• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1292-1295
• /
• 2004

본 연구는 Cu CMP공정 중 알루미나 연마입자의 wafer 표면에서의 점착과 오염을 AFM (Atomic Force Microscopy)을 사용하여 슬러리내에서 점착력 측정과 실제 연마 후 wafer 표면의 오염을 실험적으로 비교 평가하였다. 연마입자의 adhesionn force 측정에 있어서도 역시 wafer들의 zetapotential 결과와 잘 일치하였으며, 모든 wafer 종류에 관계없이, 산성 영역에서 염기성영역의 슬러리가 적용됨에 따라 adhesion force가 작아짐을 확인할 수 있었다. 특히 FSG wafer의 zetapotential 결과는 비록 산성 분위기에서는 양성 전하값을 나타내었으나, 염기성 분위기의 pH에서는 급격하게 음성 전하값을 나타내었고, 이는 adhesionn force결과와 FESEM 결과와 잘 일치하였다.

• Journal of Welding and Joining
• /
• v.30 no.3
• /
• pp.26-31
• /
• 2012

Three-dimensional integrated circuit (3D IC) technology has become increasingly important due to the demand for high system performance and functionality. We have evaluated the effect of Buffered oxide etch (BOE) on the interfacial bonding strength of Cu-Cu pattern direct bonding. X-ray photoelectron spectroscopy (XPS) analysis of Cu surface revealed that Cu surface oxide layer was partially removed by BOE 2min. Two 8-inch Cu pattern wafers were bonded at $400^{\circ}C$ via the thermo-compression method. The interfacial adhesion energy of Cu-Cu bonding was quantitatively measured by the four-point bending method. After BOE 2min wet etching, the measured interfacial adhesion energies of pattern density for 0.06, 0.09, and 0.23 were $4.52J/m^2$, $5.06J/m^2$ and $3.42J/m^2$, respectively, which were lower than $5J/m^2$. Therefore, the effective removal of Cu surface oxide is critical to have reliable bonding quality of Cu pattern direct bonds.

• Korean Journal of Metals and Materials
• /
• v.46 no.5
• /
• pp.321-327
• /
• 2008

Cu based amorphous ($Cu_{54}Zr_{22}Ti_{18}Ni_6$) coating was produced by cold spraying as a new fabrication process. The microstructure and macroscopic properties of amorphous coating layer was investigated and compared with those of cold sprayed pure Cu coating. Amorphous powders were prepared by gas atomization and Al 6061 was used as the substrate plate. X-ray diffraction results showed that Cu based amorphous powder could be successfully deposited by cold spraying without any crystallization. The Cu based amorphous coating layer ($300{\sim}400{\mu}m$ thickness) contained 4.87% porosity. The hardness of Cu based amorphous coating represented $412.8H_v$, which was correspond to 68% of the hardness of injection casted bulk amorphous material. The wear resistance of Cu based amorphous coating was found to be three times higher than that of pure Cu coating. The 3-point bending test results showed that the adhesion strength of Cu based amorphous coating layer was higher than that pure Cu coating. It was also observed that hard Cu base amorphous particle could easily deform soft substrate by particle collisions and thus generated strong adhesion between coating and substrate. However, the amorphous coating layer unexpectedly represented lower corrosion resistance than pure Cu coating, which might be resulted from the higher content of porosity in the cold sprayed amorphous coating.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.1
• /
• pp.45-50
• /
• 2014

Effects of wet chemical treatment and thermal cycle conditions on the quantitative interfacial adhesion energy of $Cu/SiN_x$ thin film interfaces were evaluated by 4-point bending test method. The test samples were cleaned by chemical treatment after Cu chemical-mechanical polishing (CMP). The thermal cycle test between Cu and $SiN_x$ capping layer was experimented at the temperature, -45 to $175^{\circ}C$ for 250 cycles. The measured interfacial adhesion energy increased from 10.57 to $14.87J/m^2$ after surface chemical treatment. After 250 thermal cycles, the interfacial adhesion energy decreased to $5.64J/m^2$ and $7.34J/m^2$ for without chemical treatment and with chemical treatment, respectively. The delaminated interfaces were confirmed as $Cu/SiN_x$ interface by using the scanning electron microscope and energy dispersive spectroscopy. From X-ray photoelectron spectroscopy analysis results, the relative Cu oxide amounts between $SiN_x$ and Cu decreased by chemical treatment and increased after thermal cycle. The thermal stress due to the mismatch of thermal expansion coefficient during thermal cycle seemed to weaken the $Cu/SiN_x$ interface adhesion, which led to increased CuO amounts at Cu film surface.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1997.10a
• /
• pp.78-78
• /
• 1997

• Journal of Radiation Industry
• /
• v.4 no.4
• /
• pp.335-339
• /
• 2010

In this study, the surface of polyimide (PI) films was modified using ion implantation to enhance its adhesion to a deposited copper (Cu) layer. The surfaces of the PI films were implanted with 150 keV $Xe^+$ ions at fluences varying from $1{\times}10^{14}$ to $1{\time}10^{16}ions\;cm^{-2}$. The Cu layers were then deposited on the implanted PI. The surface properties of the implanted PI film were investigated based on the contact angle measurements, Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). Furthermore, the adhesive strength between the deposited Cu layer and PI film was estimated through a scratch test using a nanoindenter. As a result, the surface environment of the PI film was changed by the ion implantation, which could have a significant effect on the adhesion between the deposited Cu layer and the PI.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.7
• /
• pp.929-933
• /
• 2010

Four-point bending tests were performed to investigate the interfacial adhesion of Cu-Cu bonding fabricated by thermo-compression process for three dimensional packaging. A pair of Cu-coated Si wafers was bonded under a pressure of 15 kN at $350^{\circ}C$ for 1 h, followed by post annealing at $350^{\circ}C$ for 1 h. The bonded wafers were diced into $30\;mm\;{\times}\;3\;mm$ pieces for the test. Each specimen had a $400-{\mu}m$-deep notch along the center. An optical inspection module was installed in the testing apparatus to observe crack initiation at the notch and crack propagation over the weak interface. The tests were performed under a fixed loading speed, and the corresponding load was measured. The measured interfacial adhesion energy of the Cu-to-Cu bonding was $9.75\;J/m^2$, and the delaminated interfaces were analyzed after the test. The surface analysis shows that the delamination occurred in the interface between $SiO_2$ and Ti.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.84-84
• /
• 2012

소자가 고집적화 됨에 따라, 비저항이 낮고 electro migration (EM), Stress Migration (SM) 특성이 우수한 구리(Cu)를 배선재료로서 사용하고 있다. 그러나, 구리는 Si과 $SiO_2$의 내부로 확산이 빠르게 일어나, Si 소자 내부에 deep donor level을 형성하고, 누설 전류를 증가시키는 등 소자의 성능을 저하시킬 수 있는 문제점을 가지고 있다. 그러나, electroplating 을 이용하여 증착한 Cu 박막은 일반적으로 확산 방지막으로 쓰이는 TiN, TaN, 등의 물질과의 접착 (adhesion) 특성이 나쁘다. 따라서, Cu CMP 에서 증착된 Cu 박막의 벗겨지거나(peeling), EM or SM 저항성 저하 등의 배선에서의 reliability 문제를 야기하게된다. 따라서 Cu 와 접착 특성이 좋은 새로운 확산방지막 또는 adhesion layer의 필요성이 대두되고 있다. 본 연구에서는 이러한 Cu 배선에서의 접착성 문제를 해결하고자 Metal organic chemical vapor deposition (MOCVD)을 이용하여 제조한 코발트(Co) 박막을 $Cu/TaN_x$ 사이의 접착력 개선을 위한 adhesion layer로 적용하려는 시도를 하였다. Co는 비저항이 낮고, Cu 와 adhesion이 좋으며, Cu direct electroplating 이 가능하다는 장점을 가지고 있다. 하지만, 수소 분위기에서 $C_{12}H_{10}O_6(Co)_2$ (dicobalt hexacarbonyl tert-butylacetylene, CCTBA) 전구체에 의한 MOCVD Co 박막의 경우 탄소, 산소와 같은 불순물이 다량 함유되어 있어, 비저항, surface roughness 가 높아지게 된다. 따라서 구리 전착 초기에 구리의 핵 생성(nucleation)을 저해하고 핵 생성 후에도 응집(agglomeration)이 발생하여 연속적이고 얇은 구리막 형성을 방해한다. 이를 해결하기 위해, MOCVD Co 박막 증착 시 수소 반응 가스에 암모니아를 추가로 주입하여, 수소/암모니아의 분압을 1:1, 1:6, 1:10으로 변화시켜 $Co/TaN_x$ 박막의 특성을 비교 분석하였다. 각각의 수소/암모니아 분압에 따른 $Co/TaN_x$ 박막을 TEM (Transmission electron microscopy), XRD (X-ray diffraction), AES (Auger electron spectroscopy)를 통해 물성 및 조성을 분석하였고, AFM (Atomic force microscopy)를 이용하여, surface roughness를 측정하였다. 실험 결과, $Co/TaN_x$ 박막은 수소/암모니아 분압 1:6에서 90 ${\mu}{\Omega}-cm$의 낮은 비저항과 0.97 nm 의 낮은 surface roughness 를 가졌다. 뿐만 아니라, MOCVD 에 의해 증착된 Co 박막이4-6 % concentration 의 탄소 및 산소 함량을 가지는 것으로 나타났고, 24nm 크기의 trench 기판 위에 약 6nm의 $Co/TaN_x$ 박막이 매우 균일하게 형성된 것을 확인 할 수 있었다. 이러한 결과들은, 향후 $Co/TaN_x$ 박막이 Cu direct electroplating 공정이 가능한 diffusion barrier로서 성공적으로 사용될 수 있음을 보여준다.

• Journal of Adhesion and Interface
• /
• v.4 no.2
• /
• pp.10-20
• /
• 2003

This paper is relative to the electroless deposition of nickel or copper films on polyimide and polytetrafluoroethylene substrates. First, it is presented an original approach of the electroless process which consists in grafting nitrogenated functionalities on the polymer surfaces via plasma or VUV-assisted treatments operating in a nitrogen-based atmosphere ($NH_3$, $N_2$), and then in catalysing the grafted surfaces in an aqueous tin-free, Pd(+2)-based solution. Adhesion of the Pd(+2) catalytic species on polymer surfaces is explained by the formation of strong covalent bonds between these species and the grafted nitrogenated groups. Second, it is show how a fragmentation test performed in conjunction with electrical measurements can be used to characterize the practical adhesion of the electroless coatings deposited on flexible polymer substrates, and to evidence the influence of some experimental parameters (plasma treatment time and nature of the gas phase).

• Journal of the Korean institute of surface engineering
• /
• v.47 no.4
• /
• pp.162-167
• /
• 2014

The primary purpose of this research is to investigate how much the complexing agent in electroless Cu electrolytes will affect adhesion strength between copper film and Ta diffusion barrier for Cu interconnect of semiconductor. The adhesion strength using rochelle's salt as complexing agent was higher than the case of using EDTA-4Na. Effect of complexing agent on adhesion strength and electrical resistivity was studied in crystal structural point of view.