• 한국주조공학회지
• /
• 제34권4호
• /
• pp.130-135
• /
• 2014

Efforts have been made to develop new silicon-free aluminum casting alloys that possess high electrical and thermal conductivity. In this research Al-Fe-Cu-Mg alloys with various Cu and Mg contents were investigated for their various properties. As the Cu or Mg content was increased, the electrical conductivity gradually decreased, while the tensile strength of the Al-Fe-Cu-Mg alloy tended to be improved. It was found that fluidity was generally inversely proportional to the Cu content, but the alloys containing 1%Mg showed considerably low fluidity, regardless of the Cu content.

• 소성∙가공
• /
• 제23권2호
• /
• pp.116-121
• /
• 2014

Low pressure die casting and flow forming have been successfully used to produce sound road wheels from magnesium alloy AM80. In the current study, high speed compression testing was initially conducted to simulate the flow forming of a Mg wheel. Subsequently the flow forming was simulated with "Forge$^{TM}$", an FEM software package. On the basis of flow forming simulations, the flow forming of the Mg wheel was performed under different conditions. For the flow forming experiments, the preform castings were made by low pressure die casting from AM80, a commercial magnesium alloy. In flow forming of the magnesium preform wheel, the flow forming of the Mg wheel was successfully accomplished when the feed rate was less than half that for the forming of an aluminum road wheel. The reduction in feed rate was 52%. Finally, a comparison with the flow forming simulations was made.

• 한국주조공학회지
• /
• 제32권3호
• /
• pp.127-132
• /
• 2012

Al-Zn-Mg alloys, being high strength aluminum alloys, have attracted attention as a material of automobile parts that require higher mechanical properties and lightness. Automobile parts with complex shapes are manufactured by low-priced casting method, but Al-Zn-Mg alloys are difficult to cast because of its poor hot cracking, feeding, and fluidity. Thus fluidity experiments on Al-Zn-Mg alloys were conducted for the castability evaluation. The effects of Mg and Zn, representative elements of Al-Zn-Mg alloys, on fluidity were observed. Spiral mold was used for fluidity experiments and the lengths of solidified specimens were measured after melting and gravity casting. Correlation between microstructures and fluidity length based on the alloy composition was considered. According to the experimental results, as the amount of Mg and Zn increased, fluidity decreased. Also, it was confirmed that fluidity change by the variation of Mg composition was greater than that of Zn.

• 한국주조공학회지
• /
• 제31권4호
• /
• pp.205-211
• /
• 2011

Al-Si alloys have been steadily used as a potential material for the achievement of an efficient weight reduction in the automobile and aerospace industries due to its excellent castability and high strength-to-weight ratio. In this study, riser effect and mechanical properties were investigated according to the size of the sleeve. In addition, the effects of riser size on mechanical properties of castings were investigated. On the other hand flow and solidification process were simulated with a hybrid FDM/FEM package named ZCast. As a result, results of simulation and experiments were comparable regarding to the yield strength, tensile strength, elongation and hardness of casting. It proves the reliability of the simulation. It is expected that the proper size of riser can improve the recycling rate of metallic materials and reduce the cost of casting.

• 한국주조공학회지
• /
• 제27권2호
• /
• pp.83-87
• /
• 2007

Aluminum plates of the same materials as the foam were attached by the casting process inserting the foam as a core to investigate the tensile property of open cell foams. Tensile properties of the open cell 6063 aluminum alloy foam of $10{\sim}30$ PPI were measured before and after heat treatment. Densities of test specimens were between 0.14 and $0.29g/cm^3$. Tensile strength of the 6063 aluminum foam after heat treatment showed little change. C values were in the range of $0.41{\sim}0.87$ for as cast foams and $0.11{\sim}0.27$ for T6 heat treated foams in the eq. of ${\sigma}^* _{pl}/{\sigma}_{ys}=C({\rho}/{\rho}_s)^{1.5}$, and increased with increase in the cell size.

• 열처리공학회지
• /
• 제21권6호
• /
• pp.300-306
• /
• 2008

Solid state diffusion brazing of aluminum castings (AC4C) and wrought alloys (Al6061) was conducted in order to improve thermal conductivity and temperature uniformity of the aluminum heater which was generally fabricated by casting method. Tensile strength and thermal conductivity are raised with increasing brazing temperature, obtaining 122.5 MPa and $206W/m{\cdot}K$ at $540^{\circ}C$ 5hrs brazing conditions, respectively. The diffusion brazed heater, shows maximum temperature difference of $4^{\circ}C$, exhibits a enhanced temperature uniformity compared with the cast heater having the maximum temperature difference of $11^{\circ}C$.

• 대한치과기공학회지
• /
• 제23권2호
• /
• pp.161-170
• /
• 2002

The Purpose of this study was to investigate the chemically improvement of metal-ceramics bond strength in the course of recasting Ni-Cr metal composite system with 10wt.%, 20wt.% and 30wt.% aluminum respectively. We have tested the bond strength, micro-structure, chemical composition of each metal composites and metal- ceramic bond interfaces by 3-point bending strength tester, SEM and EDS. We have made the conclusions through this study as follow: 1. The most suitable amount of aluminum to the Ni-Cr metal composite recasting is 20wt. % for improving metal-ceramics bond strength with debonding strength value of 49.54 kgf/mm2. 2. The aluminum must be changed to small spread alumina like phases and second aluminum-metal composites phases in the morphology of Ni-Cr metal composite system by adding during it's casting. These second phases have inclined functional oxide phases mixed with metal elements and they must take roll to improvement of metal-ceramics bond strength. 3. In the case of 30wt.% aluminum appended to Ni-Cr metal composite system, an excess of second inclined functional oxide phases produce cracks and spalling of them apart from it's base material. It must be a important factor of reduction of metal-ceramics bond strength.

• 한국주조공학회지
• /
• 제14권6호
• /
• pp.530-540
• /
• 1994

Aluminium-silicon alloy(JIS AC8A) matrix composites reinforced with SiC particles were fabricated by spray-cast forming process, and the microstructure of powders and preforms produced were studied by using an optical and scanning electron microscopy. SiC particles were co-sprayed by mixed phase injection method during the spray casting process. Most of the composite powders formed by this mixed phase injection method exhibit morphology of particle-embedded type, and some exhibits the morphology of particle attached type due to additional attachment of the SiC particles on the surface of the powders in flight. The preforms deposited were resulted in dispersed type microstructure. The pre-solidified droplets and the deposited preform of SiC-reinforced aluminium alloy exhibit finer equiaxed grain size than that of unreinforced aluminium alloy. Eutectic silicons of granular type are crystallized at the corner of the aluminum grains in the preforms deposited, and some SiC particles seem to act as nucleation sites for primary/eutectic silicon during solidification. Such primary/eutectic silicons seem to retard grain growth during the continued spray casting process. It is envisaged from the microstructural observations for the deposited preform that the resultant distribution of SiC injected particles in the Al-Si microsturcture is affected by the amount of liquid phase in the top part of the preform and by the solidification rate of the preform deposited.

• 한국주조공학회지
• /
• 제32권5호
• /
• pp.231-240
• /
• 2012

In present study, the effect of heat treatment on the microstructure and mechanical properties of the gravity cast superchargers housing using A356 alloy were investigated. In order to identify the characteristics of superchagers housing casting with heat treatment, Vickers hardness test, electrical conductivity test, opical and scanning electron microscopy were performed. And also, to investigate their mechanical properties, the T6 treated superchagers housing casting in optimum heat treatment condition were carried out tensile test using UTM (Universal Testing Machine).

• 한국주조공학회지
• /
• 제23권2호
• /
• pp.63-68
• /
• 2003

Al-Ti-C grain refiner form a relatively new alternative to the existing class of Al-Ti-B type grain refiners for achieving fine equiaxed structures in aluminum alloys during casting and solidification. The present study was carried out to investigate the influence of Al-Ti-C master alloys on the grain structure of Al-7Si alloys. The present study also investigates the relationship between grain refining efficiency and concentrations of Fe and Si in hypo-eutectic Al-Si alloys using Al-3Ti-0.13C master alloys. It is found that several parameters affect significantly the grain refining performance in silumin alloys. The present study reports the influence of various parameters such as alloy content, master alloy addition level, melt holding time and superheat on the grain refining efficiency in Al-7Si alloys.