• Journal of the Korea Institute of Building Construction
• /
• v.12 no.5
• /
• pp.490-502
• /
• 2012

The use of recycled aggregate, even for low-performance concrete, has been very limited because recycled aggregate, which contains a large amount of old mortar, is very low in quality. To produce a high-quality recycled aggregate, removing the paste that adheres to the recycled aggregate is very important. We have conducted research on a complex abrasion method, which removes the component of cement paste from recycled fine aggregate by using both a low-speed wet abrasion crusher as a mechanical process and neutralization as chemical processes, and well as research on the optimal manufacturing condition of recycled fine aggregates. Subsequently, we evaluated the quality of recycled fine aggregate manufactured using these methods, and tested the specimen made by this aggregate. As a result, it was found that recycled fine aggregates produced by considering the aforementioned optimal abrasion condition with the use of sulfuric acid as reactant showed excellent quality, recording a dry density of 2.4 and an absorption ratio of 2.94. Furthermore, it was discovered that gypsum, which is a reaction product occurring in the process, did not significantly affect the quality of aggregates. Furthermore, the test of mortar using this aggregate, when gypsum was included as a reaction product, showed no obvious retarding effect. However, the test sample containing gypsum recorded a long-term strength of 25.7MPa, whereas the test sample that did not contain gypsum posted a long-term strength of 29.4MPa. Thus, it is thought to be necessary to conduct additional research into the soundness and durability because it showed a clear reduction of strength.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.11a
• /
• pp.71-74
• /
• 2007

With the changes of times the building materials tend to extend the demand for application under the special environment. Since high-ductile mortar is developed, the building materials show excellent performance like toughness, compression, tensile, and bending, etc. in the general concrete from the existing brittle point. And, recently they are widely used as repairing and reinforcing materials both at home and abroad because they are recognized as excellence like durability and fire-resistance. However, it is in a situation of creating problems in durability because it frequently happened deterioration of buildings that have already repaired and reinforced at a time when it requires reconstruction of recently deteriorated construction structure recently. Therefore, in this study improved with a more repair Material development and reinforcement of the second high-ductile mortar products for a variety of basic materials were presented want, research plans used include traditional repair materials and the newly developed PCM (polymer cement mortar) structural reinforcement type indicated that comparison. PCM analysis in order to present a rate depending on the types fiber 0, 1.2 and 2.0(%) at three levels and mixture water according to ratios of weight to Plain in the 2.0 and 1.85(kg) at two levels is set, the results were as follows. 1) This study has shown that PCM had excellent strain hardening behavior at the same time that the bending stress increased according to the fiber contents. 2) This study has shown that it had the durability performance due to the high substance transmission according to the fiber contents.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.5
• /
• pp.409-416
• /
• 2020

In this paper, strength correction factors of the concretes incorporating ordinary Portland cement(OPC), fly ash(FA) and blast furnace slag(BS) with 50% of water to binder ratio due to temperature drop for standard room temperature(20±3℃) are provided. For this, strength development was done based on equivalent age method. For calculating the equivalent age, apparent activation energy was obtained with 24.69 kJ/mol in OPC, 46.59 kJ/mol in FA, 54.59 kJ/ol in BS systems. According to the estimation of strength development of the concretes, the use of FA and BS resulted in larger strength drop than that of OPC under low temperature compared to standard room temperature. Hence, strength correction factors(Tn) for OPC, FA and BS are suggested within 4~17℃ with every 3MPa levels.

• KIEAE Journal
• /
• v.16 no.4
• /
• pp.41-46
• /
• 2016

Purpose: This is a study on the planning of temporary housing for post application of Mega Sports facilities. The subject of the study is 2018 Pyeongchang Winter Olympics, which is to suggest building an alternative temporary housing using shipping containers(high cube), which solve the lack of accommodations and recycle temporary housing after Olympics, save money and be eco-friendly in Olympics. Method: This study includes this ; research on the a fact-finding survey about Mega sports facilities post application and demand survey on 2018 Pyeongchang Winter Olympics accomodations and an analysis about temporary housing plan. Furthermore we decided temporary housing building plan by analyzing residents' needs and traits of the housing etc. Through this, we made a schematic design for household units. Result: As a result, this study is a plan of making space, forms, and structure. The planned size is $38.4m^2$(L:12m, W:3.2m) except balcony, and indoor height is 2.5m. The space consists of entrance, bathroom, bedroom and living room with folding furniture system. Also there's a detailed floor plan of the ceiling, wall, and floor we drew up. The ceiling and wall consist of dampproof film, noncombustible board, fire proof urethane form, and color-designed sheet. The floor is composed of floor tile, cement mortar, light concrete(with heat coil), insulation, and dampproof film. Additionally, this study is a plan of interior dry wall with detail using modular construction method for work efficiency and quality improvement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.367-374
• /
• 2019

Drying shrinkage in the hardened cement is known to change in volume by decreasing the moisture content in the hardened body, and it is known that the higher the W / C and the higher the content of the paste, the larger the drying shrinkage. In the case of ECC, more drying shrinkage occurs compared to concrete, since it does not contain coarse aggregate. Since ECC is an important material for tensile performance, the effect of restrained tensile stress on mechanical tensile behavior should be considered. The purpose of this study is to analyze the effect of stress caused by restraint on the tensile behavior of ECC. The mechanical properties of the specimens were tested by uniaxial tension tests with different restraints. As a result, the difference of tensile behavior according to restraint stress was observed and the cause was analyzed.

• Resources Recycling
• /
• v.23 no.4
• /
• pp.37-46
• /
• 2014

Carbon dioxide generated from construction materials and construction material industry among the fields of construction is approximately 67 million tons. It is about 30% of the carbon dioxide generated in the fields of construction. In order to reduce carbon dioxide in the fields of construction, it is necessary to control the use of fossil fuel consumed and decrease carbon emission by reducing the secondary and tertiary curing generating carbon dioxide in construction material industry. Therefore, this study manufactured mortar by having cement as the Plain and substituting three binding materials up to 50% and then adopted different curing methods to analyze congelation and strength characteristics. Test results for strength property by changing binding materials showed that specimens with blast furnace slag, CSA 15% and CAMC 5% resulted in positive effect for strength.

• Computers and Concrete
• /
• v.17 no.6
• /
• pp.787-799
• /
• 2016

Climate anomalies in recent years, numerous natural disasters caused by landslides and a large amount of entrained sands and stones in Taiwan have created significant disasters and greater difficulties in subsequent reconstruction. How to respond to these problems efficaciously is an important issue. In this study, the sands and stones were doped with recycled materials (waste LCD glass sand, slag powder), and material was mixed for recycled ready-mixed soil. The study is based on security and economic principles, using flowability test to determine the water-binder ratio (W/B=2.4, 2.6, and 2.8), a fixed soil: sand ratio of 6:4 and a soil: sand: glass ratio of 6:2:2 as fine aggregate. Slag (at concentrations of 0%, 20%, and 40%) replaced the cement. The following tests were conducted: flowability, initial setting time, unit weight, drop-weight and compressive strength. The results show that the slump values are 220 -290 mm, the slump flow values are 460 -1030 mm, and the tube flow values are 240-590 mm, all conforming to the objectives of the design. The initial setting times are 945-1695 min. The unit weight deviations are 0.1-0.6%. The three groups of mixtures conform to the specification, being below 7.6 cm in the drop-weight test. In the compressive strength test, the water-binder ratios for 2.4 are optimal ($13.78-17.84kgf/cm^2$). The results show that Recycled ready-mixed soil materials (RRMSM) possesses excellent flowability. The other properties, applied to backfill engineering, can effectively save costs and are conducive to environmental protection.

• Advances in concrete construction
• /
• v.4 no.1
• /
• pp.15-26
• /
• 2016

In Algeria, wastes are often stored in such conditions that do not meet standards. Today and more than ever, we really must implement an environmentally management of wastes. Recovery of waste in Algeria has a considerable delay due to the absence of a policy favorable to the development of waste management. But many researchers have shown the possibility to reuse dredged sediments in road construction. Through Europe, recent research works have been already performed on dam sediments. Present study fits into the context of the valorization of dredged sediments from Fergoug dam. They are found in considerable quantities and mainly composed of mineral phases, organic matters and water. The reservoir sedimentation poses problems for the environment and water storage, dredging becomes necessary. Civil engineering is a common way of recycling for such materials. Dredged sediments have not the required mechanical characteristics recommended by the standards as GTR guide (LCPC-SETRA 1992). So as to obtain mechanical performance, dredged sediment can be treated with cement, lime, or replaced materials like quarry sand. An experimental study has been conducted to determine physical and mechanical characteristics of sediments dredged from dam. Then different mixtures of sediment and/or quarry sand with hydraulic binders are proposed for improving the grain size distribution of the mixes. Finally, according these mixtures, different formulations have been tested as alternative materials with dredged sediments.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.216-222
• /
• 2021

This is an experiment to complement new ways of using concentrated water discharged from the seawater desalination plant. In this study, metakaolin, which has excellent chloride ion immobilization effect, was used as the main binder, and 10% and 20% of calcium oxide were substituted with the activator. In addition, tap-water(TW) and reverse osmosis brine water(RW) were used as mixed water. As a result of the experiment, the mixture using RW showed higher compressive strength than TW. It also showed low water absorption and high density. In the mixture using RW as mixed water, a hydration reaction substance called Friedel's salt could be observed. Considering the corrosion problem of steel, RW is considered to be applicable to products such as non-reinforced concrete, brick, and curb stone. Through this study, it is thought that it is meaningful to propose a new application method other than the ocean release of RW.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.17 no.2
• /
• pp.203-212
• /
• 2019

Disposal nonconformity of radioactive wastes refers to radioactive wastes that need to be treated, solidified and packaged during operation or decommissioning of NPPs, and are typically exemplified by particulate radioactive wastes with dispersion characteristics. These wastes include the dried powders of concentrated wastes generated in the process of operating NPPs, slurry and sludge, various powdered wastes generated in the decommissioning process (crushed concrete, decontamination sludge, etc.), and fine radioactive soil, which is not easy to decontaminate. As these particulate wastes must be packaged so that they become non-dispersive, they are solidified with solidification agents such as cement and polymer. If they are treated using existing solidification methods, however, the volume of the final wastes will increase. This drawback may increase the disposal cost and reduce the acceptability of disposal sites. Accordingly, to solve these problems, this study investigates the pelletization of particulate radioactive wastes in order to reduce final waste volume.