• 대한치과기공학회지
• /
• 제39권2호
• /
• pp.83-91
• /
• 2017

Purpose: The objective of this study was to evaluate influence of mechanical properties of gingival shade composite resins(GSCRs) according to thermocycling treatment. Methods: The material utilized in this study was Crea.lign(CGR), Twiny flow(TGF) and Twiny(TGP). Total sixty specimens were fabricated with a dimension of $25{\times}2{\times}2mm$ according to the ISO 4049. After fabrications, specimens of before and after thermocycling(to $55^{\circ}C$ from $5^{\circ}C$) were stored in the distilled water for 24 hours at the $37^{\circ}C$. Three-point flexural test was performed in universal testing machine(Instron 5966, USA) at a crosshead speed of 1 mm/min. Flexural strength, flexural modulus and work of fracture according to the thermocycling were analyzed using a one-way ANOVA analysis. Surface analysis of GSCRs after thermocycling evaluated using the scanning electron microscope. Results: : The highest FS was measured in TGP group of NTC group and lowest in CGR group after TC. After TC, FS and FM decreased in CGR and TGP groups, but TGF increased. There was a statistically significant difference between FS and WOF in GSCRs(p<0.05). But FM did not show any significant difference after TC (p>0.05). The strength of the characteristic exceeded the flexural strength required by ISO 4049(> 80 MPa). Weibull modulus(m) showed the highest reliability in the TGP group (m = 14.22), and the reliability of the TGF and TGP groups after TC decreased. Conclusion: Thermocycling treatment is important factor influence of mechanical properties with gingival shade composite resins. Therefore, we recommended that mechanical properties need to get useful information and accuracy for life-span expectancy according to the thermocycling treatment.

• 한국막학회:학술대회논문집
• /
• 한국막학회 1999년도 Energy Saving Membrane Separtion Systems 에너지 절약형 막분리 시스템
• /
• pp.39-39
• /
• 1999

Membrane separation technology has become a more attractive technology on waste water treatment and water recycle in recent years. On this application, membrane does not take main part of treatment, such as decomposition or handling of organic matter in the waste water, but it is very important supporting method in the total system. Activated sludge is most popular method as main part. In the system , membrane works as a separator to obtain clear water after biological treatment, by which the permeate could be released, recycled or applied to further additional treatment, instead of conventional sedimentation, coagulation and sand filtration. We would like to introduce our system cases for waste water treatment and water recycle, in which membrane separation technology works. In most of cases, membranes are applied to solid- liquid separation of activated sludge. Our experiences will be introduced as following items.

• 한국재료학회지
• /
• 제28권3호
• /
• pp.174-181
• /
• 2018

Three kinds of STS304-Zr alloys were fabricated by varying the Zr content, and their microstructure and fracture properties were analyzed. Moreover, we performed heat treatment to improve their properties and studied their microstructure and fracture properties. The microstructure of the STS304-Zr alloys before and after the heat treatment process consisted of ${\alpha}-Fe$ and intermetallics: Zr(Cr, Ni, Fe)2 and Zr6Fe23. The volume fraction of the intermetallics increased with an increasing Zr content. The 11Zr specimen exhibited the lowest hardness and fine dimples and cleavage facets in a fractured surface. The 15Zr specimen had high hardness and fine cleavage facets. The 19Zr specimen had the highest hardness and large cleavage facets. After the heat treatment process, the intermetallics were spheroidized and their volume fraction increased. In addition, the specimens after the heat treatment process, the Laves phase (Zr(Cr, Ni, Fe) 2) decreased, the Zr6Fe23 phase increased and the Ni concentration in the intermetallics decreased. The hardness of all the specimens after the heat treatment process decreased because of the dislocations and residual stresses in ${\alpha}-Fe$, and the fine lamellar shaped eutectic microstructures changed into large ${\alpha}-Fe$ and spheroidized intermetallics. The cleavage facet size increased because of the decomposition of the fine lamellar-shaped eutectic microstructures and the increase in spheroidized intermetallics.

• 환경위생공학
• /
• 제14권4호
• /
• pp.137-142
• /
• 1999

Current semiconductor industry factories are relying on the end-of-pipe treatment technology for waste water treatment and thus they mostly suffer from severe industrial water shortage. As a result in order to solve those waste and industrial water problems, there requires to be changed to the Clean Technology, that is Pollution Prevention Technology. Through above strategic actions with the Clean Technology, we shall strength more powerful and logical environmental pollution prevention system than those in the past. By changing the end-of-pipe treatment technology for waste water treatment and thus they mostly suffer from severe industrial water problems, there requires to be changed to the Clean Technology, that is Pollution Prevention Technology. Through above strategic actions with the Clean Technology, we shall strength more powerful and logical environmental pollution prevention system than those in the past. By changing the end-of-pipe treatment technology with physical, chemical and biological treatment methods as a mixed stream basis for treating of semiconductor waste stream into clean technology with pollution prevention technology as a waste segregation basis, we can bet 20 to 30% investment reduction as compared with end-of-pipe treatment technology.The results for water quality analysis were as follows : 1. Water quality analysis of the before treatment : pH : 9~10.5, Conductivity : $300~7,000{\mu}s/cm$, TDS : more then $3,000mg/{\ell}$, COD : $200~250mg/{\ell}$, SS : $500~600mg/{\ell}$, n-H : $8.3mg/{\ell}$ 2. Water quality analysis of the after treatment : pH : 6.5~7.5, Conductivity : 0.059, TDS : $40{\mu}s/cm$, COD : $20mg/{\ell}$, SS : $5mg/{\ell}$ n-H : $0.6mg/{\ell}$

• 대한감각통합치료학회지
• /
• 제1권1호
• /
• pp.9-16
• /
• 2003

Objective : The experiment consists of measuring functional grasp ability of a child suffering from sensory defense disability of the hands as the child is treated with sensory integration therapy. Methods : We treated two-year-old child with developmental disability to set up the reversal design(ABAB design). We used treatment equipments, free activities, and toys for sensory integration therapy. Results : A child's functional grasp ability did not show anything before the sensory integration therapy, however, after the sensory integration was applied during the first treatment(Treatment 1), the five minutes before the treatment, it averaged 1.87 times(ranges=0 to 5 times), the five minutes after the treatment, it averaged 1.25 times(ranges=0 to 8 times) showing an increased. After ending the sensory integration therapy, the functional grasp ability averaged 2.5 times before the therapy and 4 times after the therapy, which showed a totally different tendency, when we reapplied the treatment during the second treatment(Treatment 2), it averaged 2.4 times(ranges=1 to 4 times) before the treatment, and it averaged 5.3 times(ranges=4 to 6 times) after the treatment, which showed a big improvement. Conclusion : The sensory integration therapy brought an increase in functional grasp ability along with improvement in daily life functions of the child. For this result, there should be more research to see more effects and results to help those in need.

• Preventive Nutrition and Food Science
• /
• 제9권2호
• /
• pp.121-125
• /
• 2004

Effects of chemical treatment with a citric acid solution or ozonated water on microbiological changes in lettuce and cabbage during storage were studied. Fresh lettuce and cabbage samples were cut into small pieces and treated by soaking in either ozonated water or a citric acid solution. After treatment, populations of total bacteria, yeast and mold, and E. coli were determined. Numbers of microorganisms increased during storage, but ozonated water and citric acid treatments retarded the increase in microbial growth. Among treatments, 1 % citric acid treatment was the most effective in terms of microbiological change and inhibition of polyphenoloxidase (PPO). For lettuce, citric acid treatment decreased the microbial growth overall by 1.5 log CFU/g and inhibited the PPO activity by 80%. These results indicate that chemical-treated lettuce and cabbage retained a better quality than those of the control during storage.

• 대한치과기공학회지
• /
• 제33권4호
• /
• pp.441-452
• /
• 2011

Purpose: Identify the factors that influence following up control and reuse intention of patient who used dental health care institution after dental heath care service and in order to prepare the method which improve the quality of dental health service which dental heath care institution service afford. Methods: Data were collected through random sampling from June 20th to August 20th 2010 (for 60 days). Once we explained the purpose of our survey to people who experienced the dental service within one year, we distributed the questionnaires to someone who volunteered to respond and they answered all questions by themselves based on the actual experience of dental health care organizations. Even if the survey was conducted for 610 people, only 585 properly answered questionnaires were analyzed because responses which had many unanswered questions and had errors in responsive way were excluded. Results: Result of multiple regression analysis, the value of dental clinic service, the following up control after dental treatment, the technique and kindness of dentist, the environment of treatment, type of dental service and the kindness of dental staff is significant main cause to intention of reuse dental clinic. Conclusion: In order to increase the rate of patient reuse, enhance the value of service with following up control after health treatment and the high quality of dental health service.

• 대한치과기공학회지
• /
• 제44권4호
• /
• pp.111-117
• /
• 2022

Purpose: This study was conducted to compare the Vickers hardness on the denture acrylic resins using the glaze color system. Methods: The specimens (20×2 mm) were prepared by mixing according to the manufacturer's protocols through thermal polymerization and self-polymerization. The surface roughness was measured using a testing machine after water-soaking for 48 hours. For the Vickers hardness measurement, the completed specimen was soaked in water for 48 hours and then applied at 200 gf for 30 seconds. Was the specimen immersed after being soaked in water for 48 hours at temperatures of 5℃ and 55℃, respectively, for 30 seconds for the thermos-cycling treatment, and it was carried out 5,000 times. Results: Surface roughness was higher in the more glazing group than in the control group. A significant difference was observed in all groups, except for the Retec Don 2000 and Luciton 199 groups (p<0.05). As a result of measuring the Vickers hardness, the treatment by glaze color showed slightly lower but the thermo-cycling treatment group appeared higher than control group in all. Conclusion: Therefore, the glaze color was found to affect the surface roughness and showed a significant difference. The surface glaze color showed a very high Vickers hardness after the thermo-cycling treatment, indicating that the surface-strengthening effect is greater in the oral environment.

• Transactions on Electrical and Electronic Materials
• /
• 제3권4호
• /
• pp.27-31
• /
• 2002

Thin film diode with reliable interfacial structure was fabricated by using multi-step anodic oxidation. The thickness of the oxide layer was preciously controlled with anodic voltage. Also, interfacial structure between oxide layer and top electrode was improved by applying post heat-treatment. The thin film diode showed symmetric and stable I-V characteristics after the post heat-treatment.

• 열처리공학회지
• /
• 제37권2호
• /
• pp.79-85
• /
• 2024

The effects of annealing heat treatment and the addition of Cu element on the shape memory effect of the NiTi-based alloy were investigated by analyzing differential scanning calorimeter results and characterizing recovery rate through 3D scanning after Vickers hardness test. Through 3D scanning of impressions after Vickers hardness test, the strain recovery rates for specimens without annealing treatment and annealed specimens at 400, 450, and 500℃ were measured as 45.96%, 46.76%, 52.37%, and 43.57%, respectively. This is because as the annealing temperature increases, both B19' and NiTi₂ phases, which can impede martensitic transformation, are incorporated within the NiTi matrix. Particularly, additional phase transformation from R-phase to B19' observed in specimens annealed at 400 and 450℃ significantly contributes to the improvement in strain recovery rates. Additionally, the results regarding the Cu element content indicate that when the total content of Ni and Cu is below 49.6 at.%, the precipitation of fine B19' and NiTi₂ phases within the matrix can greatly influence the transformation enthalpy and temperature range, resulting in relatively lower strain recovery rates in NiTi alloys with a small amount of Cu element produced in this study.