• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.601-608
• /
• 1988

The effect of SiO2 addition on sintering characteristics of 8 mole percent yttria-stabilized zirconia ceramics is investigated. As the addition of SiO2 is increased, sinterbility, microstructure, and Vickers hardness of the zirconia ceramic increased but fracture toughness and electrical conductivity are decreased. It is considered that the electrical conductivity decrease with the increase of SiO2 is due to the decrease of defect concentration of ionized oxygen. From the complex impedance measurement, it is shown that the influence of SiO2 is more dominant at the resistivity of bulk region than of grain boundary region.

• Journal of the Korean Ceramic Society
• /
• v.27 no.8
• /
• pp.955-964
• /
• 1990

A new process of emulsiion-spray pyrolysis for synthesizing ceramic powders was developed and the characteristics of Al2O3-20w/o ZrO2 composite powders prepared by this method were investigated. The composite powders synthesized in this study were spherical dense particles with 0.1~0.4${\mu}{\textrm}{m}$ of diameter. As found in powders derived by the emulsion-hot kerosene drying method, all zirconia in Al2O3-20w/o ZrO2 powders heat-treated at 120$0^{\circ}C$ was in the tetragonal form at room temperature. The relative density and the fracture toughness of composites sintered at 1$650^{\circ}C$ for 4hrs were 95% and 5.2MPa.m1/2, respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.11
• /
• pp.1197-1202
• /
• 1998

To check the possibility for microwave sintering of MLCC(multi layer ceramic capacitor) the tape cast-ed BaTiO3 thick films in zirconia insulation box were sintered by the domestic microwave oven. Microwave sintered samples had higher density lower porosity than coventionally sintered ones. but they didn't show Z5U electrical properties due to short sintering time about 15 minutes.

• Journal of the Korean Ceramic Society
• /
• v.49 no.4
• /
• pp.380-384
• /
• 2012

This paper deals with the recent developments of high thermal conductivity silicon nitride ceramics. First, the factors that reduce the thermal conductivity of silicon nitride are clarified and the potential approaches to realize high thermal conductivity are described. Then, the recent achievements on the silicon nitride fabricated through the reaction bonding and post sintering technique are presented. Because of a smaller amount of impurity oxygen, the obtained thermal conductivity is substantially higher, compared to that of the conventional gas-pressure sintered silicon nitride, while the microstructures and bending strengths are similar to each other between these two samples. Moreover, further improvement of the thermal conductivity is possible by increasing ${\beta}/{\alpha}$ phase ratio of the nitrided sample, resulting in a very high thermal conductivity of 177 W/($m{\cdot}K$) as well as a high fracture toughness of 11.2 $MPa{\cdot}m^{1/2}$.

• Journal of the Korean Ceramic Society
• /
• v.43 no.7 s.290
• /
• pp.439-444
• /
• 2006

Artificial graphite generally manufactured by carbonization sintering of shape-body of kneaded mixture using granular cokes as filler and pitch as binder, going through pitch impregnation process if necessary and finally applying graphitization heat treatment. Graphite materials are used for core internal structural components of the High-Temperature Gas-cooled Reactors (HTGR) because of their excellent heat resistibility and resistance of crack progress. The HTGR has a core consisting of an array of stacked graphite fuel blocks are machined from IG-110, a high-strength, fine-grained isotropic graphite. In this study, crack stabilization and micro-structures were measured by bend strength and fracture toughness of isotropic graphite grade IG-110. It is important to the reactor designer as they may govern the life of the graphite components and hence the life of the reactor. It was resulted crack propagation, bend strength, compressive strength and micro-structures of IG-110 graphite by scanning electron microscope and universal test machine.

• Journal of the Korean Ceramic Society
• /
• v.34 no.9
• /
• pp.915-920
• /
• 1997

Tetragonal ZrO2 polycrystal (TZP), consisted of 90.24 mol% ZrO2-5.31 mol% Y2O3-4.45 mol% Nb2O5, were prepared using hot-press and mechanical properties and high-temperature degradation were investigated. The specimen, hot-pressed for 1 h at 140$0^{\circ}C$ in Ar atmosphere, exhibited flexural strength of 1010 MPa and fracture toughness of 7.5 MPam1/2 and experienced no low-temperature degradation below 40$0^{\circ}C$. However, as aged for 100h at temperatures higher than 40$0^{\circ}C$, TZP was suffered by high-temperature degradation due to an extensive cavitation caused by the oxidation of carbon. XPS observation revealed that the carbon incorporated in TZPs during hot-pressing exists as either an ether-type CO or a carbonyl-type C=O. Despite of the high-temperature degradation of t-ZrO2 co-doped with Y2O3 and Nb2O5, its flexural strength and fracture toughness were superior to those of the commercial 3 mol% Y2O3-TZP hot-pressed under the identical condition as determined before and after the aging treatments.

• Journal of the Korean Ceramic Society
• /
• v.34 no.12
• /
• pp.1240-1246
• /
• 1997

Silicon carbides with self-reinforced microstructure which hore a small grain matrix and dispersed large grains with rod-like type were prepared by the liquid-phase sintering and the control of starting phases of raw materials. The specimens with self-reinforced microstructure could be obtained from the compacts with mixed compositions of $\alpha$-SiC and 10-50 % $\beta$-SiC powders and by the pressureless sintering at 185$0^{\circ}C$ for 5h. Large grains with rod or plate-like types were 4H-SiC and small grains with equi-axed type were 6H-SiC. Fracture grains with rod or plate-like types were 4h-SiC and small grains with equi-axed type were 6H-SiC. Fracture toughness of specimens with self-reinforced microstructure was increased by the crack deflection and formation of microcracking due to the existence of rod-like large grains during crack propagation.

• Journal of the Korean Ceramic Society
• /
• v.45 no.8
• /
• pp.486-492
• /
• 2008

Reaction bonded silicon carbide(RBSC) composite for heat-exchanger was fabricated by molten Si infiltration method. The raw materials with variable particle sizes were used in this experience. The finer the particle size in sintered silicon carbide was the more increasing 3-point bending strength and fracture toughness. As the adaptable particle sizes had been occupied interstice arising from packing sample, the mechanical properties were increased. In the PCS1-1 sample, the 3-point bending strength and fracture toughness were 323MPa and $4.9\;MPa{\cdot}m^{1/2}$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.33 no.8
• /
• pp.855-862
• /
• 1996

The nucleation and the crystal growth rates of Ge-Se-Te chalcogenide glass by two step heat-treatment and its effect on the mechanical optical properties and water-resistance were determined. The maximum nuclea-tion and crystal growth rate were 2.1$\times$103/mm3 .min at 28$0^{\circ}C$ and 0.4${\mu}{\textrm}{m}$/min at 33$0^{\circ}C$ respectively. When the crystal volume fraction with crystal size $1.5mutextrm{m}$ was about 4% the (hardness and fracture toughness were about 117kg/mm2 and 6.0 MPa.mm1/2)respectively. The weight loss of crystallized glass in water was lower than parent glass($25^{\circ}C$ for 32 hrs : 0.03% 8$0^{\circ}C$ for 16 hrs : 0.1%) as 0.01% at $25^{\circ}C$, 0.03% at 8$0^{\circ}C$ for 16 hrs : 0.1%) at $25^{\circ}C$ 0.03% at 8$0^{\circ}C$ respectively. The IR-transmittance decreased with increasing crystal size and crystal volume fraction. The IR-transmittance of crystallized glass with the crystal size of $1.5mutextrm{m}$ (crystal volume fraction : 4%) presented 56% which was about 4% lower than that of parent glass.

• Journal of the Korean Ceramic Society
• /
• v.33 no.5
• /
• pp.536-546
• /
• 1996

The TiC-Ni/Al reaction-bonding composites were prepared by the infiltration of Ni/Al melt into the TiC preforms. The microstructure the reaction composition crystalline phase and the mechanical properties of the composites were investigated. During the reaction-bonding Ni/Al mixture had a good wettability and per-meability with TiC preform and pore-free and fully dense sintered bodies were produced. In the case of the Ni/Al atomic ratio of 0.3 and 0.5 TiC raw particle shape was changed to irregular particles because of the decomposition in the liquid matrix and its phenomena was more distinguished in the Al-rich liquid matrix. With increasing more than 1 of the Ni/Al atomic ratio the sample of TiC grain shape was changed from spherical to palatelet particles. Also with increasing the atomic ratio of Ni/Al bending strength and fracture spherical to palatelet particles. Also with increasing the atomic ratio of Ni/Al bending strength and fracture toughness were increased and its maximum value was 1073 MPa and 11 MPa.m1/2 respectively.