$Bi_2Sr_2Ca_1Cu_2O_x$(BSCCO 2212) superconductors for current lead were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted at $1200^{\circ}\C$ in a resistance furnace using a Pt crucible and poured in a rotating cylindrical mold preheated at $550^{\circ}\C$ for 2 hour. The solidified BSCCO-2212 samples were heat-treated by partial melting process in oxygen atmosphere. The current-voltage curves at 77 K of the samples were obtained by transport measurement, and the microstructure was investigated by scanning electron microscope. The $J_c$ values at 77 K of the tubes partially melted at $840^{\circ}C,\;860^{\circ}C\;and\;880^{\circ}C$ were 492, 430 and 398 $A/cm^2$, respectively. It was observed that the plate-like grains in BSCCO 2212 tube was more developed in the sample heat-treated at $840^{\circ}C$. It was found that the critical current of the BSCCO 2212 samples was dependent on the partial melting schedule regarding the grain shape and size of the BSCCO 2212.
Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
/
2005.07a
/
pp.589-590
/
2005
BSCCO:2212-2223 thin films were fabricated by using the ion beam sputter with a evaporation method at various substrate temperatures, $T_{sub}$, and ozone gas pressures, $pO_3$. The correlation diagrams of the BSCCO phases with Tsub and $pO_3$ are established in the 2212 and 2223 compositional films. In spite of 2212 compositional sputtering, Bi2201 and Bi2223 as well as Bi2212 phases come out as stable phases depending on Tsub and $pO_3$. From these results, the thermodynamic evaluation of ${\Delta}H$ and ${\Delta}S$, which are related with Gibbs' free energy change for single Bi2212 or Bi2223 phase, was performed.
[$Bi_2Sr_2Ca_1Cu_2O_x$](BSCCO 2212) tubes were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted in a Pt crucible and solidified in a rotating steel mold. The BSCCO 2212 tube samples separated from steel mold were heat-treated at $800^{\circ}C\;and\;810^{\circ}C$ in oxygen flow. The critical current($I_c$) of the samples was measured by transport measurement at 77K, and the microstructure was investigated by scanning electron microscope. The $J_c$ at 77K of the tubes heated treated at $800^{\circ}C\;and\;810^{\circ}C$ were 197 and 240 $A/cm^2$, respectively. It was observed that the plate like grains in BSCCO 2212 tube was more developed in the sample heat treated at $810^{\circ}C\;and\;800^{\circ}C$ heated tube. It is found that the critical current($I_c$) of the BSCCO 2212 sample was dependent on the heating schedule regarding the growth of the BSCCO 2212 grains.
The effect of the initial BSCCO 2212 grain size on the final gain size and the formation of the BSCCO 2223 was studied using a powder precursor synthesized by two-powder method. 2212 and CaCuO$_2$ tapes were prepared by dip coating and joined by pressing and then followed by the repeated thermo mechanical treatment. The samples were characterized by XRD and SEM analysis. The formation and grain size of the BSCCO 2223 depended on the initial BSCCO 2212 grain size.
Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
/
2006.06a
/
pp.267-267
/
2006
전력에 큰 손실을 초래하는 고장전류를 차단하기 위한 한류기(FCL) 소재로서 고온 초전도체인 BSCCO 2212가 사용된다. 고온에서 용융된 BSCCO 2212 분말은 원심성형법에 의해 한류기용 튜브로 제조되었다. BSCCO 튜브의 기계적 특성을 높이고 용융온도를 낮추기 위해 $SrSO_4$(10wt-%)를 첨가하였다. 용탕은 $1200^{\circ}C$에서 완전히 용융되어 금속 몰드로 주입되었고 원심성형에 사용되는 금속 몰드는 $550^{\circ}C$ 온도로 2시간 예열 후 1020 ~ 2520 RPM으로 회전시켰다. 원심력에 의해 성형된 BSCCO 튜브는 약 48시간 동안 로에서 서냉 후 금속 몰드로부터 분리하였다. 튜브의 용이한 분리를 위해 이형제로서 BSCCO 2212 powder를 사용하였고 임계전류측정을 고려하여 Ag tape 단자를 튜브 끝단에 부착하였다. BSCCO 제조 공정에 있어서 몰드의 예열온도, 용융온도, 몰드 회전속도 등의 변수를 조절하여 최적의 조건을 확립하였다. 제조한 BSCCO 튜브의 임계전류($I_c$)와 임계전류밀도($J_c$)는 77K에서 536A와 $205A/cm^2$ 이었다. 본 연구에서는 BSCCO 2212 튜브를 제조하는 공정조건 변화와 각 조건에서 제조된 BSCCO 2212 튜브의 전기적 특성 및 그에 따른 분석에 대해 기술하였다.
Proceedings of the Korean Institute of Navigation and Port Research Conference
/
2000.11a
/
pp.104-105
/
2000
High quality BSCCO thin films have been fabricated by means of an ion beam sputtering at various substrate temperatures, T$_{sub}$, and ozone gas pressures, PO$_3$. The correlation diagrams of the BSCCO phases appeared against T$_{sub}$ and PO$_3$are established in the 2212 and 2223 compositional films. In spite of 2212 compositional sputtering, Bi2201 and Bi2223 phases as well as Bi2212 one come out as stable phases depending on T$_{sub}$ and PO$_3$. From these results, the thermodynamic evaluations of ΔH and ΔS which are related with Gibbs'free energy change for single Bi2212 or Bi2223 phase are performed.ormed.i2212 or Bi2223 phase are performed.
Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
/
2000.11a
/
pp.104-107
/
2000
High quality BSCCO thin films have been fabricated by means of an ion beam sputtering at various substrate temperatures, T$\_$sub/, and ozone gas pressures, PO$_3$. The correlation diagrams of the BSCCO Phases appeared against T$\_$sub/ and PO$_3$ are established in the 2212 and 2223 compositional films. In spite of 2212 compositional sputtering, Bi2201 and Bi2223 phases as well as Bi2212 one come out as stable phases depending on T$\_$sub/ and PO$_3$. From these results, the thermodynamic evaluations of ΔH and ΔS which are related with Gibbs' free energy change for single Bi2212 or Bi2223 phase are performed.
Kim Kyu-Tae;Park Eui-Cheol;Jang Seok-Hern;Lim Jun-Hyung;Joo Jin-Ho;Kim Chan-Joong;Kim Hye-Rim;Hyun Ok-Bae
Journal of the Korean Institute of Electrical and Electronic Material Engineers
/
v.19
no.6
/
pp.579-585
/
2006
We fabricated BSCCO-2212 (2212) rod by the melt casting process (MCP) and evaluated the effect of the melt flowing on the critical current ($I_c$) by using vertical and tilt casting. It was observed that the $2212-SrSO_4$ rod processed by the tilt casting method with homogeneous pre-heating temperature of the mold had a higher $I_c$ than that processed by the vertical casting method. We also evaluated the influence of the strontium sulfates ($SrSO_4$) addition on the texture, microstructure, critical current and temperature, and mechanical hardness of the $2212-SrSO_4$ rods. It was observed that the addition of $SrSO_4$ improved the critical current ($I_c$) and mechanical hardness of the 2212. The $I_c$ of the 2212 increased as the $SrSO_4$ content increased and reached a peak value (260 A at 77 K) at an $SrSO_4$ content of 6 wt.%. In addition, the addition of $SrSO_4$ had a beneficial effect on the mechanical hardness of the 2212. We studied the possible cause of the variation in the $I_c$ with the melt flowing and the $SrSO_4$ content based on the XRD, EPMA analysis and the microstructural observation.
The superconductor characteristics of BSCCO spray films by Heat treatment was studied. $Bi_2Sr_2CaCu_2O_x$(Bi-2212) is high-Tc superconductor(HTS) coatings have been prepared by Heat treatment. Where high current carrying capabilities are required and therefore thick film and bulk material are called for, the Bi2Sr2Ca1Cu2O8-d(Bi-2212)compound has evoleved as one of the most promising. and the Bi-2212 HTS coating layer is synthesized through the peritectic reaction between Sr-Ca-Cu oxide coating layer and Bi-Cu oxide coating layer by partial melting process. The superconducting characteristics depends on the spray distance which was related to the spray particle melt. The Bi-2212 HTS layer consists of the whisker growth and secondary phase in 2212 layer were observed.
Kim, Kyu-Tae;Kim, Chan-Joong;Lim, Jun-Hyung;Park, Eui-Cheol;Park, Jin-Hyun;Joo, Jin-Ho;Hyun, Ok-Bae;Kim, Hye-Rim
Progress in Superconductivity
/
v.9
no.2
/
pp.193-198
/
2008
We fabricated BSCCO-2212(2212) bulk superconductors by using a casting process and evaluated the superconducting properties. The effects of annealing conditions on microstructure and critical properties were studied. It was found that the homogeneous and uniform microstructure improved the critical properties and the microstructures of ingot and annealed rods were different with the size of 2212 rod and tube. The critical current($I_c$) of rods increased with increasing annealing time, probably due to increased grain size of 2212. Annealing time of the highest $I_c$ for the smaller rod(diameter of 10 mm) was shorter(150 hr) than that of the larger rod(diameter of 16 mm, 400 hr). This size effect seems to be related to different grain sizes of the intermediate phases such as 2201 and secondary phases in the ingot. In addition, we fabricated 2212 tubes from the rod by removing the center region which contained inhomogeneous microstructures. The $I_c$ of 2212 tube with the outer diameter of 16 mm and the thickness of 2 mm was measured to 844 A, which corresponds to the critical current density of $1017\;A/cm^2$ at 77 K.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.