• BMB Reports
• /
• v.28 no.2
• /
• pp.170-176
• /
• 1995

Rhodanese from mouse liver was purified to near homogeneity by ammonium sulfate precipitation, CM-Sephadex ion exchange, hydroxyapatite and Sephacryl S-200-HR gel filtration chromatographies with a purification of 776 folds. The molecular weight was determined by Sephadex G-150 gel filtration and found to be 34.8 KDa. SOS-PAGE showed molecular weight 34 KDa and two identical subunits splitting by aging for 3 weeks at $-70^{\circ}C$ the molecular weight of which was 17 KDa. The optimal pH of enzyme activity was 9.4 and the pI value of the enzyme was 6.6. Rhodanese showed the optimal reaction temperature of $25^{\circ}C$ and near linear increasing pattern until 10 min. incubation. $K_m$ values of rhodanese for KCN and $Na_{2}S_{2}O_{3}$ as substrates were 12.5 mM and 8.3 mM, respectively. Rhodanese activity was inhibited by more than 70% at a concentration of 100 ${\mu}M$ of $Ni^{2+}$, $Zn^{2+}$, $Cd^{2+}$, $Hg^{2+}$ and $Cu^{2+}$. Other metal ions, such as $Mn^{2+}$, $Mg^{2-}$, $Ca^{2+}$, and $Fe^{2+}$ showed no effect on rhodanese activity.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.119-125
• /
• 2007

We investigated recovery in $Au/YBa_2Cu_3O_7$ (YBCO) thin film meander lines on sapphire substrates. The meander lines were fabricated by patterning YBCO films coated with gold layers. The lines were subjected to simulated AC fault current and then small current was applied for recovery measurements. The samples were immersed in liquid nitrogen during the experiment. After the fault, the resistance decreased linearly, first slowly and then fast to zero. The initial slow decrease was due to the decrease of the meander line temperature, whereas the fast decrease was originated from the transition from the normal state to the superconducting state. The recovery speed depended on the size of samples, and was faster in the smaller samples during the whole period of recovery. The experimental results were analyzed quantitatively with the concept of heat transfer within the sample and to the surrounding liquid nitrogen. A heat balance equation was solved for the initial phase of recovery, and an expression for the time dependence of resistance was obtained. The result agreed with data well.

• Journal of Applied Biological Chemistry
• /
• v.42 no.1
• /
• pp.12-18
• /
• 1999

Sucrose synthase (EC 2.4.1.13) has been purified from the plant cytosolic fraction of chickpea (Cicer arietinum L. cv. Amethyst) nodules. The native enzyme had a molecular mass of $356{\pm}15kD$. The subunit molecular mass was $87{\pm}2kD$, and a tetrameric structure is proposed for sucrose synthase of chickpea nodule. Optimum activities in the sucrose cleavage and synthesis directions were at pH 6.5 and 9.0, respectively. The purified enzyme displayed typical hyperbolic kinetics with substrates in cleavage and synthesis reactions. Chickpea nodules sucrose synthase had a high affinity for UDP ($K_m$, $8.0{\mu}M$) and relatively low affinities for ADP ($K_m$, 0.23 mM), CDP ($K_m$, 0.87 mM), and GDP ($K_m$, 1.51 mM). The $K_m$ for sucrose was 29.4 mM. In the synthesis reaction, UDP-glucose ($K_m$, $24.1{\mu}M$) was a more effective glucosyl donor than ADP-glucose ($K_m$, 2.7 mM), and the $K_m$ for fructose was 5.4 mM. Divalent cations, such as $Ca^{2+}$, $Mg^{2+}$, and $Mn^{2+}$, stimulated the enzyme activity in both the cleavage and synthesis directions, and the enzyme was very sensitive to inhibition by $HgCl_2$ and $CuSO_4$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.1080-1083
• /
• 2002

In this paper, we have studied with regard to the use of lasers for modifying the surface properties of silicon in order to improve it's wettability and adhesion characteristics. Using an Nd:YAG pulse laser, the wettability and adhesion characteristics of silicon surface have been developed by an Nd:YAG pulse laser. It was found that the laser treatment of silicon surfaces modified the surface energy. In the result of wetting experiments, by the sessile drop technique using the distilled water, wetting characteristic of silicon after the laser irradiation shows a decreased value of the contact angle. In case of the laser treated silicon surface, laser direct writing of copper lines has been achieved by pyrolytic decomposition of copper formate films$(Cu(HCOO)_2{\cdot}4H_2Q)$, using a focused $Ar^+$ laser beam$(\lambda=514.5nm)$ on the silicon substrates. The deposited patterns were measured by energy dispersive X-ray(EDX), Scanning Electron Microscopy(SEM) and surface profiler($\alpha$-step) to examine the cross section of deposited copper lines and linewidth.

• Electrical & Electronic Materials
• /
• v.28 no.2
• /
• pp.25-33
• /
• 2015

Ruthenium (Ru) thin films were grown on thermally-grown $SiO_2$ substrates by atomic layer deposition (ALD) using a sequential supply of four kinds of novel zero-valent Ru precursors, isopropyl-methylbenzene-cyclohexadiene Ru(0) (IMBCHDRu, $C_{16}H_{22}Ru$), ethylbenzen-cyclohexadiene Ru(0) (EBCHDRu, $C_{14}H_{18}Ru$), ethylbenzen-ethyl-cyclohexadiene Ru(0) (EBECHDRu, $C_{16}H_{22}Ru$), and (ethylbenzene)(1,3-butadiene)Ru(0) (EBBDRu, $C_{12}H_{16}Ru$) and molecular oxygen (O2) as a reactant at substrate temperatures ranging from 140 to $350^{\circ}C$. It was shown that little incubation cycles were observed for ALD-Ru processes using these new novel zero-valent Ru precursors, indicating of the improved nucleation as compared to the use of typical higher-valent Ru precursors such as cyclopentadienyl-based Ru (II) or ${\beta}$-diketonate Ru (III) metallorganic precursors. It was also shown that Ru nuclei were formed after very short cycles (only 3 ALD cycles) and the maximum nuclei densities were almost 2 order of magnitude higher than that obtained using higher-valent Ru precursors. The step coverage of ALD-Ru was excellent, around 100% at on a hole-type contact with an ultra-high aspect ratio (~32) and ultra-small trench with an aspect ratio of ~ 4.5 (top-opening diameter: ~ 25 nm). The developed ALD-Ru film was successfully used as a seed layer for Cu electroplating.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.124-128
• /
• 1999

We report microwave properties of high-T$_c$ superconducting (HTS) microstrip antennas without impedance matching circuits, where the impedance mismatching is obvious under the critical temperature (T$_c$). The superconducting thin films used in this report were YBa$_2Cu_3O_{7-x}$ (YBCO) films deposited on MgO substrates produced by pulse laser deposition (PLD) technique. At around T$_c$, 86 K the reflection coefficient rapidly drops, and the standing wave ratio (SWR) becomes almost unity, and the characteristic impedance based on the Smith chart is nearly 50 ${\Omega}$. The reflection coefficient and the SWR of the HTS microstrip antenna were - 62.52 dB and 1.0015, respectively, at the resonant frequency of 11.812 CHz at 86 K.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.87-90
• /
• 1999

We have studied the annealing effects of 570 (SrTiO$_3$) single crystal substrate and the I-V properties of step-edge junctions after Ar ion milling. YBa$_2Cu_3O_7$ (YBCO) thin films are fabricated on the substrates by using pulsed laser deposition (PLD) and photolithography. The surface of Ar ion milled substrate was characterized with atomic force microscope (AFM) and scanning electron microscope (SEM) images. After the substrate was damaged by milling, the critical current density of YBCO thin films deposited on the substrate was lowered. The annealing of the damaged substrate at about 1000 $^{\circ}C$ recovered the critical current density to that before the milling. Futhermore the annealing helped junction formation due to high quality film and increased the yield rate for the fabrication of high quality step-edge junction.

• Progress in Superconductivity
• /
• v.6 no.1
• /
• pp.19-23
• /
• 2004

YBCO do superconducting quantum interference device (SQUID) magnetometers based on bicrystal Josephson junctions on 10 mm ${\times}$ 10 mm $SrTiO_3$ substrates have been fabricated. The pickup coil of the device was designed to have 16 parallel loops with 50-fm-wide lines. We could obtain optimised direct coupled YBCO SQUID magnetometer design with field sensitivity $B_{N}$ $\Phi$/ of $4.5 nT/\Phi_{0}$ and magnetic field noise $B_{N}$ of about $22 fT/Hz^{1}$2/ with an I/f corner frequency of 2 Hz measured inside a magnetically shielded room. Preliminary results of magnetocardiograph measurement using the HTS SQUID magnetometers show signal to noise ratio of about 110, which is comparable to the quality of a commercial MCG system based on Nb-SQUIDs.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.142-146
• /
• 1999

CeO$_2$ buffer layers and in-situ YSa$_2Cu_3O_{7-{\delta}}$ (YBCO) thin films were grown by pulsed laser deposition method on R-plane sapphire substrates. Superconducting properties and surface morphologies of YBCO thin films exhibit strong dependence on the crystallinity of CeO$_2$ buffer layer. The best a-axis oriented CeO$_2$ buffer layers could be grown at 800 $^{\circ}C$ of deposition temperature, 1.5 J/ cm$^2$ of laser energy density and 50 mTorr of oxygen pressure. The YBCO thin films on the a-axis CeO$_2$ buffer layer have Tc (R=0) ${\ge}$ 89.5 K, ${\delta}$Tc ${\sim}$ 0.5 K, and Jc ${\ge}$ 3.2 ${\times}$ 10$^6$ A/ cm$^2$ at 77 K.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.308-312
• /
• 2007

Chromium oxide thin films have been deposited on silicon substrates using a tabletop 9kJ mathertyped plasma focus (PF) device. Before deposition, pinch behavior with gas pressure was observed. Strength of pinches was increased with increasing working pressure. Deposition was performed at room temperature as a function of working pressure between 50 and 1000 mTorr. Composition and surface morphology of the films were analyzed by Auger Electron Spectroscopy and Scanning Electron Microscope, respectively. Growth rates of the films were decreased with pressure. The oxide films were polycrystalline containing some impurities, Cu, Fe, C and revealed finer grain structure at lower pressure.