• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.716-721
• /
• 2001

The present study describes the experimental method to measure the strain of tire. In this study. the strain distributions of tire with air pressure and vertical load were measured at the bead filler edge region and on the carcass cord using strain gauges and the results were compared with indoor bead durability test results. The strain amplitude of carcass cord near the rim check line of tire is one of the main factors that affects bead durability characteristic.

• Laser Solutions
• /
• v.8 no.3
• /
• pp.11-19
• /
• 2005

In automotive industry, light weight vehicle is one of issues because of the air pollution and the protection of environment. Therefore, automotive manufacturers have tried to adopt light materials such as aluminum alloy to production line. Aluminum welding using laser has some advantages high energy density and high productivity. It is very important to understand weld characteristic according to welding condition in order to determine the possibility of application to car body. In this study, Nd:YAG laser welding of 5182 aluminum alloy with filler wire AA5356 was carried out through experimental design according to wire feed rate, laser power and welding speed. Weld bead shape in terms of cross section photo, bead with, height of reinforcement and penetration depth and mechanical property in terms of tensile strength and formability was investigated. Analysis of variation (ANOVA) was performed to know the effect of weld parameter for weldability, laser power was statistically most significance factor of three variables.

• Journal of Welding and Joining
• /
• v.26 no.6
• /
• pp.54-58
• /
• 2008

Laser welding with AZ61 filler wire was carried out to improve formability though reduction of porosity and formation of under fill bead. Optimum welding condition and mechanical properties of butt joint for $400{\times}500{\times}1.3mm$ magnesium sheets were studied. Optimal welding conditions of laser power, welding speed, and defocusing length are 1000W, 3m/min, and 2mm, respectively. Results of tensile test indicated that both tensile strength and elongation of specimens welded with filler wire were improved at room temperature because of reduction of porosity and under-filled bead formation in addition to the precipitation hardening and microstructure refinement by Al-Mn and Mg-Al-Zn precipitates. At elevated temperature of $200{\sim}350^{\circ}C$, fracture location of tensile specimen was shifted from weld metal to base metal, indicating less softening of weld metal than base metal.

• 제어로봇시스템학회:학술대회논문집
• /
• 1996.10b
• /
• pp.792-795
• /
• 1996

In TIG welding of pipe, back bead size monitoring is important for weld quality assurance. Many researches have been performed on estimation of the back bead size by heat conduction analysis. However numerical conduction model based on many uncertain thermal parameters causes remarkable errors and thermomechanical phenomena in molten pool can not be considered. In this paper, filler wire feeding force in addition to weld current, wire feedrate, torch travel speed and orbital position angle is monitored to estimate back bead size in orbital TIG welding. Monitored welding process variables are fed into an artificial neural network estimator which has been trained with the monitored process variables (input patterns) and actual back bead size (output patterns). Experimental verification of the proposed estimation method was performed. The predicted results are in a good agreement with the actual back bead shape. The results are quite promising in that estimation of invisible back bead shape can be achieved by analyzing the welding parameters without any conventional NDT of welds.

• Journal of Welding and Joining
• /
• v.26 no.4
• /
• pp.44-49
• /
• 2008

Generally, wear plate is steel plate having improved surface contact strength and impact strength by surface hardening which is welded using materials with good corrosion resistance, wear resistance and thermal resistance property. CFP GMAW(Compound Filler Plate Gas Metal Arc Welding) is the cladding method using GMAW with the CFP, which is bound with waterglass, on the substrate. It has advantages of reducing compound powder loss, uniform penetration, and preventing hardness decrease. To develope mass production technique of CFP GMAW process for production of high quality wear plate, the method for controling shallow penetration and increasing productivity is required. In this study, twin torch method applied to CFP GMAW process for increasing productivity. And the method was developed by controling penetration control, CFP dry time, gas formation flux and water glass concentration. As a result, applying twin torch method to CFP GMAW process was possible and high quality wide bead could be made without overlap joint.

• Journal of Welding and Joining
• /
• v.22 no.1
• /
• pp.71-76
• /
• 2004

In the standpoint of the arc pressure, the effects of the filler wire feed rate on the penetration was investigated in this study. The pure Ar gas was used as a shield gas and the parameters investigated were the welding current and the filler wire feed rate. By making the experiment on the arc pressure, we could know that the arc pressure was fluctuated as the depth-into-arc of the tungsten rod. Instead of the filler wire, the tungsten rod was supplied into the molten pool to make this experiment. Because the filler wire melted in arc and then we couldn't measure the arc pressure. So, the tungsten rod - the highest melting point - was used. According to the depth-into-arc of the tungsten rod, the arc pressure could be measured by using the manometer. It was proved that the arc pressure got higher as the wire feed rate was slow. It is reported the arc pressure is proportion to welding voltage and the square of welding current. But, in the filler wire TIG welding, we could blow that arc pressure was fluctuated as the depth-into-arc of filler wire was changed. We could measure the arc pressure by the variation of the filler wire feed rate and could verify that it affected bead shape and penetration.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.226-234
• /
• 2009

The purpose of this study was to investigate the melting phenomenon of filler wire in detail and to obtain the precise temperature distribution of filler wire during GTA welding under the ultra-high welding speed condition in order to develop the ultra-high-speed GTA welding process with the pulse-heated hot-wire system by using three kinds of materials. The melting phenomenon of filler wire was observed using a high-speed camera and the temperature distribution of filler wire was measured using a radiation thermometer. From the above result, the adequate welding conditions of each material to make the GTA welding process with the ultra-high welding speed could be obtained. The ultra-high-speed GTA welding process needed the adequate wire current in order to obtain the adequate temperature distribution and the adequate melting position of filler wire. Moreover, the temperature distributions of three kinds of filler wire could be estimated by using the proposed simple estimation method.

• Journal of Ship and Ocean Technology
• /
• v.11 no.3
• /
• pp.14-23
• /
• 2007

Welding processes cause undesirable problems, such as residual stresses and deformations due to the thermal loads imposed by local heating, melting, and cooling processes. This paper presents a computational modeling technique to simulate the Gas Metal Arc Welding (GMAW) process, emphasizing the effect of the melting bead on the residual stress distribution. Both a three-bar analogy and a three-dimensional thermo-mechanical finite element analysis are carried out in order to explain the effect. Element (de)activation, enthalpy, and adjustment of the reference temperature of thermal strain are considered with respect to the effect of the weld filler metal added to the base metal during a thermo-elastic-plastic analysis. Stress distributions obtained by the present study are compared with measured values and available data from other studies. The effect of the melting bead on the residual stress distribution is discussed and demonstrated.

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.144-145
• /
• 2004

Submerged arc welding technique using metal powder as supplementary filler metal has been studied. Forward feeding was used, and the deposit rate was increased by 50%. Good bead appearance, soundness and mechanical properties were obtained with feed rate of 120g/min..

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.152-154
• /
• 2005

Austenitic stainless steel has good weldability but is sensitive to hot cracking such as solidification crack and liquation crack. In this study, the specimens of dissimilar metals made between austenitic stainless steel and Al-brass were welded by GTAW process using four different filler metals. Cracks were detected in the heat-affected zone of the stainless steel when welded with CuAl, CuSn and NiCu filler metals, but no cracks were detected a Ni filler metal was used. The cracks propagated along the grain boundary in the heat affected zone near the fusion line to base metal of 316L stainless steel. The cracks were located inside the weld bead with very fine hairline crack. All cracks initiated at the fusion line and moved forward in the base metal. From energy dispersion spectroscopy (EDS), Cu peak was detected only in the crack-opening area.