• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.89-92
• /
• 2001

Drop weight impact tests were performed to investigate the impact behavior of carbon fiber/epoxy composite laminates reinforced by short fibers and other interleaving materials. Characterization techniques, such as cross-sectional fractography and scanning acoustic microscopy, were employed quantitatively to assess the internal damage of some composite laminates. Scanning electron microscopy was used to observe impact damage and fracture modes on specimen fracture surfaces. The results show that composite laminates experience various types of fracture; delamination, intra-ply cracking, matrix cracking and fiber breakage depending on the interlayer materials. Among the composite laminates tested in this study, the composites reinforced by Zylon fibers showed very good impact damage resistance with medium level of damage, while the composites interleaved by poly(ethylene-co-acrylic acid) (PEEA) film is expected to deteriorate the bulk strength due to the reduction of fiber volume fraction, even though the damaged area is significantly reduced.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.11 no.6
• /
• pp.169-174
• /
• 2012

Electromagnetic interference(EMI) shielding effectiveness(SE) was investigated in of woven fabric made of epoxy/copper-nickel fabrics and nickel coated carbon fiber reinforced acrylonitrile-butadiene-styrene(ABS) composites. The coaxial transmission line method was used to measure the EMI shielding effectiveness of the composites. We designed and constructed a measuring system, consisting of a network analyzer and a device that plays the serves as a sample holder and at the same time as a transmission medium of the incident electromagnetic wave. The measurement of SE were carried out frequency range from 100MHz to 2GHz. It is observed that the SE of the composits is the frequency dependent increase with the increase in nickel coated carbon fibre volume fraction. The nickel coating with 20wt% ABS composite was shown to exhibit up to 60dB of SE. The result that nickel coated carbon fibre ABS composite can be used for the purpose of EMI shielding as well as for some microwave applications.

• Composites Research
• /
• v.34 no.2
• /
• pp.82-87
• /
• 2021

The mechanical properties of carbon fiber-reinforced epoxy composites (CFRPs) are greatly dependent on the interfacial adhesion between the carbon fibers and the epoxy matrix. Introducing nanomaterial reinforcements into the interface is an effective approach to enhance the interfacial adhesion of CFRPs. The main purpose of this work was to introduce graphitic nanofiber (GNFs) between an epoxy matrix and carbon fibers to enhance interfacial properties. The composites were reinforced with various concentrations of GNFs. For all of the fabricated composites, the optimum GNF content was found to be 0.6 wt%, which enhanced the interlaminar shear strength (ILSS) and fracture toughness (KIC) by 101.9% and 33.2%, respectively, compared with those of neat composites. In particular, we observed a direct linear relationship between ILSS and KIC through surface free energy. The related reinforcing mechanisms were also analyzed and the enhancements in mechanical properties are mainly attributed to the interfacial interlocking effect. Such an effort could accelerate the conversion of composites into high performance materials and provide fundamental understanding toward realizing the theoretical limits of interfacial adhesion and mechanical properties.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.10a
• /
• pp.116-120
• /
• 2001

Fiber fracture is one of the dominant failure phenomena to determine total mechanical properties in composites. Fiber fracture locations were measured by optical microscopic method and acoustic emission (AE) as functions of matrix toughness and surface treatment by the electrodeposition (ED), and then two methods were compared. Two AE sensors were attached on the epoxy specimen and fiber fracture signals were detected with elapsed time. The interfacial shear stress (IFSS) was measured using tensile fragmentation test and AE system. In ED-treated case, the number of the fiber fracture measured by an optical method and AE was more than that of the untreated case. The signal number measured by AE were rather smaller than the number of fragments measured by optical method, since some fiber fracture signals were lost while AE detection. However, one-to-one correspondence between the x-position location by AE and real break positions by optical method was generally established well. The fiber break source location using AE can be a valuable method to measure IFSS for semi- or nontransparent matrix composites nondestructively (NDT).

• Composites Research
• /
• v.30 no.3
• /
• pp.215-222
• /
• 2017

The effect of a multi walled carbon nanotubes (MWNCT) on the adhesive properties and thermal properties of epoxy were studied by double lap-shear tests. Epoxy/MWCNT resins were prepared from a different amount of the MWCNT incorporated into the epoxy resins (araldite 2011). Steel plates and carbon fiber reinforced plastics (CFRP) were chosen as materials. Mechanical tests were performed by a universal testing machine (UTM). The analysis of thermal properties were conducted by a thermogravimetric analyzer (TGA) and a differential scanning calorimetry (DSC). The fracture surface morphology was examined using a scanning electron microscopy (SEM) and optical microscope. Compared to neat epoxy, it was found that the mechanical properties of epoxy/MWCNT resins are increased.

• Composites Research
• /
• v.36 no.3
• /
• pp.154-161
• /
• 2023

This study explored the feasibility of replacing a metal link with a carbon fiber/epoxy composite link and assessed its capacity to withstand a given load condition using failure criteria. The micromechanics of failure (MMF) criterion was employed to predict the failure mode of the composite material, and mechanical tests were conducted to obtain reference strength parameters for MMF. The findings revealed that the stress distribution was concentrated near the hole, and weaknesses were found around the hole and at the end of the link under bending conditions. Based on the failure index, matrix tensile failure was predicted at the end of the link, and fiber compression failure occurred near the hole. The methods and results obtained from this study can provide valuable guidelines for assessing the safety of composite materials under specific load conditions when replacing metal parts with carbon fiber/epoxy composites to achieve weight reduction.

• Composites Research
• /
• v.19 no.4
• /
• pp.7-14
• /
• 2006

Interfacial shear strength between epoxy and carbon fiber has been analyzed utilizing the microbond specimen with an epoxy micro-droplet adhered onto single carbon fiber. The interfacial shear stress distributions along the fiber/matrix interface were calculated by finite element analysis using three kinds of finite element models such as droplet model, circular-crosssection model and pull-out model. Conclusions were obtained as follows. (1) Interfacial shear stress distribution showed that larger stresses were concentrated in the fiber/matrix interface for microbond test than for pull-out test. Thus, debonding at the fiber/matrix interface during microbond test was liable to occur at low load level. (2) Microbond test showed higher interfacial strength which was caused by various effects of micro-droplet geometry and size as well as stress concentration in the region contacting with the micro-vise tip.

• Composites Research
• /
• v.27 no.4
• /
• pp.168-173
• /
• 2014

The optimum condition of glass fiber/epoxy composites was investigated according to mixing ratio of two epoxy matrices. Novolac type epoxy and isocyanate modified epoxy were used as composites matrix. Based on chemical composition of mixing matrix, optimum mixing ratio of epoxy resins was obtained through various experiments. In order to investigate thermal stability and interface of epoxy resin, glass transition temperature was observed by DSC instrument, and static contact angle was measured by reflecting microscope. Change of IR peak and $T_g$ was conformed according to different epoxy mixing ratio. After fabrication of glass fiber/epoxy composites, tensile, compression, and flexural properties were tested by UTM by room and high temperature. The composites exhibited best mechanical properties when epoxy mixing ratio was 1:1.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.134-138
• /
• 1999

For the stable operation of high speed aerostatic spindle, the low rotational inertia and high damping ratio of spindle shafts as well as high fundamental natural frequency are indispensable. Conventional steel spindles are not appropriate for very high speed operation because of their high rotational inertia and low damping ratio. In this study, the composite spindles with aerostatic bearing were designed and manufactured with carbon fiber/epoxy composite. The fundamental natural frequency of the composite spindle was evaluated through the modal testing.

• Journal of the Korean Ceramic Society
• /
• v.38 no.1
• /
• pp.52-55
• /
• 2001

Polyacrylonitrile(PAN)-based 탄소섬유와 epoxy resin matrix 내에 장착된 PAN-based 탄소섬유의 전기저항을 탄소섬유와 파괴될 때까지 인장강도를 증가시키며 측정하였다. 탄소섬유가 끊어져 측정 계기가 open-circuit을 나타내기 전까지 탄소섬유의 전기저항 값은 strain이 증가할수록 증가하였으며, epoxy resin은 탄소섬유의 저항값 측정에 거의 영향을 미치지 않았다. 탄소섬유의 저항값 변화는 strain에 대해 정확도 1% 이내로 예측(calibrate)할 수 있었으며 재현성 또한 우수하였다. 따라서 탄소섬유는 재료의 기계적 강도를 증가시키기 위해 사용될 수 있을 뿐만 아니라 구조재료의 파괴를 예측할 수 있는 스마트 센서로서도 사용할 수 있다는 가능성을 확인하였다.