• 대한치과보철학회지
• /
• 제32권2호
• /
• pp.225-233
• /
• 1994

The restorations of the severely damaged teeth by post core have been increased with the developement of endodontic procedures. But high failure rates of these procedures being reported, various restorative modifications were induced for successful treatments. Cast post-core and prefabricated post with core buildups are choice of treatment. The main causes of failure of the restorations are the fracture of post and core, root fracture, and recurrent caries due to microleakage. Recently, the acid etching technique and the use of dentin bonding agent at tooth surface to reduce the possible microleakage at the tooth-restoration interfaces were introduced. The object of this study was to measure and compare the microleakage by the types and cementation methods of post-core. For this study, forty extracted human anterior teeth were selected for specimen. After cleansing and routine endodontic procedures, anatomic crowns of each specimen were removed at the level of 2mm above the cementoenamel junction. Canals were preparated for post insertion and specimens were divided into four groups randomly. Post-cores were fabricated according to method for each group. Microleakage was measured by length of dye penetration at the tooth-restoration interfaces with measuring microscope at 50 magnification. Oneway ANOVA and t-test were performed for statistical analysis of resulting data. The following results were obtained from this study. 1. There wert significant statistical differences in degree of microleakage between each group (p<0.01). 2. Cast post-core cemented with ZPC (Group I) showed the most severe microleakage pattern$(1.5547{\pm}0.0872mm)$, and cast post-core cemented with adhesive resin cement after tooth surface treatment with dentin bonding agent (Group II) showed the least microleakage $(0.1497{\pm}0.0872mm)$. 3. Group IV revealed less dye penetrations than group III, but no statistical significance was seen between two groups.

• 한국전산구조공학회논문집
• /
• 제23권2호
• /
• pp.191-198
• /
• 2010

이 연구에서는 접착패치보강의 서로 다른 형태 즉, 패치와 접착제의 재료, 크기, 두께 뿐만 아니라 일면보강 또는 양면보강에 따른 일변균열판의 응력감소에 대한 연구가 수행되었다. 수치해석 도구로는 p-수렴 부분층별 모델이 사용되었다. 이 모델의 면내 변위는 구간별 연속인 선형변화로 가정하였고, 두께방향으로의 면외 변위는 일정한 상수로 가정하여 적용하였다. 변위장의 정의는 적분형 르장드르 다항식을 적용하였고, 수치적분은 별도의 외삽법 없이 각 층별의 절점에서 발생하는 적분값을 바로 얻을 수 있는 가우스-로바토 적분법을 사용 하였다. 또, 에너지 방출률법을 사용하여 응력확대계수를 산출하였다. 수치예제를 통해 제안된 모델의 정확도는 물론이고 접착패치 보강형태에 따라 변화되는 무차원 응력확대계수와 처짐의 항으로 응력감소 효과를 분석하였다.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2006년도 춘계학술대회 논문집
• /
• pp.295-299
• /
• 2006

The inner-structure bonded(ISB) sheet metal is defined as a composite sheet metal which has middle layer of truss-structure between two skin sheets. The characteristics such as ultra-light weight, high rigidity, high strength, etc are required especially for automobile parts. The characteristic of ISB sheet metal depends on inner-structure pattern or method of bonding. Pyramid type of crimped expanded metal is used for inner-structure and both of resistance welding and adhesive bonding are applied to make a specimen. As a result of compression test, it is appeared that forming limit is 10% reduction in thickness under a load of 8kgf per unit element(one inner-structure). In case of uniaxial tensile test the non-uniform surface integrity rather than the buckling of inner-structure happened at a load of 450kgf, which indicates elongation of 7.2% and thickness reduction of 13%. The eye-inspection method was applied to examine the defects occurring on the specimen during stretch forming. In case of biaxial stretch forming only the non-uniform deformation on the surface of a skin sheet could be observed. The forming limit in stretching of ISB sheet metal with the hemi-spherical punch of 150mm in diameter was 3mm in forming depth and 5% reduction in thickness.

• Advances in pediatric surgery
• /
• 제13권1호
• /
• pp.23-29
• /
• 2007

Tapering enteroplasty was first described by Thomas in 1969 as one method of intestinal anastomosis. The advantages of tapering enteroplasty in the intestinal atresia are: First, it makes end-to-end anastomosis possible between the atretic bowel ends with considerable differences in diameters. Second, it promotes the recover of the postoperative bowel function. Third, it prevents the possibility of the short bowel syndrome by eliminating the need of resecting the dilated bowel. A total of 22 patients with intestinal atresia who underwent tapering enteroplasty from January 1988 to December 2005 at our institute were reviewed. In 3 of 22 cases, tapering enteroplasty was the $2^{nd}$ operation after an initial end-to-oblique anastomosis. We reviewed the following items: age, sex, type and location of intestinal atresia, initial feeding and total enteral feeding start day, the length of hospital stay and complications. The average age of the patients was 7 days. Male to female ratio was 1 to 1.2 (10 cases: 12 cases). We performed the tapering enteroplasty on all types and locations of the intestinal atresia from the duodenum to the colon: type I (n=3), type II (n=4), type IIIA (n=7), type IIIB (n=5), type IIIB and IV (n=1), type IV (n=1) and type C (duodenum) and type IIIB and IV (jejunum). On the average, the oral feeds were started on the postoperative $8.8^{th}$ day, and full caloric intake via the enteric route was achieved on postoperative $13.3^{th}$ day. The average length of hospital stay was 19.6 days. There were 1 case (4.5 %) of anastomotic complication and 2 cases (9 %) of adhesive ileus among 22 patients. The tapering enteroplasty on all types of intestinal atresia is a usefull operative method when there are considerable diameter differences between the atretic bowel ends.

• Tribology and Lubricants
• /
• 제30권5호
• /
• pp.271-277
• /
• 2014

Hydraulic reciprocating seals have been widely used to prevent fluid leakage and to provide lubricant film on counter surface in various hydraulic system. The degradation of the seal may cause the catastrophic failure of the hydraulic system. To assess the durability of the seals and the compatibility with counter surface, accelerated life testing (ALT) has been typically employed from industry. However, ALT often takes up to a few months to cause a failure of the seals, and therefore, there is a need to develop more efficient ALT methods. In this work, the degradation characteristics of polyurethane (PU) seals from field test are investigated and they are compared to those from the component and bench tests, with an aim to contribute to the development of ALT method. From the comparison of the cross-sectional profiles of the sealing surface of the PU specimens before and after the tests, both wear and compression set are found to be responsible for degradation of the PU seals. It is also shown that the major wear mechanisms of the PU seals from the field is abrasive wear and formation of pits. The component and bench tests performed in this work are shown to reproduce such wear mechanisms, and therefore, those test methods can be used as an ALT method for PU seals. In particular, the bench test proposed in this work may be effectively utilized to assess the durability and the compatibility of the seals with the counter surface. The results of this work are expected to aid in the design of ALT for PU seal.

• 한국전기전자재료학회논문지
• /
• 제17권5호
• /
• pp.486-491
• /
• 2004

Dimensionally stable anode(DSA) can be used for the hydro-metallurgy of non-ferrous metals like as Zn, and the electrolysis of sea water. MnO$_2$ electrode satisfies the requirements of DSA, and has a good cycle life and a low overpotential for oxygen evolution. MnO$_2$ electrodes based on Ti matrix were prepared by using thermal decomposition method and also MnO$_2$ was coated on Ti and Pb matrix with DMF and PVDF compositions. The MnO$_2$ electrodes prepared by thermal decomposition method had very weak adhesive strength onto Ti matrix and MnO$_2$ layer was removed out so that electrochemical properties for MnO$_2$ were not investigated. The viscosity of solvent used as a binder of MnO$_2$ Powder increased with the increasing PVDF contents. The thickness of the MnO$_2$ layer on Pb matrix in DSA, which was prepared with 5 times dipping at the solution mixed with PVDF : DMF = 1 : 9, was 150${\mu}{\textrm}{m}$. When the ratio of PVDF to MnO$_2$ was lower than 1 : 6, the Pb electrode didn't show any reaction irrespective of the concentrations of DMF. However, When the ratio of PVDF to MnO$_2$ was higher than 1: 6, the Pb electrode showed constant current reactions and homogeneous cyclic voltammetry even though at a high cycle. The reason for the high current and homogeneous cyclic voltammetry is the good catalytic reactions of MnO$_2$ powder in electrode.

• Composites Research
• /
• 제30권6호
• /
• pp.393-398
• /
• 2017

손상된 치아의 복구에 사용되는 재료인 치과용 복합레진 Clearfil AP-X (Kuraray, Japan)을 대상으로 디지털 이미지 상관법을 이용하여 광중합 시 발생하는 수축분포를 관찰하였다. 디지털 이미지 상관분석법을 위해, CCD 카메라를 이용하여 광조사 중과 광조사 이후의 촬영 조건을 달리하여 사진을 획득하였다. 광조사중의 최적의 촬영 조건을 설정하기 위하여 노출시간을 0.15 ms부터 0.55 ms까지 0.05 ms 간격으로 촬영한 사전 실험을 통해 촬영 조건을 획득하였다. DIC 분석 결과 복합레진의 비균일한 수축 분포를 관찰하였으며 복합레진의 중심 부분에서 시편의 계면부보다 좀 더 자유로운 유동성으로 더 큰 수축이 발생하였다. 복합레진의 중합수축은 초기 20 s 의 광조사에서 최종경화수축률의 50~60% 수준까지 발생하였다. 이러한 치과용 복합레진의 큰 수축량은 레진/기질계면 근처에서 인장응력이 집중하도록 영향을 주었다.

• Composites Research
• /
• 제33권1호
• /
• pp.1-6
• /
• 2020

탄소나노튜브의 함량에 따라 폴리우레탄 타입 탑코트의 분산도 및 전기저항의 평가를 통해 탄소나노튜브의 최적함량을 찾기 위한 연구를 진행하였다. 초음파 분산을 통하여 탄소나노튜브를 폴리우레탄 탑코트 내에 분산하였고, 중력식 스프레이건을 이용하여 탄소섬유/에폭시 복합재 표면에 탄소나노튜브/폴리우레탄 탑코트의 코팅을 진행하였다. 4가지 용매를 이용하여 탄소섬유복합재와 탄소나노튜브/폴리우레탄 탑코트의 정적접촉각을 측정하였고, 이를 이용하여 접착일을 계산하였다. 탄소나노튜브/폴리우레탄 탑코트의 표면저항을 측정하였고 이를 통하여 탄소나노튜브의 최적 함량조건을 파악하였다. ASTM D3359를 기반으로 크로스 컷 시험을 진행하였고 이를 통하여 탄소나노튜브/폴리우레탄 탑코트의 부착특성을 평가하였다. 실험결과를 통해 탄소나노튜브의 최적 조건을 파악하였다.

• 한국환경복원기술학회지
• /
• 제2권4호
• /
• pp.64-73
• /
• 1999

This study was conducted to find out the effects of hydroseeding material and seed mixture on the revegetation of rock cut-slopes by PEC4 (Polymer-Ecology-Control) Hydroseeding Measures. PEC4 hydroseeding material was applied to four cut-slopes using hydroseeding measures from April to August, 1999, and the field survey was carried out by monthly. PEC4 material consisted of bark compost and organic soil amendments. This material has high content of organic matter and high level of water holding capacity. PEC4 hydroseeding material shows low level of soil hardness, so it gives to good condition for seed germinating and plant growing in early stage. PEC4 material attached at rock cut-slopes by two types of adhesive agent was not eroded by rainfall. The plant coverage and number of plant species were affected by mixing ratio of seeds and seeding timing. From the viewpoint of plant establishment, the optimal hydroseeding timing of mixed seeds for plant growth seems to be in May. Most of the plant seeds were germinated well and they covered rock cut-slopes so quickly and effectively. Plant importance value of Silene armeria and Platycodon grandiflorum. were higher than any other seeded-native species in the competition between native species and exotic species, so they have enough possibility to be used for slope revegetation works. Thus it leads to conclusion that the revegetation method used in this experiment was a very effective method for plant establishment on rock cut-slopes.

• 한국표면공학회지
• /
• 제32권2호
• /
• pp.144-156
• /
• 1999

Thermal Barrier Coating with Functional Gradient Materials (FGM-TBC) can play an important role to protect the parts from harmful environments in high temperatures such as oxidation, corrosion, and wear and to improve the efficiency of aircraft engine by lowering the surface temperature on turbine blade. FGM-TBC can increase the life spans of product and improve the operating properties. Therfore, in this study the evaluations of mechanical and thermal properties of FGM-TBC such as fatigue, oxidation and wear-resistance at high temperatures have been conducted. The samples of both the TBC with 2, 3, 5 layers (YSZ/NiCrAlY) to be produced by Air Plasma Spray method (APS) and the bulk TBC with 6 layers to be produced by Plasma Assisted Sintering method (PAS) were used. Furthermore, residual stress, bond strength, and thermal conductivity were evaluated. The average thickness of the APS was 500$\mu\textrm{m}$ to 600$\mu\textrm{m}$ and the average thickness of the PAS was 3mm. The hardness number of the top layer of APS was 750 Hv to 810Hv and that of PAS was 950 Hv to 1440Hv. The $ZrO_2$ coating layer of APS was composed of tetragonal structure after spraying as the result of XRD analysis. As shown in the results of the high temperature wear test, the 3 layer coating of APS had the best wear resistance at $800^{\circ}C$ and the 5 layer coating of APS had the best wear resistance at $600^{\circ}C$. But, these coatings had the tendency of the low-temperature softening at $300^{\circ}C$. The main mechanism of wear was the adhesive wear and the friction coefficient of coatings was increased as increasing the test temperatures. A s results of thermal conductivity test, the ${\Delta}T$ of the APS coating was increased as number of layer and the range of thermal conductivity of the PAS was $800^{\circ}C$ to $1000^{\circ}C$.