• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.314-319
• /
• 2013

In this study, nitrogen doped $TiO_2$ ($N-TiO_2$) coated on an activated carbon pellet (ACP) was prepared using sol-gel and the solid state heat treatment of urea to improve the removal property of volatile organic compounds (VOCs). To explore the visible light photocatalytic activity of the ACP under the light emitting diods (LED), the removal property of benzene gas was characterized by gas chromatography. The SEM and BET results show that the increment of titanium tetra isopropoxide contents leads to the increased $TiO_2$ coating amount of ACP surface and decreased specific surface area. From the results of benzene gas removal, the breakthrough time of ACP10 increased about 2 times compared to that of the ACP. The improved performance was attributed to the $N-TiO_2$ coating on ACP surface, which could be more effective to remove benzene gas under the condition of LED lamp.

• Ecology and Resilient Infrastructure
• /
• v.3 no.4
• /
• pp.215-220
• /
• 2016

A new immobilization technique of nanoscale $TiO_2$ powder to expanded polystyrene (EPS) balls with temperature-controlled melting method was developed, and the photocatalytic activity of $TiO_2$ powder-embedded EPS balls were evaluated using methylene blue (MB) solution under ultraviolet irradiation (${\lambda}=254nm$). Based on the scanning electron microscope (SEM) images and associated energy-dispersive X-ray spectroscopy (EDX) analysis, the components of the intact EPS balls were mainly carbon and oxygen, whereas those of $TiO_2$-immobilized EPS balls were carbon, oxygen, and titanium, indicating that relatively homogenous patches of $TiO_2$ and glycerin film were coated on the surface of EPS balls. Based on the comparison of degradation efficiencies of MB between intact and $TiO_2$-immobilized EPS balls under UVC illumination, the degradation efficiencies of MB can be significantly improved using $TiO_2$-immobilized EPS balls, and surface reactions in heterogeneous photocatalysis were more dominant than photo-induced radical reactions in aqueous solutions. Thus, $TiO_2$-immobilized EPS balls were found to be an effective photocatalyst for photodegradation of organic compounds in aqueous solutions without further processes (i.e., separation, recycling, and regeneration of $TiO_2$ powder). Further study is in progress to evaluate the feasibility for usage of buoyant $TiO_2$-immobilized EPS to inhibit the excessive growth of algae in rivers and lakes.

• Journal of Sensor Science and Technology
• /
• v.30 no.5
• /
• pp.320-325
• /
• 2021

Biochemical oxygen demand (BOD) and chemical oxygen demand (COD) methods are conventional analytical methods to analyze water quality. Both of these methods are technically indirect measurement methods, require complicated preconditions, and are time-consuming. On the other hand, the total organic carbon (TOC) method is a direct and fast measurement method which is more intuitive and accurate than the BOD and COD methods. However, general TOC analysis methods involve complicated processes and high power consumption owing to the process of phase transition from liquid to gas by a high-temperature heater. Furthermore, periodic consumables are also required for the removal of inorganic carbon (IC). Titanium dioxide (TiO₂) is one of the most suitable photocatalysts for simple processes. Its usage involves low power consumption because it only reacts with the organic carbon (OC) without the requirement of any other reagents and extra processes. We investigated a TiO₂ photocatalyst-based TOC analysis for simple and affordable products. TiO₂-coated fiber substrate maintained under carbon included water was exposed to ultraviolet (UV) radiation of wavelength 365 nm. This method is suitable for the real-time monitoring of water pollution because of its fast reaction time. Its linear property is also sufficient to match the real value.

• Journal of Electrochemical Science and Technology
• /
• v.1 no.1
• /
• pp.63-68
• /
• 2010

The $Li_4Ti_5O_{12}$/AC composite was prepared by sol-gel process with ultrasonication. The prepared composite was characterized by SEM, XRD and TG analysis, and their electrochemical behaviors were investigated by cyclic voltammetry, electrochemical impedance spectroscopy and charge-discharge test in 1M $LiBF_4$/PC electrolyte. From the results, the $Li_4Ti_5O_{12}$ particles coated on AC surface had an average particle size of 100 nm and showed spinel-framework structure. When the potential range of the $Li_4Ti_5O_{12}$/AC composite was extended from 0.1 to 2.5 V, redox peaks and electric double layer property were revealed. The initial discharge capacity of $Li_4Ti_5O_{12}$/AC composite was 218 mAh $g^{-1}$ at 1 C. The enhancement of discharge capacity was attributed to electric double layer of added activated carbon.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.267-267
• /
• 2012

$TiO_2$-Ni inverse catalysts were prepared using atomic layer deposition (ALD) process and catalytic $CO_2$ reforming of methane (CRM) reaction over catalysts (either bare Ni or $TiO_2$ coated-Ni particles) were performed using a continuous flow reactor at $800^{\circ}C$. $TiO_2$-Ni inverse catalyst showed higher catalytic reactivity at initial stage of CRM reactions at $800^{\circ}C$ comparing to bare Ni catalysts. Moreover, catalytic activity of $TiO_2$/Ni catalyst was kept high during 13 hrs of the CRM reactions at $800^{\circ}C$, whereas deactivation of bare Ni surface was started within 1hr under same conditions. The results of surface analysis using SEM, XPS, and Raman showed that deposition of graphitic carbon was effectively suppressed in a presence of $TiO_2$ nanoparticles on Ni surface, thereby improving catalytic reactivity and stability of $TiO_2$/Ni catalytic systems. We suggest that utilizing decoration effect of metal catalyst with oxide nanoaprticles is of great potential to develop metal-based catalysts with high stability and reactivity.

• Journal of Environmental Health Sciences
• /
• v.47 no.6
• /
• pp.540-547
• /
• 2021

Background: Indoor air pollutants are caused by a number of factors, such as coming in from the outside or being generated by internal activities. Typical indoor air pollutants include nitrogen dioxide and carbon monoxide from household items such as heating appliances and volatile organic compounds from building materials. In addition there is carbon dioxide from human breathing and bacteria from speaking, coughing, and sneezing. Objectives: According to recent research results, most indoor air pollution is known to be greatly affected by internal factors such as burning (biomass for cooking) and various pollutants. These pollutants can have a fatal effect on the human body due to a lack of ventilation facilities. Methods: We fabricated a polydopamine (PDA) layer with Ti substrates as a coating on supported glass fiber fabric to enhance its photo-activity. The PDA layer with TiO₂ was covalently attached to glass fiber fabric using the drop-casting method. The roughness and functional groups of the surface of the Ti substrate/PDA coated glass fiber fabric were verified through infrared imaging microscopy and field emission scanning electron microscopy (FE-SEM). The obtained hybrid Ti substrate/PDA coated glass fiber fabric was investigated for photocatalytic activity by the removal of ammonia and an epidermal Staphylococcus aureus reduction test with lamp (250 nm, 405 nm wavelength) at 24℃. Results: Antibacterial properties were found to reduce epidermal staphylococcus aureus in the Ti substrate/PDA coated glass fiber fabric under 405 nm after three hours. In addition, the Ti substrate/PDA coated glass fiber fabric of VOC reduction rate for ammonia was 50% under 405 nm after 30 min. Conclusions: An electron-hole pair due to photoexcitation is generated in the PDA layer and transferred to the conduction band of TiO₂. This generates a superoxide radical that degrades ammonia and removes epidermal Staphylococcus aureus.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.156.1-156.1
• /
• 2016

Nickel sulfide (NiS) is one of the most promising candidates as an electrode material for supercapacitors due to its good capacitive properties, high electrical conductivity and low cost. In addition to the development of the new electrode materials, nanostructuring the electrode surface is one of the main issues in enhancing the capacitive performance of the supercapacitors because the increased surface area can improve the charge transfer and energy storage processes occurring at the electrode surface. However, most nanofabrication techniques require complicated and delicate nanoprocesses, and hence are not suitable for practical use. In this work, we developed a simple method to fabricate nanostructured NiS electrodes by depositing NiS onto $TiO_2$ nanoparticles. First, $TiO_2$ nanoparticles were spin-coated on a fluorine-doped tin oxide (FTO) substrate, and then NiS layers were deposited onto the $TiO_2$ nanoparticles by consecutive dip-coatings in the solutions containing nickel and sulfur precursors. This nanostructured NiS electrode showed significantly improved capacitive properties compared to the electrode of NiS films deposited without $TiO_2$ nanoparticles. The asymmetric full-cell supercapacitor with this nanostructured NiS electrode and activated carbon electrode was also fabricated and investigated.

• Journal of Sensor Science and Technology
• /
• v.31 no.2
• /
• pp.102-106
• /
• 2022

Currently, the demand for real-time monitoring of water quality has increased dramatically. Total organic carbon (TOC) analysis is a suitable method for real-time analysis compared with conventional biochemical oxygen demand (BOD) and chemical oxygen demand (COD) methods in terms of analysis time. However, this method is expensive because of the complicated internal processes involved. The photocatalytic titanium dioxide (TiO2)-based TOC method is simpler as it omits more than three preprocessing steps. This is because it reacts only with organic carbon (OC) without extra processes. We optimized the rate between the TiO2 photocatalyst and binder solution and the TiO2 concentration. The efficiency was investigated under 365 nm UV exposure onto a TiO2 coated substrate. The optimized conditions were sufficient to apply a real-time monitoring system for water quality with a short reaction time (within 10 min). We expect that it can be applied in a wide range of water quality monitoring industries.

• Journal of Surface Science and Engineering
• /
• v.28 no.6
• /
• pp.368-375
• /
• 1995

Thermal CVD method is in general used for the fabrication of TiC/$Al_2O_3$-coated carbide tools. The growth of TiC layer and the coating morphology depended on the chemical composition of the hard metal substrate on which the tool properties were strongly influenced. TiC-coated layer was grown by the diffusion of carbon from the substrate, whereas the growth of $Al_2O_3$ layer was unrelated to the composition of substrate. In the nitride hard coatings of Zr, Nb and Mo metals deposited on high speed steel substrate by magnetron sputtering, the reactivity of the metal elements was decreased with increasing group number in one period of the periodic system. The hard material films exhibited the highest adhesion with the chemical composition of stoichiometry or substoichiometry. The critical load as a measure of adhesion was evaluated using scratch tester. The CVD tools indicated the values of 80 and 40N in the coated layers with proper bonding to the substrate and with $\eta$ phase of 1$\mu\textrm{m}$ in the interface respectively, but the nitride films prepared by sputtering of PVD showed only the values between 10 and 20N.

• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.167-173
• /
• 2010

In this study, we used activated carbon (AC) and titanium oxysulfate as a titanium precursor to prepare carbon/titania composites. We then mixed it with bentonite in different ratios to make a carbon/titania/bentonite monolith for use in architecture bricks by using Phenolic rosin (PR) as a bonding agent. The physicochemical properties of the prepared composites were analyzed by BET surface area, scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray analysis (EDX), self-cleaning effect and bactericidal tests. The BET surface areas increased as the ratio of carbon/titania composites increased. The SEM microscopy showed that the $TiO_2$ and bentonite were coated on the surface of the AC. The XRD patterns showed a mixture structure of anatase and rutile of $TiO_2$ with a clear $SiO_2$ structure. The EDX spectra of the carbon/titania/bentonite monolith confirmed the presence of various elements, namely C, O, Ti and Si, as well as other, impure elements. Moreover, to determine the self-cleaning effect of the carbon/titania/bentonite monolith, we used methylene blue (MB, $C_{16}H_{18}N_3S{\cdot}Cl{\cdot}3H_2O$) in an aqueous solution under the irradiation of visible light. Accordingly, all of the samples had excellent degradation of the MB solution. Furthermore, it was observed that the composites with sunlight irradiation had a greater effect on E. coli than any other experimental conditions.