 000 and 100, 000hrs aged material was decreased 29.5%, 24.4%, 28.6%, 35.7% than that of virgin material at $10^7$ cycles of room temperature. The major cracks of virgin and aged materials initiated at the inclusions including Si, P and Mn compositions which were located at the outer periphery of the specimen.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.118-118
• /
• 2008

The oxide CMP has been applied to interlayer dielectric(ILD) and shallow trench isolation (STI) in chip fabrication. Recently the slurry used in oxide CMP being changed from silica slurry to ceria (cerium dioxide) slurry particularly in STI CMP, because the material selectivity of ceria slurry is better than material selectivity of silica slurry. Moreover, the ceria slurry has good a planarization efficiency, compared with silica slurry. However ceria abrasives make a material removal rate too high at the region of wafer center. Then we focuses on why profile of material removal rate is convex. The material removal rate sharply increased to 3216 $\AA$/min by $4^{th}$ run without conditioning. After $4^{th}$ run, material removal rate converged. Furthermore, profile became more convex during 12 run. And average material removal rate decreased when conditioning process is added to end of CMP process. This is due to polishing mechanism of ceria. Then the ceria abrasive remains at the pad, in particular remains more at wafer center contacted region of pad. The field emission scanning electron microscopy (FE-SEM) images showed that the pad sample in the wafer center region has a more ceria abrasive than in wafer outer region. The energy dispersive X-ray spectrometer (EDX) verified the result that ceria abrasive is deposited and more at the region of wafer center. Therefore, this result may be expected as ceria abrasives on pad surface causing the convex profile of material removal rate.

• Journal of the Korean Chemical Society
• /
• v.61 no.6
• /
• pp.339-345
• /
• 2017

Carbonaceous adsorbent (CA-WTP) was prepared by heat treatment at $400^{\circ}C$ for 2 h in N2 atmosphere using waste tire powder (WTP). WTP and CA-WTP were first characterized by thermo-gravimetric analysis (TGA), energy dispersive X-ray spectrometer (EDS), scanning electron microscopy (SEM), specific surface area analysis (BET) and FT-IR spectroscopy. Then, they were tested as adsorbents for removal of Cd in water. CA-WTP exhibited much higher specific surface area and total pore volume than WTP itself and showed higher adsorption capacity for Cd. Equilibrium data of adsorption were analyzed using Freundlich and Langmuir isotherm models. It was seen that both Freundlich and Langmuir isotherms have correlation coefficient $R^2$ value larger than 0.95. The results of studies indicate that CA-WTP developed from WTP by heat treatment could be used as efficient adsorbent for the removal Cd from water.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.17 no.5
• /
• pp.47-53
• /
• 2013

In this study, In order to develop the measurement method of high energy density metal aluminum dust cloud combustion, flame temperature and emission spectrum was measured using spectrometer. Because of the ultra high ${\mu}m$-sized aluminum flame temperature more than 2400 K, it was measured by non-contact optical technique which is the modified two wavelength pyrometry with 520, 640 nm and spectrum comparison method. These methods were applied to experiment after accurate verification. As a result, we could identify that flame temperature is more than 2400 K in bottom of combustor in both methods. And on the emission spectrum analysis, we could measure AlO radical which is occurred dominantly in aluminum combustion.

• Nuclear Engineering and Technology
• /
• v.40 no.3
• /
• pp.225-232
• /
• 2008

To understand the effect of the cyclic strain rate on the environmentally assisted cracking behaviors of SA508 Gr.1a low alloy steel in deoxygenated water at $310^{\circ}C$, the fatigue surface and a sectioned area of specimens were observed after low cycle fatigue tests. On the fatigue surface of the specimen tested at a strain rate of 0.008 %/s, unclear ductile striations and a blunt crack tip were observed. Therefore, metal dissolution could be the main cracking mechanism of the material at this strain rate. On the other hand, on the fatigue surfaces of the specimens tested at strain rates of 0.04 and 0.4 %/s, brittle cracks and flat facets, which are evidences of the hydrogen induced cracking, were observed. In addition, a tendency of linkage between the main crack and the micro-cracks was observed on the sectioned area. Therefore, at higher strain rates, the main cracking mechanism could be hydrogen induced cracking. Additionally, evidence of the dissolved MnS inclusions was observed on the fatigue surface from energy dispersive x-ray spectrometer analyses. Thus, despite the low sulfur content of the test material, the sulfides seem to contribute to environmentally assisted cracking of SA508 Gr.1a low alloy steel in deoxygenated water at $310^{\circ}C$.

• Korean Chemical Engineering Research
• /
• v.48 no.2
• /
• pp.178-184
• /
• 2010

The aim of this work is the fabrication of polyelectrolyte microcapsules composed of biocompatible polymers such as chitosan, heparin and alginate, to encapsulate the fluorescein isothiocyanate(FITC)-albumin, and to investigate the protein release behavior therefrom. Polyelectrolyte capsules with 4-layer structures could be prepared with biocompatible materials by oppositely charged adsorption using melamin-foramide as a template. Transmission electron microscope(TEM), scanning electron microscope(SEM) and optical microscope confirmed hollow capsule structures. Protein release before and after encapsulation was monitored with a UV-Vis spectrometer. Microcapsules have different behaviors depending on the kind of polyelectrolyte polymers, chitosan-heparin capsules or chitosan-alginate capsules. In conclusion, the polyelectrolyte multilayer shells can be switched between an open and closed state by means of tuning the pH value.

• Journal of the Korean Ceramic Society
• /
• v.51 no.6
• /
• pp.618-622
• /
• 2014

Oxide phosphorescent phosphor has an wide application in ceramic art and decoration due to its chemical and mechanical properties. Here, phosphorescent properties of strontium aluminate phosphor ($SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$) emitting yellowish-green light was investigated with thermal treatment at $1250^{\circ}C$ under air and reducing atmosphere. The characterizations of thermally treated samples were analyzed using X-ray fluorescence (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), fluorescence spectrometer. $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ still showed a good phosphorescent properties after annealing process in reducing atmosphere, while phosphorescence of $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ annealed in air seriously degraded, due to oxidation of $Eu^{2+}$ to $Eu^{3+}$ ions. It was also observed that $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ annealed in reducing atmosphere emitted yellowish-green light during 3 h after being exposed to sunlight.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.531-535
• /
• 2017

Enormous amount of waste oyster-shell (OS) has a major disposal problem in coastal regions. OSs have attracted much attention for recycling, because these are mainly composed of calcium carbonate with rare impurities. In this study, we demonstrate the calcareous deposit films on steel plate by using OSs on the basic of cathodic protection technique. The composition of the OSs was analyzed by wavelength dispersive X-ray fluorescence spectrometer. Carbon dioxide gas was pumped into distilled water to make carbonic acid solution for dissolution of OS. The calcareous deposit was characterized by second electron microscope (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffraction. Corrosion rates were estimated by measurements of anodic polarization and immersion test. It is confirmed that calcareous deposits on steel plate are formed under all condition of cathodic protection by using waste OS from the SEM and EDX results. Calcareous deposits on steel by OS provide good corrosion resistance by acting as a barrier to oxygen supply to the steel surface.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.44 no.9
• /
• pp.789-795
• /
• 2016

Laser-induced combustions and explosions generated by high laser irradiances were explored by Laser-Induced Breakdown Spectroscopy (LIBS). The laser used for target ablation is a Q-switched Nd:YAG laser with 7 ns pulse duration at wavelength of 1064 nm laser energies from 40 mJ to 2500 mJ ($6.88{\times}10^{10}-6.53{\times}10^{11}W/cm^2$). The plasma light source from aluminum detected by the echelle grating spectrometer and coupled to the gated ICCD(a resolution (${\lambda}/{\Delta}{\lambda}$) of 5000). This spectroscopic study has been investigated for obtaining both the atomic/molecular signals of aluminum-oxygen and the calculated ambient condition such as plasma temperature and electron density. The essence of the paper is observing specific electron density ratio which can support the processes of chemical reaction and combustion between ablated aluminum plume and oxygen from air by inducing high laser energy.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.165-165
• /
• 2007

투명전도박막은 ITO, $SnO_2$, ZnO, 등이 있으나 $SnO_2$는 자외선 영역까지 투과시키는 우수한 광학적 특성을 나타내지만, 상당히 큰 전기저항으로 인해 현재는 현재 ITO가 널리 이용되고 있다. ITO(Indium Tin Oxide)박막은 자외선 영역에서 반사율이 높으며 가시광선영역에서는 80%이상의 뛰어난 투과율을 가지고 있다. 또한 낮은 전기저항과 넓은 광학적 밴드갭 때문에 가장 유용한 투과전도성 재료 중에 하나이다. 이러한 특성 때문에 여러 가지 문자 표시소자의 투명전극, 태양전지의 창재료, 정전차폐를 위한 반도체 포장재료, 열반사막, 면발열체, 광전변환 소자에 응용되고 있다. 일반적으로 박막의 제작에는 저항가열법과 전자선가열법, 스퍼터링법의 물리적 증착과 화학적 증착으로 나뉜다. 본 논문에서는 증착온도를 달리 하여 RF-sputtering에 의해 ITO박막을 증착한 후 온도증가에 따른 박막의 특성을 연구하였으며 또한 광역평탄화를 위한 CMP공정을 적용하여 증착온도가 연마에 미치는 영향을 연구하였다. 본 실험에서 사용된 ITO박막은 $2{\times}2Cm$의 Corning glass위에 증착되었으며 타겟은 $In_2O_3$와 $SnO_2$가 9:1로 혼합된 Purity 99.99%이상의 직경 2 inch인 ITO타겟을 사용하였다. 박막 증착시 기판온도는 상온에M $200^{\circ}C$까지 변화시켰으며 RF power는 100W로 일정하게 하였으며 증착압력은 $8{\times}10^{-2}$Torr이였다. CMP공정조건은 헤드속도 60rpm, 플레이튼 속도 60rpm, 슬러리 주입 유량 60mml/min, 압력 $300g/cm^2$이였다. 전기적 특성은 four point probe를 이용하여 측정하였으며 광학적 특성은 UV-Visible Spectrometer를 이용하여 200~900nm의 파장범위에서 광투과도를 측정하였다.