• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.108-109
• /
• 2009

In this study we investigated the characteristics of GZOB thin film on $O_2$ plasma treated Polycarbonate substrate using DC magnetron sputtering method. In our experiments results, GZOB thin film on $O_2$ plasma treated Polycarbonate substrate showed low resistivity than As-grown GZOB thin film, and visible transmission of 85% with a thickness 400 nm. Compared with As-Grown the electrical properties of GZOB were relatively improved by $O_2$ plasma treated substrate. From these results, we could confirm the suitable GZOB thin films for transparent electrode.

• 한국전기전자재료학회논문지
• /
• 제14권6호
• /
• pp.470-474
• /
• 2001

This paper describes the fabrication and characteristics of CrN thin-film type pressure sensors, in which the sensing elements were deposited on SuS. 630 diaphragm by DC reactive magnetron sputtering in an argon-nitride atmosphere(Ar-(10%)N$_2$). The optimized condition of CrN thin-film sensing elements was thickness range of 3500$\AA$ and annealing condition(300$\^{C}$, 3 hr) in Ar-10%N$_2$ deposition atmosphere. Under optimum conditions, the CrN thin-films for strain gauges is obtained a high resistivity, ρ=1147.65 $\mu$Ωcm, a low temperature coefficient of resistance, TCR=186ppm/$\^{C}$ and a high temporal stability with a good longitudinal, 11.17. The output sensitivity of fabricated CrN thin-film type pressure sensors is 2.36 mV/V, 4∼20nA and the maximum non-linearity is 0.4%FS and hysteresis is less than 0.2%FS.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1992년도 하계학술대회 논문집 B
• /
• pp.897-899
• /
• 1992

This paper deals with the characteristics of Indium Tin Oxide(ITO) sputtered by the reactive magnetron sputtering process. ITO films have been grown at various substrate temperatures(R.T, 100$^{\circ}C$, 200$^{\circ}C$, 240$^{\circ}C$) and we used the target material of alloy of Indium and Tin. The electrical and optical properties of the ITO film have been investigated and the effect of magnetic field to the properties of ITO was studied. We have studied how much the improvement of transmission rate and sheet resistivity by heat treatment was. The sample with good electrical and optical properties can be obtained for the low substrate temperature of 200$^{\circ}C$-250$^{\circ}C$.

• 한국진공학회지
• /
• 제3권2호
• /
• pp.190-197
• /
• 1994

본 연구에서는 DC magnetron 스퍼터링법을 이용하여 고정밀, 고저항 저항체 박막으로 TaNx film을 제조하였을 때 형성될 수 있는 화합물 중 TaN0.1, TaN0.8과 TaN 박막의 Rs와 TCR특성을 평가하 고 film층의 우선방향성을 XRD를 이용하여 판명한 뒤 저항체의 Rs와 TCR에 미치는 영향을 조사하였 다. TaN0.1 박막이 35$\Omega$/$\square$의 면저항값과 안정된 TCR값을 나타내는 것을 알수 있었다. 두께50~200nm 의 TaN0.1과 Alumina 기판 사이에 정(+)의 TCR을 갖는 약 50nm의 Cr층을 증착하였을 때 Rs는 180$\Omega$/ $\square$ 과 TCR는 20ppm/$^{\circ}C$인 적층박막을 제조할 수 있었다. TaN0.1, TaN0.8 과 TaN 시편에서 화합물 형성 에 따른 Ta의 결합에너지를 ESCA를 이용하여 조사하였다. 이상의 연구결과로부터 TaN0.1 film이 TaNfilm 보다 고정밀, 고저항 박막 저항체 제조에 있어 우수한 전기저항 특성을 가지며 Cr 중간층 형성 으로 TCR이 $\pm$ppm/$^{\circ}C$정도로 안정된 고정밀 다층 저항체 박막을 형성할 수 있었다.

• 한국전기전자재료학회논문지
• /
• 제18권3호
• /
• pp.253-258
• /
• 2005

This paper presents characteristics of CrOx thin-film, which were deposited on $Al_2$O$_3$ wafer by DC reactive magnetron sputtering in an argon-oxide atmosphere for high temperature applications. The present paper deals with a study of the technological characteristics of thin film resistors to provide a control in obtaining temperature coefficients of resistance of given value. The optimized condition of CrOx thin-film were thickness range of 2500 $\AA$ and annealing condition(350 $^{\circ}C$, 1 hr) in oxide partial pressure(3.5${\times}$10$^{-4}$ torr). Under optimum conditions, the CrOx thin-films is obtained a high resistivity, p=340 $\mu$Ωcm, a low temperature coefficient of resistance, TCR=-55 ppm/$^{\circ}C$. The CrOx thin films resistors which were fabricated in this paper had excellent characteristics as high precision resistors.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.737-740
• /
• 2001

This paper describes the fabrication and characteristics of CrN thin-film type pessure sensors, which the sensing elements were deposited on SUS. 630 diaphragm by DC reactive magnetron sputtering in an argon-nitride atmosphere(Ar-(10%)N$_2$). The optimized condition of CrN thin-film sensing elements was thickness range of 3500${\AA}$ and annealing condition(300$^{\circ}C$, 3 hr) in Ar-10 %N$_2$deposition atmosphere. Under optimum conditions, the CrN thin-films for strain gauges is obtained a high resistivity, $\rho$=1147.65 ${\mu}$$\Omega$cm, a low temperature coefficient of resistance, TCR=-186 ppm/$^{\circ}C$ and a high temporal stability with a good longitudinal, 11.17. The output sensitivity of fabricated CrN thin-film type pressure sensors is 2.36 mV/V, 4∼20 mA and the maximum non-linearity is 0.4 %FS and hysteresis is less than 0.2 %FS.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1995년도 추계학술대회 논문집
• /
• pp.302-305
• /
• 1995

ITO(indium tin oxide) that is both conductive in electricity and transparent to the visible ray is called transparent conducting thin film. Nowaday, according to the development of flat panel display such as LCD(Liquid Crystal display, EL(electolumine- scence display), PDP(plasma display panel), ECD(electrocromic display), the higher quality in the low temperature process has been asked to reduce the production cost and to have a good uniformity on a large substrate. In this study, we prepared indium tin oxide(ITO) by a cylindrical DC magnetron sputtering with Indium-tin (9:1) alloy target instead of indium-tin oxide target. To reduce the defact in ITO, the effect on ITO by varing the magnetic field intensity and the applied voltage ares studied. the resistivity of the film deposited in oxygen partial pressure of 5% and substrate temperature of 140$^{\circ}C$. is 1.6${\times}$10$\^$-1/$\Omega$$.$cm with 85% optical transmission in viaible ray.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.857-860
• /
• 2002

The material that is both conductive in electricity and transparent to the visible-ray is called transparent conducting thin film. It has many field of application such as solar cell, liquid crystal display, transparent electrical heater, selective optical filter, and a optical electric device. In this study, indium tin oxide (ITO ; Sn-doped $In_2O_3$) thin films were deposited on $SiO_2$/soda-lime glass plates by a dc magnetron sputtering technique. The crystallinity and electrical properties of the films were investigated by X-ray diffraction(XRD), atomic force microscopy (AFM) scanning and 4-point probe. The optical transmittance of ITO films in the range of 300-1000nm were measured with a spectrophotometer. As a result, we obtained polycrystalline structured ITO films with (222), (400), and (440) peak. Transmittance of all the films were higher than 90% in the visible range.

• Transactions on Electrical and Electronic Materials
• /
• 제17권2호
• /
• pp.121-124
• /
• 2016

ZnSnO₃ (ZTO)/Ag/ ZnSnO₃ (ZTO) trilayer films were prepared on glass substrates by radio frequency (RF) and direct current (DC) magnetron sputtering. The electrical resistivity and optical transmittance of the films were investigated as a function of the Ag interlayer thickness. ZTO films with a 15 nm thick Ag interlayer show the highest average visible transmittance (83.2%) in the visible range. In this study, the highest figure of merit (2.1×10⁻² Ω cm) is obtained with the ZTO 50 nm/Ag 15 nm/ZTO 50 nm films. The enhanced optical and electrical properties of ZTO films with a 15 nm thick Ag interlayer are attributed to the crystallization of the Ag interlayer, as supported by the distinct XRD pattern of the Ag (111) peaks. From the observed results, higher optical and electrical performance of the ZTO film with a 15 nm thick Ag interlayer seems to make a promising alternative to conventional transparent conductive ITO films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.334-337
• /
• 2002

The Quantum Hall Resistance(QHR) device which consists of GaAs/AlGaAs heterojunction structure is used for the realization of QHR Standard based on QHE. In order to characterize electrical contact resistances and dissipations of the device, it is slowly cooled down for eliminating thermal shock and unwanted noise. Then, the two properties are measured under 1.5 K and 5.15 T. Contact resistances are all within 1.2 Ω and longitudinal resistivities are all within 1 mΩ up to DC 90${\mu}$A. The results mean the device is operated well to realize the QHR Standard. To confirm it, the QHR Standard having the device is compared using a direct current comparator bridge with a 1 Ω resistance standard which the calibrated value is known from QHR standards maintained by other countries. The difference between them is agreed well within measurement uncertainty. It is thus considered that the properties of the device is estimated well and has good performance.