$Cu(In_xGa_{1-x})Se_2$ thin films were prepared and characterized with various Ga contents. As the Ga content increased, the grain size of CIGS film became smaller. The 2 $\theta$ values in XRD patterns were shifted to larger values and the overlapped peaks were splitted. The energy bandgap increased from 1.04 to 1.67 eV and the resistivity decreased. The solar cell fabricated with ZnO/CdS/$Cu(In_{0.7}Ga_{0.3})Se_2/Mo$ structure yielded an efficeincy of 14.48% with an acitive area of 0.18 $cm^2$. The efficiency decreased with further increase of Ga content.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.05a
• /
• pp.13-13
• /
• 1996

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.1
• /
• pp.1-4
• /
• 2007

The total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcinations process and XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcinations was improved to be 2.8um by applying slot-die coating method. In particular, addition of Samarium shows critical current of $I_c=273A/cm-w(J_c=3.8MA/cm^2)$. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solution in MOD process.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.877-887
• /
• 1994

Cu-Ni-Si-P alloys have been studied in order to develop connector material which has a favorable combination of strength, electrical conductivity, elastic limit, thermal softening resistence and bend formability. Three kinds of trial alloys with various nickel and silicon content were melted and cast, hot rolled at about $900^{\circ}C$ and cold rolled. Mechanical properties and electrical conductivities of these alloys annealed at $450^{\circ}C$, $500^{\circ}C$ and $550^{\circ}C$ were investigated. An alloy with the composition of Cu-2.7%Ni-0.53%Si-O.O29%P, which shows a favorable combination of high strength and high electrical conductivity, has been developed. Various characteristics of the alloy 1 connector material were evaluated and compared with phospher bronze(C521OR-H) and brass(C26OOR-EH) connector material.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.5
• /
• pp.314-320
• /
• 2021

Controlling ambient humid condition through high performance humidity sensors has become important for various fields, including industrial process, food storage, and the preservation of historic remains. Although aerosol deposited humidity sensors using ceramic BaTiO₃ (BT) material have been widely studied because of their longtime stability, there remain critical disadvantages, such as low sensitivity, low linearity, and slow response/recovery time in case of the sensors fabricated at room temperature. To achieve superior humidity sensing properties even at room temperature condition, BT-Cu composite films utilizing aerosol deposition (AD) process have been proposed based on the percolation theory. The BT-Cu composite films showed gradually improved sensing properties until the Cu concentration reached 15 wt% in the composite film. However, the excessive Cu (above 30 wt%) containing BT-Cu composite films showed a rapid decrease of the sensing properties. The results of observed surface morphology of the AD fabricated composite films, to figure out the metal filler effect, showed correlation between surface topography as well as size and the amount of open pores according to the metal filler content. Overall, it is very important not only dielectric constant of the humidity sensing films but also microstructures, because they affect either the variation range of capacitance by ambient humidity or adsorption/desorption of ambient humidity onto/from the humidity sensing films.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2004.12a
• /
• pp.3-11
• /
• 2004

The power loss analysis was carried out for Ni-Cu-Zn ferrite samples with different content of NiO and ZnO. The power loss, Pcv decreases monotonically wi increasing temperature and attains to a certain value at around $100\~120$ degrees Celsius. The frequency dependence of Pcv can be explained by $Pcv\~f^n$', and n is independent of the frequency, f up to 1MHz. The Pcv decreases with an increase in ZnO/NiO. The Pcv was separated to hysteresis loss, Ph and residual loss, (Pcv-Ph). The temperature characteristics and compositional dependence of Pcv can be attributed to the Ph, while (Pcv-Ph) is not affected by both temperature and ZnO/NiO. By analyzing temperature and composition dependence of Ph and initial permeability, ${\mu}^i$ following equations could be formularized. $${\mu}_i{\mu}o=I_x\;^2/(K_1+bs_ol_s)\;\;\;\;(1)$$ $Wh=13.5(I_s\;^2/{\mu}_i{\mu}_o)\;\;\;\;(2)$$ Were ${\mu}_o$ is permeability of vacuum, $I_s$ saturation magnetization, $K_1$ anisotropy constant, $S_o$ internal heterogeneous stress, $I_s$, magnetostriction constant, b unknown constant. Wh hysteresis loss per one cycle of excitation (Ph: Wh*f). Steinmetz constant of Ni-Cu-Zn ferrites, $m=1.64\~2.2$ is smaller than the one of Mn-Zn ferrites, which suggests the difference of loss mechanism between these materials.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.4
• /
• pp.175-180
• /
• 2011

The doping effect of Cu in the Sr-doped lanthan manganites (LSM) has been investigated in terms of structural analysis and thermal expansion coefficient (TEC). The $La_{0.8}Sr_{0.2}Mn_{1-x}Cu_xO_3$ ($0{\leq}x{\leq}0.3$) were prepared by solid state reaction method and their crystal structure and TEC were measured. A decrease in the lattice parameters and the TEC were observed with increase eu content, whereas they were decreased for x = 0.3. For $0{\leq}x{\leq}0.2$, the decrease of the lattice parameter and the TEC with increase Cu content were attributed to the reduction of ionic radius of Cu ions due to the presence of $Cu^{3+}$ ions. For x = 0.3, however, the increase was originated from the formation of oxygen vacancies due 10 the presence of $Cu^{2+}$ and $Mn^{4+}$.

• Journal of the Korean institute of surface engineering
• /
• v.14 no.1
• /
• pp.5-9
• /
• 1981

The effects of silicon content on the corrosion rates of Cu-7wt% Al alloys have been investigated by the use of electrochemical methods. The corrosion current densities of the alloys are decreased with the addition of Si up to 2wt%, and the slightly increased at 2.5%Si. This increased corrosion rates are attributed to the precipitation of more anodic gamma-2 phase. The X-ray diffraction tests reveal the dealuminumification of these alloys and mixtures of CuCl and Al2O3 formed on the surface of the specimens, which are considered to passivate the alloys at noble potentials.

• Journal of the Korean Ceramic Society
• /
• v.39 no.12
• /
• pp.1119-1123
• /
• 2002

Nanostructured spinel NiZn ferrites were prepared by the sol-gel method from metal nitrate raw materials. Analyses by X-ray diffraction and scanning electron microscopy showed the average particle size of NiZn ferrite was under 50 nm. The single phase of NiZn ferrites was obtained by firing at 250${\circ}C$, resulting in nanoparticles exhibiting normal ferrimagnetic behavior. The nanostructured $Ni_{1-X}Zn_XFe_2O_4$ (x=0.0∼1.0) were found to have the cubic spinel structure of which the lattice constants ${\alpha}_2$ increases linearly from 8.339 to 8.427 ${\AA}$ with increasing Zn content x, following Vegard's law, approximately. The saturation magnetization $M_s$ was 48 emu/g for x=0.4 and decreased to 8.0 emu/g for higher Zn contents suggesting the typical ferrimagnetism in mixed spinel ferrites. Pure NiZn ferrite phase substituted by Cu was observed before using the additive but hematite phase was partially appeared at $Ni_{0.2}Zn_{0.2}Cu_{0.6}Fe_2O_4$. On the other hand, the hematite phase in this NiZn Cu ferrite was disappeared after using the additive of acethyl aceton with small amount. The saturation magnetization Ms of $Ni_{0.2}Zn_{0.8-y}Cu_yFe_2O_4$(y=0.2∼0.6) as measured was about 51 emu/g at 77K and 19 emu/g at room temperature, respectively.

• Korean Journal of Environmental Agriculture
• /
• v.13 no.1
• /
• pp.10-17
• /
• 1994

To investigate differences with the polluted sources on Cu contents in soils and paddy rices under water pollutions, soils with the distance, the surface(0-15㎝ depth) and subsurface(15-30㎝ depth) in 1982 and 1990, and rice plants at the soil sampling sites in 1990 were separately sample at Mangyeong River area under the influence of municipal and industrial waste water from Jeonju city. Soil samples were extracted with $4M-HNO_3$ and plant samples were digested with mixture of $HNO_3$ and $HClO_4$ for analyzing Cu, Cd, Zn, Pb by atomic absorption spectrophotometry. Cu contents in soils ranged from 5.20 to 71.70 mg $kg^{-1}$. Average Cu level in 1990 was higher than that in 1982. Variation of Cu content with the distances from the source of waste water in 1990 was more regularly decreased than that in 1982. A significant correlation was observed between Cu contents in leaf sheath of rice plant and Cu, Zn and Pb contents in soils. Cu contents in soil was correlated with Zn and Pb in soil at area affected by waste water, regardless of years and soil depths. Cu contents in brown rice ranged from 0.4 to 10 mg $kg^{-1}$, and it was the lowest in parts of rice plant, and Cu content in panicle axis was 2.3 times higher than that in brown rice.