• Corrosion Science and Technology
• /
• v.7 no.1
• /
• pp.61-67
• /
• 2008

In this paper, electrochemical and microstructural characteristics of nickel-plated Alloy 600 were investigated in order to identify the performance of electroless Ni-plating on Alloy 600 in high-temperature aqueous condition with the comparison of electrolytic nickel-plating. For high temperature corrosion test of nickel-plated Alloy 600, specimens were exposed for 770 hours to typical PWR primary water condition. During the test, open circuit potentials (OCP's) of all specimens were measured using a reference electrode. Also, resistance to flow accelerated corrosion (FAC) test was examined in order to check the durability of plated layers in high-velocity flow environment at high temperature. After exposures to high flow rate aqueous condition, the integrity of surfaces was confirmed by using both scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). For the field application, a remote process for electroless nickel-plating was demonstrated using a plate specimen with narrow gap on a laboratory scale. Finally, a practical seal design was suggested for more convenient application.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.5
• /
• pp.218-223
• /
• 2013

In this study, the reflectivity characteristics of Ag nano-coating grown by electroless plating were investigated in order to use as the reflecting plate of BLU (Back Light Unit) in the LCD (Liquid Crystal Display) or LED (Light Emitting Diode) display equipment. The microstructure of Ag nano-coating was polycrystalline nano-structure that consisted of Ag nano-crystals to be reduced and precipitated, and the size of reduced nano-crystals increased as the thickness of nano-coating increased. The reflectivity of Ag nano-coating in the visible light decreased as the thickness of nano-coating increased and the reduction of reflectivity was more severe in the short wavelength region of visible light. The decrease of reflectivity was closely related to the size of Ag nano-crystal and was thought to be due to the larger surface roughness of larger nano-coating thickness. Therefore, the finer Ag nano-crystals and thinner nano-coating thickness could be favorable for the higher reflectivity of Ag nano-coating grown by electroless plating.

• Applied Chemistry for Engineering
• /
• v.8 no.5
• /
• pp.742-748
• /
• 1997

Diamond films which have high hardness and thermal conductivity can be used to improve the performance of WC-Co as a cutting tool material. However, it is difficult to get such coatings of good uniformity and adhesiveness due to the surface characteristics of WC-Co. To get better coatings, some techniques, such as the surface treatment of substrate or the formation of interlayer between substrate and diamond film, have been tried. In the present work, the nickel interlayer is formed onto WC-Co by electroless Ni-P plating, which is introduced as a new method, and then diamond film is deposited on the interlayer. Formation and uniformity of three layers, i.e., substrate, electroless plate, and diamond film, and the adhesiveness of interlayers were studied. To investigate the effects of pretreatment on electroless plating, two different methods such as acid treatment and diamond powder treatment were used. The effects of heat treatment of the electroless plated surface on adhesiveness between the substrate and the interlayer were examined. It was found that as the temperature increases, the Ni crystals grow and then result in improved adhesiveness. Diamond film coatings of pure diamond phase were obtained at $800^{\circ}C$. It is concluded that the heat treated electroless Ni-P plating can be effectively used as a interlayer between WC-Co substrate and diamond film.

• Transactions of the Korean hydrogen and new energy society
• /
• v.20 no.5
• /
• pp.361-370
• /
• 2009

Ni-PTFE composite plated on graphite (C/Ni-PTFE) and PTFE (PTFE/Ni-PTFE) particles were prepared uniformly by electroless composite plating. The conductivity of C/Ni-PTFE particles was 280 S/m higher than 95 S/m of PTFE/Ni-PTFE particles at same composite plating condition (Ni:35~36 wt%, PTFE:8 wt%). The C/Ni-PTFE particles were formed into the C/Ni-PTFE plate using heat treatment at $350^{\circ}C$ under 10~$1000\;kg/cm^2$. The C/Ni-PTFE plate showed 1) high conductivity of $5.7\;{\times}\;10^4\;S/m$ due to the existence of graphite as conducting aid and the formation of 3-dimensional Ni network 2) good gas diffusion caused by various pore volumes (0.01~$100\;{\mu}m$) in the plate. The plate could be useful for an electrode in an alkaline fuel cell (AFC). The current density of C/Ni-PTFE electrode indicated $84\;mA/cm^2$ at 0.3V and it was 3.0 times higher than that of PTFE/Ni-PTFE electrode.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.5 no.5
• /
• pp.433-437
• /
• 2004

The MmSH is a process of injecting ABS to produce innovated physical properties compared to the conventional injection process. Physical properties such as thickness and adhesion strength of Ni plate electrolessly coated on a conventional and a MmSH injected ABS have been studied in the pH range 4~8. Thickness of the plate on the MmSH and the conventionally injected ABS appeared to be directly proportional to pH. The ABS processed by the conventional injection showed adhesion strength corresponded to ASTM 4B above pH 5. On the other hand, the ABS processed by the MmSH injection showed a superior adhesion strength corresponded to ASTM 5B above pH 6. It was calculated the shielding effectiveness of above 50 dB in all conditions.

• Journal of the Korean institute of surface engineering
• /
• v.45 no.4
• /
• pp.162-167
• /
• 2012

Ni-P/C multi-layer was synthesized by electroless plating and paste coating for better corrosion and surface conductance as a metallic bipolar plate. The Ni-P layer could be synthesized with the range of 2.6~22.4 at.% P contents and it's surface morphology and corrosion resistance depend on content of P. Corrosion resistance of the Ni-P layer in sulfuric acid by electrochemical test is similar with pure Ni. Surface resistance of pure Ni after corrosion was increased about 8% compared to pure Ni. On the other hand, that of the Ni-P/C composite with 20% carbon content was increased only 1%.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.1
• /
• pp.7-11
• /
• 2003

The semiconductor chips or electronic components generate heat, which causes malfunction of the parts when it was not cooled properly. Bulky heat sink and cooling fan are used to get rid of the heat. However, with this bulky system, it is hard to integrate the electronics system in a small scale. The cooling efficiency of the system depends on the surface area of the heat sink, thermal conductivity of the material and the method of integration. In order to develop a novel cooling system, a micro-heatsink with a large surface area while retaining small volume was fabricated by electroless deposition of gold/copper inside a Track-etched membrane. The structure of the micro-heatsink was investigated using SEM or optical microscope. It was also found that the micro-heatsink is more efficient than a flat copper plate.

• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.794-801
• /
• 1995

To connect the driver IC and Al coated glass, a method has been developed to plate electrolessly Ni on Al/PR system. It Is necessary to pretreat Al to remove oxide film before plating. In order to find pretreatment process which does not damage photoresist or glass, alkaline and fluoride zincate process have been investigated. Because photoresist and aluminum thin film can easily dissolve in alkaline solution, it is considered that the fluoride zincate process was a suitable one. After immersion in the zincate solution containing 1.5 g/$\ell$ ammonium bifluoride and 100 g/$\ell$ zinc sulfate, electroless nickel plating could be performed. The additive in the zincate solution and thiourea in the plating solution increased smoothness of the plated surface. Acld dip could improve the uniformit of the surface.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.2
• /
• pp.132-138
• /
• 2016

In this study, we report the fabrication of functional complex fibers, which have been studied widely globally for numerous applications. Here, we fabricated conductive complex fibers with antibacterial properties by coating metal ions on the surface of plastic (polypropylene) fibers using the electroless and electrochemical deposition. First, we polished the polypropylene melt-blown fiber surface and obtained an absorbing Pd seed layer on its surface. Subsequently, we substituted the Pd with Cu. Bis-3-sulfopropyl-disulfide disodium salt (SPS), polyethylene glycol (PEG), and ethylene thiourea (ETU) were used as the brightener, carrier, and leveler, respectively for the electroplating. We focused on most achieving the stable plating condition to remove dendrites, which are normally during electroplating metals so that smooth layer is formed on the fiber surface. The higher the amount of SPS, the higher was the extent of irregular plate-like growth. Many irregularities in the form of round spheres were observed with increase in the amount of PEG and ETU. Hence, when the additives were used separately, a uniform coating could not be obtained. A stable coating was obtained when the three additives were combined and a uniform 5-9 μm thick copper layer with a stable morphology could be obtained around the fiber. We believe that our results can be applied widely to obtain conductive fibers with antibacterial properties and are useful in aiding research on conductive lightweight composite fibers for application in information technology and robotics.

• Journal of Powder Materials
• /
• v.18 no.5
• /
• pp.430-436
• /
• 2011

Joining of NiO-YSZ to 316 stainless steel was carried out with B-Ni2 brazing alloy (3 wt% Fe, 4.5 wt% Si, 3.2 wt% B, 7 wt% Cr, Ni-balance, m.p. 971-$999^{\circ}C$) to seal the NiO-YSZ anode/316 stainless steel interconnect structure in a SOFC. In the present research, interfacial (chemical) reactions during brazing at the NiO-YSZ/316 stainless steel interconnect were enhanced by the two processing methods, a) addition of an electroless nickel plate to NiO-YSZ as a coating or b) deposition of titanium layer onto NiO-YSZ by magnetron plasma sputtering method, with process variables and procedures optimized during the pre-processing. Brazing was performed in a cold-wall vacuum furnace at $1080^{\circ}C$. Post-brazing interfacial morphologies between NiO-YSZ and 316 stainless steel were examined by SEM and EDS methods. The results indicate that B-Ni2 brazing filler alloy was fused fully during brazing and continuous interfacial layer formation depended on the method of pre-coating NiO-YSZ. The inter-diffusion of elements was promoted by titanium-deposition: the diffusion reaction thickness of the interfacial area was reduced to less than 5 ${\mu}m$ compared to 100 ${\mu}m$ for electroless nickel-deposited NiO-YSZ cermet.