• Corrosion Science and Technology
• /
• v.18 no.4
• /
• pp.148-153
• /
• 2019

Pure nickel with a thickness of 1 mm was plated on type 304 stainless steels and low alloy steels (JIS G3131 SPHC) by electrolytic plating method in a circulating plating bath. Plating performance, mechanical properties, and surface characteristics were evaluated in terms of pretreatment process, anode material, pH, current density, and flow rate of the plating solution. Addition of hydrochloric acid during pre-treatment process improved the adhesion performance of plating. To improve plating efficiency, it is desirable to use S-nickel rather than electrolytic nickel. The use of S-nickel was also confirmed to be desirable for maintaining the pH and concentration of the plated solution. The defect of the plating using S-nickel anode produced pit on the surface. However, it is believed that proper control can be obtained by increasing the flow rate. Internal stress and hardness values of electrolytic nickel plating according to current density need to be carried out with further studies.

• Steel and Composite Structures
• /
• v.31 no.5
• /
• pp.517-527
• /
• 2019

To move forward in large steps rather than in small increments, the community would benefit from a systematic and comprehensive database of multi-scale composites and measured properties, driven by comprehensive studies with a full range of types of fiber-reinforced polymers. The multi-scale hierarchy is a promising chemical approach that provides superior performance in synergistically integrated microstructured fibers and nanostructured materials in composite applications. Achieving high-efficiency thermal conductivity and mechanical properties with a simple surface treatment on single-walled carbon nanotubes (SWCNTs) is important for multi-scale composites. The main purpose of the project is to introduce ozone-treated SWCNTs between an epoxy matrix and basalt fibers to improve mechanical properties and thermal conductivity by enhancing dispersion and interfacial adhesion. The obvious advantage of this approach is that it is much more effective than the conventional approach at improving the thermal conductivity and mechanical properties of materials under an equivalent load, and shows particularly significant improvement for high loads. Such an effort could accelerate the conversion of multi-scale composites into high performance materials and provide more rational guidance and fundamental understanding towards realizing the theoretical limits of thermal and mechanical properties.

• Journal of Surface Science and Engineering
• /
• v.55 no.6
• /
• pp.425-432
• /
• 2022

Antifouling paints that inhibit the attachment and contamination of marine organisms mainly use TBT compounds, but because of their toxic components, they cause ecosystem disturbance and environmental destruction problems, so It is necessary to research eco-friendly antifouling paints that are easy to maintain and effective antifouling technologies. In this study, physical surface treatment of silane coating and chemical antifouling technology were applied to the metal surface to secure the stability of the surface of the marine structure and inhibit the attachment and growth of marine organisms. Adhesion of marine organisms was evaluated according to the coating conditions through surface evaluation of the charged material for 15 months in the waters of the west coast of Korea. In accordance with ASTM D6990-05, antifouling properties fouling rates (FR) and physical degradation rates(PDR) were evaluated through visual inspection of the evaluation specimens. As a result of evaluating the antifouling performance of the coated surface, it was confirmed that the antifouling performance was maintained at the 50% level even after 15 months in the sample subjected to physical processing and silane coating.

• Advances in concrete construction
• /
• v.11 no.2
• /
• pp.163-171
• /
• 2021

This paper studies the effect of using multi-scale reinforcement additives on mechanical strengths, damage performance, microstructure, and water absorption of cementitious composites. Small dosages of carbon nanotubes (CNTs) or polypropylene (PP) microfibers; 0.05%, 0.1%, and 0.2% by weight of cement; were added either separately or simultaneously into cement mortar. The experimental results show the ability of these additives to enhance the mechanical behavior of the mortar. The best improvement in compressive and flexural strengths of cement mortar reaches 28% in the case of adding a combination of 0.1% CNTs and 0.2% PP fibers for compression, and a combination of 0.2% CNTs and 0.2% PP fibers for flexure. Adding CNTs does not change the brittle mode of failure of plain mortar whereas the presence of PP fibers changes it into ductile failure and clearly enhances the fracture energy of the specimens. Scanning electron microscopic (SEM) images of the fracture surfaces highlights the role of CNTs in improving the adhesion between the PP fibers and the hydration products and thus enhance the ability of the fibers to mitigate cracks propagation and to enhance the mechanical performance of the mortar.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.1
• /
• pp.73-84
• /
• 2018

Recently, the importance of flame retardation treatment technology has been emphasized due to the increase in urban fire accidents and fire damage incidents caused by building exterior materials. Particularly, in the utilization of wood-based building materials, the flame retarding treatment technology is more importantly evaluated. An Intumescent system is one of the non-halogen flame retardant treatment technologies and is a system that realizes flame retardancy through foaming and carbonization layer formation. To apply the Intumescent system, composite material was prepared by using Ethylene vinyl acetate (EVA) as a matrix. To enhance the flame retardant properties of the Intumescent system, a nano-clay was applied together. Composite materials with Intumescent system and nano - clay technology were processed into sheet - like test specimens, and then a new structure of cross laminated timber with improved flame retardant properties was fabricated. In the evaluation of combustion characteristics of composite materials using Intumescent system, it was confirmed that the maximum heat emission was reduced efficiently. Depending on the structure attached to the surface, the CLT had two stages of combustion. Also, it was confirmed that the maximum calorific value decreased significantly during the deep burning process. These characteristics are expected to have a delayed combustion diffusion effect in the combustion process of CLT. In order to improve the performance, the flame retardation treatment technique for the surface veneer and the optimization technique of the application of the composite material are required. It is expected that it will be possible to develop a CLT structure with improved fire characteristics.

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.3172-3179
• /
• 2011

Several materials using polymer-portland-cement concrete have developed to have not only strength of attachment with body, but also waterproof function and strong anti-sodium chloride properties. Especially, in case of railway, unlike other public transportation, it is very difficult to doing the repair and reinforcement work of structure during service time. Therefore, the development and study of materials having characteristics of structural strength, unification behavior with body, and resistance of crack are very important. Accordingly, the characteristic of material of polymer based concrete is indicated compared with the experiment and analysis through this study, and suggested application to railway tunnel, bridge, and concrete track structure.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.354.1-354.1
• /
• 2016

Nanoporous gold (NPG) is a very promising material in various fields such as sensor, actuator, and catalysis because of its high surface to volume ratio and conducting nature. In this study, we fabricated a NPG based amperometric sensor on a glass substrate by means of co-sputtering of Au and Si. During the sputtering process, we found the optimum conditions for heat treatment to reduce the residual stress and to improve adhesion between NPG films and the glass substrate. Subsequently, Si was selectively etched from Au-Si alloy by KOH solution, which forms nanoporous structures. Scanning electron microscopy (SEM) and auger electron spectroscopy (AES) were used to estimate the structure of NPG films and their composition. By employing appropriate heat treatments, we could make very stable NPG films. We tested the performance of NPG sensor with aniline molecules, which shows high sensitivity for sensing low concentration of aniline.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.368-373
• /
• 1998

Prepackaged system consists out of a dry mix which contains cement, sand, redispersible polymer powder and admixtures in the right proportions. The purpose of this study is to evaluate the quality of prepackaged-type polymer-modified mortar products using redispersible poly(ethylene-vinyl acetate)(EVA) powder. Polymer-modified mortars using the redispersible polymer powder with powdered with powdered shrinkage-reducing agent were prepared with cellulose fiber contents of 0, 0.5, 1.0% and shrinkage-reducing agent contents of 0, 4%, and tested for drying shrinkage, strength, adhesion in tension, water absorption. From the test results, the prepackaged-type polymer-modified mortar products with 4% of shrinkage-reducing agent content give good properties. and that their properties largely depends on the shrinkage-reducing agent content rather than the cellulose fiber contents.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.04a
• /
• pp.158-162
• /
• 1994

Test results to evaluate the mechanical properties of epoxy-coated bars and corrosion protection characteristics of epoxy coating on the bars are described. The results show good adhesion and abrasion resistance satisfying the requirements in relevant standards. The test results also show that for a coating thickness ranging from 150${\mu}{\textrm}{m}$ to 300${\mu}{\textrm}{m}$, satisfactory results are obtained regarding bendability. Cautions shall be required when bending epoxy-coated bars at a high bending degree and at a low temperature. The results of accelerated corrosion tests show good corrosion resistance. However, surface defects from the steel itself and insufficient blast-clean process form weak points resulting blistering or disbonding of the coating. The use of epoxy-coated bars is expected to help protect corrosion of reinforcement and extend the service life of reinforced concrete structures.

• The Korean Journal of Ceramics
• /
• v.2 no.4
• /
• pp.203-211
• /
• 1996

CVD diamond tools are becoming more widely used in industry as an economic alternative to polycrystalline diamond (PCD) for machining non-ferrous and non-metallic materials. Although CVD diamond-sheet tools have been on the market for several years, diamond-coated carbide inserts have become available only recently, with the successful resolution of long-standing adhesion problems. Diamond coating morphology on the rake surface of the tool affects chip formation favorably, whereas a microscopically rough, faceted morphology on the flank surface of the tool produces a rough workpiece finish. Workpiece finish can be improved by using a coated tool with a larger nose radius. The tool life provided by diamond-coated tools(~30 $\mu\textrm{m}$ thick) can meet or exceed that of PCD tools, depending on the characteristics of the workpiece material. When using diamond-coated carbide tools in milling, a sharp-edged PCD tool should be used in the wiper position of the cutter to minimize workpiece roughness and burr formation.