• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.117-121
• /
• 2000

Er-doped sodiumborosilicate glass films for waveguides amplifier were fabricated by Aerosol Flame Deposition(AFD) method. Al2O3 was added to sodium borosilicate glass films to suppress the formation of crystalline phase and control the refractive index. the formation of crystalline phase was suppressed above Al2O3 of 6 wt%. As the amount of Al2O3 increased from 2 to 12 wt% the refractive index of glass films increased lineary from 1.4595 up to 1.4710. After the core of 77SiO2-15B2O3-8Na2O＋6 wt%Al2O3＋8wt%Er2O3 was coated on the buffer layer of 77SiO2-15B2O3-8Na2O＋6 wt%Al2O3, the core was etched by reactive ion etching. The absorption spectrum of 3 cm waveguide amplifier showed two peaks of 1530 and 1550 nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.338-341
• /
• 2002

$(Ba_{1-x}Sr_{0.4}Ca_x)TiO_{3}$ (x=0.10, 0.15, 0.20) powders were prepared by the sol-gel method and BSCT thick films were fabricated by the screen-printing method. Their structural and dielectric properties were investigated with variation of composition ratio and $Al_{2}O_{3}$ doping contents. As results of the X-ray diffraction and microstructure analysis, the grain size of BSCT thick films was decreased with increasing $Al_{2}O_{3}$ amount. The thickness of BSCT thick films by 4-coating/drying is about $110{\sim}120{\mu}m$. The tunability increased with decreasing Ca content, and the BSCT(50/40/10) specimen doped with 1.0wt% $Al_{2}O_{3}$ showed the highest value of 12.94% at 5kV /cm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.6
• /
• pp.493-498
• /
• 2008

This Paper describes the Raman scattering characteristics of polycrystalline (Poly) 3C-SiC thin films, in which they were deposited on AlN buffer layer by APCVD using hexamethyldisilane (MHDS) and carrier gases (Ar+$H_2$). When the Raman spectra of SiC films deposited on the AlN layer of before and after annealing were worked according to growth temperature, D and G bands of graphite were measured. It can be explained that poly 3C-SiC films admixe with nanoparticle graphite and its C/Si rate is higher than ($C/Si\;{\approx}\;3$) that of the conventional SiC, which has no D and G bands related to graphite. From the Raman shifts of 3C-SiC films deposited at $1180^{\circ}C$ on the AlN layer of after annealing, the biaxial stress of poly 3C-SiC films was obtained as 896 MPa.

• Journal of the Korean Ceramic Society
• /
• v.41 no.5
• /
• pp.364-369
• /
• 2004

The barrier and optical properties of AlO$_{x}$ thin films on polycarbonate deposited by Reactive Ion Beam Sputtering (RIBS) were investigated at different oxygen partial pressure. We measured the deposition rate of AlO$_{x}$ thin films. As the oxygen partial pres-sure increased, the deposition rate increased then decreased. The changes of deposition rate are associated with the properties of deposited films. The properties of deposited AlO$_{x}$ thin films were studied using X-ray Photoelectron Spectroscopy (XPS), Scan-ning Electron Microscopy (SEM), and Atomic Force Microscopy (AFM). Optimum deposition parameters were found for fabricat-ing aluminum oxide thin films with high optical transparency for visible light and low Oxygen Transmission Rate (OTR). The optical transmittance of AlO$_{x}$ thin film deposited on polycarbonate (PC) showed the same value of bare PC.bare PC.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.11
• /
• pp.905-910
• /
• 2011

To study encapsulation method for large-area organic light emitting diodes (OLEDs), red emitting OLEDs were fabricated, on which LiF and Al were deposited as inorganic protective films. And then the OLED was attached to flat glass by printing method using epoxy. In case of direct coating of epoxy onto OLED by printing method, luminance and current efficiency were remarkably decreased because of the damage to the OLED by epoxy. In case of depositing LiF and Al as inorganic protective films and then coating of epoxy onto OLED, luminance and current efficiency were not changed. OLED lifetime was more increased through inorganic protective films between OLED and flat glass than that without any encapsulation (8.8 h), i.e., 47 (LiF/Al/epoxy/glass), 62 (LiF/Al/LiF/epoxy/glass), and 84 h (LiF/Al/Al/epoxy/glass). The characteristics of OLED encapsulated with inorganic protective films (attached to flat glass) showed the possibility of application of protective films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.303-304
• /
• 2008

Al, N-codoped ZnO(ZnO:N,Al) thin films were deposited on n-type Si(100) substrate at $450^{\circ}C$ with various conditions of ambient gas$(N_2:O_2)$ by DC magnetron sputtering method using ZnO:$Al_2O_3$(2wt%) as a target, and then were annealed at 500, 700, $800^{\circ}C$ in $N_2$ gas for one hour. XRD patterns showed that all of the ZnO:N,Al thin films annealed at $80^{\circ}C$ grew with two peaks, which means poor crystallinity of the thin films deposited. Hall effects in Van der Pauw configuration proved that after annealing the films deposited showed low resistivity and high carrier concentration. While the films annealed at $800^{\circ}C$ showed low resistivity of $\sim10^{-2}\Omega$ cm and high carrier concentration of $\sim10^{19}cm^{-3}$.

• Journal of the Semiconductor & Display Technology
• /
• v.10 no.1
• /
• pp.57-61
• /
• 2011

To develop high efficiency crystalline solar cells, the rear surface passivation is very important. In this paper, $Al_2O_3$ films deposited by thermal ALD(atomic layer deposition) method were studied for rear surface passivation of crystalline solar cells and their passivation properties were evaluated. After the deposition of $Al_2O_3$ films on p-type Si wafers, the lifetime was increased very much due to the reduction of interface state density and the field effects of the negative fixed charge in the films. Also, optimum annealing condition and effects of SiNx capping layer were investigated. The best lifetime was obtained when the films were annealed at $400^{\circ}C$ for 15min. And the lifetime degradation of the $Al_2O_3$ films with SiNx capping layers was improved compared to those without the capping layers.

• Electrical & Electronic Materials
• /
• v.10 no.7
• /
• pp.706-712
• /
• 1997

AlN(Aluminium Nitride) thin films were prepared using by RF sputtering method on the Si(100) and Si(111) substrates as the parameters of the substrate temperature, RF power, sputtering duration and the $N_2$/Ar ratio and investigated by X-ray diffraction, IR spectrometry, n&k analyzer. For the Si(100) substrate, the AlN thin films of (101) orientation were obtained under the conditions of room temperature and the nitrogen of 60 vol.%. For the Si(111) substrate, the (002) AlN thin films were obtained under the nitrogen of 100 vol.%. In case of the thin film prepared in the condition of above 60 vol.% of the nitrogen, the average value of the surface roughness of the film was 151$\AA$. From the changes of the half widths of E$_1$[TO] phonon bands at the wavenumber of 680$cm^{-1}$ /, it were compared of the crystallinities of the films which were grown under the different conditions. The thicknesses of AlN films were decreased dramatically in the region of the nitrogen of 40~60 vol.%. Its due to the nitridation of the Al target surface and getting low of the sputtering yield by the $N_2$/Ar ratio being increased.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.189-189
• /
• 2016

In this study, the Al-rich AlTiSiN thin films that consisted of TiN/AlSiN nano-multilayers were deposited on the steel substrate by magnetron sputtering, and their high-temperature oxidation behavior was investigated, which has not yet been adequately studied to date. Since the oxidation behavior of the films depends sensitively on the deposition method and deposition parameters which affect their crystallinity, composition, stoichiometry, thickness, surface roughness, grain size and orientation, the oxidation studies under various conditions are imperative. AlTiSiN nano-multilayer thin films were deposited on a tool steel substrate, and their oxidation behavior of was investigated between 600 and $1000^{\circ}C$ in air. Since the amount of Al which had a high affinity for oxygen was the largest in the film, an ${\alpha}-Al_2O_3-rich$ scale formed, which provided good oxidation resistance. The outer surface scale consisted of ${\alpha}-Al_2O_3$ incoporated with a small amount of Ti, Si, and Fe. Below this outer surface scale, a thin ($Al_2O_3$, $TiO_2$, $SiO_2$)-intermixed scale formed by the inwardly diffusing oxygen. The film oxidized slower than the $TiO_2-forming$ kinetics and TiN films, but faster than ${\alpha}-Al_2O_3-forming$ kinetics. During oxidation, oxygen from the atmosphere diffused inwardly toward the reaction front, whereas nitrogen and the substrate element of iron diffused outwardly to a certain extent.

• Journal of Electrical Engineering and Technology
• /
• v.8 no.1
• /
• pp.163-167
• /
• 2013

Aluminum doped zinc oxide (AZO) thin films have been prepared on the glass substrates (Corning 1737) by sol-gel dip-coating method employing zinc acetate and aluminum chloride hexahydrate for the transparent conducting oxide (TCO) applications. 1 at% Al was doped to the ZnO thin films. The effects of post-heating temperature on the crystallization, optical and electrical properties of the AZO films have been investigated. Experimental results showed that post-heating temperature affected the microstructure, electrical resistance, and optical transmittance of the AZO films. From the X-ray diffraction analysis, all films have hexagonal wurtzite crystal structure. Optical transmittance spectra of the AZO films exhibited transmittance higher than about 80% within the visible wavelength region and the optical direct band gap ($E_g$) of these films was increased with increasing post-heating temperature. A minimum resistivity of $2.5{\times}10^{-3}{\Omega}cm$ was observed at $650^{\circ}C$.