• 한국재료학회지
• /
• 제22권3호
• /
• pp.118-122
• /
• 2012

We synthesized porous $Co_3O_4/RuO_2$ composite using the soft template method. Cetyl trimethyl ammonium bromide (CTAB) was used to make micell as a cation surfactant. The precipitation of cobalt ion and ruthenium ion for making porosity in particles was induced by $OH^-$ ion. The porous $Co_3O_4/RuO_2$ composite was completely synthesiszed after anealing until $250^{\circ}C$ at $3^{\circ}C$/min. From the XRD ananysis, we were able to determine that the porous $Co_3O_4$/RuO2 composite was comprised of nanoparticles with low crystallinity. The shape or structure of the porous $Co_3O_4/RuO_2$ composite was studied by FE-SEM and FE-TEM. The size of the porous $Co_3O_4/RuO_2$ composite was 20~40 nm. From the FE-TEM, we were able to determine that porous cavities were formed in the composite particles. The electrochemical performance of the porous $Co_3O_4/RuO_2$ composite was measured by CV and charge-discharge methods. The specific capacitances, determined through cyclic voltammetry (CV) measurement, were ~51, ~47, ~42, and ~33 F/g at 5, 10, 20, and 50 mV/sec scan rates, respectively. The specific capacitance through charge-discharge measurement was ~63 F/g in the range of 0.0~1.0 V cutoff voltage and 50 mAh/g current density.

• 한국표면공학회지
• /
• 제55권1호
• /
• pp.32-37
• /
• 2022

In a carbon-zero social atmospher, research is underway to reduce the use of fossil fuels. Interest in cleaner energy sources and their storage system is growing, and among them, research on effective energy storage is being actively conducted. Energy storage system(ESS) can be divided into secondary batteries, fuel cells, and capacitors, and the superiority of energy density of secondary batteries has a dominent influence on the ESS market. However, as problems with secondary batteries, charge/discharge speed, safety, and deterioration of electrodes are being highlighted. In this study, an electrode for supercapacitor with superior charge/discharge speed and specific capacitance is manufactured. The manufactured spinel nickel cobalt electrodes had specific capacitances of 1018.8 F/g, 690.8 F/g, and 475.1 F/g at 1 A/g in 1 M KOH electrolyte, and shows a performance retention rate of 77.48%, 63.30%, and 58.16% after 2000cycles at 7 A/g.

• 전기화학회지
• /
• 제25권1호
• /
• pp.22-31
• /
• 2022

Carbon nanomaterials are considered to be the materials of choice for the fabrication of electrochemical energy storage devices due to their stability, cost-effectiveness, well-established processing techniques, and superior performance compared to other active materials. In the present work, reduced graphene oxide (rGO) has been synthesized and used for the fabrication of a symmetric supercapacitor. The electrochemical performance of the fabricated supercapacitors with three different aqueous electrolytes namely 0.5 M H₂SO₄, 0.5 M H₃PO₄, and 1.0M Na₂SO₄ have been compared and analyzed. Among the three electrolytes, the highest areal specific capacitance of 14 mF/cm² was calculated at a scan rate of 5 mV/s observed with 0.5M H₃PO₄ electrolyte. The results were also confirmed from the charge/discharge results where the supercapacitor with 0.5M H₃PO₄ electrolyte delivered a specific capacitance of 11 mF/cm² at a current density of 0.16 mA/cm². In order to assess the stability of the supercapacitor with different electrolytes, the cells were subjected to continuous charge/discharge cycling and it was observed that acidic electrolytes showed excellent cyclic stability with no appreciable drop in specific capacitance as compared to the neutral electrolyte.

• 한국인터넷방송통신학회논문지
• /
• 제24권2호
• /
• pp.127-132
• /
• 2024

최근 이차전지는 다양한 산업 분야에서 사용되고 있다. 특히 소형 및 경량의 특성으로 스마트폰, 노트북, 태블릿 등 다양한 휴대용 전자기기에서 높은 에너지 밀도와 충·방전 효율을 토대로 전기자동차와 에너지저장시스템(Energy Storage System, ESS)의 핵심 부품으로 사용되고 있다. 하지만 이차전지의 과도한 충·방전에 따른 수명감소, 파열, 손상, 화재 등의 문제점이 발생하고 있다. 따라서 BMS(Battery Management System)를 통하여 과도한 충·방전을 보호하고 성능을 향상시킨다. 하지만 실제 리튬이온 배터리를 사용하여 BMS의 차단 및 보호범위 설정하는 데 있어서 이차전지의 수명감소, 파열, 손상, 화재의 문제점이 따른다. 따라서 본 논문에서는 배터리 충방전기와 시뮬레이터를 활용하여 이차전지 중 사용이 높은 리튬이온 배터리와 납축전지의 충전 및 방전 특성을 살펴본다.

• 한국분말재료학회지
• /
• 제23권4호
• /
• pp.317-324
• /
• 2016

Tin is one of the most promising anode materials for next-generation lithium-ion batteries with a high energy density. However, the commercialization of tin-based anodes is still hindered due to the large volume change (over 260%) upon lithiation/delithiation cycling. To solve the problem, many efforts have been focused on enhancing structural stability of tin particles in electrodes. In this work, we synthesize tin nano-powders with an amorphous carbon layer on the surface and surroundings of the powder by electrical wire explosion in alcohol-based liquid media at room temperature. The morphology and microstructures of the powders are characterized by scanning electron microscopy, X-ray diffraction, Raman spectroscopy, and transmission electron microscopy. The electrochemical properties of the powder for use as an anode material for lithium-ion battery are evaluated by cyclic voltammetry and a galvanometric discharge-charge method. It is shown that the carbon-coated tin nano-powders prepared in hexanol media exhibit a high initial charge specific capacity of 902 mAh/g and a high capacity retention of 89% after 50 cycles.

• 한국응용과학기술학회지
• /
• 제40권6호
• /
• pp.1191-1200
• /
• 2023

The lithium ion battery has applied to various fields of energy storage systems such as electric vehicle and potable electronic devices in terms of high energy density and long-life cycle. Despite of various research on the electrode and electrolyte materials, there is a lack of research for investigating of the binding materials to replace polymer based binder. In this study, we have investigated petroleum pitch/polymer composite with various ratios between petroleum pitch and polymer in order to optimize the electrochemical and physical performance of the lithium-ion battery based on petroleum pitch/polymer composite binder. The electrochemical and physical performances of the petroleum pitch/polymer composite binder based lithium-ion battery were evaluated by using a charge/discharge test, cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and universal testing machine (UTM). As a result, the petroleum pitch(MP-50)/polymer(PVDF) composite (5:5 wt % ratio) binder based lithium-ion battery showed 1.29 gf mm^-1 of adhesion strength with 144 mAh g^-1 of specific dis-charge capacity and 93.1 % of initial coulombic efficiency(ICE) value.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 영호남학술대회 논문집
• /
• pp.39-41
• /
• 2000

Carbon is an attractive candidate for use in eletrochemical supercapacitors that depend on charge storage in the electrode/eletorlyte international double layer. Property of an electrical double layer capacitor depend both on the technique used to prepare the electrode and on the current collector structure. The study is to research that $V_2O_5$-carbon (SP270) composite electrode for supercapacitor. The discharge capacitance of $V_2O_5$-SP270 (20wt%) in 1st and 35cyc1e was 14F/g and 8.5F/g at current density of $0.1mA/cm^2$. The discharge process of $V_2O_5$-SP270 (20wt%) composite electrode is larger than that others.

• 전기화학회지
• /
• 제11권2호
• /
• pp.100-104
• /
• 2008

Titanium sheet metal substrates used in thin film batteries were wet etched and their surface area was increased in order to increase the discharge capacity and power density of the batteries. To obtain a homogeneous etching pattern, we used a conventional photolithographic process. Homogeneous hemisphere-shaped wells with a diameter of approximately $40\;{\mu}m$ were formed on the surface of the Ti substrate using a photo-etching process with a $20\;{\mu}m{\times}20\;{\mu}m$ square patterned photo mask. All-solid-state thin film cells composed of a Li/Lithium phosphorous oxynitride (Lipon)/$LiCoO_2$ system were fabricated onto the wet etched substrate using a physical vapor deposition method and their performances were compared with those of the cells on a bare substrate. It was found that the discharge capacity of the cells fabricated on wet etched Ti substrate increased by ca. 25% compared to that of the cell fabricated on bare one. High discharge rate was also able to be obtained through the reduction in the internal resistance. However, the cells fabricated on the wet etched substrate exhibited a higher degradation rate with charge-discharge cycling due to the nonuniform step coverage of the thin films, while the cells on the bare substrate demonstrated a good cycling performance.

• 한국수소및신에너지학회논문집
• /
• 제8권3호
• /
• pp.137-141
• /
• 1997

The effects of Ag addition to Zr-based hydrogen storage alloys ($Zr_{0.7}Ti_{0.3}V_{0.4}Ni_{1.2}Mn_{0.4}$, $Zr_{0.7}Ti_{0.3}V_{0.4}Ni_{1.2}Mn_{0.3}Cr_{0.1}$ and $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.3}Fe_{0.1}$) on the electrode properties were examined. Ag-free and Ag-added Ze-based alloys were prepared by arc melting, crushed mechanically, and subjected to the electrochemical measurement. In $Zr_{0.7}Ti_{0.3}V_{0.4}Ni_{1.2}Mn_{0.4}$ alloy, 0.08 wt% Ag addition to the alloy improved the activation rate. Also Ag addition improved both activation property and discharge capacity in $Zr_{0.7}Ti_{0.3}V_{0.4}Ni_{1.2}Mn_{0.3}Cr_{0.1}$. For these Ag-added alloys, discharge capacities with the change of charge-discharge current density(10mA, 15mA and 30mA) are almost constant. Showing very high rate capability, discharge capacity of $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.3}Fe_{0.1}$ alloy increased by Ag addition to the alloy. When the amount of Ag addition in $Zr_{0.7}Ti_{0.3}V_{0.4}Ni_{1.2}Mn_{0.4}$ alloy increased too much, the electrode properties became worse. Unveiling mechanism of effect of Ag addition is now progressing in our laboratory.

• 전기화학회지
• /
• 제2권3호
• /
• pp.123-129
• /
• 1999

리튬이온전지용 $LiCoO_2$ 전극의 super s black 도전재료의 함량에 따른 초기 충방전 특성을 1 mol/l $LiPF_6/EC+DEC(1:3\;by\;w/w)$의 전해액에서 리튬기준전극에 대하여 4.3 V에서 2.0 V의 전위 구간에 대하여 C/4 및 C/2율로 충방전하여 측정하였다. 최초의 충전과정에서 high impedance충전 특성을 보였으며, super s black도전재료를 $3\%w/w$ 사용한 경우, $0.5 mA/cm^2$ 전류밀도의 충전에서 high impedance의 해소에 따라 $3.82\;{\Omega}\;{\cdot}\;g-LiCoCo_2$의 저항 감소를 나타내었으며, $0.728\;{\Omega}{\cdot}g-LiCoCo_2$의 전극저항과 비교하여 약 7배 높은 값을 나타내었다. 제2차 충전에의 high impedance해소는 약 $63\;{\Omega}{\cdot}g-LiCoCo_2$으로서 전극저항의 $12\%$ 정도이며, 제1차 충전의 high impedance해소에 비하여 $1.7\%$의 수준으로 감소하였다. 제1차 충전 및 방전 비용량은 C/4방전율에서 각각 160-161 및 $153\~155mAh/g-LiCoO_2$으로, 쿨롱효율은 $95.4\~96.4\%$였으며, 비가역 비용량은 약 6 mAh/g-$LiCoO_2$였다. 충전종료 지점에서 측정한 비저항은 도전재료 함량 $2\~7\%w/w$범위에서 낮은 값을 나타내어 비가역 비용량 특성의 변화와 일치하였다. 도전재료의 함량 증가에 따라 용량밀도가 감소하였으며, C/4율 방전에서 super s black함량 $2\%w/w$와 $2.9\%w/w$의 도전재료를 사용한 전극의 용량밀도는 각각 447mAh/ml 및 431 mAh/ml였다