• Journal of Ceramic Processing Research
• /
• 제13권spc2호
• /
• pp.241-245
• /
• 2012

The barrier rib on plasma display panel (PDP) is a typical 3D-patterned thick film with thickness of 120 ㎛ and it is hard to measure its dielectric constant in this state of the product. Because the porosity of ceramic thick film influenced the mechanical and dielectric characteristics, it was expected that there was the relationship between two properties. Therefore, the correlation analysis between porosity, hardness and dielectric constant of the barrier rib was studied and the exponential curve between porosity and hardness, and the quadratic curve between porosity and dielectric constant were drawn. The dielectric constant was well related to hardness by K400kHz = 0.5672 + 5.695 ln(Hv). The hardness was measured at five points on two real panels which sintered by two types of profiles and then dielectric constants and deviation were estimated by the above equation.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.400-403
• /
• 2004

The dielectric properties of $BaTiO_3/SrTiO_3$ multilayered thick films with printing times were investigated. $BaTiO_3/SrTiO_3$ thick films were deposited by Screen-printing method on alumina substrates. The obtained films were sintered at $1400^{\circ}C$ with bottom electrode(Pt) for 2hours. The structural and the dielectric properties were investigated for various printing times. The BST phase appeared in all of the $BaTiO_3/SrTiO_3$ mutilayered thick films. The $BaTiO_3/SrTiO_3$ multilayered thick film thickness, obtained by one printings, was $50{\mu}m$. The dielectric constant and dielectric loss of the $BaTiO_3/SrTiO_3$ multilayered thick film, obtained by five printings, were about 266, 0.8% at 1Mhz, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.260-261
• /
• 2005

The heterolayered thick/thin structure consisting of $Pb(Zr_{0.52}Ti_{0.48})O_3$ and $BaTiO_3(BT)$ were fabricated by a sol-gel process. PZT powders, prepared by the sol-gel method, were mixed with an organic vehicle and the PZT thick films were fabricated by the screen printing techniques on alumina substrate with Pt electrodes. The microstructural and dielectric characteristics of the stacked heterolayered PZT/BT/PZT films were investigated by varying the number of coating $BaTiO_3$ layers. The existence of a $BaTiO_3$ layer between the PZT thick films of the tri-layer $Pb(Zr_xTi_{1-x})O_3/BaTiO_3/Pb(Zr_xTi_{1-x})O_3$thick/thin/thick film can greatly improve the leakage current properties of the PZT thick films. The average thickness of a PZT(5248)/$BaTiO_3$ heterolayered thick/thin film was 25$\mu$m. The relative dielectric constant and dielectric loss of the PZT(5248)/$BaTiO_3$-3 heterolayered thin film coated three times were 1087 and 1.00% at 1[MHz].

• 한국전기전자재료학회논문지
• /
• 제16권4호
• /
• pp.304-310
• /
• 2003

(Ba$\sub$0.6-x/Sr$\sub$0.4/Ca$\sub$x/)TiO$_3$(BSCT) (x=0.10, 0.15, 0.20) powder, prepared by the sol-Bel method, were mixed with organic binder and then BSCT thick films were fabricated by the screen printing techniques on alumina substrates using the BSCT paste. The structural and the dielectric Properties were investigated for various composition ratio and sintering temperature. The second phase appeared in BSCT(40/40/20) thick film sintered at 1450$^{\circ}C$. BSCT thick film thickness, obtained by four printings, was approximately 110∼120$\mu\textrm{m}$. The Curie temperature and dielectric constant at room temperature were decreased with increasing Ca content. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) specimen, which was sintered at 1420$^{\circ}C$ and measured at 1MHz, were about 910, 0.46% and 9.28% at 5㎸/cm, respectively.

• 한국전기전자재료학회논문지
• /
• 제22권4호
• /
• pp.297-302
• /
• 2009

We have successfully fabricated the alumina thick films using inkjet printing processes without a high temperature sintering process. Alumina suspension as dielectric ink was formulated by combining nano-sized alumina powders with an anionic polymer dispersant in formamide/water as co-solvent. The thickness of the printed alumina thick film was measured at around 5 um by field emission scanning electron microscope. The calculated packing density of 68.5 % from the printed alumina thick film was much higher than the same films fabricated by conventional casting or dip coating processes. Q factor of the dielectrics thick film infiltrated with cyanate ester resin was evaluated by impedance analyzer.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.656-658
• /
• 2004

Pb$(Zr_{0.8}Ti_{0.2})TiO_3$ powder were prepared by the sol-gel method using a solution of Pb-acetate, Zr n-propoxide and Ti iso-propoxide. PZT thick film were fabricated by the screen printing method, and the structural and ferroelectric properties asafunting of the sintering temperature were studied. PZT film thickness, obtained by four screen printing, was approximately $70\sim90{\mu}m$. The relative dielectric constant and the dielectric loss of the PZT thick film sintered at $1050^{\circ}C$t were approximately 676 and 1.4%, respectively. The remanent polarization and the coercive field of the PZT thick film sintered at $1050^{\circ}C$ were $21.15{\mu}C/cm^2$ and 10.1 kV/cm, mapetively

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2003년도 하계학술대회 논문집 C
• /
• pp.1529-1531
• /
• 2003

Thick film mechanical sensors can be categorized into four main areas piezoresistive, piezoelectric, piezocapastive and mechanic tube. In this areas, the thick film strain gage is the earliest example of a primary sensing element based on the substrates. The latest thick film sensor is used various pastes that have been specifically developed for pressure sensor application. The screen printing technique has been used to fabricate the pressure sensors on alumina substrate($Al_2O_3$). Thick film capacitive of strain sensing characteristics are reported and dielectric paste based on (Ti+Ba) materials. The electric property of dielectric paste has been studied and exhibit good properly with good gage factor comparable to piezoresistive strain gage. New piezocapacitive strain sensor was designed and tested. The output of capacitive value was good characteristics.

• Journal of Electrical Engineering and Technology
• /
• 제4권4호
• /
• pp.527-530
• /
• 2009

$(Ba_{0.57}Sr_{0.33}Ca_{0.10})TiO_3$(=BSCT) powders, prepared by the sol-gel method, were doped using $MnCO_3$ as the acceptor and $Dy_2O_3$ as the donor. This powder was mixed with an organic vehicle. BSCT thick films were fabricated by the screen-printing techniques on the alumina substrate. The structural and dielectric properties of BSCT thick films were investigated with variation of the $Dy_2O_3$ amount. As a result of the differential thermal analysis (DTA), the exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All the BSCT thick films showed the XRD patterns of a typical polycrystalline perovskite structure. The average grain size of BSCT thick films decreased with an increasing amount of $Dy_2O_3$. The relative dielectric constant and dielectric loss of the BSCT thick film doped $Dy_2O_3$ 0.1mol% were 4637.4 and 1.6% at 1kHz, respectively.

• Journal of Information Display
• /
• 제7권3호
• /
• pp.27-30
• /
• 2006

This paper presents a comprehensive study on threshold voltage $(V_{th})$ control of organic thin-film transistors (OTFTs) with dual-gate structure. The fabrication of dual-gate pentacene OTFTs using plasma-enhanced atomic layer deposited (PEALD) 150 nm thick $Al_{2}O_{3}$ as a bottom gate dielectric and 300 nm thick parylene or PEALD 200 nm thick $Al_{2}O_{3}$ as both a top gate dielectric and a passivation layer was investigated. The $V_{th}$ of OTFT with 300 nm thick parylene as a top gate dielectric was changed from 4.7 V to 1.3 V and that with PEALD 200 nm thick $Al_{2}O_{3}$ as a top gate dielectric was changed from 1.95 V to -9.8 V when the voltage bias of top gate electrode was changed from -10 V to 10 V. The change of $V_{th}$ of OTFT with dual-gate structure was successfully investigated by an analysis of electrostatic potential.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 제36회 하계학술대회 논문집 C
• /
• pp.2013-2015
• /
• 2005

In this paper, Effect of $BaSrTiO_3/Li_2CO_3$ on low temperature sintering and dielectric property of thick films has been investigated for variable capacitor on high frequency. The thick films were fabricated by the tape casting and then the structural and dielectric properties as a function of an addition composition ratio and sintering temperature were studied. For the thick film sintered at $1050^{\circ}C$, it was densified to 96% of $BaSrTiO_3$ theoretical density by the addition of 10 $wt{\cdot}%$ $BaSrTiO_3/Li_2CO_3$. Dielectric constant increased and Curie temperature lowered with the increased of $BaSrTiO_3/Li_2CO_3$ content, which probably can be explained by the substitution of $Ba^{3+},Li^{1+}$ on $RaTiO_3$ lattice. The tunability and dielectric loss of the $BaSrTiO_3/Li_2CO_3$ thick film, sintered at $1350^{\circ}C$, were about 26% and 0.234 at $10{\sim}15MHz$, respectively.