• 한국전기전자재료학회논문지
• /
• 제19권11호
• /
• pp.1014-1019
• /
• 2006

The influence of the number of solution coatings on the densification of the PZT thick films was studied. PZT powder and PZT precursor solution was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were (A) PZT(80/20)/PZT(20/80), (B) PZT(70/30)/PZT(30/70) and (C) PZT(60/40)/PZT(40/60), (D) PZT(52/48)/PT. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 moth and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about $60{\mu}m$. A grain size was increased with increasing the coating number. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant of PZT thick films was improved 30-100% as the number of coatings.

• Corrosion Science and Technology
• /
• 제11권1호
• /
• pp.29-36
• /
• 2012

The resistance spot welding of high strength steel degrades the weldability because of its high strength with rich chemical composition and coating layer to protect from corrosion. During the each resistance welding process the electrodes tip reacts with coating layer, then subsequently deteriorates and shorten electrode life. In this study, the Al-coated HPF (Hot Press Forming) steels and Zn-coated TRIP steels were used to investigate the electrode life for resistance spot welding. Experimental results show that the reactivity of Al-coating on HPF steels to electrode tip surface behaviors different from the conventional Zn-coated high strength steels. The electrode tip diameter and nugget size in electrode life test of Al-coated HPF steels are observed to be constant with respect to weld numbers. For Al-coated HPF steels, the hard aluminum oxide layer being formed during high temperature heat treatment process reduces reactivity with copper electrode during the resistance welding process. Eventually, the electrode life in resistance spot welding of Al-coated HPF steels has the advantage over the galvanized steel sheets.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 춘계학술대회 논문집
• /
• pp.278-281
• /
• 2009

Selective laser sintering(SLS), a kind of rapid prototyping technology, can provide a process to form many types of coatings. Coated layers by selective laser melting are highly influenced by substrate, powder and laser parameters such as laser power, scan rate, fill spacing and layer thickness. Therefore an attempt to fabricate Fe-Ni-Cr coating on AISI H13 tool steel has been performed by selective laser sintering. In this study, Fe-Ni-Cr coating was produced by experimental facilities consisting of a 200W fiber laser which can be focused to 0.08mm and atmospheric chamber which can control atmospheric pressure with Ar. With power increase or energy density decrease, line width was decreased and line surface quality was improved with energy density increase. Surface quality of coating layer was improved with fill spacing optimization or layer thickness decrease.

• 한국표면공학회지
• /
• 제50권6호
• /
• pp.523-530
• /
• 2017

In this study, we developed the h-BN interphase for ceramic matrix composites (CMCs) through a wet chemical coating method, which has excellent price competitiveness and is a simple process as a departure from the existing high cost chemical vapor deposition method. The optimum condition for nitriding an h-BN interphase using boric acid and urea as precursors were derived, and the h-BN interphase coating through a wet method on a carbon preform of 2.5 D was conducted to apply the optimum conditions to the CMCs. In order to control the coating property via the wet coating method, four parameters were investigated such as dipping time of the specimen in the precursor solution, the ratio of boric acid and urea in the precursor, the concentration of solution where the precursor was dissolved, and the cycle of dipping and dry process. The CMCs was fabricated through polymer impregnation and pyrolysis (PIP) processes and a three-point flexural strength test was conducted to verify the role of the coated h-BN interphase.

• 한국전기전자재료학회논문지
• /
• 제20권11호
• /
• pp.991-994
• /
• 2007

In this paper, we have designed the anti-reflection(AR) coating for $1400{\sim}1600$ nm wavelength range on the ferrule facet of optical connector. The low-temperature ion-assisted deposition was applied to AR coating on the ferrule facet in order to avoid damage of optical connector. We have measured the refractive index of coating film($Ta_2O_5\;and\;SiO_2$) using the ellipsometer and optimized the film thickness using the SEM and thickness measurement equipment. UV-VIS-NIR spectrophotometer is used to measure transmissivity of the AR coated ferrule facet. The refractive index of $Ta_2O_5\;and\;SiO_2$ is $2.123{\sim}2.125$ and $1.44{\sim}1.442$, respectively, for $1400{\sim}1600$ nm wavelength range. The transmissivity of the AR coated ferule facet is more than 99.8 % for $1425{\sim}1575$ nm wavelength range and more than 99.5 % for $1400{\sim}1600$ nm wavelength range. The return loss of the AR coated ferrule facet is 30.1 dB.

• 한국정밀공학회지
• /
• 제26권9호
• /
• pp.121-126
• /
• 2009

Stainless steel 316L (STS 316L) is widely used as a material of biopsy needle. However it has a side effect that tissue can be damaged by electrochemical operation between tissue and STS 316L. Many studies have been made on the ceramic coating of biopsy needle to reduce the side effect. In this study, STS 316L was coated with three bioceramics, $Al_2O_3$, $SiO_2$ and $ZrO_2$ using a RF magnetron sputtering method. The effects of ceramic coating on the electrical conductivity and coating strength of ceramic-coated STS 316L were investigated. The results showed that the electrical conductivity of ceramic-coated STS 316L was much lower than that of uncoated STS 316L. The coating strength of $ZrO_2$-coated STS 316L was 30% and 70% higher, respectively than those of $Al_2O_3$-coated STS 316L and $SiO_2_3$-coated STS 316L.

• Journal of Welding and Joining
• /
• 제23권6호
• /
• pp.72-76
• /
• 2005

Friction surfacing of STS304 consumable rod on S45C substrate was investigated by microstructural observation and mechanical tests. STS304 layer formed a strongly-bonded thick layer under a wide range of surfacing conditions. The highest coating eefficiency was obtained in the condition of 1000rpm-2.5mm/sec-2.5mm/sec. The hardness distribution showed the peak value in the boundary layer and as the consumable rotation speed increased, the boundary layer also hardness increasing. As the consumable rotation speed and the traveling speed increased, the coating efficiency tended to decrease. On the other hand, as the feeding speed increased, the coating efficiency appeared to be increased. The new Fe-Cr-Ni alloy layer is showed in the interface layer on $5\~15{\mu}m$ width. After friction surfacing, corrosion resistance of STS 304 surfacing layers were equaled to that of STS304 consumable rod.

• 열처리공학회지
• /
• 제19권2호
• /
• pp.103-108
• /
• 2006

Microstructural evolution of Pt-aluminide coated Ni-based superalloy has been investigated with ductilization heat treatment. The Pt coat was prepared on the superalloy and then aluminide coating was conducted using a pack cementation process. Samples were heat-treated at $1050^{\circ}C$ for 2 hrs and the microstructure and element analysis were preformed. A various precipitated compounds were observed within the coating layer and the diffusion region in the Pt-aluminide coating and heat treatment, indicating that the bi-phase compounds of $PtAl_2$ and NiAl were performed during the Pt-aluminide coating, whereas $M_{23}C_6$, MC, $Ni_3Al$ and ${\sigma}$ phases were precipitated in the inter-diffusion region. The bi-phase compounds of $PtAl_2$ and NiAl were transformed into the single phase compound of $PtAl_2$ with the heat treatment, increasing the amount of carbide and ${\sigma}$ phase.

• 염색가공
• /
• 제2권
• /
• pp.39-50
• /
• 2007

• 한국고분자학회지:고분자과학과기술
• /
• 제17권2호
• /
• pp.217-225
• /
• 2006