• Journal of Advanced Marine Engineering and Technology
• /
• v.32 no.8
• /
• pp.1240-1247
• /
• 2008

Leakage trouble on the sea water pipeline in engine room is often resulted from a localized corrosion due to severe corrosive environment caused by both high speed and high pressure of sea water flowing through the inner pipe. In addition, when the ship is in stand-by or emergency condition, underwater welding to control the leakage of sea water from a hole of its pipe is very important in an industrial safety point of view. In this study possibility of underwater welding to control leakage of sea water and corrosion property of its welding zone were investigated with the electrochemical methods by parameters of welding methods and welding electrodes when underwater welding is achieved with a such case that sea water is being leaked out with a height at 50mm from a hole of $2.5mm{\emptyset}$ of test pipe. Corrosion resistance of weld metal zone is better than the base metal and its hardness is higher than that of the base metal. However corrosion potential of weld metal zone showed a negative value than that of the base metal, therefore weld metal zone is preferentially corroded rather than the base metal by performance of galvanic cell due to difference of corrosion potential between weld metal zone and base metal. Eventually it is suggested that leakage of sea water is successfully controlled by underwater welding,

• Journal of Aerospace System Engineering
• /
• v.11 no.2
• /
• pp.43-50
• /
• 2017

The sea of the Korean peninsula has undergone various marine changes, including naval vessels, naval operational aircrafts, air force fighters, coastal airports and airfields. In particular, salt directly affected by the marine environment, equipment operating under a high temperature / high speed as the gas turbine is the high temperature corrosion (Hot Corrosion) caused by sulfur components and salinity of the fuel used. When the height of the demister (air intake) is less than 7 m, the salinity of the salt entering the sea increases and the corrosion increases rapidly. In addition, the weapon systems operating in the East Sea than in the West Sea showed a 17% increase in the corrosion rate due to the relatively high salinity scattered by saline, wind, and wave. In order to minimize the salinity inflow, it should be operated at more than 13 m from the sea to minimize rapid hot corrosion.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.137-138
• /
• 2017

The sea of the Korean peninsula has various marine changes, including naval vessels, naval operational aircrafts, air force fighters, coastal airports and airfields. In particular salt directly affected by the marine environment, equipment operating in a high temperature / high speed as the gas turbine is the high temperature corrosion(Hot Corrosion) caused by sulfur components and salinity of the fuel used. When the height of the demister (air intake) is less than 7m, the salinity entering the sea increases and the corrosion increases rapidly. In addition, the weapon systems operating in the East Sea than the West Sea showed a 17% increase in corrosion rate due to the relatively high salinity scattered by saline, wind, and wave. In order to minimize the salinity inflow, it should be operated at more than 13m from the sea to minimize rapid hot corrosion.

• Proceedings of the KSME Conference
• /
• 2007.05b
• /
• pp.2378-2383
• /
• 2007

Direct Numerical Simulation was carried out to predict mass transfer in turbulent flow around a rotating stepped cylinder. This investigation is a follow-up study of Nesic et al. [Corrosion, Vol. 56, No. 10, pp. 1005 - 1014] The original motivation of this work stemmed from the efforts to design a simple device which can generate flows of high turbulence intensity at low cost for corrosion researchers. Two cases were considered; Sc=1 and 10 both at Re=335. Here, Sc and Re stand for Schmidt number and Reynolds number, respectively, based on the step height and the surface speed of the cylinder upstream the step. Main focus was placed on the correlation between turbulent fluctuation and concentration field. The spatio-temporal evolution of concentration field is discussed. The numerical results are qualitatively compared with those of the experiment conducted with the same flow configuration.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.33 no.2
• /
• pp.60-66
• /
• 2005

Corrosion highly affects the lifetime and performance of machinery metallic components. The effects of shot peening on the fatigue life of Al 7075-T6 under corrosive environment are investigated in this paper. Experimental results show that the fatigue limit of shot peened specimen increases about 52%. That means the fatigue life of metallic components is highly extended by shot peening. The corrosion greatly reduces the fatigue strength depending on the corrosive condition from one week up to one year. In case of shot peened specimen, the corrosion does not reduce the fatigue strength and fatigue life up to six months. It means that the shot peening has superior effectiveness to reduce the influence of corrosion to the metallic materials.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.4
• /
• pp.76-82
• /
• 2018

Grout in duct is very effective protection from tendon corrosion in PSC(Prestressed Concrete) structure. In the work, durability and mechanical tests are performed for two types of grout which are conventionally used one and the improved grout with reduced w/c (water to cement) ratio and silica fume. Tendon system with 1000mm height is prepared and various tests including strength, flow, absorption, and bleeding ratio are conducted. ICM(Impressed Current Method) is adopted for corrosion acceleration in tendon with 12.7mm diameter inside grout. For 2 and 4 days, corrosion acceleration is performed for 2 different type of grout and corrosion amount is investigated. The improved grout shows higher compressive strength by 10 MPa and lower absorption ratio by 50% than the conventional one. It also provides an excellent corrosion reduction to 39.8 %~48.2 % for 2~4 days of acceleration period.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.113-113
• /
• 2008

Cu CMP (Chemical Mechanical Planarization) has been used to remove copper film and obtain a planar surface which is essential for the semiconductor devices. Generally, it is known that chemical reaction is a dominant factor in Cu CMP comparing to Silicon dioxide CMP. Therefore, Cu CMP slurry has been regarded as an important factor in the entire process. This investigation focused on understanding the effect of corrosion inhibitor on copper surface and CMP results. Benzotriazole (BTA) was used as a corrosion inhibitor in this experiment. For the surface analysis, electrochemical characteristics of Cu was measured by a potentiostat and surface modification was investigated by X-ray photoelectron spectroscopy (XPS). As a result, corrosion potential (Ecorr) increased and nitrogen concentration ratio on the copper surface also increased with BTA concentration. These results indicate that BTA prevents Cu surface from corrosion and forms Cu-BTA layer on Cu surface. CMP results are also well matched with these results. Material removal rate (MRR) decreased with BTA concentration and static etch rate also showed same trend. Consequently, adjustment of BTA concentration can give us control of step height variation and furthermore, this can be applicable for Cu pattern CMP.

• Journal of Magnetics
• /
• v.4 no.1
• /
• pp.5-9
• /
• 1999

Effect of sulfur segregation on tertiary recrystallization and magnetic induction during final annealing was investigated in a 3% Si-Fe electrical strip containing 6 ppm(LS) and 15 ppm(HS) sulfur. During final annealing, Auger peak height of segregated sulfur on the surface of the strips reached a maximum, and then decreased to low level with increasing annealing time, which is attributed to sulfur segregation and evaporation. The magnetic induction of the thin-gauged 3% Si strip was inversely proportional to the Auger peak height of segregated sulfur on the surface. The overall profile for surface segregation of sulfur and B10 was observed, irrespective of sulfur content in Si-Fe strips, but the peaks of LS strips appeared earlier than those of HS strips. The grain growth rate of the LS strips during final annealing was faster than that of the HS strips, which may be attributed to the pinning effects of segregated sulfur. With increasing final annealing temperature, B10 value increased rapidly and the saturation level in B10 increased.

• Journal of Korean Society of Coastal and Ocean Engineers
• /
• v.22 no.4
• /
• pp.241-247
• /
• 2010

Corrosion of steel embedded in concrete is one of the foremost factors that affect the durability of concrete structures in marine environments. This paper presents an application technique of anode-ladder-system to evaluate corrosion behaviours of marine concrete structure. In order to investigate the behaviours quantitatively, the measurement of potential and current was performed on the concrete elements subjected to the penetration and diffusion of chloride ions. The main variable was the heights from seawater level; namely 3.7, 6.0 and 8.2 m. As a result of the monitoring, it was found that the corrosion characteristics differently behaved with the increasing height. Additionally, through migration test, the relationship between compressive strength of concrete and diffusivity of chloride ions was observed. It is suggested, ultimately, that in order to reduce or mitigate steel corrosion, both appropriate concrete cover depth and high-quality of concrete in early ages should be done.

• Tribology and Lubricants
• /
• v.34 no.6
• /
• pp.226-234
• /
• 2018

Copper chemical mechanical planarization (CMP) has become a key process in integrated circuit (IC) technology. The results of copper CMP depend not only on the mechanical abrasion, but also on the slurry chemistry. The slurry used for Cu CMP is known to have greater chemical reactivity than mechanical material removal. The Cu CMP slurry is composed of abrasive particles, an oxidizing agent, a complexing agent, and a corrosion inhibitor. Citric acid can be used as the complexing agent in Cu CMP slurries, and is widely used for post-CMP cleaning. Although many studies have investigated the effect of citric acid on Cu CMP, no studies have yet been conducted on the interfacial friction characteristics and step height reduction in CMP patterns. In this study, the effect of citric acid on the friction characteristics and step height reduction in a copper wafer with varying pattern densities during CMP are investigated. The prepared slurry consists of citric acid ($C_6H_8O_7$), hydrogen peroxide ($H_2O_2$), and colloidal silica. The friction force is found to depend on the concentration of citric acid in the copper CMP slurry. The step heights of the patterns decrease rapidly with decreasing citric acid concentration in the copper CMP slurry. The step height of the copper pattern decreases more slowly in high-density regions than in low-density regions.