• Journal of Sensor Science and Technology
• /
• v.16 no.3
• /
• pp.240-245
• /
• 2007

AlN thin film for SAW filter application was deposited on (100) silicon, sapphire, $Si_{3}N_{4}$/Si, and $Al_{2}O_{3}$/Si substrates by reactive magnetron sputtering method, respectively. The structural characteristics were dependent on the structure of substrates. Scanning Electron Microscope (SEM), X-ray Diffraction (XRD) and Atomic Force Microscope (AFM) have been used to analyze structural properties and preferred orientation of AlN thin films. Preferred orientation and SAW characteristic of AlN were improved by insertion of $Al_{2}O_{3}$ buffer layer. Insertion loss of SAW devices using AlN/Si and AlN/$Al_{2}O_{3}$/Si were about 33.27 dB and 30.20 dB, respectively.

• Journal of Korea Foundry Society
• /
• v.15 no.4
• /
• pp.416-421
• /
• 1995

Recently Al-Cu-P alloys are used to refine primary Si of hypereutectic Al-Si alloys. Because it has inside AlP compound that acts as nucleation site in the melt, Al-Cu-P alloy has good refinement effect in lower holding temperature and after shoter holding times. In this study Al-Cu-P refinement agent was made by mechanical alloying method. When Al-13.5wt%Cu-1.5wt%P was alloyed mechanically for 30hr in Ar atmosphere by high energy ball mill, it had the refinement effect that showed primary Si size of about $30{\mu}m$ in Al-20wt%Si at $760^{\circ}C$, treated for 15min.

• Corrosion Science and Technology
• /
• v.12 no.3
• /
• pp.119-124
• /
• 2013

Nano-multilayered, crystalline AlTiSiN thin films were deposited on WC-TiC-Co substrates by the cathodic arc plasma deposition. The deposited film consisted of wurtzite-type AlN, NaCl-type TiN, and tetragonal $Ti_2N$ phases. Their oxidation characteristics were studied at 800 and $900^{\circ}C$ for up to 20 h in air. The WC-TiC-Co oxidized fast with large weight gains. By contrast, the AlTiSiN film displayed superior oxidation resistance, due mainly to formation of the ${\alpha}-Al_2O_3$-rich surface oxide layer, below which an ($Al_2O_3$, $TiO_2$, $SiO_2$)-intermixed scale existed. Their oxidation progressed primarily by the outward diffusion of nitrogen, combined with the inward transport of oxygen that gradually reacted with Al, Ti, and Si in the film.

• Journal of the Korean Ceramic Society
• /
• v.26 no.1
• /
• pp.13-20
• /
• 1989

After sintering Si3N4 containing 20wt% of variable composition ratio of Y2O3 and Al2O3 at 1$600^{\circ}C$, the specimens were annealed at 125$0^{\circ}C$ and 135$0^{\circ}C$ for 5, 10, 15 hours in order to crystallize the remanining oxynitride glass phases. The main grain-boundary crystalline phases in the Si3N4-Y2O3-Al2O3 system were melilite and YAG. By annealing 15hrs. at 125$0^{\circ}C$, almost all of the glasses were crystallized. During the growth of melilite, lattice volyume of $\beta$-Si3N4 was increased as Al3+ and O2- ions in the oxynitride glass diffuse into $\beta$-Si3N4 lattice, but during the growth of YAG, lattice volume of $\beta$-Si3N4 was decreased by reverse diffusion of Al3+ and O2- ions. In case of crystallization of glass phase to melilite, thermal expansion of sample was decreased, but in case of crystallization to YAG, inverse phenomen on was observed.

• Korean Chemical Engineering Research
• /
• v.56 no.4
• /
• pp.600-606
• /
• 2018

The influence of acidity in MTT zeolite of different Si/Al molar ratio's on the catalyst activity in methanol-to-olefin (MTO) reaction has been investigated. The Si/Al ratio was controlled with the Al content in the gel when N,N,N',N'-tetramethyl-1,3-diaminopropane was used as a structure directing agent (SDA). The gel composition was controlled to $20SiO_2$ : 30SDA : x (=0.25~1.25)$NaAlO_2$ : 2NaOH : $624H_2O$, which was subject to the hydrothermal synthesis at 433 K for 4 days. As the composition of sodium aluminate decreased, the particle size of MTT zeolite increased, and also the amount of acid sites decreased. To investigate the catalytic performance, MTO reaction was carried out at 673 K with $1.2h^{-1}$ WHSV. It was found that the H-MTT (1.00Al) catalyst with a Si/Al molar ratio of 24 maintained the methanol conversion over 90% for 900 min.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.12
• /
• pp.48-54
• /
• 2003

Alumium alloys casting are gaining increased acceptance in the automotive and electronic industeries and squeeze casting is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of Al-7.0Si-0.4Mg (AC4C) alloy fabricated by squeeze casting process for development of Fuel system Parts (Fuel rail). The microstructure of squeeze casted specimen were composed of eutectic structure Alumimim solid solution and $Mg_2$Si precipitates. The tensile strength of as-solid solution treatment Al-7.0Si-0.4Mg ahoy revealed 298.5MPa. It was found that Al-7.0Si-0.4Mg alloy have good corrosion resistance in electrochemical polarization test.

• Journal of the Korean Ceramic Society
• /
• v.20 no.1
• /
• pp.25-30
• /
• 1983

This experiment was studied in the system of (1-x) CaO MgO $2SiO-Al_2O_3$ to investigate forming of solid solution. The technique empolyed was the well known water-quenching method. Differential thermal analysis of the each glass water quenched indicated that under 30 mole% $Al_2O_3$ was lowered with increasing of the amount of $Al_2O_3$ It was supposed by X-ray diffraction patterns of each specimen sintered at various temperature that only solid solution was formed under the 30mole % $Al_2O_3$ compositions solid solution and anorthite were formed at the 20mole% $Al_2O_3$ composition anorthite solid solution and spinel$(MgAl_2O_4)$ were formed over the 40mole% $Al_2O_3$ compositions. The maximum density and thermal expanison coefficient was 2.89g/cm 7.74x106./C$^{\circ}$ respectively in the composi-tion of 10 mole% $Al_2O_3$ . All the specimens showed linear thermal expansion behavior. Microhardness was as high as 850kg/nm2 in the composition of 5, 10, 20 mole % $Al_2O_3$ and dielectric constant was 7.3-6.9.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1991.11a
• /
• pp.34-37
• /
• 1991

Al계 베어링합금은 소착저항력등의 베어링특성이 우수하여 최근에 자동차의 엔진부품에 많이 사용되고 있다. Al계 베어링합금으로는 Al-Sn계, Al-Pb계, Al-Si계 합금이 개발되어 사용되어 왔다. Al-Si계 합금은 높은 강도, 우수한 부식성, 주조성이 향상되는 장점등을 갖고 있다. 또한 Al-Pb계 합금은 Pb가 고체윤활제로 작용하여 소착저항성이 높으며 가격도 저렴한 장점을 갖고 있다. Al과 Pb는 용융상태에서 넓은 용융간극을 갖어 중력편석을 일으키기 때문에 일반적인 주조방법으로 Al계 베어링합금을 제조할 수없다. 또한 Al에 Si이 첨가됨에 따라 높은 경도등의 기계적성질의 향상이 얻어지지만 Al 기지에 Si의 함량이 증가할 수록 편석이 심해져 조대한 Si-rich상이 미세조직에 존재하여 합금이 취약해지는 단점을 갖고 있다. 따라서 본 연구에서는 Al 기지에 Pb의 중력편석을 최소화하고 Al 기지에 조대한 Si-rich상이 생성되는 것을 막기 위하여 Al과 Pb가 공존하는 온도구역에서 높은 교반속도로 용탕을 강제교반하여 액상에서 Pb와 Si을 미세하게 분산시킨 후 수냉되는 동주형에서 급속응고시켜 Pb와 Si-rich 상이 균일하게 분포된 Al계 베어링합금을 제조하였다. 본 연구에서는 Pb의 양을 0%에서 35%까지 변화시켰으며, Si의 양을 0%에서 20%까지 변화시켜서 베어링합금을 제조하였으며, 강제교반속도는 500rpm에서 2500rpm 까지 변화시켜 베어링합금을 제조하였다.

• Journal of Korea Foundry Society
• /
• v.20 no.5
• /
• pp.300-306
• /
• 2000

The objective of this work was to investigate the effects of SiC particle size(50, 100 ${\mu}m$) and additional elements such as Si, Cu and Ti on aging behavior in Al-5Mg-X(Si,Cu,Ti)/SiCp composites fabricated by pressureless infiltration method using hardness and wear test, scanning electron microscopy(SEM) and differential scanning calorimetry(DSC). The peak aging time in Al-5Mg-X(Si, Cu, Ti)/SiCp(50, 100 ${\mu}m$) composites is shorter than Al-5Mg-0.3Si alloy.The peak aging time of 50 ${\mu}m$ SiC particle reinforced Al-5Mg-X(Si,Cu,Ti) composites is shorter than those of 100 ${\mu}m$ SiC particle reinforced of Al-5Mg-X(Si,Cu,Ti) composites. The Al-5Mg-0.3Si-0.1Cu-0.1Ti/SiCp(50 ${\mu}m$) composites aged at $180^{\circ}C$ has higher hardness and better wear resistance than any other aged composite.The aging effect is promoted by the addition of Si and Cu in Al-5Mg/SiCp composites, so the wear resistance of Al-5Mg/SiCp composites with Si and Cu elements is enhanced by the aging treatment.

• Journal of Powder Materials
• /
• v.12 no.4 s.51
• /
• pp.296-302
• /
• 2005

In order to improve mechanical properties, the hypereutectic Al-20 wt%Si based prealloy powder was prepared by gas atomization process. Microstructure and compressibility of the atomized Al-Si powder were investigated. The average powder size was decreased with increasing the atomization gas pressure. Size of primary Si particles of the as-atomized powder was about $5-8\;\mu{m}$. The as-atomized Al-Si powder such as AMB 2712 and AMB 7775 to increase compressibility and sinterability. Relative density of the mixed powder samples sintered at $600^{\circ}C$ was reached about 96% of a theoretical density.