• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.4
• /
• pp.592-601
• /
• 2001

Fiber reinforced metal laminates(FRMLs) are new types of hybrid materials. FRMLs consists of high strength metal(Al 5052-H34) and laminated fiber with structural adhesive bond. The mixture ratio effect of epoxy resin$.$curing agent$.$accelerator on the fatigue behavior of FRMLs was investigated in this study. The epoxy, diglycidylether of bisphenol A(DGEBA), was cured by methylene dianiline(MDA) with or without an accelerator(K-54). Eight different kinds of resin mixture ratios were selected for the test ; five kinds of FRMLs(1) and three others of FRMLs(2). The relationship between da/dN and ΔK with variation of resin mixture ratio was studied. FRMLs(1) and FRMLs(2) indicated approximately 2 times and 2.2 times more improved maximum bending strengths in comparison with those of Al 5052-H34. The resin mixture ratio <1:1> in case of FRMLs(1) indicated the maximum fatigue life, while the resin mixture ratio <1:1:0.2> in case of FRMLs(2) indicated the maximum fatigue life. As results, FRMLs(2) turned out to have more effective characteristics on the fatigue properties and the bending strength than those of FRMLs(1).

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.18 no.5
• /
• pp.481-487
• /
• 2012

Recently, the construction of the small Al alloy ships is an increasing trend in viewpoint such as the disposal issue of a retired ship, the enhancement of environmental regulation and resources recycling etc. for FRP ships. However, Al alloy ship which can achieve high speed by light weight in marine environment is exposed to a problem on materials damage by cavitation-erosion which is generated by large impact pressure with the collapse of air bubbles due to cavitation. Consequently, in this study, water cavitation peening technology was applied in Al alloy for ship to enhance durability life by preventing cavitation damage. So, the water cavitaton peening application time that presented the excellent cavitation characteristic investigated. The weight-loss of 5456-H116, 5083-H321 and 5052-O Al alloy at the optimum water cavitation peening time were improved to 42.11 %, 50.0 % and 25.7 %, respectively.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.1
• /
• pp.30-36
• /
• 2021

In this study, double-layered anodizing films were formed on Al 5052 and Al 6061 alloys consecutively first in sulfuric acid and then in oxalic acid, and hardness, withstand voltage, surface roughness and acid resistance of the anodizing films were compared with single-layered anodizing films in sulfuric acid and oxalic acid electrolytes. Hardness of the double-layered anodizing film decreased with increasing ratio of inner layer to outer layer for both Al 5052 and Al 6061 alloys, suggesting that outer anodizing film formed in sulfuric acid electrolyte is damaged during the second anodizing in oxalic acid electrolyte. Withstand voltage of the double-layered anodizing films increased with increasing the thickness ratio of inner layer to outer layer. Surface roughness of the double-layered anodizing films were comparable with that of single-layered anodizing film formed in sulfuric acid but higher than that of single layer anodizing film formed in oxalic acid electrolyte. In acid resistance test, all of the double-layered and single-layered anodizing films showed good acid resistance more than 3 h without any visible gas evolution, which is attributable to sealing of pores. Based on the experimental results obtained in this work, it is possible to design a double-layered anodizing film with cost-effectiveness and improved physical and electrical properties by combining two consecutive anodizing processes of sulfuric acid anodizing and oxalic acid anodizing methods.

• Proceedings of the KSME Conference
• /
• 2001.06c
• /
• pp.616-620
• /
• 2001

The wrinkling in the flange and wall of a part is a predominent failure mode in stamping of sheet metal parts. In many cases this wrinkling may be eliminated by appropriate control of the blank holding force(BHF), but BHF affects the draw depth. Although the wrinkles of flange have been made in the incipient stage of drawing, if the height of wrinkles is maintained under a prescribed limit by decrease or extinction of wrinkles in the course of drawing, small BHP can be allowed so that the depth of drawing could be increased. Authors research the variation of the wrinkles in flange in the course of square cup drawing by using aluminium A1015 and aluminium alloy A5052.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.5 no.3
• /
• pp.50-57
• /
• 1996

This study was performed the blankholding force and Vee-ring effects on blanking characteristics, such as maximum blanking force, burnish, dish-shape, hardness. etc. in fine-blanking die by the experimental method. Two types of aluminum (Al.1050-O, Al, 5052-H) Such as annealed and unannealed materials were used for the experiment. In order to get a hydrostatic pressure effect, the clearance was set to 0.5% of the thickness of strip, and the counter punch and stripper plate with Vee-ring was set-up. While this experiment was carry8ing out, the average blanking velocity was constant (37.5mm/sec). As a result of this study, we got a good surface roughness and a dimensions, the good squareness and the reduction of dish-shape could be obtained, and also the additional results obtained were such that the hardness of shear plane was increased and the maximum blanking force was reduce in the condition of Vee-ring height of 1.0~1.5mm, and blankholding force of 1200kg.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2002.10a
• /
• pp.845-848
• /
• 2002

The wrinkling in the flange and wall of a part is a predominent failure mode in stamping of sheet metal parts. In many cases this wrinkling may be eliminated by appropriate control of the blank holding forco(BHF), but BHF affects the draw depth. Gotoh had studied the wrinkles under 0.02mm in height. In general, the height of wrinkles could be limited under 0.2mm practically. Therefore small BHP can be allowed so that the depth of drawing could be increased. Authors research the variation of the wrinkles in flange in the course of cup drawing by using aluminium alloy Al050 and A5052.

• Journal of Welding and Joining
• /
• v.27 no.3
• /
• pp.44-51
• /
• 2009

In this study, welding distortion analysis is performed for various design of tube shape structures which are assembled with aluminum sheet metal. Aluminum 5052 plates of 1mm thickness are used to analyze. An efficient keyhole model, as a welding heat source, is used for the prediction of full penetration weld size and shape which is required for the thermal analysis. The thermal and mechanical material properties are considered as temperature dependent functions, due to the high temperature variations during the welding. The numerical model is calculated by using a commercial software and evaluated with the experiments. The calculation results could make a comparative study in the view of distortion for the various size and shape of structure.

• International Journal of Precision Engineering and Manufacturing
• /
• v.4 no.4
• /
• pp.45-50
• /
• 2003

In order to investigate the effect of surface treatment (Anodizing) and rolling on AI 5083-H131 alloy, under hyper velocity impact, a ballistic testing was conducted. Ballistic resistance of these materials was measured by a protection ballistic limit ($V_{50}$)' a statistical velocity with 50% probability of penetration. Perforation behavior and ballistic tolerance, described by penetration modes, were respectfully observed, by $V_{50}$ test and Projectile Through Plates (PTP) test at velocities greater than $V_{50}$. PTP tests were conducted with 0$^{\circ}$ obliquity at room temperature using 5.56mm ball projectiles. $V_{50}$ tests with 0$^{\circ}$ obliquity were also done with projectiles that were able to achieve near or complete penetration during PTP tests. Resistance to penetration, and penetration modes of Al 5052-H34 alloy were compared to those of Al 5083-H 131 alloy.

• Transactions of Materials Processing
• /
• v.24 no.1
• /
• pp.20-27
• /
• 2015

Hot tensile tests were conducted at different temperatures ranging from $20^{\circ}C$ to $550^{\circ}C$ to evaluate the mechanical properties of Al5052 seamless tubes. Such tubes can provide the technological foundation for complex forming using hot air bulging. Hot air bulging is one of the recently developed hydroforming techniques and it has some limitations in terms of cycle times. The benefits of hot air bulging are weight and cost savings through part consolidation and reduced post-forming processes such as welding and piercing. In order to extend the forming limits of Al lightweight material hot air bulging was investigated. A heated tube was placed in a heated die and sealed at the ends by sealing cylinders. The heated tube was subsequently expanded against the die cavity wall by internal pressure using air medium. The results of the current study show that axial feeding speed and air pressure have an effect on the formability of Al tubes during air bulging at elevated temperatures.

• International Journal of Precision Engineering and Manufacturing
• /
• v.1 no.1
• /
• pp.33-41
• /
• 2000

Fiber reinforced metal laminates(FRMLs) were new type of hybrid materials. FRMLs consist of high strength metals(Al 5052-H34) and laminated fiber with structural adhesive bond. The effect of resin mixture ratios on the fatigue crack propagation behavior and mechanical properties of aramid fiber reinforced aluminum composites was investigated. The epoxy, diglycidylether of bisphenol A(DGEBA), was cured with methylene dianiline(MDA) with or without an accelerator(K-54). Eight kinds of resin mixture ratio were used for the experiment ; five kinds of FRMLs(1)(mixture of epoxy and curing agent) and three kinds of FRMLs(2)mixture of epoxy, curing agent and accelerator). The characteristic of fatigue crack propagation behavior and mechanical properties FRMLs(2) shows more effecting than that of FRMLs(1).