• Journal of the Korea Furniture Society
• /
• v.26 no.1
• /
• pp.22-30
• /
• 2015

In order to prevent decay, distortion, bending, twist on wood products such as wooden furnitures, variety of coating materials were developed and used so far. The coating materials for wood finishing can be synthesized by natural resource or petroleum. However, these coating materials can cause contamination of indoor air quality due to emission of volatile organic compounds (VOCs). In this study, commercialized coating materials for wood finishing such as varnish, coat, and stain were evaluated on emission characteristics of VOCs. Among the varnish, eco-friendly products had about 15~46% lower TVOC emission ($1,042{\mu}g/m^2h{\sim}3,257{\mu}g/m^2h$, respectively, than typical product ($7,100{\mu}g/m^2h$). Natural resource based coating material showed lowest TVOC emission level. However, one of natural resource based waterborne stain showed higher TVOC emission level because waterborne stain already contained higher amount of natural VOC. Oil-based stain might not be suitable for indoor use on interior wall and furniture due to exceed amount of TVOC. Based on results, natural resource based coat or waterborne stain are recommenced to use on wood products.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.5
• /
• pp.1741-1746
• /
• 2010

This study is on development of UV-cured anti-stain coating compounds which have more improved anti-stain function to prevent a surface of PVC tile from stain. To make an anti-stain coating composition, water soluble antistatic agent made from ammonium(IV) salt, antistatic agents for acrylic and polyurethane were used. Their contents varied from 5 to 20wt% against quantities of resin in coating composition. After coating PVC tiles using bar-coating method that can adjust a thickness, we estimated surface properties of coated layer such as anti-stain, electric resistance, adhesive power, thickness of coating, and so on. Results showed that a coating composition added 15wt% of water soluble antistatic agent and coated with No.12 bar-coater had the optimum surface property in electric resistance($3.24{\times}10^9{\Omega}/cm^2$), anti-stain(ink Test, Dust Test) and adhesive power. We could also find electric resistance and anti-stain effect were improved as antistatic agent content increased. However, excessive addition of antistatic agents(over 20wt%) caused the migration.

• Special Issue of the Society of Naval Architects of Korea
• /
• 2009.09a
• /
• pp.18-23
• /
• 2009

After the installation of electric cables at block, PE(pre-erection) and hull stages, the coating stains on the electric cable sheath were unavoidably occurred by additional painting process. According to class rules paint or coating applied on the electric cables shall not adversely affect the mechanical, chemical of fire resistant characteristics of the electric cable sheath. However, there has not been quantitatively studied about the effect of coating stains on properties of sheath materials. In this study, we tried to investigate the effect of coating stains on the performance and deterioration of sheath materials by using FTIR, SEM analysis, flame retardant, high potential voltage and tensile test. The results sowed that coating stains, which were occurred during painting work on site could not adversely affect on the performance and deterioration of sheath materials.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.2
• /
• pp.58-67
• /
• 2006

The relationship between acoustic property and coating hardness of musical instruments was investigated using a sound level meter and a pendulum hardness tester. Urethane topcoat, oil stain, natural oil varnish, and UV-curable epoxy acrylate coatings were applied on four different substrates: Paulownia coreana, Pinus koraiensis, Castanea crenata var. dulcis and Pinus densiflora. The influence of the coating type on the acoustic properties was stronger than that of the substrate. In the case of an oil stain formed with tacky coating layer, the sound pressure level (SPL) and surface hardness decreased with increasing of coating thickness. In the other coatings, SPL decreased and hardness increased as the coating layer thickened. However, SPL began to increase again at coating thickness above $100{\mu}m$.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.9
• /
• pp.3615-3620
• /
• 2010

This study is development of UV-cured coating compounds which has more improved anti-stain and anti-biosis, about surface prevention of PVC Tile. We added water-soluble anti-static and anti-microbial agent to the resin. The process has prevented electrostatic and bacterial contagious disease. The result, which added 15wt% of water-soluble anti-static and 1wt% anti-microbial agent and coated with No.12 Bar-coater, coating composition had optimum surface property. It appear electric resistance($10^9{\Omega}/cm^2$), anti-stain (Ink Test, Dust Test), anti-biosis (99.99%), and adhesive power(100%).

• Transactions of Materials Processing
• /
• v.28 no.2
• /
• pp.71-76
• /
• 2019

Corrosion resistance is one of the essential properties required in steel bolts. The various types of coatings are used to improve the corrosion resistance of steel bolts. But, roll formed, subsequently Zn alloy electrodeposited and top coated steel bolt easily takes place the white storage stain or white rust under high humidity condition. To investigate the corrosion resistance of roll formed and subsequently the various types of coated steel bolts, their polarization curves were measured by potentio-dynamic tester in this study. Based on the measured polarization curves, the more times of chromate and top coating on roll formed steel bolt, the higher corrosion resistance was shown. The roll formed steel bolt, which was Zn-Ni electro-deposited, two times chromated, one time inorganic top coated, one time organic top coated and annealed, showed the best corrosion resistance.

• Journal of the Korean Wood Science and Technology
• /
• v.34 no.3
• /
• pp.30-37
• /
• 2006

The present study examined the formaldehyde (HCOH) emission characteristic of various wood-based panel used in interior design, and measured changes in formaldehyde emission when a number of VOC reduction methods were applied. Formaldehyde emission showed a clear tendency of increase with the rise of temperature, and the concentration of formaldehyde emitted changed according to the preprocessing condition before measuring. Formaldehyde emission from wood board after bake out treatment was lower than that of the control group. When specimens were coated with urethane, cashew, water, oil stain, they generally showed the decrease of formaldehyde emission, although varying according to finishing material, and when edge sealing was applied the decrease became significant. $TiO_2$ coating was more effective in decreasing formaldehyde under ultraviolet lamps than under ordinary lamps. When the irradiation of ultraviolet lamps gets longer, formaldehyde emission decreased.

• Korean Journal of Environmental Agriculture
• /
• v.33 no.3
• /
• pp.198-204
• /
• 2014

BACKGROUND: Caused by cultural environment, the fruit skin stain results in serious damages to pear fruit. Particularly susceptible to this damage, 'Niitaka' pear accounts for 82% of pear cultivation in Korea and many farmers growing the pear trees have suffered economic losses due to fruit skin stain. This study investigated the effect of different treatments of 'Niitaka' pear during growing period on the occurrence of fruit skin stain. METHODS AND RESULTS: The treatments in the field included gibberellin (GA) paste, spraying with amino acid tree fertilizer, functional bagging, and coating of the inner paper bag with agents. The relationships between tree vigor, mineral nutrition concentration and fruit skin stain occurrence were also investigated. The fruit skin stain symptoms occurred from young fruit (May 25) until harvest. There was no exposed fruit flesh. The occurrence of fruit skin stain was significantly reduced in normal tree (shoot length 110 cm), as well as using GA paste treatment, and bagging in calcium and lime sulfur coated bags. However, spraying with amino acid tree fertilizer made no difference in comparison to control. In addition, bags in which the inner paper was coated with lime sulfur and soybean oil resulted in chemical injury to the fruit skin caused by bagging. The K concentration of shoot wood and fruit skin were higher than those of the control. Also, there were lower T-N, K concentration of leaf. CONCLUSION: These results suggest that occurrence of fruit skin stain in 'Niitaka' pear fruits during the growing period can be reduced by GA paste and bagging in calcium and lime sulfur coated bags. The symptoms of chemical injury to the fruit skin caused by bagging in lime sulfur and soybean oil coated inner paper were different compared to skin stain occurring in fruit during the growing period.

• Journal of Adhesion and Interface
• /
• v.24 no.2
• /
• pp.69-75
• /
• 2023

Recently, the application of paint protection films (PPFs) for automobiles having a self-recovery coating layer has been grown up. In this study, we report the evaluation results on the basic physical properties of a poly(vinyl chloride)- based PPF containing poly(urea-urethane) hybrid self-recovery coating layer. Depending on the main chemical composition and the thickness of poly(urea-urethane)-based coating layer for PPF, the self-recovery performance by an optical microscope and the stain resistance through color difference value are measured. To improve the surface properties and show its easy-cleaning effect against the polluted things, silicone-modified polyacrylate is introduced to the self-recovery coating composition. The contact angle of water on the coated surface is confirmed to show its hydrophobic surface. Finally, accelerated weathering test of paint protection film with poly(urea-urethane) hybrid coating layer is performed to check the possibility of discoloration and deformation due to long-term exposure on harsh condition.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2004.04a
• /
• pp.192-210
• /
• 2004

Application methods of chemicals were investigated tn minimize strength reduction of corrugated boards under the high humidity environment encountered in the cold chain system. Starch insolubilizers were introduced in the starch solution preparation of the Stain hall method and their insolubilization effect of starch binder were estimated. The performance of water repellent agents(WRA) and moisture proof agents(MPA) were evaluated in terms of water and moisture resistance. And effects of the combination of the chemicals and the coating method were also examined. Addition of the polyamine polyamide insolubilizer to the main part in the Stain hall process improved the binding force and water resistance of starch, which contributed to minimize the strength reduction of paper under the high humidity environment. AZC and Glyoxal type insolubilizers could not be used in the experiment due to an excessively increased viscosity of starch solution and the poor stability. Conventional WRA treatment to the base paper enhanced water and moisture resistance very slightly even though water repellency of the paper reached R10 by the treatment. MPA showed excellent performance than WRA not only in water and moisture resistance but in water repellency. Double coating on paper with MPA was more effective than the single coating at the same coating weight. A newly developed MPA showed excellent performance and runnability only by a single coating instead of a double coating.