Evaluation of Corrosion Resistance with Grout Type and Tendon

그라우트 품질을 고려한 텐던의 부식저항성 평가

  • Received : 2018.03.16
  • Accepted : 2018.06.30
  • Published : 2018.07.01
Download PDF
⟨ Previous Next ⟩

Abstract

Grout in duct is very effective protection from tendon corrosion in PSC(Prestressed Concrete) structure. In the work, durability and mechanical tests are performed for two types of grout which are conventionally used one and the improved grout with reduced w/c (water to cement) ratio and silica fume. Tendon system with 1000mm height is prepared and various tests including strength, flow, absorption, and bleeding ratio are conducted. ICM(Impressed Current Method) is adopted for corrosion acceleration in tendon with 12.7mm diameter inside grout. For 2 and 4 days, corrosion acceleration is performed for 2 different type of grout and corrosion amount is investigated. The improved grout shows higher compressive strength by 10 MPa and lower absorption ratio by 50% than the conventional one. It also provides an excellent corrosion reduction to 39.8 %~48.2 % for 2~4 days of acceleration period.

PSC 구조에서 덕트 내부의 그라우트는 텐던 부식에 효과적인 부식방어 기재이다. 본 연구에서는 일반적으로 사용되고 있는 그라우트와 낮은 물-시멘트비와 실리카 퓸을 혼입한 그라우트를 대상으로 역학적, 내구적 시험을 수행하였다. 높이 1000mm의 덕트를 이용하여 텐던 시스템을 제작하였으며, 두 가지 그라우트에 대하여 강도, 흡수율, 플로우, 블리딩, 팽창률 등을 평가하였다. 또한 내부 12.7mm 텐던에 대하여 ICM(Impressed Current Method)를 이용하여 2일 및 4일 동안 부식을 촉진시켰으며 부식량을 조사하였다. 개선된 그라우트에서는 10MPa 이상의 높은 강도와 50% 이하의 낮은 흡수율을 나타내었다. 또한 2일~4일 동안의 부식촉진실험에서 39.8%~48.2%의 뛰어난 부식감소율 나타내었다.

Keywords

References

  1. B. Y. Lee, K. T. Koh, M. A. Ismail, H. S. Ryu, and S. J. Kwon. (2017), Corrosion and Strength Behaviors in Prestressed Tendon under Various Tensile Stress and Impressed Current Conditions, Advances in Materials Science and Engineering, 7.
  2. Broomfield, J. P. (1997), Corrosion of Steel in Concrete: Understanding, Investigation and Repair, E&FN, London, 1-15.
  3. F. Li, Y. Yuan, and C.-Q. Li,. (2011), Corrosion propagation of prestressing steel strands in concrete subject to chloride attack, Construction and Building Materials, 25(10), 3878-3885. https://doi.org/10.1016/j.conbuildmat.2011.04.011
  4. H. Shuxian, W. Herbert, H. Rosemarie, D. Biqin, D. Peng, and X. Feng. (2017), Long-term monitoring of reinforcement corrosion in concrete using ground penetrating radar, Corrosion Science, 114(1), 123-32. https://doi.org/10.1016/j.corsci.2016.11.003
  5. Ishida, T., Maekawa, K., and Kishi, T. (2007), Enhanced modeling of moisture equilibrium and transport in cementitious materials under arbitrary temperature and relative humidity history, Cement and Concrete Research, 37(4), 565-578. https://doi.org/10.1016/j.cemconres.2006.11.015
  6. Japan Society of Civil Engineering(JSCE). (2007), Standard Specification for Concrete Structures-Design JSCE Guidelines for Concrete 15, Tokyo, Japan.
  7. Kingsley Lau. (2016), Corrosion of Post-Tensioned Tendons with Deficient Grout, Final report, Florida Department of Transportation Research Center, BDV29-977-04, 202.
  8. KS F 2433 (1972), Standard test method for bleeding and expansion ratios of grouting mortar, KSSN, 1-10.
  9. KS F 2451 (1968), Method of test for waterproof agent and admixture of cement for mortar in building construction, 1-12.
  10. KS F 4044 (2004), Hydraulic cement grout(Nonshrink), KSSN, 1-12.
  11. KS F 4919 (2003), Cement-polymer modified waterproof coatings, 1-19.
  12. KS L 5105 (1966), Testing method for compressive strength of hydraulic cement mortar, 1-9.
  13. L. Dai, L. Wang, J. Zhang, and X. Zhang. (2015) A global model for corrosion-induced cracking in prestressed concrete structures, Engineering Failure Analysis, 62(1), 263-275.
  14. Permeh. S, Krishna Vigneshwaran. K. K, Lau. K, Lasa. I and Paredes. M. (2015), Material and Corrosion Evaluation of Deficient PT Grout with Enhanced Sulfate Concentrations, NACE Corrosion, NACE International, 5828, 13.
  15. Powers, R.G. (1999), "Corrosion Evaluation of Post-Tensioned Tendons on the Niles Channel Bridge," FDOT, Gainesville, FL.
  16. Pradhan, B. (2014), Corrosion behavior of steel reinforcement in concrete exposed to composite chloride-sulfate environment. Construction and Building Materials, 72, 398-410. https://doi.org/10.1016/j.conbuildmat.2014.09.026
  17. RILEM (1997), Avoidance of thermal cracking in concrete at early age, Report of RILEM Technical Committee 199-TCE, E&FN Spon.
  18. S. Baek, W. Xue, M. Q. Feng, and S. Kwon. (2012), Nondestructive corrosion detection in RC through integrated heat induction and IR thermography, Journal of Nondestructive Evaluation, 31(2), 181-190. https://doi.org/10.1007/s10921-012-0133-0
  19. S. H. Kim, J. G. Choi, S. M. Ham, and W. H. Heo. (2016) Reliability evaluation of a PSC highway bridge based on resistance capacity degradation due to a corrosive environment, Applied Sciences, 6(12), 423. https://doi.org/10.3390/app6120423
  20. S. Sakurada, H. Irie, and Y.Yoshida. (2008), Development of reinforced concrete corrosion amount presumption method by ultrasonic method, in Proceedings of the 17thWorld Conference on Nondestructive Testing.
  21. Seung-Kyoung Lee and James Zielske. 2014, An FHWA Special Study: Post-Tensioning Tendon Grout Chloride Thresholds, Federal Highwat Administration, FHWA-HRT-14-039.
  22. Song, H. W., Back, S. J., Lee C. H., and Kwon, S. J. (2006), Service Life Prediction of Concrete Structures Under Marine Environment Considering Coupled Deterioration, Restoration of Buildings and Monuments, 12(4), 265-284.
  23. Song, H. W., Jang, J. C., Saraswathy, V., and Byun, K. J. (2006), An estimation of the diffusivity of silica fume concrete, Building and Environment, 42(3), 1348-1354. https://doi.org/10.1016/j.buildenv.2005.11.007
  24. Song, H. W., Pack, S. W., Nam, S. H., Jang, J. C., and Saraswathy, V. (2010), Estimation of the permeability of silica fume cement concrete, Construction and Building Materials, 24(3), 315-321. https://doi.org/10.1016/j.conbuildmat.2009.08.033
  25. Tazawa E., and Miyazawa S. (1995), Influence of cement and admixture on autogenous shrinkage of cement paste, Cement and Concrete Research, 25, 281-287. https://doi.org/10.1016/0008-8846(95)00010-0
  26. W. Podolny Jr. (1992), Corrosion of prestressing steels and its mitigation, Special Report, Precast Concrete Institute Journal, 37(5), 34-55.
  27. Z. Zhou, J. P. He, G. D. Chen, and J. P. Ou. (2009), A smart steel strand for the evaluation of prestress loss distribution in post tensioned concrete structures, Journal of Intelligent Material Systems and Structures, 20(16), 1901-1912. https://doi.org/10.1177/1045389X09347021