• Journal of Periodontal and Implant Science
• /
• 제32권4호
• /
• pp.753-767
• /
• 2002

The purpose of this study was to evaluate histologically the effect of LiF-maleic acid added calcium aluminate(LM-CA) bone cement & CA-PMMA composite bone cement on the healing of calvarial defect in Sprague-Dawley rats. The critical size defects were surgically produced in the calvarial bone using the 8mm trephine bur. The rats were divided in three groups : In the control group, nothing was applied into the defect of each rat. LM-CA bone cement was implanted in the experimental group 1 and CA-PMMA composite bone cement was implanted in the experimental group 2. Rats were sacrificed at 2, 8 weeks after surgical procedure. The specimens were examined by histologic analysis, especially about the bone-cement interface and the response of surrounding tissue. The results are as follows; 1. In the control group, inflammatory infiltration was observed at 2 weeks. At 8 weeks, periosteum and duramater were continuously joined together in the defect area. But the center of defect area was filled up with the loose connective tissue. 2. In the experimental group 1, the bonding between implanted bone cement and the existing bone was seen, which more increased in 8 weeks than 2 weeks. Inflammatory infiltration and the dispersion of implanted bone cement particles were seen in both 2 weeks and 8 weeks. 3. In the experimental group 2, implanted bone itself had a dimensional stability and no bonding between implanted bone cement and the existing bone was seen in both 2 weeks and 8 weeks. Implanted bone cement was encapsulated by fibrous connective tissue. In addition, inflammatory infiltration was seen around implanted bone cement. On the basis of these results, when LM-CA bone cement or CA-PMMA composite bone cement was implanted in rat calvarial defect, LM-CA bone cement can be used as a bioactive bone graft material due to ability of bonding to the existing bone and CA-PMMA can be used as a graft material for augmentation of bone-volume due to dimensional stability.

• 한국구조물진단유지관리공학회 논문집
• /
• 제24권2호
• /
• pp.78-85
• /
• 2020

숏크리트용 콘크리트는 일반적으로 1종 보통 포틀랜드시멘트(이하 OPC)를 100% 사용한 레미콘 제품에 현장에서 별도로 숏크리트용 급결제를 약 5% 혼합하는 방식으로 사용된다. 본 연구에서는 국내에서 사용률이 높은 시멘트 광물계 급결제(calcium aluminate)를 사용한 숏크리트용 결합재로서 OPC의 분말도 및 SO₃ 함량이 모르타르 관입저항 및 압축강도, 페이스트 수화물 및 공극구조에 미치는 영향을 시험 및 분석하여 재령별 수화물의 생성량과 공극구조가 숏크리트의 모르타르 성능에 미치는 영향을 파악하였다. 향후 숏크리트용 결합재로서 최적화된 OPC를 제조하는데 활용할 수 있을 것으로 기대된다.

• 한국건설순환자원학회논문집
• /
• 제12권2호
• /
• pp.214-221
• /
• 2024

본 연구에서는 알루민산칼슘 시멘트(CAC)의 철근 부식 저항성에 관한 것으로서 철근 부식의 위험성을 예측하기 위하여 철근 부식 거동, 염화물 고정화/완충 및 염화물 침투성을 평가하였다. 알루민산칼슘 시멘트 모르타르는 양생 온도와 시멘트의 종류에 관계없이 철근에 부식이 발생하지 않은 반면, 보통포틀랜드시멘트(OPC)는 철근 표면에 심각한 부식이 발생하였다. CAC의 염화물 결합력은 OPC에 비하여 낮은 것으로 나타났지만, pH 감소에 대한 완충 능력은 CAC 페이스트가 훨씬 더 높은 것으로 나타났다. 또한 알루민산칼슘 시멘트를 사용한 시편의 모든 깊이에서 염화물 유입이 감소함으로서 철근 부식의 위험성이 낮아지는 것으로 나타났다.

• 한국세라믹학회지
• /
• 제52권6호
• /
• pp.483-488
• /
• 2015

Blast furnace slag(BFS) is well known for its hardening mechanism in ordinary Portland cement with alkali activation due to its latent hydraulic property. The possibility of using calcium compound as activator for BFS has been investigated in this study. The hydration properties of calcium compound activated BFS binders were explored using heat of hydration, powder X-ray diffraction and compressive strength testing. Heat of hydration results indicate that the hydration heat of BFS is lower than OPC paste by about 50%. And ettringite as hydration product was formed continuously as the calcium sulfate was decreased. The maximum compressive strength of hardened BFS mortar at 28 days is confirmed to be 83% as compared with hardened OPC mortar.

• 한국세라믹학회지
• /
• 제37권5호
• /
• pp.438-443
• /
• 2000

This dissertation is focused on the study over the improvement for the early strength of belite-rich cement(BRC). For this purpose, the initial hydration behaviors according to addition of different calcium sulfate types were evaluated. From the observations by XRD, DSC and SEM, the BRC II and III with the addition of natural anhydrate and flue gas desulphurization(FGD) gypsum, respectively, formed much ettringite after 7 days more than the BRC I with the addition of chemical gypsum. The compressive strength of the BRC II and III developed outstandingly due to the formation of calcium aluminate hydrate within pores of hardened BRC paste. Especially, in the case of BRC III adding FGD with low impurities, the early as well as long term compressive strengths were shown very high, compared with other specimens.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2010년도 춘계 학술대회 제22권1호
• /
• pp.475-476
• /
• 2010

Hydration products formed on the steel surface may impose the resistance to corrosion of steel when a concrete is exposed to a salt environment. In the present study, ordinary Portland cement (OPC), calcium aluminate cement (CAC) and calcium hydroxide are applied as coating materials on the steel surface to consider the hydrations of each binder at corrosion. Corrosion is measured in terms of the corrosion potential and galvanic current to detect the effects in mitigating the corrosion behavior.

• 한국건설순환자원학회논문집
• /
• 제3권3호
• /
• pp.199-205
• /
• 2015

이 연구에서는 고온의 축열재료로 사용하기 위한 알루미나 시멘트 복합재료의 역학적 및 열적 특성을 파악하고자 하였다. 알루미나 시멘트를 기본 바인더로 하고 플라이애시, 실리카퓸, CSA (calcium sulfo-aluminate) 및 그라파이트의 치환에 따른 고온에서의 물성을 파악하였다. 알루미나 시멘트 기반 복합재료의 역학적 특성으로서 열사이클 전과 후의 압축강도 및 인장강도를 측정하였다. 또한, 복합재료의 열적 특성으로서 열전도율과 비열을 측정하였다. 열사이클링 적용 이후의 잔류압축강도 측정결과, 알루미나 시멘트만을 사용한 배합과 알루미나 시멘트를 실리카퓸으로 치환한 배합의 압축강도가 크게 나타나며, 이 두 배합의 잔류강도 비는 65%를 상회한다. 그라파이트를 혼합한 복합재료의 비열이 가장 크고 이는 그라파이트의 비열이 크기 때문이다. 연구결과는 콘크리트를 고온조건에서의 축열매체로 활용하기 위한 실제적인 기초실험 자료로 활용될 수 있을 것으로 사료된다.

• 한국건축시공학회지
• /
• 제18권5호
• /
• pp.403-412
• /
• 2018

최근 순환골재의 활용에 관한 필요성이 증대되고 있으나, 순환골재의 강알칼리성으로 인해 다양한 문제들이 발생되고 있다. 순환골재의 강알칼리성은 대부분 골재 표면에 완전히 제거되지 못한 시멘트 페이스트에 의해 발현되는 것으로써 이를 해결하기 위해 이산화탄소를 활용하여 순환골재의 pH를 저감하기 위해 노력이 지속되어왔다. 그러나 기존의 이산화탄소를 이용한 처리 방법에 의해 중성화 처리된 순환골재는 시간이 지남에 따라 pH가 다시 회복된다는 문제점을 가지고 있다. 따라서 본 연구에서는 이러한 문제점을 해결하기 위한 방법으로 반응성이 뛰어난 초임계이산화탄소의 활용을 제안하며, 이를 위해 초임계상의 이산화탄소와 수화된 시멘트 페이스트간의 반응 메커니즘을 분석하였다. 그 결과 입자 형태 및 $scCO_2$ 주입량에 따라 중성화 반응정도가 현저하게 달라지는 것으로 나타났다. 특히 powder 형태 시험체에서 $scCO_2$ 주입량이 많은 고온 고압 상태에서 중성화 반응은 활발하게 이루어졌다. 이때 시멘트의 높은 pH를 주도하는 portlandite가 대부분 calcite와 aragonite의 형태로 변환되었으며, ettringite, hemicarbonate 및 monocarbonate와 같은 calcium aluminate 수화물 또한 안정적으로 존재하지 못하고 분해된 것으로 나타났다. 반면, 10mm 크기의 수화된 시멘트 페이스트는 $scCO_2$가 시험체 내부깊이 침투하지 못하고 표면에서만 반응하여, 반응 후에도 내부에 portlandite와 calcium aluminate 수화물이 잔존한다. 이로 인해 시간이 경과할수록 내부의 portlandite가 점차 용출되어 pH가 다시 상승하는 것으로 나타났다.

• 한국세라믹학회지
• /
• 제18권3호
• /
• pp.157-162
• /
• 1981

A converter slag has been heat-treated above melting point at reduced condition by cokes. As the result, most iron was separated. To make hydraulic compounds, calcium oxide was added to the reduced converter slag and the mixtures were sintered. This modified converter slag clinker mainly contained tricalcium silicate and calcium aluminates, and have a great potential to be a good hydraulic cement. The hydrates of the hydraulic compounds and gypsum with and without granulated slags, were mainly C-S-H, ettringite, calcium monosulfoaluminate hydrate, calcium aluminate hydrate, and $Ca(OH)_2$

• 한국세라믹학회지
• /
• 제16권3호
• /
• pp.164-168
• /
• 1979

In the previous paper, it was reported that formation of desirable calcium alunimate(CA) in clinker was considerably affected by sulfur-contaminated alumina which was prone to form a disadvantageous mineral, $C_4A_3S$. In this study, however, sulphate-free alumina cement was made from sulfur-free alumina refined from alunite and corresponding materials. The major minerals in the clinker were identified by X-ray diffraction patterns as calcium aluminate (CA), calcium dialuminate $(CA_2)$ and dicalcium alumino silicate $(C_2AS)$. The formation of CA was more effective with decreasing contents of silica to 2 per cent or less and sulfur in the refined alumina. Physical properties of prepared alumina cement such as setting time, stability and compressive strength were measured. The values were similar to those of commercial alumina cements.