• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.2
• /
• pp.142-151
• /
• 1995

Complex alkoxides were synthesized using metal alkoxide method and were then hydrolyzed to prepare the precursors using sol - gel method. Then, the precursors were calcined in order to make barium hexaaluminate. Factors affecting the material properties of the barium hexaaluminate precursors were studied and they are the kinds and amount of alcohols, and reaction time. In addition, in the course of hydrolysis, the effects of the amount of water, reaction temperature and aging time were also studied in terms of the specific surface area and average particle size of the barium hexaaluminates.

• Journal of Magnetics
• /
• v.2 no.1
• /
• pp.16-21
• /
• 1997

Those were investigated, the crystallographic, morphological, and magnetic properties of barium ferrite film (SiO2/Si substrate) prepared by sol-gel dip coating. Appropriate sol was prepared by dissolvin barium and iron nitrate in ethylene glycol at 80$^{\circ}C$. To obtain the films, thermally oxidized p-type silicon substrate with (111) of crystallographic orientation were dipped into the sol, dried at 250$^{\circ}C$ to remove organic material, and heated at 800$^{\circ}C$ for 3 hours in air for the crystallization of barium ferrite. It was found that the particles of barium ferrite formed on the substrate exhibited needle-like shape placing parallel to the substrate and its c-axis is long axis direction. There was tendency that the coercive force in horizontal direction to the substrate was higher than that in vertical direction to it. This tendency was profound in large thickness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.714-718
• /
• 2003

Usually for the commercial preparation of barium titanate films or ceramics the reaction atmosphere must be preferably in air. However, normally air is not used because it contains carbon dioxide, which can easily react with barium to form the undesired product barium carbonate, leading to unwanted second-phase formation in the (mal stages of the process. In the present work a series of perovskite barium titanate films was prepared by the sol-gel method, using a metal alkoxide solutions in the electrophoretic deposition (EPD). The influence of several process parameters, like sintering temperature of sol preparation before EPD and heat-treatment temperature and non-oxidized atmosphere, on the film properties is described.

• Journal of the Korean Ceramic Society
• /
• v.43 no.11 s.294
• /
• pp.710-714
• /
• 2006

Barium titanate nanoparticles were synthesized under N$_2$ atmosphere by the hydrolysis and condensation of barium hydroxide octahydrate and titanium (IV) isopropoxide. The synthesized particles were aggregates of nanosized primary particles. The primary particles of about 20-50 nm in diameter became building blocks of larger secondary particles, which are in most cases spherical in shape. The size and morphological evolution of secondary particles are strongly related to the precursor concentration. The observations suggest that formation and control of secondary particles is an essential step in the alkoxidehydroxide sol-precipitation process to obtain monodispersed barium titanate nanopowders.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.37-44
• /
• 1997

Barium ferrite thin films on the thermal oxidized Si substrate were prepared by using sol-gel method (dip coating) from the sol of composition ratio of 5.25, designated by mole ratio 2Fe/Ba. The gelation process was largely divided into 4 step, and the sol prepared by reaction for 90 minutes at 8$0^{\circ}C$ was the suit-able for coating. Needle shaped particles formed on the coating layer were placed parallel to substrate and the inclination was increased with film thickness. The easy-direction of magnetization of needle shaped par-ticles was long-axis direction.

• Journal of Magnetics
• /
• v.21 no.4
• /
• pp.496-502
• /
• 2016

Doped and undoped barium hexaferrite powders ($BaFe_{12}O_{19}$, $Ba_{0.7}Ti_{0.3}Fe_{12}O_{19}$ and $Ba_{0.7}La_{0.3}Fe_{12}O_{19}$) were produced by the sol-gel method. The effects of substituting elements were studied in terms of the magnetic properties of barium hexaferrite powders. The magnetic properties were remarkably changed by the substitution of $La^{3+}$ and $Ti^{4+}$ ions for the $Ba^{2+}$ ion and were accompanied by oxygen deficiency in the $BaFe_{12}O_{19}$. Coercivities ($H_C$) from 4200 to 5100 Oe, remanences ($M_R$) from 22 to 49 emu/g and saturation magnetizations ($M_S$) from 41 to 73 emu/g were obtained for different samples. The obtained results were discussed in detail.

• Journal of the Korean Ceramic Society
• /
• v.32 no.12
• /
• pp.1383-1391
• /
• 1995

Hexagonal $\delta$-FeOOH was coated with Ba-Sol, which was produced by hydrolizing Ba(OC2H5)2, Ba-Sol coated $\delta$-FeOOH spread on a stainless plate, dried at 8$0^{\circ}C$ and then heat-treated. In this way, Ba-ferrite fine particles were produced. although there was a difference in a degree of hydrolysis of Ba(OC2H5)2, crystalline phase of Ba-ferrite appeared around 617$^{\circ}C$, and Ba-ferrite single phase was obtained after heat treatment at 80$0^{\circ}C$ for 2 hr. When Ba-ferrite was made from Ba-Sol coated $\delta$-FeOOH, $\delta$-FeOOH was thermally decomposed to $\alpha$-Fe2O3 at $700^{\circ}C$, producing a porous structure which was observed by TEM photographs. But the porous structure was not observed at 80$0^{\circ}C$. Ba-ferrite, heat-treated at 80$0^{\circ}C$ for 2 hr, had mean particle size of 1000$\AA$, lattice parameter of a0=5.889243 $\AA$ and c0=23.214502 $\AA$, a saturation magnetization ($\sigma$8) of 45.3 emu/g and a coercive force (Hc) of 5200Oe.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1997.05a
• /
• pp.60-61
• /
• 1997

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.10
• /
• pp.30-39
• /
• 2020

Single-phase barium ferrite powder was synthesized using the sol-gel method. At this time, an attempt was made to find the optimal experimental conditions for the production of single-phase barium ferrite by varying the Fe to Ba molar ratio (Fe/Ba) and the heat treatment temperature. In addition, cobalt-substituted barium ferrite particles were prepared using cobalt, which has an excellent effect on coercivity control for the production of ferrite fine particles having a coercivity of 2.5 to 5.5 kOe for use in high-density magnetic recording media. The changes in the magnetic properties of these were investigated. X-ray diffraction (XRD), thermogravimetric-differential thermal analysis (TG-DTA), and field emission scanning electron microscopy (FE-SEM) were used to observe the synthesis of single-phase, and Fourier transform infrared spectroscopy (FT-IR) and energy dispersive X-ray spectrometry (EDS) were used to analyze the chemical structure and composition. The coercivity of the cobalt-substituted barium ferrite powder was measured by vibrating sample magnetometry (VSM). As a result, single-phase Barium ferrites were synthesized when the Fe/Ba molar ratio was 10, and the heat treatment temperature was 900 ℃. The coercivity decreased with increasing the amount of Co added. Barium ferrite, having a coercivity of 2.5 to 5.5 kOe for use in high-density magnetic recording media, was synthesized when the Co to Fe(Co/Fe) molar ratio was less than 0.16.

• Transactions on Electrical and Electronic Materials
• /
• v.4 no.4
• /
• pp.18-21
• /
• 2003

Sol-gel processing of $BaTiO_3$ ceramics doped with La(0.01-1.00 at. $\%$) were prepared from metal barium, titanium n-butoxide and lanthanum iso-propoxide. Characterization of the sol-gel-derived powder using XRD, SEM is also reported. The obtained results showed that insulator to semiconductor transition for highly donor-doped barium titanate was closely related to the incorporation of donor into the grains and to the resultant grain size, which were significantly affected by the sinterability of $BaTiO_3$ powders and sintering conditions used.