• Journal of Advanced Marine Engineering and Technology
• /
• v.10 no.2
• /
• pp.156-164
• /
• 1986

In the case of boiling on high temperature wall, vapor film covers fully or parcially the surface. This phenomenon, film boiling or transition boiling, is very important in the surface heat treatment of metal, design of cryogenic heat exchanger and emergency cooling of nuclear reactor. Mainly supposed hydraulic-thermal accidents in nuclear reactor are LCCA (Loss of Coolant Accident) and PCM (Power-Cooling Mismatch). Recently, world-wide studies on reflooding of high temperature rod bundles after the occurrence of the above accidents focus attention on wall temperature history and required time in transient cooling process, wall superheat at rewet point, heat flux-wall superheat relationship beyond the transition boiling region, and two-phase flow state near the surface. It is considered that the further systematical study in this field will be in need in spite of the previous results in ref. (2), (3), (4). The paper is the study about the fast transient cooling process following the wall temperature excursion under the CHF (Critical Heat Flux) condition in a forced convective subcooled boiling system. The test section is a vertically arranged concentric annulus of 800 mm long and 10 mm hydraulic diameter. The inner tube, SUS 304 of 400 mm long, 8 mm I.D, and 7 mm O.D., is heated uniformly by the low voltage AC power. The wall temperature measurements were performed at the axial distance from the inlet of the heating tube, z=390 mm. 6 chromel- alumel thermocouples of 76 .mu.m were press fitted to the inner surface of the heating tube periphery. To investigate the heat transfer characteristics during the fast transient cooling process, the outer surface (fluid side) temperature and the surface heat flux are computed from the measured inner surface temperature history by means of a numerical method for inverse problems of transient heat conduction. Present cooling (boiling) curve is sufficiently compared with the previous results.

• Korean Journal of Materials Research
• /
• v.13 no.8
• /
• pp.519-523
• /
• 2003

We report the synthesis of cubic spinel $ZnCo_2$$O_4$thin films and the tunability of the conduction type by control of the oxygen partial pressure ratio. Zinc cobalt oxide films were grown on$ SiO_2$(200 nm)/Si substrates by reactive magnetron sputtering method using Zn and Co metal targets in a mixed Ar/$O_2$atmosphere. We found from X-ray diffraction measurements that the crystal structure of the zinc cobalt oxide films grown under an oxygen-rich condition (the $O_2$/Ar partial pressure ratio of 9/1) changes from wurtzite-type $Zn_{1-x}$ $Co_{X}$O to spinel-type $ZnCo_2$$O_4$with the increase of the Co/Zn sputtering ratio,$ D_{co}$ $D_{zn}$ . We noted that the above structural change accompanied by the variation of the majority electrical conduction type from n-type (electrons) to p-type (holes). For a fixed $D_{co}$ $D_{zn}$ / of 2.0 yielding homogeneous spinel-type $_2$O$ZnCo_4$films, the type of the majority carriers also varied, depending on the$ O_2$/Ar partial pressure ratio: p-type for an $O_2$-rich and n-type for an Ar-rich atmosphere. The maximum electron and hole concentrations for the Zn $Co_2$ $O_4$films were found to be 1.37${\times}$10$^{20}$ c $m^{-3}$ and 2.41${\times}$10$^{20}$ c $m^{-3}$ , respectively, with a mobility of about 0.2 $\textrm{cm}^2$/Vs and a high conductivity of about 1.8 Ω/$cm^{-1}$ /.

• The Korean Journal of Physiology and Pharmacology
• /
• v.18 no.2
• /
• pp.129-134
• /
• 2014

It has been suggested that transition metal ions such as iron can produce an oxidative injuries to nigrostriatal dopaminergic neurons, like Parkinson's disease (PD) and subsequent compensative increase of tetrahydrobiopterin ($BH_4$) during the disease progression induces the aggravation of dopaminergic neurodegeneration in striatum. It had been established that the direct administration of $BH_4$ into neuron would induce the neuronal toxicity in vitro. To elucidate a role of $BH_4$ in pathogenesis in the PD in vivo, we assessed the changes of dopamine (DA) and $BH_4$ at striatum in unilateral intranigral iron infused PD rat model. The ipsistriatal DA and $BH_4$ levels were significantly increased at 0.5 to 1 d and were continually depleting during 2 to 7 d after intranigral iron infusion. The turnover rate of $BH_4$ was higher than that of DA in early phase. However, the expression level of GTP-cyclohydrolase I mRNA in striatum was steadily increased after iron administration. These results suggest that the accumulation of intranigral iron leads to generation of oxidative stress which damage to dopaminergic neurons and causes increased release of $BH_4$ in the dopaminergic neuron. The degenerating dopaminergic neurons decrease the synthesis and release of both $BH_4$ and DA in vivo that are relevance to the progression of PD. Based on these data, we propose that the increase of $BH_4$ can deteriorate the disease progression in early phase of PD, and the inhibition of $BH_4$ increase could be a strategy for PD treatment.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1998.02a
• /
• pp.133-133
• /
• 1998

In the thin film alloy formation of the transition metals ion-beam-mixing technique forms a metastable structure which cannot be found in the arc-melted metal alloys. Sppecifically it is well known that the studies about the electronic structure of ion-beam-mixed alloys pprovide the useful information in understanding the metastable structures in the metal alloy. We studied the electronic change in the ion-beam-mixed ppt-Ct alloys by XppS and XANES. These analysis tools pprovide us information about the charge transfer in the valence band of intermetallic bonding. The multi-layered films were depposited on the SiO2 substrate by the sequential electron beam evapporation at a ppressure of less than 5$\times$10-7 Torr. These compprise of 4 ppairs of ppt and Cu layers where thicknesses of each layer were varied in order to change the alloy compposition. Ion-beam-mixing pprocess was carried out with 80 keV Ae+ ions with a dose of $1.5\times$ 1016 Ar+/cm2 at room tempperature. The core and valence level energy shift in these system were investigated by x-ray pphotoelectron sppectroscoppy(XppS) pphotoelectrons were excited by monochromatized Al K ａ(1486.6 eV) The ppass energy of the hemisppherical analyzer was 23.5 eV. Core-level binding energies were calibrated with the Fermi level edge. ppt L3-edge and Cu K-edge XANES sppectra were measured with the flourescence mode detector at the 3C1 beam line of the ppLS (ppohang light source). By using the change of White line(WL) area of the each metal sites and the core level shift we can obtain the information about the electrons pparticippating in the intermetallic bonding of the ion-beam-mixed alloys.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.1
• /
• pp.104-114
• /
• 2023

Three dimensional (3D) porous structures consisting of Cu@CoO core-shell-type nano-dendrites were synthesized and tested as the anode materials in lithium secondary batteries. For this purpose, first, the 3D porous films comprising Cu@Co core-shell-type nano-dendrites with various thicknesses were fabricated through the electrochemical co-deposition of Cu and Co. Then the Co shells were selectively anodized to form Co hydroxides, which was finally dehydrated to get Cu@CoO nanodendrites. The resulting electrodes exhibited very high reversible specific capacity almost 1.4~2.4 times the theoretical capacity of commercial graphite, and excellent capacity retention (~90%@50^th cycle) as compared with those of the existing transition metal oxides. From the analysis of the cumulative irreversible capacity and morphology change during charge/discharge cycling, it proved that the excellent capacity retention was attributed to the unique structural feature of our core-shell structure where only the thin CoO shell participates in the lithium storage. In addition, our electrodes showed a superb rate performance (70.5%@10.8 C-rate), most likely due to the open porous structure of 3D films, large surface area thanks to the dendritic structure, and fast electron transport through Cu core network.

• Journal of Magnetics
• /
• v.8 no.2
• /
• pp.98-102
• /
• 2003

Microstructure and magnetic transport phenomina in rf sputtered AIN/CO type ten- layered discontinuous films of nanoscaled [AIN(3 nm)/Co(t nm)]…$_10$ with t$_Co$=1.0∼2.0 nm have been investigated. The microstructure and tunneling magnetic resistance of the samples are strongly dependent on the thickness of Co layer, Negative tunneling magneto-resistance due to the spin-dependent transport has been observed along the current-in-plane configuration in the samples having the Co layers below 1.6 nm thick. When the thickness of Co layer was less than 1.2 nm, randomly oriented granular Co particles were completely isolated and embedded in amorphous AIN matrix, and the films showed the superparamagnetic behavior with a high MR value of ${\Delta}p/p_0$=1.8%. As t$_Co$ increases, a transition from the regime of co-existence of superparamagnetic and ferromagnetic behaviors to ferromagnetic behavior was observed. funneling barrier called “decay length far tunneling” fur the films haying the thickness of Co layer from 1.4 to 1.6 nm was measured to be ranged from 0.004 to 0.021 ${\AA}$$^{-1}$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.161-161
• /
• 2011

Titanium (IV) dioxide (TiO2) is one of the most attractive d-block transition metal functional oxides. Many applications of TiO2 such as dye-sensitized solar cells and photocatalyst have been widely investigated. To utilize solar energy efficiently, TiO2 should be well-aligned with a high surface area and promote the charge separation as well as electron transport. Herein, the TiO2 nanotubes were successfully fabricated by a template-directed method. The electrospun PEO(Polyethylene oxide, Molecular weight, 400k)fibers were used as a soft template for coating with titanium dioxide using an atomic layer deposition (ALD) technique. The deposition was conducted onto a template at 50$^{\circ}C$ by using titaniumisopropoxide [Ti(OCH(CH3)2)4; TTIP] as precursors of TiO2. While the as-deposited TiO2 layers onto PEO fibers were completely amorphous with atomic layer deposition, the TiO2 layers after calcination at 500$^{\circ}C$ for 1 h were properly converted into polycrystalline nanostructured hallow TiO2 nanotube. The TiO2 nanotube with high surface area can be easily handled and reclaimed for use in future applications related to solar cell fabrications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.60-60
• /
• 2015

Nanosheets of graphene and related 2D materials have attracted much attention due to excellent physical, chemical and mechanical properties. Single-layer graphene (SLG) was first synthesized by Blakely et al in 1974 [1]. Following his achievements, we initiated the growth and characterization of graphene and h-BN on metal substrates using surface segregation and precipitation in 1980s [2,3]. There are three important steps for nanosheet growth; surface segregation of dopants, surface reaction for monolayer phase, and subsequent 3-D growth (surface precipitation). Surface phase transition was clearly demonstrated on C-doped Ni(111) by in situ XPS at elevated temperatures [4]. The growth mode was clarified by inelastic background analysis [5]. The surface segregation approach has been applied to C-doped Pt(111) and Pd(111), and controllable growth of SLG has been demonstrated successfully [6]. Recently we proposed a promising method for producing SLG fully covering an entire substrate using Ni films deposited on graphite substrates [7]. A universal method for layer counting has been proposed [8]. In this paper, we will focus on the effect of competitive surface-site occupation between carbon and other surface-active impurities on the graphene growth. It is known that S is a typical impurity of metals and the most surface-active element. The surface sites shall be occupied by S through surface segregation. In the case of Ni(110), it is confirmed by AES and STM that the available surface sites is nearly occupied by S with a centered $2{\times}2$ arrangement. When Ni(110) is doped with C, surface segregation of C may be interfered by surface active elements like S. In this case, nanoscopic characterization has discovered a preferred directional growth of SLG, exhibiting a square-like shape (Fig. 1). Also the detailed characterization methodologies for graphene and h-BN nanosheets, including AFM, STM, KPFM, AES, HIM and XPS shall be discussed.

• Journal of Electrochemical Science and Technology
• /
• v.12 no.1
• /
• pp.112-125
• /
• 2021

The new emerging "High entropy materials" attract the attention of the scientific society because of their simpler structure and spectacular applications in many fields. A novel nanocrystalline high entropy (Be,Mg,Ca,Sr,Zn,Ni)3O4 oxide has been successfully synthesized through mechanochemical treatment followed by sintering and air quenching. The present research work focuses on the possibility of single-phase formation in the aforementioned high entropy oxide despite the great difference in the atomic sizes of reactant alkaline earth and 3d transition metal oxides. Structural properties of (Be,Mg,Ca,Sr,Zn,Ni)3O4 high entropy oxide were explored by confirmation of its single-phase Fd-3m spinel structure by x-ray diffraction (XRD). Further, nanocrystalline nature and morphology were analyzed by scanning electron microscopy (SEM). Among thermal properties, thermogravimetric analysis (TGA) revealed that the (Be,Mg,Ca,Sr,Zn,Ni)3O4 high entropy oxide is thermally stable up to a temperature of 1200℃. Whereas phase evolution in (Be,Mg,Ca,Sr,Zn,Ni)3O4 high entropy oxide before and after sintering was analyzed through differential scanning calorimetry (DSC). Electrochemical studies of (Be,Mg,Ca,Sr,Zn,Ni)3O4 high entropy oxide consists of a comparison of thermodynamic and kinetic parameters of water and hydrazine hydrate oxidation. Values of activation energy for water oxidation (9.31 kJ mol-1) and hydrazine hydrate oxidation (13.93 kJ mol-1) reveal that (Be,Mg,Ca,Sr,Zn,Ni)3O4 high entropy oxide is catalytically more active towards water oxidation as compared to that of hydrazine hydrate oxidation. Electrochemical impedance spectroscopy is also performed to get insight into the kinetics of both types of reactions.

• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.51-54
• /
• 2007

By substituting Cr in inverse-spinel $Fe_3O_4,\;Cr_xFe_{3-x}O_4$ thin film samples were prepared by sol-gel spin-coating method and their structural electronic, and magnetic properties were analyzed. X-ray diffraction indicates that the lattice constant decrease with increasing Cr composition (x). This result can be explained in terms of occupation of octahedral sites by $Cr^{3+}$ ions with smaller ionic radius than that of $Fe^{3+}$ Vibrating sample magnetometry measurements on the samples at room temperature revealed that saturation magnetization ($M_s$) decrease by Cr substitution, explainable by comparing spin magnetic moment among the related transition-metal ions. A decrease of magnetoresistence effect with x was observed, similar to that of $M_s$. The coercivity of the $Cr_xFe_{3-x}O_4$ films was found to increase with x, attributed to the increase of magnetic anisotropy by the existence of octahedral $Cr^{3+}(d^3)$.