Polysilicon on insulator has been recrystallized by zone melting recrystallization method with graphite strip heaters. Experiments are performed with non-seed SOI structures. When the capping layer thickness of Si$\_$3/N$\_$4//SiO$\_$2/ is 2.0.mu.m, grain boundaries are about 120.mu.m spacing and protrusions reduced. After the seed SOI films are annealed at 1100.deg. C in NH$\_$3/ ambient for 3 hours, the recrystallized silicon surface has convex shape. After ZMR process, the tensile stress is 2.49*10$\^$9/dyn/cm$\^$2/ and 3.74*10$\^$9/dyn/cm$\^$2/ in the seed edge and seed center regions. The phenomenon of convex shape and tensile stress difference are completely eliminated by using the PSG/SiO$\_$2/ capping layer. The characterization of SOI films are showed that the SOI films are improved in wetting properties. N channel SOI MOSFET has been fabricated to investigate the electrical characteristics of the recrystallized SOI films. In the 0.7.mu.m thickness SOI MOSFET, kink effects due to the floating substrate occur and the electron mobility was calculated from the measured g$\_$m/ characteristics, which is about 589cm$\^$2//V.s. The recrystallized SOI films are shown to be a good single crystal silicon.
The influence of silicon surface damage on nickel-silicide (NiSi) has been characterized and H$_2$ anneal and TiN rapping has been applied to suppress the electrical, morphological deterioration phenomenon incurred by the surface damage. The substrate surface is intentionally damaged using Ar IBE (Ion beam etching) which can Precisely control the etch depth. The sheet resistance of NiSi increased about 18% by the surface damage, which is proven to be mainly due to the reduced silicide thickness. It is shown that simultaneous application of H: anneal and TiN capping layer is highly effective in suppressing the surface damage effect.
Impurity-free vacancy diffusion 방법을 이용하여 압축 응력을 가진 InGaAs/InGaAsP 다중 양자 우물 구조에서 열처리 온도에 따른 무질서 정도를 조사하였다. InGaAs/SiO$_2$ cap 구조가 InP/$SiO_2$ cap 구조보다 급속열처리 (rapid thermal annealing : RTA) 과정에서 더 많은 청색 천이를 나타내었다. 열처리 온도 $700^{\circ}C$에서, InGaAs/$SiO_2$ cap 구조의 경우 다중양자우물의 밴드갭 파장은 1.55 $\mu\textrm{m}$대역에서 1.3 $\mu\textrm{m}$ 대역으로 이동하였으며, InGaAs/$SiO_2$ cap 구조와 InP/$SiO_2$ cap 구조의 밴드갭 파장차이는 195 nm (123 meV)로 높은 선택성을 나타내었다. 또한, DCXRD 스펙트럼으로부터 다중양자우물 구조에서 균일한 합금형태로 완전히 무질서화되는 것을 볼 수 있었다.
반도체 소자의 고속화, 고집적화, 고신뢰성화에 대한 요구는 알루미늄 합금으로부터 구리로의 배선 물질의 변화를 유도하였다. 낮은 비저항과 높은 내열화성을 특징으로 하는 구리는 그 전기적, 재료적 특성이 알루미늄과 상이하여 배선 형성에 있어 새로운 주변 재료와 공법을 필요로 한다. 본 총설에서는 상감공정(damascene process)을 사용하는 다층 구리 배선 공정에 있어 핵심이 되는 구리 전해 도금(electrodeposition) 공정을 중심으로 확산 방지막(diffusion barrier) 및 도전층(seed layer), 바닥 차오름(bottom-up filling)을 위한 전해/무전해 도금용 유기 첨가제, 화학적 기계적 평탄화(chemical mechanical polishing) 및 표면 보호막(capping layer) 기술 등의 금속화 공정에 대한 개요와 개발 이슈를 소개하고 최근의 연구 결과를 통해 구리 배선 공정의 최신 연구 동향을 소개하였다.
오염된 퇴적물로부터 인 용출 저감을 위한 최적의 capping 소재를 개발하기 위해 lab-scale 실험을 25 L 아크릴 컬럼을 이용하여 실시하였다. 실험에 사용된 퇴적물 내 입도는 8.8 $\Phi$로 매우 세립한 clay로 조성되어 있으며, 유기탄소 함량($C_{org}$)은 2%로 높다. Batch 실험에 사용된 capping 소재는 Brucite($Mg(OH)_2$), Sea sand($SiO_2$), Granular-gypsum($CaSO_4{\cdot}2H_2O$), Double layer(brucite+sand)와 Control을 30일 동안 비교 평가하였다. 실험기간 동안 용출된 인의 flux는 14.6 $mg{\cdot}m^{-2}{\cdot}d^{-1}$, 9.5 $mg{\cdot}m^{-2}{\cdot}d^{-1}$, 5.2 $mg{\cdot}m^{-2}{\cdot}d^{-1}$, 4.2 $mg{\cdot}m^{-2}{\cdot}d^{-1}$, 3.1 $mg{\cdot}m^{-2}{\cdot}d^{-1}$로 Control>Sea sand>Granular-gypsum>Double layer>Brucite 순으로 각각 나타났다. Brucite를 적용한 컬럼의 경우, 인 용출 제어 효율이 70% 이상 높게 나타났으며, Sea sand를 적용한 경우에는 35%의 효율만을 보였다. 특히, Brucite를 적용한 컬럼의 표층 퇴적물내 pH는 $8.0{\sim}9.5$로 다소 높게 유지되었으며, 이러한 효과는 퇴적물을 약알카리성으로 유지하여 황산염환원균이 증식할 수 없는 환경을 조성하여 생물에 독성이 있는 $H_2S$ 발생을 억제시킬 수 있다. Gypsum을 적용할 경우, 퇴적물내 빠른 초기 속성화작용의 진행과 충분한 $SO_4^{2-}$-의 공급으로 methanogenesis 진행를 저하시킬 수 있다. 따라서 Brucite와 Gypsum을 적용할 경우, 퇴적물 내 인의 존재형태가 광물(mineral)의 형태인 $Mg_5(OH)(PO_4)_3$, pyrite, apatite-mineral의 형태로 진행되어 퇴적물로부터 인의 용출을 줄일 수 있다.
정체수역 호소 퇴적물로부터 인 용출 저감을 위한 최적의 In-situ 처리 방법을 제시하고자 실험실 규모의 batch test를 수행하였다. 실험에 사용된 퇴적물의 성상은 평균입도 $7.7{\phi}$(mud)로 매우 세립하고, 유기탄소 함량은 2.4%로 매우 높다. 인 용출 실험은 수층 미생물의 영향을 고려한 경우와 미생물의 영향을 배제한 호소수와 증류수로 구분하여 총 12개 컬럼을 비교 평가하였다. In-situ capping 소재로는 모래와 황토를 사용하였으며, in-situ chemical treatment로는 Fe-Gypsum, $SiO_2$-Gypsum의 산화제를 적용하였다. 또한 산화제와 모래층을 결합시킨 복합층에 대해서도 비교 평가하였다. 미생물의 영향을 고려한 호소수의 경우, 실험 초기에는 인의 농도가 급격히 감소하다 10일 이후부터 서서히 증가되는 것을 확인할 수 있었다. 이는 수층의 미생물에 의해 인이 섭취(uptake)되었다가 다시 용출되는데 시간이 소요되는 것으로 나타났다. 30일간 퇴적물로부터 용출된 인의 flux는 control의 경우 $3.0mg/m^2{\cdot}d$로 매우 높고, 모래층(5 cm), 황토층(5 cm)으로 rapping을 한 경우 역시 충분한 압밀이 이루어지지 않아 $2.5mg/m^2{\cdot}d,\;1.8mg/m^2{\cdot}d$로 인 저감 효율이 낮았다. 화학적 소재를 적용한 Fe-gypsum와 $SiO_2$-gypsum은 $1.4mg/m^2{\cdot}d$로 control과 비교시 인 용출 저감 효율이 약 40% 이상으로 나타났다. 복합층으로 rapping을 한 경우는 $1.0mg/m^2{\cdot}d$로 60% 이상의 높은 인 저감 효율을 보였다. 즉, 오염퇴적물에 산화제로서 gypsum($CaSO_4{\cdot}2H_2O$) 적용은 인의 용출을 감소시키며, 퇴적물내 황산염이 서서히 용해되어 SRB(sulfate reducing bacteria)의 활성과 유기물의 광물화를 촉진시킬 수 있다.
한국정보디스플레이학회 2007년도 7th International Meeting on Information Display 제7권1호
/
pp.724-726
/
2007
We have developed the synthesis method to reduce the surface oxide layer in Cu nanoparticle, which is based on controlling the molecular weight of capping polymer. In addition, we demonstrated how the variation of oxide layer thickness influences the resistivity of conductive Cu film.
We investigated the influence of blistering on $Al_2O_3$/SiON stacks and $Al_2O_3$/SiNx:H stacks passivation layers. $Al_2O_3$ film provides outstanding Si surface passivation quality. $Al_2O_3$ film as the rear passivation layer of a p-type Si solar cell is usually stacked with a capping layer, such as $SiO_2$, SiNx, and SiON films. These capping layers protect the thin $Al_2O_3$ layer from an Al electrode during the annealing process. We compared $Al_2O_3$/SiON stacks and $Al_2O_3$/SiNx:H stacks through surface morphology and minority carrier lifetime after annealing processes at $450^{\circ}C$ and $850^{\circ}C$. As a result, the $Al_2O_3$/SiON stacks were observed to produce less blister phenomenon than $Al_2O_3$/SiNx:H stacks. This can be explained by the differences in the H species content. In the process of depositing SiNx film, the rich H species in $NH_3$ source are diffused to the $Al_2O_3$ film. On the other hand, less hydrogen diffusion occurs in SiON film as it contains less H species than SiNx film. This blister phenomenon leads to an increase insurface defect density. Consequently, the $Al_2O_3$/SiON stacks had a higher minority carrier lifetime than the $Al_2O_3$/SiNx:H stacks.
InP 기판위에 자발성장법으로 성장된 InAs 양자점은 $1.55{\mu}m$ 영역에서 발진하는 양자점 반도체 레이저 다이오드 및 광 증폭기를 제작할 수 있기 때문에 많은 관심을 받고 있다. 광통신 대역의 $1.55{\mu}m$ 반도체 레이저 다이오드 및 광 증폭기 분야에서 InAs/InP 양자점이 많은 관심을 받고 있으나, InAs/GaAs 양자점에 비해 제작이 어려운 단점을 가지고 있다. InAs/InP 양자점은 InAs/GaAs 양자점에 비해 격자 불일치가 작아 양자점의 크기가 크고 특히 As 계 박막과 P 계박막의 계면에서 V 족 원소 교환 반응으로 계면 특성 저하가 발생하여 성장이 까다롭다. As 과 P 간의 교환반응은 성장온도와 V/III 에 의해 크게 영향을 받는 것으로 보고되었다. 그러나, P계 InGaAsP 박막 위에 InAs 성장 시 발생하는 As/P 교환반응에 대한 연구는 매우 적다. 본 연구에서는 InGaAsP 박막 위에 InAs 양자점 성장 시 GI (growth interruption)에 의한 As/P 교환반응이 InAs 양자점의 형상 및 광학적 특성에 미치는 영향을 연구하였다. 시료는 수직형 저압 Metal Organic Chemical Vapor Deposition (MOCVD)를 이용하여 $520^{\circ}C$의 온도에서 성장하였다. 그림1(a) 구조의 양자점은 InP (100) 기판위에 InP buffer layer를 성장한 후 InP와 격자상수가 일치하는 $1.1{\mu}m$ 파장의 InGaAsP barrier를 50 nm 성장하였다. 그 후 As 분위기 하에서 다양한 GI 시간을 주었고 그 위에 InAs 양자점을 성장하였다. 양자점 성장 후 InGaAsP barrier를 50 nm, InP capping layer를 50 nm 성장하였다. AFM측정을 위해 InP capping layer 위에 동일한 GI 조건의 InAs/InGaAsP 양자점을 성장하였고 양자점 성장 후 As분위기 하에 온도를 내려주었다. 그림1(b) 구조의 양자점은 그림1(a) 와 모든 조건은 동일하나 InAs 양자점과 InGaAsP barrier 사이에 GaAs 2ML를 삽입한 구조이다. 양자점 형상 특성 평가는 Atomic force microscopy를 이용하였으며, 광특성 분석은 Photoluminescence를 이용하였다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.