• 한국결정성장학회지
• /
• 제10권3호
• /
• pp.233-238
• /
• 2000

생체적합성과 상 안정성이 우수한 t-$ZrO_2/Al_2O_3$복합체에 $Eu_2O_3$을 0~4 mol%첨가한 복합체를 $1600^{\circ}C$ 온도에서 1 시간 소결하여 상 안정성, 색상변화, 기계적 특성을 조사하였다. $180^{\circ}C$, 3.5MPa의 수증기 압력 하에서 20시간 열처리 후 X-선 회절법으로 관찰한 결과 $Eu_2O_3$가 첨가된 (Y,Nb,Eu)-TZP/$Al_2O_3$복합체는 우수한 상 안정성이 유지되었다. $Eu_2O_3$의 양이 증가함에 따라 백색계통의 상아색에서 미색의 핑크색으로 서서히 변화하였다 $Eu_2O_3$가 3 mol%까지 첨가된 복합체의 경우 620MPa, 7.6MPa.$m^{1/2}$ 이상의 강도와 인성값이 관찰되었다.

• 한국세라믹학회지
• /
• 제40권6호
• /
• pp.525-529
• /
• 2003

Biotribological properties, such as wear rate and friction coefficient, of 3Y-TZP and Low Temperature Degradation (LTD) free materials were investigated via a ball(SiC)-on-plate sliding wear test to evaluate the relationship between wear mechanism and phase transformation. Wear test was conducted with a sliding speed of 0.035 m/s at room temperature and at 25$0^{\circ}C$ in air under a normal load of 49 N, respectively. Although friction coefficient of 3Y-TZP was the lowest due to the fine grain size, the highest wear loss and rate were observed due to the debris of monoclinic grains introduced during sliding and their values increased drastically with raising temperature. However, the biotribological properties of LTD-free materials were insensitive to temperature due to the inertness of the phase transformation, suggesting that they may be applicable to the biomechanical parts.

• 대한치과기공학회지
• /
• 제35권4호
• /
• pp.271-280
• /
• 2013

Purpose: This study was to assess the effect of surface and heat treatment on the bond strength of veneering ceramics to zirconia. Methods: The specimens were divided into 7 groups according to surface treatment and heat treatment conditions prior to porcelain application. ten specimens from each group were subjected to a 3-point flexural test. In addition the influence of surface and heat treatment on surface roughness values and phase transformation of zirconia was evaluated. Statistical analysis was performed with one-way ANOVA and post hoc Tukey's test. Results: Bond strength ranged from $20.67{\pm}3.13MPa$ to $32.69{\pm}4.52$. Bond strength of surface treatment group was lower than that of control group but only $Al_2O_3$ sandblasting group was significant difference. Bond strength of heat treatment group was higher than that of surface treatment group but there was no statistical significance. Conclusion: Bond strength of veneering ceramics to zirconia was affected by surface and heat treatment.

• 대한치과보철학회지
• /
• 제48권4호
• /
• pp.251-258
• /
• 2010

연구 목적: 이 연구의 목적은 표면처리방법이 지르코니아와 네 종류의 시멘트의 전단결합 강도에 미치는 영향을 평가하는 것이다. 연구 재료 및 방법: 총 120개의 디스크 모양의 산화 지르코늄 (3Y-TZP, Kyoritsu, Tokyo, Japan) 시편을 다음과 같이 표면처리 하였다: (1) $110\;{\mu}m$ 산화 알루미나 분사처리 (2) Silica coating ($Rocatec^{TM}$ 3M ESPE)를 이용한 표면처리 (3) 처리하지 않음. 각각의 표면 처리 후, 2종의 자가 접착형 시멘트 (RelyX Unicem, Maxcem)와 레진 강화 글라스 아이오노머 시멘트 (RelyX Luting), Bis-GMA 레진 시멘트 (Nexus3)를 시편에 부착하였으며 각 군은 UTM을 이용하여 전단결합강도를 측정하였다. 표면처리, 시멘트의 종류에 따른 결합강도의 차이를 살펴보기 위하여 일원변량분석 (One-way ANOVA)과 이원변량분석 (two-way ANOVA)을 이용하고 사후 분석으로 Tukey HSD test를 실시하였다. 결과: 로카텍 처리 후, RelyX Unicem을 부착한 군이 가장 높은 결합 강도를 보였으며 (P<.05) 알루미나 분사처리를 한 군과 로카텍 처리를 한 군은 아무런 처리를 하지 않은 군보다 유의하게 높은 결합 강도를 보였다 (P<.05). 또한 모든 표면상태에서 RelyX Luting은 다른 군에 비해 통계적으로 유의하게 가장 낮은 결합강도를 보였다 (P<.05). 결론: 본 연구의 결과에 따르면 RelyX Unicem은 지르코니아와 강한 결합력을 보였으며 로카텍 처리는 결합을 증진시키는데 효과적이었다.

• 한국세라믹학회지
• /
• 제48권2호
• /
• pp.152-159
• /
• 2011

The green and hard machining characteristics of dental ceramics are of great interest to dental industry. The green bodies of TZP/$Al_2O_3$ composites were prepared by the cold isostatic pressing, and machined on the CNC lathe using PCD (polycrystalline diamond) insert under various machining conditions. With increasing nose radius of PCD insert, surface roughness initially increased due to increased cutting resistance, but decreased by the onset of sliding fracture. The lowest surface roughness was obtained at spindle speed of 1,300 rpm and lowest feed rate. Hard bodies were prepared by pressureless sintering the machined green bodies at several temperatures. The grinding test for sintered hard body was conducted using electroplated diamond bur with different grit sizes. During grinding, grain pull out in the composite was occurred due to thermal expansion mismatch between the alumina and zirconia. The strength of the composite decreased with alumina contents, due to increased surface roughness and high monoclinic phase transformed during grinding process. The final polished samples represented high strength by the elimination of a phase transformation layer.

• Tribology and Lubricants
• /
• 제21권5호
• /
• pp.216-220
• /
• 2005

The sliding wear behaviors of three different compositions of novel low temperature degradation-free zirconia/alumina (LTD-free Z/A) composites were examined in a ceramic-ceramic contact pair. The wear tests were performed by using a pin-on-disk type wear tester in a linear reciprocal sliding motion with a line contact in both dry and bovine serum lubricated conditions at room temperature. From the results of dry sliding wear tests, Z/A#1((5.3Y, 4.6Nb)-TZP/80 $vol\%Al_2O_3$) showed the best wear resistance among three kinds of LTD-free Z/A composites. For the bovine serum lubricated sliding wear tests, wear was too little to be measured for all kinds of Z/A composites. These novel LTD-free Z/A composites having excellent wear resistance demonstrated a potential as the alternative materials for the ceramic-ceramic contact pairs of femoral head and acetabular liner in total hip replacement.

• 구강회복응용과학지
• /
• 제29권1호
• /
• pp.69-79
• /
• 2013

본 연구의 목적은 각각 다른 표면처리를 한 지르코니아를 레진시멘트로 접착한 후 전단결합강도를 평가, 비교하는 것이다. 디스크 모양의 산화 지르코늄(3-TZP, Kyoritsu, Tokyo, Japan) 시편 120 개를 다음과 같이 표면처리 하였다. (1)110 ${\mu}m$ 산화 알루미나 분사 처리 (2)Silica coating(RocatecTM, 3M ESPE) (3)처리하지 않음 시편을 한 군당 10 개씩 총 6 개군으로 나누어 두 개의 지르코니아 시편을 자가 접착형 레진 시멘트(RelyX U-200, 3M ESPE)로 합착하였다. (1)처리하지 않음/처리하지 않음 (2)처리하지 않음/110 ${\mu}m$ 산화 알루미나 분사처리 (3)처리하지 않음/Silica coating (4)110 ${\mu}m$ 산화 알루미나 분사 처리/110 ${\mu}m$ 산화 알루미나 분사 처리 (5)110 ${\mu}m$ 산화 알루미나 분사 처리/Silica coating (6)Silica coating/Silica coating. 각 군의 전단결합강도를 만능시험기로 측정하였다. 표면처리에 따른 결합강도의 차이를 살펴보기 위해 일원변량분석(One-way ANOVA)을 이용하고 사후 분석으로 Tukey HSD test를 실시하였다. Silica coating을 한 두 개의 시편을 접착한 군이 가장 높은 결합 강도를 보였다(P<0.05). 표면 처리하지 않은 시편을 접착한 군과 두 개의 시편 모두 알루미나 분사 처리한 시편을 접착한 군은 서로 간에 유의한 차이를 보이지 않았으며, 그 외의 군에 비해서는 유의하게 낮았다(P<0.05). 본 연구의 결과에 따르면 Silica coating은 자가중합형 레진시멘트를 이용하여 접착한 두 지르코니아 간의 결합을 증진시키는데 효과적이었다.

• 대한치과기공학회지
• /
• 제38권3호
• /
• pp.135-142
• /
• 2016

Purpose: The aim of this research was to evaluate the influence of different surface treatments on the shear bond strength of zirconia ceramic to composite resin. Methods: Seventy two cylinder-shape (diameter: 5 mm; height: 12 mm) blocks of experimental industrially manufactured Y-TZP ceramic were abraded with $125{\mu}m\;Al_2O_3$ particles and randomly divided into 4 groups. All the materials were categorized as group Gc(control group - composite resin veneering on zirconia surface), Gr - composite resin veneering after surface treatment of Rocatec system (3M ESPE, Seefeld, Germany) group; Gz - composite resin veneering after surface treatment of Zirconia primer (Z-primer, Bisco, U.S.A) group; Gm - composite resin veneering after surface treatment of zirconia primer (Monobond plus, ivoclar vivadent AG, Liechtenstein) group. Two different zirconia primers and Rocatec system were used to zirconia cylinders (n=16) onto the zirconia surface. Zirconia specimens, polished and roughened, were pretreated and composite bilayer cylinders bonded using conventional adhesive techniques. Results: Shear bond strengths were analyzed using single-factor ANOVA(p<0.05). Bond strength values achieved after airbone particle abrasion and zirconia surface pre-treatments(p<0.05). Conclusion: Shear bond strength tests denmonstrated that zirconia primer is a viable method to improved bond strength between zirconia ceramic core and veneering composites.

• 대한치과보철학회지
• /
• 제53권4호
• /
• pp.318-324
• /
• 2015

목적: 본 연구에서는 서로 다른 인산염계 기능성 단량체가 첨가된 5종의 자가 접착 레진시멘트와 지르코니아 사이의 열순환 전후 전단결합강도를 비교 평가하고자 하였다. 재료 및 방법: Airborne particle abrasion ($50{\mu}m$ $Al_2O_3$)을 시행한 디스크 모양의 Y-TZP 지르코니아 블록을 총 100개 준비하였다. 그리고 composite resin cylinder ($Filtek^{TM}$ Z250, 3M ESPE, St. Paul, MN, USA) 100개를 준비하였다. 서로 다른 인산염계 기능성 단량체가 첨가된 5종의 이중 중합형 자가 접착 레진시멘트 즉, Permacem 2.0 (DMG, Hamburg, Germany), $Clearfil^{TM}$ SA Luting (Kuraray Medical, Tokyo, Japan), $Multilink^{(R)}$ Speed (Ivoclar Vivadent, Schaan, Liechtenstein), $RelyX^{TM}$ U200 Automix (3M ESPE, Neuss, Germany), G-Cem $LinkAce^{TM}$ (GC Corporation, Tokyo, Japan)를 이용하여 지르코니아 블록과 composite resin cylinder를 접착하고 1군당 20개의 시편을 갖는 5개의 군을 만들었다. 시편을 $37^{\circ}C$ 의 증류수에 24시간 동안 보관한 후 각 군의 시편 절반(n=10)은 곧 바로 그리고 나머지 절반(n=10)은 5000회 열순환(5 - $55^{\circ}C$) 후에 전단결합강도를 측정하였다. 파절면은 FE-SEM을 이용하여 관찰하였다. 통계분석은 레진시멘트 종류 및 열순환 유무에 따른 전단결합강도의 비교를 위해 Two/One-way ANOVA를 시행하고 Tukey HSD post-hoc test를 이용하여 사후 검정하였으며, 열순환 전후의 비교를 위해 paired t-test를 이용하였다($\alpha$=.05). 결과: 열순환 전과 후 모두 $Multilink^{(R)}$ Speed 군은 나머지 4종류의 시멘트 군 보다 큰 전단결합강도를 나타내었다. G-Cem $LinkAce^{TM}$ 군은 열순환 전과 비교하여 열순환 후에 유의하게 낮은 전단결합강도를 나타내었지만, 다른 4종류 군은 열순환 전후 유의한 차이가 없었다. 결론: 인산염계 단량체를 포함한 대부분의 이중 중합형 자가 접착 레진시멘트는 지르코니아와 높은 전단결합강도를 보이고 열순환에 의해 유의한 영향을 받지 않아 지르코니아 보철물의 접착에 유용할 것이라고 사료된다.