• Journal of the Korean Society for Precision Engineering
• /
• v.15 no.1
• /
• pp.51-59
• /
• 1998

The purposes of the paper are to consider the failure phenomenon based on delamination and crack when the encapsulant of plastic IC package under hygrothermal loading in the IR soldering process is on elastic and viscoelastic behavior due to the temperature and to show the optimum design using fracture mechanics. The model for analysis is the plastic SOJ package with a dimpled diepad. The package model with the perfect delamination between chip and diepad is chosen to estimate the resistance to fracture by calculating J-integrals in low temperature and C(t)-integrals in high temperature with the change of the design under hygrothermal loading. The optimum design to depress the delamination and crack in the plastic IC package is presented.

• Proceedings of the KWS Conference
• /
• 1998.10a
• /
• pp.317-320
• /
• 1998

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.6 s.261
• /
• pp.710-717
• /
• 2007

This paper presents plastic limit loads and approximate J-integral estimates for circumferential part-through surface crack at the interface between elbows and pipes. Based on finite element limit analyses using elastic-perfectly plastic materials, plastic limit moments under in-plane bending are obtained and it is found that they are similar those for circumferential part-through surface cracks in the center of elbow. Based on present FE results, closed-form limit load solutions are proposed. Welds are not explicitly considered and all materials are assumed to be homogeneous. And the method to estimate the elastic-plastic J-integral for circumferential part-through surface cracks at the interface between elbows and straight pipes is proposed based on the reference stress approach, which was compared with corresponding solutions fur straight pipes.

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.179-181
• /
• 2003

The present study focuses on the effect of geometrical discontinuity, strength mismatch, which can elevate plastic constraint due to heterogeneous plastic straining, and loading rate on the ductile crack initiation using two-parameter criterion. Fracture initiation testing has been conducted under static and dynamic loading using circumferentially notched round-bar specimens. In order to evaluate the stress/strain state in the specimens, especially under dynamic loading, a thermal elastic-plastic dynamic finite element (FE) analysis considering the temperature rise due to plastic deformation has been carried out.

• Steel and Composite Structures
• /
• v.1 no.4
• /
• pp.411-426
• /
• 2001

This paper treats the failure analysis of prestressing steel wires with different kinds of localised damage in the form of a surface defect (crack or notch) or as a mechanical action (transverse loads). From the microscopical point of view, the micromechanisms of fracture are shear dimples (associated with localised plasticity) in the case of the transverse loads and cleavage-like (related to a weakest-link fracture micromechanism) in the case of cracked wires. In the notched geometries the microscopic modes of fracture range from the ductile micro-void coalescence to the brittle cleavage, depending on the stress triaxiality in the vicinity of the notch tip. From the macroscopical point of view, fracture criteria are proposed as design criteria in damage tolerance analyses. The transverse load situation is solved by using an upper bound theorem of limit analysis in plasticity. The case of the cracked wire may be treated using fracture criteria in the framework of linear elastic fracture mechanics on the basis of a previous finite element computation of the stress intensity factor in the cracked cylinder. Notched geometries require the use of elastic-plastic fracture mechanics and numerical analysis of the stress-strain state at the failure situation. A fracture criterion is formulated on the basis of the critical value of the effective or equivalent stress in the Von Mises sense.

• Nuclear Engineering and Technology
• /
• v.54 no.5
• /
• pp.1726-1746
• /
• 2022

This paper presents fracture mechanics analysis results for various cracks located at pressurized water reactor pressure vessel nozzle crotch corners taking into consideration constraint effect. Technical documents such as the ASME B&PV Code, Sec.XI were reviewed and then a fracture mechanics analysis procedure was proposed for structural integrity assessment of various nozzle crotch corner cracks under normal operation conditions considering the constraint effect. Linear elastic fracture mechanics analysis was performed by conducting finite element analysis with the proposed analysis procedure. Based on the evaluation results, elastic-plastic fracture mechanics analysis taking into account the constraint effect was performed only for the axial surface crack of the reactor pressure vessel outlet nozzle with cladding. The fracture mechanics analysis result shows that only the axial surface crack in the reactor pressure vessel outlet nozzle has the stress intensity factor exceeding the low bound of upper-shelf fracture toughness irrespectively of considering the constraint effect. It is confirmed that the J-integral for the axial crack of the outlet nozzle does not exceed the ductile crack initiation toughness. Hence, it can be ensured that the structural integrity of all the cracks is maintained during the normal operation.

• Nuclear Engineering and Technology
• /
• v.55 no.12
• /
• pp.4647-4658
• /
• 2023

In this paper, elastic-plastic fracture mechanics analysis is performed to determine the critical crack sizes of the multipurpose canister (MPC) manufactured using austenitic stainless steel under dynamic loading conditions that simulate drop accidents. Firstly, dynamic finite element (FE) analysis is performed using Abaqus v.2018 with the KORAD (Korea Radioactive Waste Agency)-21 model under two drop accident conditions. Through the FE analysis, critical locations and through-thickness stress distributions in the MPC are identified, where the maximum plastic strain occurs during impact loadings. Then, the evaluation using the failure assessment diagram (FAD) is performed by postulating an external surface crack at the critical location to determine the critical crack depth. It is found that, for the drop cases considered in this paper, the principal failure mechanism for the circumferential surface crack is found to be the plastic collapse due to dominant high bending axial stress in the thickness. For axial cracks, the plastic collapse is also the dominant failure mechanism due to high membrane hoop stress, followed by the ductile tearing analysis. When incorporating the strain rate effect on yield strength and fracture toughness, the critical crack depth increases from 10 to 20%.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.8 no.4
• /
• pp.87-92
• /
• 1999

Generally the life of die is limited by fatigue fracture or dimensional inaccuracy originated from wear. In this paper to predict the fatigue life of die the stress and strain histories of die can be predicted by the analysis of elastic-plastic finite element method and the elastic analysis of die during the process analysis of workpiece. Also the stress-life curve of die material can be obtained through experiment. With the above to재 facts we propose the analysis method of prediction fatigue life in die,. In the proposed model the analysis of elastic-plastic finite element method for material is carried out by using ABAQUS. Surface force resulted from the contacting border of the die and workpiece is transformed into the nodal force of die to implement elastic analysis. besides the proposed analysis model of die is applied to extrusion die and forging. die.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.10 s.181
• /
• pp.2405-2412
• /
• 2000

A cast stainless steel may experience an embrittlement when it is exposed to approximately 30$0^{\circ}C$ for long period. In the present investigation, The three classes of the thermally aged CF8M specimie n are prepared using an artificially accelerated aging method. Namely, after the specimen are held for 300, 1800 and 3600hrs. at 43$0^{\circ}C$ respectively, the specimens are quenched in water to room temperature. Load versus load line displacement curves and J-R curves are obtained using the unloading compliance method. $J_{IC}$ values are obtained following ASTM E 813-87 and ASTM E 813-81 methods. In addition to these methods, JIC values are obtained using SZW(stretch zone width) method described in JSME S 001-1981. The results of the unloading compliance method are $J_Q$=485.7 kJ/m$^2$ for virgin material, $J_{IC}$ of the degraded materials associated with 300, 1800 and 3600hrs are obtained 369.25 kJ/m$^2$, 311.02 kJ/m$^2$, 276.7 kJ/m$^2$, respectively. The results of SZW method are similar to those of the unloading compliance method. Through the elastic-plastic fracture toughness test, it is found that the value of $J_{IC}$ is decreased with increasing of the aging time. The results obtained through the investigation can provide reference data for a leak before break(LBB) of reactor coolant system of nuclear power plants.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.310-315
• /
• 2001

This paper provides validations of the reference stress based J and $C^*$ estimations, proposed in Part I, for inner, circumferential surface cracked pipes under internal pressure and global bending against detailed 3-D elastic-plastic and elastic-creep FE results. For this purpose, actual tensile properties of two typical stainless steels (TP304 and TP316) are used for elastic-plastic FE analyses and two realistic creep laws are used for elastic-creep FE analyses. For a total of twenty cases considered in this paper, agreements between the proposed reference stress based J and $C^*$ estimations and the FE results are excellent. More important aspect of the proposed estimations is that they can be used to estimate J and $C^*$ not only at the deepest point of the surface crack but also at an arbitrary point along the crack front.