• Journal of the Korean Society of Tobacco Science
• /
• v.17 no.1
• /
• pp.15-19
• /
• 1995

This study was made of the effects from exposure to air temperature and amount of solar radiation during the wilting period on the sunburn of burley tobacco. Tobacco stalks were cult with one hour interval from 8:00 to 16:00, and were left on the field to expose to weather, and tobacco single leaf placed under 4 temperatures regimes in indoor. Sun-burn of the leaves was occurred when the leaves were exposed to temperature higher than 33$^{\circ}C$, and to solar radiation more than 800w/$m^2$ between 11:00-15:00 in a day during the curing season. The leaf temperature was increased until 52$^{\circ}C$ under the weather condition. The tobacco leaves were also burned without solar radiation when the leaves were exposed to high temperature until 5$0^{\circ}C$ of leaf temperature. Sun-bum was increased at upper leaves and at higher moisture content of leaf.

• Journal of the Korea Concrete Institute
• /
• v.14 no.6
• /
• pp.942-948
• /
• 2002

When fresh concrete is exposed to low temperature, the concrete may suffer frost damage due to freezing at early ages and the strength development may be delayed. One of the solution methods to resolve these problems is to reduce freezing temperature of concrete by the use of chemical admixture called Accelerator for freeze protection. In this study we Investigate the effect on the strength development of cement mortar using accelerator for freeze protection with the variable curing condition. As the result of this study, the mortar using accelerator for freeze protection show continuously the strength development in curing condition of -5$^{\circ}C$. And the compressive strength under variable temperature condition was higher than constant temperature condition in same maturity.

• Journal of the Korea Concrete Institute
• /
• v.25 no.3
• /
• pp.295-304
• /
• 2013

Ultra-High Performance Concrete (UHPC) has recently been one of the most active research fields in Korea as well as in foreign countries, because it can contribute to a longer life and economic efficiency of structures. Although precast-type UHPC fabricated in a factory is preferable in terms of quality control and reduction of construction period, there exist, even in the precast structure, some parts that need to be cast in-place such as the joints between precast segments. In the cast-in-place UHPC, however, it is probable that an optimum curing condition can hardly be realized in contrast to the factory production. In this study, therefore, the trend of compressive strength development of UHPC was experimentally investigated by assuming various inferior curing conditions that may be anticipated at a construction site. Concrete specimens were fabricated and cured under different conditions with the variables such as curing temperature, delay time before the initiation of curing, duration of curing time and moisture condition. The strengths were compared with those of the specimens cured by standard high temperature steam. Through the analysis of the test results, some minimum requirements for curing have been proposed that are required when the UHPC is cast in-place. It is expected, through this study, that practical use of UHPC in construction sites can be increased.

• Membrane Journal
• /
• v.14 no.3
• /
• pp.207-217
• /
• 2004

In this study, we prepared nanofiltration membrane by applying the interfacial polymerization method as a way of manufacturing composite membranes. We have examined the effects of various preparation factors such as monomer concentration and composition, thermal curing condition, post treatment condition. In addition to preparation conditions, we also monitored the effects of operation conditions such as feed solution concentration and operation pressure on the permeation properties of the resulting nanofiltration membrane. We intended to increase the permeation rate of nanofiltration membrane by the enlargement of effective surface area using additives during interfacial polymerization step. With increasing the monomer concentration, membrane permeation rate are decreased with maintaining almost constant rejection. With respect to curing condition, with increasing the curing temperature both permeation rate and rejection are decreased. With increasing the ratio of MPD in amino monomer composition, permeation rate decreased drastically with high rejection. With increasing the feed solution concentration, both permeation rate and rejection decreased. Both permeation rates and rejection increased with increasing the operating pressure. Nanofiltration membrane have higher surface roughness with increasing additive concentration in the case of using MPD contained amine composition than using piperazine alone. Permeation rates are much lower than the nanofiltration membrane prepared by piperazine.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.34 no.3
• /
• pp.235-238
• /
• 1989

This study was carried out to investigate the effect of environmental conditions of air temperature and relative humidity, varieties, and water content of leaves at harvesting time on the occurrence of barn rot during curing of burley tobacco. The curing environmental condition was combined with 4 air temperatures ranging from 25$^{\circ}C$ to 40$^{\circ}C$ and 3 different relative humidities. The harvested leaves with 3 different water contents were cured during the rainy season in curing barn. Barn rot occurred the most at 30$^{\circ}C$, and reduced at 25$^{\circ}C$ and remarkably decreased at above 35$^{\circ}C$. But no barn rot was observed at 40$^{\circ}C$. In influence of relative humidity, the percentage of rotten leaves was highest at 100% RH and remarkably reduced at lower RH. Among two varieties, KB 101 was rotted smaller than Burley 21 under the all temperature and relative humidity conditions, however those considerably showed no difference. The rate of disease development increased in the lower leaves more than in the upper leaves. In the water content of leaves at harvesting time, 29.5% of the rotten leaves was observed at W.S.D. (water saturation deficit) 10.3%, but no barn rot was found at W.S.D. 6.4%.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.251-257
• /
• 2018

There are various quality deteriorations of concrete such as plastic, drying shrinkage due to abrupt moisture evaporation, slump loss and cold joint under hot weather condition. To protect from above deteriorations, several kinds of modified bubble sheets have been applied to secure heat insulation performance. But, there is not enough application cases of bubble sheets at job site under hot weather condition. The objective of the paper is to investigate the temperature profile and crack occurrence of the concrete covered with five different kinds of surface curing sheets, which is placed under hot weather condition. Single layer transparent bubble sheet, white colored bubble sheet, aluminum metalizing bubble sheet and PE film are adopted for surface curing sheets. Test results indicated that application of aluminum metalizing bubble sheet had most favorable effect on the reduction of on temperature rise and on the crack reduction of concrete. But due to larger reflection of light by aluminum, it brings about visual pollution to the workers. Hence, the application of white colored bubble sheet can be the most desirable alternative to protect the concrete from hot weather in the field.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.65 no.1
• /
• pp.53-56
• /
• 2016

Because of the low pollution resistance of the porcelain electrical insulator itself, in this work the anti-pollution performance of insulator was improved by using the functional coating. The ceramic substrates that components were same as the porcelain electrical insulator were used in this experiment. The functional films were coated on the ceramic substrate by using a spray coating method, and then the coated substrate were annealed under different coating condition such as natural curing and annealing temperature of $200^{\circ}C$, $300^{\circ}C$ and $400^{\circ}C$. Then, the contact angles of the coated surfaces were measured and the minimum angle ($8.3^{\circ}$) was obtained at $400^{\circ}C$. The anti-contamination properties were measured, revealing that as the contact angle decreased, the anti-contamination properties improved. The hardness and adhesion were small at the natural curing condition however the excellent mechanical properties were obtained under higher temperature annealing.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.6
• /
• pp.1080-1086
• /
• 2007

The aim of this paper is to establish the optimum fabrication condition of specimens, using the Vapor Deposition Polymerization Method(VDPM), which is one of modesto prepare functional organic thin films using a dry process, and to develop a thin film type humidity sensor which has good humidity sensitive characteristics. The inner part of the film became denser and roughness of the film surface eased as curing temperature increased so that thickness of the film could be made uniform. This also shows the appropriate curing temperature was $250^{\circ}C$. The basic structure of the humidity sensor is a parallel capacitor which consists of three layers of Aluminum/Polyimide/Aluminum. The result of SEM and AFM measurement shows that the thickness of PI thin films decreased and the refraction increased as curing temperature increased, which indicates that a capacitance-type humidity sensor utilizing polyimide thin film is fabricated on a glass substrate. The characteristics of fabricated samples were measured under various conditions, and the samples had linear characteristics in the range of 20-80 %RH, independent of temperature change, and low hysteresis characteristic.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.10 no.1
• /
• pp.17-24
• /
• 2008

Many problems exist in the current cast in place concrete lining used in domestic tunnel construction. Especially, the crack of tunnel lining brings about a social and economic problem. It has a lot of influence on stability of structure and the fine finish of lining. So enormous repair-work and reinforcement of tunnel lining could occur an running out of government's budget. In our country, there are domestic production enterprises which produce a special pre-cast concrete product, but the technical level of them is still far behind compared to developed countries. Also, optimum steam coring method is important for the production of high quality product. But there is no regulation of steam curing method in our country. This study is to investigate the properties of PC panel according to the variation of steam curing conditions such as presteaming time and rate of temperature rise. The result shows that the optimum presteaming time of steam curing method in PC panel is more than 1 hour and the desirable rate of temperature in curing chamber is about $20^{\circ}C/hr$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.6
• /
• pp.278-285
• /
• 2006

Coating mixtures of the resin B-H for the application to the desulfurization system of power plant were coated on carbon steels and cured at the temperature of $65^{\circ}C{\sim}80^{\circ}C$. After being contacted with 70wt% $H_2SO_4$ solution of $100^{\circ}C\;and\;120^{\circ}C$ for several hours, their composition, Vicker's hardness and microstructures by SEM were examined. Corrosion resistance of the coating mixtures to $H_2SO_4$ solution was related to the content of $SO_3$ in the coated specimens after corrosion test. The lower curing temperature and the shorter curing time the coated specimens went through, the higher corrosion resistance to acid they showed, but the more cracks were developed at higher temperature. It was realized that the corrosion resistance to sulfaric acid solution was increased on the condition of curing temperature above $65^{\circ}C$ and curing time above 12 hours at least.