• Applied Chemistry for Engineering
• /
• v.32 no.5
• /
• pp.497-503
• /
• 2021

In this study, different methods to coat honeycomb and metal foam substrate with platinum/titania for removing odor gases and volatile organic compounds were investigated. Among them, the powder coating and the nano coating were compared. Scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDX) analysis was used to investigate the surface conditions and exposed platinum composition ratios on honeycomb and metal foam. Also, the catalytic oxidation performance of toluene, trimethylamine and isopropyl alcohol was compared according to the coating method.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.230.2-230.2
• /
• 2010

천연가스 수증기 개질 반응에 사용되는 펠릿 촉매의 단점인 열 및 물질 전달 제한, 낮은 effectiveness factor, 압력강화와 channeling 등의 문제점을 해결 하고자 모노리스 형태의 금속 구조체 촉매를 본 연구에 적용 하였다. Fecralloy 재질의 금속 구조체에 Ni 촉매를 워시코팅 (wash coating) 하여 제조 하였으며, 이를 천연가스 수증기 개질 반응에 적용하여 수소를 생산하였다. 실험 조건으로는 S/C ratio를 3으로 고정하여 온도를 $600^{\circ}C{\sim}800^{\circ}C$로 변화 시켰으며, GHSV $3000{\sim}30000h^{-1}$에서 진행 되었다. 구조체 촉매 코팅에 사용된 Ni 촉매의 BET, TPR, H2-chemisorption, SEM, EDS의 특성분석을 수행 하였다. 온도별 테스트에서 모노리스 형태의 금속 구조체 촉매가 펠릿 형태의 촉매에 비해 우수한 열전달 효과로 인해 낮은 퍼니스 온도와 높은 반응 활성을 나타내었으며, GHSV 변화에 따른 성능평가 결과도 15wt% $Ni/MgAl_2O_4$펠릿 촉매와 비교하여 금속 구조체 촉매가 높은 활성을 보였다.

• Journal of the Korean Ceramic Society
• /
• v.34 no.12
• /
• pp.1205-1212
• /
• 1997

The matrices which consisted of SiC whisker, PES(polyesterasulfone) as a binder, span 80(sorbitan monooleate) as a surfactant, TPP(triphenyl phosphate) as a plasticizer and dichloromethane as a solvent, have been prepared by the various methods such as tape casting, rolling, tape cast-coating and roll-coating method. The fuel cells of single stack type using these matrices are characterized by ac impedance spectroscopy and cyclic voltammetry technique. A fuel cell using a matrix prepared by the tape cast-coating method shows the best performance of 466.34 mA/$\textrm{cm}^2$ at 0.6V because it has the lowest polarization resistance at the interface between electrodes and a matrix due to the largest three phase contact region of gases, catalyst and electrolyte.

• Journal of environmental and Sanitary engineering
• /
• v.20 no.4 s.58
• /
• pp.51-58
• /
• 2005

Photocatalytic degradation using $TiO_2$ Particles suspended in a reactor was experimentally performed to degrade the formaldehyde of indoor pollutants. Exponential increase of degradation appears to prove light availability due to the scattering of W light by particles themselves. Comparative removal studies of formaldehyde were done in both cases of dipping and spraying immobilized techniques of $TiO_2$ Particles suspended in solution. Experiments were performed under several different experimental conditions such as initial concentration of formaldehyde, UV intensity and concentration of photocatalysts. Optimal conditions to degrade formaldehyde were obtained under the conditions of $30\;mg/cm^2$ concentration of catalyst and UV intensity of 30 Watt at the distance of 30 cm using immobilized technique by dipping coating.

• Corrosion Science and Technology
• /
• v.8 no.6
• /
• pp.223-226
• /
• 2009

Polymer coatings are commonly applied to metal substrates to prevent corrosion in aggressive environments such as high humidity and under salt water. Once the polymer coating has been breached, for example due to cracking or scratches, it loses its effectiveness, and corrosion can rapidly propagate across the substrate. The self-healing system we will describe prevents corrosion by healing the damage through a healing reaction triggered by the actual damage event. This self-healing coating solution can be easily applied to most substrate materials, and our dual-capsule healing system provides a general approach to be compatible with most common polymer matrices. Specifically, we expect an excellent anti-corrosion property of the self-healing coatings in damaged parts coated on galvanized metal substrates.

• Elastomers and Composites
• /
• v.55 no.2
• /
• pp.103-107
• /
• 2020

Herein, resin-formed polysilsesquioxanes (PSSQs) were synthesized using monomolecular fluoro silane as a precursor. The synthesized PSSQs exhibited anti-smudge performance and were used as coating liquid. Two structures were acquired by controlling the amount of the silane precursor and the K₂CO₃ catalyst; these materials were used to prepare the anti-smudge coating liquid solution. The synthesized product was analyzed by various methods such as nuclear magnetic resonance spectroscopy, X-ray diffraction analysis, gel permeation chromatography, and water contact angle measurement. The results confirmed that the as-synthesized PSSQs exhibited the ladder structure and had a molecular weight of 5,117 g/mol and water contact angle of 102.31°.

• Bulletin of the Korean Chemical Society
• /
• v.21 no.8
• /
• pp.817-822
• /
• 2000

Crack-free hard coating siIica films were prepared by sol-gel processfrom twokinds of silicon alkoxide (tetra-ethoxysilane and methyltrimethoxysilane) and two kinds of alcohol (methanol and isopropyl alcohol) with an acid catalyst,acetic acid. A silicate framework of the precursor solution was investigated by infrared spectros-copy (IR) in the process of hydrolysis and condensation. Theextent of the condensation in the intermediates was elucidated by gel permeation chromatography (GPC) and 29Si-NMR spectroscopy. The hard coating films werecharacterized by IR,scanning electron microscope (SEM), thermo gravimetric analyzer (TGA) and dif-ferential scanning calroimeter (DSC). The synthetic condition for the crack-free and transparent silica film for-mation was optimized interms of starting materials for the precursor solution as well as preparation method of the silica film.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.1
• /
• pp.56-62
• /
• 2021

In this study, we created a DBD plasma device and a MnO2 catalyst mesh filter for evaluating ozone reduction of devices via the catalyst method. The DBD plasma device was manufactured by applying Ag paste to soda lime glass via the screen-printing method. The MnO2 catalyst mesh filter was manufactured by mixing MnO2 powder with binder with a 10% difference in concentration from 10% to 50% and then applying it using the dip-coating method. Finally, we sintered a MnO2 catalyst mesh filter in an electric furnace. We evaluated the characteristics of ozone generation according to the Ar gas flow of DBD plasma devices, the opening ratio, and ozone reduction performance of the MnO2 catalyst filters. Ozone reduction performance was approximately 20.4% at MnO2 10 wt%, 37.8% at MnO2 30 wt% and 50% at MnO2 50 wt%.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.415-417
• /
• 2009

A low temperature decal (LTD) transfer method is tried to fabricated hydrocarbon (HC) membrane based MEA. Sandwiched structures of outer ionomer/catalyst/carbon coating/substrate, which had been developed for Nafion membrane, are used for transfer of catalyst to the HC membrane. Performances of the HC MEA before and after 500hr continuous operation are compared and it is found that a severe delamination occurs at the interface between the HC membrane and the catalyst layer, which is the main reason of the low performance and its degradation. The delamination is due probably to the different nature of HC membrane to the Nafion ionomer. A substitutional method, therefore, is suggested to overcome this. In such a way, the outer ionomer process is removed and the low transfer rate of catalyst by skipping the ionomer process is compensated with optimization of other process variables such as transfer time or temperature. The resulting performance is superior to the original LTD method, which can be explained in terms of low resistive components both in ohmic and kinetic.

• Clean Technology
• /
• v.23 no.3
• /
• pp.314-324
• /
• 2017

To verify the viability of Co, Ru and Zr-based catalyst for $CO_2$ (dry) reforming reaction, catalysts were fabricated using cordierite, silicon carbide and rota monolithic substrates, and they were compared with the conventional $Co-Ru-Zr/SiO_2$ catalyst in terms of performance and durability. Cordierite monolith was showed high activity with the least amount of active component. In addition, when Cordierite monolith was coated with Co-Ru-Zr in various ways, most excellent performance was showed at a precursor solution coating method. In particular, when 0.9 wt% Co-Ru-Zr/Cordierite was used for reaction, it was observed that 95% $CO_2$ conversion was maintained for 300 h at $900^{\circ}C$.