• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 추계학술발표대회 논문집
• /
• pp.42-45
• /
• 2003

Nondestructive damage sensing and mechanical properties for acid-treated carbon nanotube (CNT) and nanofiber (CNF)/epoxy composites were investigated using electro-micromechanical technique and acoustic emission (AE). Carbon black (CB) was used to compare to CNT and CNF. The results were compared to the untreated case. The fracture of carbon fiber was detected by nondestructive acoustic emission (AE) relating to electrical resistivity under double-matrix composites test. Sensing for fiber tension was performed by electro-pullout test under uniform cyclic strain. The sensitivity for fiber damage such as fiber fracture and fiber tension was the highest for CNT/epoxy composites. Reinforcing effect of CNT obtained from apparent modulus measurement was the highest in the same content. For surface treatment case, the damage sensitivity and reinforcing effect were higher than those of the untreated case. The results obtained from sensing fiber damage were correlated with the morphological observation of nano-scale structure using FE-SEM. The information on fiber damage and matrix deformation and reinforcing effect of carbon nanocomposites could be obtained from electrical resistivity measurement as a new concept of nondestructive evaluation.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 춘계학술발표대회 논문집
• /
• pp.117-120
• /
• 2003

Electro-micromechanical techniques were applied using four-probe method for carbon nanotube (CNT) or nanofiber (CNF)/epoxy composites with their content. Carbon black (CB) was used to compare with CNT and CNF. The fracture of carbon fiber was detected by nondestructive acoustic emission (AE) relating to electrical resistivity for double-matrix composites test. Sensing for fiber tension was performed by electro-pullout test under uniform cyclic strain. The sensitivity for fiber damage such as fiber fracture and fiber tension was the highest for CNT/epoxy composites, and in CB case they were the lowest compared with CNT and CNF. Reinforcing effect of CNT obtained from apparent modulus measurement was the highest in the same content. The results obtained from sensing fiber damage were correlated with the morphological observation of nano-scale structure using FE-SEM. The information on fiber damage and matrix deformation and reinforcing effect of carbon nanocomposites could be obtained from electrical resistivity measurement as a new concept of nondestructive evaluation.

• Composites Research
• /
• 제31권6호
• /
• pp.299-303
• /
• 2018

탄소섬유 강화 PA6 복합재료의 탄소섬유-메트릭스간 계면결합력과 반응중합도 향상을 위해서 기존 탄소섬유의 에폭시 사이징제를 디사이징처리하여 에폭시를 제거한 후 우레탄계, 나일론계, 페녹시계 사이징제로 재처리해주었으며, 리사이징처리된탄소섬유의표면을관찰하였다. 리사이징처리된탄소섬유의계면결합력은 IFSS(Interfacial shear strength)를 통해서 확인하였으며, 계면 결합 강도 측정 후 파단면은 주사전자현미경을 통해서 관찰하였다. 나일론계와 페녹시계 사이징제로 처리된 탄소섬유가 우레탄계 사이징에 비해 계면 결합력이 상승한 것을 확인하였다. 우레탄계 리사이징 처리된 탄소섬유는 기존 에폭시 사이징 탄소섬유보다 계면 결합력이 감소한 것으로 확인되었다. 이 결과는 기존 탄소섬유의 저활성과 평활성을 제거하여 탄소섬유와 나일론6 사이의 계면 결합력이 향상된 것으로 판단된다.

• 한국수소및신에너지학회논문집
• /
• 제25권2호
• /
• pp.131-138
• /
• 2014

Highly conductive bipolar plate for polymer electrolyte membrane fuel cell (PEMFC) was prepared using phenol novolac-type epoxy/graphite powder (GP)/carbon fiber filament (CFF) composite, and a rubber-modified epoxy resin was introduced in order to give elasticity to the bipolar plate graphite fiber (GF) was incorporated in order to improve electrical conductivity. To find out the cure condition of the mixture of novolac-type and rubber-modified epoxies, differential scanning calorimetry (DSC) was carried out and their data were introduced to Kissinger equation. And tensile and flexural tests were carried out using universal testing machine (UTM) and the surface morphology of the fractured specimen and the interfacial bonding between epoxy matrix and CFF or GF were observed by a scanning electron microscopy (SEM).

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1990년도 제12회 학술강연회초록집
• /
• pp.63-68
• /
• 1990

Friction and wear behavior of a unidirectional high modulus carbon fiber reinforced epoxy composite exposed to high and low humidity was experimentally examined with various sliding speeds. The results show that the moisture at the sliding surface greatly influences friction and wear properties of the composite. It is also discoverd that the difference in friction and wear behavior between samples with different fiber orientations is mainly due to the anisotropic properties caused by the microstructure of oriented graphite crystals in the carbon fibers and the macrostructure of fiber orientation in the matrix.

• Tribology and Lubricants
• /
• 제6권2호
• /
• pp.88-93
• /
• 1990

Friction and wear behavior of a unidirectional high modulus carbon fiber reinforced epoxy composite exposed to high and low humidity was experimentally examined with various sliding speeds. The results show that the moisture at the sliding surface greatly influences friction and wear properties of the composite. It is also discoverd that the difference in friction and wear behavior between samples with different fiber orientations is mainly due to the anisotropic properties caused by the microstructure of oriented graphite crystals in the carbon fibers and the macrostructure of fiber orientation in the matrix.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 추계학술발표대회 논문집
• /
• pp.55-58
• /
• 2003

This paper presents a study on the permittivities of the carbon nano fiber/epoxy composite at microwave frequency. The permittivities of composite materials depend on the concentrations and the dispersion methods of the carbon nano fibers. The experimental values of complex permittivities were obtained for the specimen made by dispersion method using ethyl alcohol as dispersion media and compared with the results by simple mechanical mixing method.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1991년도 춘계학술대회 논문집
• /
• pp.22-31
• /
• 1991

Machining with boring bars frequently induce chatter vibration because of the low stiffness and damping of cantilever shape of boring bars. To increase stiffness and damping, a carbon fiber epoxy composite boring bar was designed, manufactured and tested. The natural frequency of the carbon fiber epoxy composite boring bar in the free-free end condition was incerased more than 50% over that of the steel boring bar, and the damping of the carbon fiber epoxy composite boring bar was also increased 450%. The fundamental natural frequency of the carbon fiber epoxycomposite boring bar in the cantilever beam condition was found to be increased 20-30% over that of the steel boring bar in overhang length range 140-200mm. In machining S45C tapered workpieces, the limit of the overhang length of the steel boring bar was about 170mm in cutting speed 140m/min.

• Composites Research
• /
• 제36권4호
• /
• pp.259-263
• /
• 2023

This study investigated the open hole tensile (OHT) properties of carbon fiber/epoxy composites and compared them to bolt joint tensile (BJT) properties. The net nominal modulus and strength (1376 MPa) were found to be higher than the gross nominal strength (1041 MPa), likely due to increasing hole size. The OHT and BJT specimens exhibited similar stiffness, as expected without bolt rotation causing secondary bending. OHT specimens experienced a sharp drop in stress indicating unstable crack propagation, delamination, and catastrophic failure. BJT specimens failed through shear out on the bolt side and bearing failure on the nut side, involving fiber kinking, matrix splitting, and delamination, resulting in lower strength compared to OHT specimens. The strength retention of carbon fiber/epoxy composites with open holes was 66%. Delamination initiation at the hole's edge caused a reduction in the stress concentration factor. Filling the hole with a bolt suppressed this relieving mechanism, leading to lower strength in BJT specimens compared to OHT specimens. Bolt joint efficiency was calculated as 15%. The reduction in strength in bolted joints was attributed to fiber-matrix splitting and delamination, aligning with Hart Smith's bolted joint efficiency diagram. These findings contribute to materials selection and structural reliability estimation for carbon fiber/epoxy composites. They highlight the behavior of open hole and bolt joint configurations under tensile loading, providing valuable insights for engineering applications.

• 한국해양공학회지
• /
• 제14권3호
• /
• pp.90-99
• /
• 2000

This study has been investigated about the influence of moisture environment properties in the unidirectional and cross laminated carbon fiber/epoxy and glass fiber/epoxy composites. As a results, it was found that the weight gain of water increased with the immersion time and the mechanical properties were decreased with the weight gain of water. And it was also shown that the mechanical properties of carbon fiber/epoxy laminates were better than those of glass fiber/epoxy laminates. And a gap of the mechanical properties between the two kinds of laminates was increasing with the immersion time in distilled water of 80$^{\circ}C $. Mechanical properties which decreased by moisture absorption in the CF and GF reinforced laminates were recovered up to some extent by drying in oven at 80$^{\circ}C $ for 10 days.