• Applied Chemistry for Engineering
• /
• v.27 no.1
• /
• pp.80-85
• /
• 2016

The carbon dioxide adsorption behavior of silica with a large specific surface area and pore volume functionalized with aminosilane compounds via in-situ polymerization and functionalization method were investigated. The organosilanes include amino functional group capable of adsorbing carbon dioxide. Elemental analyzer, in situ FT-IR and thermogravimetric analyzer were used to characterize the sorbents and to determine their $CO_2$ adsorption behavior. Comparison of different aminosilane loading in the support revealed that polyaminosilane functionalization of 70% of the pore volume in the support was better in terms of the adsorption capacity and amine efficiency than that of 100% of the pore volume of the support. Furthermore, the sorbents showed a higher adsorption capacity at an adsorption temperature of $75^{\circ}C$ than at $30^{\circ}C$ due to the thermal expansion of synthesized polyaminosilanes inside the pore of silica. The N-[3-(trimethoxysilyl)propyl]ethylenediamine (2NS) sorbent with 70% of the pore volume functionalized showed the highest adsorption capacity of 9.2 wt% at $75^{\circ}C$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.219-220
• /
• 2015

주석도금폐액으로부터 이온교환수지를 이용하여 주석을 회수하는 연구를 하였다. 주석 흡착이 가능한 3종류의 이온교환수지를 사용하여 기초 실험한 결과 tertiary기능기를 가진 이온교환수지는 주석을 흡착하지 못하였고, iminodiacetic 기능기를 가진 이온교환수지는 주석의 흡착률은 높으나, 불순물 함량이 높았으며, ethylhexyl-phosphar의 기능기를 가진 이온교환수지는 주석의 흡착률은 낮으나 pH 조절에 따라 불순물의 제어가 가능하였다.

• Proceedings of the KOSOMBE Conference
• /
• v.1992 no.11
• /
• pp.157-160
• /
• 1992

표면에 여러 가지 기능성기를 가지는 microspheres는 immunoassay, drug delivery system, cell separation등 의용공학분야에 응용이 기대되고 있다. 이들 분야의 응용을 위하여 유화제를 사용하지 않으면서, 기존의 회분식, 반회분식, seed 중합법등의 문제점을 극복한 two stage shot growth technique올 개발하여 여러 가지 기능성기가 표면에 도입된 microspheres를 제조하였으며, 응용의 전단계로서 이들 microspheres에 대한 모델 단백질(BSA)의 흡착실험을 pH, 기능 성기의 종류와 양, BSA농도를 변수로 행하여 최대 흡착량을 보이는 조건을 결정하였다.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.811-817
• /
• 2003

Recently, application fields of non-metallic minerals by utilizing their structure properties are broadening. Especially, layered minerals have not only excellent shielding or covering ability but also absorbing and storing characteristics of chemical elements between a layers. We considered about the above mentioned characteristics and added functional substances onto their surfaces for the preparation of new environmentally friendly functional materials. In this study, natural graphite and sericite were mainly used to produce for the new environmentally friendly functional building materials. Graphite surfaces were modified with a surfactant (Alkyl Benzyle Demethyle Ammonium Chloride) for anti-bacillus and penicillium. Surface modification mechanism are that primary adsorption by differential zeta potential between graphite and ABDM and secondary adsorption by interaction between surfactant chains take place. Surfactant layers were fully formed and it was expected up to 99.7% up the efficiency of anti-bacillus and penicillium. Also the prepared functional samples have a effect to improve a various efficiency such as electromagnetic wave shield(up to 95%), deodorization(up to 80%), heat storage(5%) etc.

• Korean Chemical Engineering Research
• /
• v.50 no.5
• /
• pp.885-889
• /
• 2012

In this study, amine and metal oxide additives were investigated to improve $CO_2$ adsorption capacity of activated carbons (ACs). The characteristics of surface modified ACs were studied by X-ray photoelectron spectroscopy (XPS), $N_2$ adsorption, X-ray diffraction (XRD), and BET. Amine surface treatment decreased specific surface area and pore volume of ACs, but increased alkalinity by the incorporated nitrogen functional groups. Adsorption capacities of amine functionalized ACs was larger than original ACs, because basic group which can react with $CO_2$ was grafted on the ACs surface. Presence of copper oxides on ACs also enhances the carbon dioxide adsorption. The copper oxides could increase the adsorption rate of carbon dioxides due to the acid-base interaction (or electron acceptor-donor interaction). It was found that copper oxide loading was a promising method to improve the $CO_2$ adsorption capacity of ACs.

• Journal of Korean Society of Environmental Engineers
• /
• v.37 no.3
• /
• pp.175-181
• /
• 2015

Activated carbon impregnated with polyethyleneimine (PEI) was evaluated as a functionalized adsorbent for $CO_2$ capture. The $CO_2$ adsorption characteristics of the adsorbents was undertaken using GC/TCD, BET surface area and FT-IR. A series of adsorbents were synthesized by impregnating 10, 30, 50 wt% of PEI on activated carbons and were investigated $CO_2$ adsorption capacity at high and low adsorption temperature. The $CO_2$ adsorption capacity at $20^{\circ}C$ and $100^{\circ}C$ was as follow: AC > PEI(10)-AC > PEI(30)-AC > PEI(50)-AC at $20^{\circ}C$ and PEI(10)-AC > PEI(30)-AC > PEI(50)-AC > AC at $100^{\circ}C$. Adsorption capacities of amine functionalized AC was lager than virgin AC at high temperature due to chemisorption by amino-group content. From the results, the PEI(10)-AC showed one of the most promising adsorbents for $CO_2$ capture from flue gas at high temperature.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.342-342
• /
• 2011

방사광을 이용한 흡수스펙트럼으로부터 그래핀 표면 위 TCPP(Tetra(4-carboxyphenyl)porphine) 유기 분자의 흡착구조에 대하여 연구하였다. 순수한 그래핀 표면의 비활성도는 소자응용 분야에 있어 그 영역을 제한할 수 있는 하나의 걸림돌이 되고 있다. 이를 극복하기 위해 유기분자막의 초기 흡착을 이용한 다양한 방법이 시도되어왔다. 그 중 TCPP 분자막을 이용한 그래핀 표면의 기능성 및 그 우수성을 이미 보고한 바 있다. 그러나 그 분자의 흡착구조에 대해 밝혀진 바 없다. 그래핀 표면과 분자간의 흡착 메커니즘 및 분자 상호간의 역학관계는 그 흡착구조의 규명으로부터 얻어질 수 있는데, 본 연구에서는 C 1s K-edge에 대한 NEXAFS 스펙트럼을 이용하여 TCPP 분자가 그래핀과 평행한 방향으로 흡착됨을 알 수 있었다. 이는 또한 분자흡착량의 증가에 따른 AFM 이미지와 일관됨을 알 수 있었다.

• Journal of Energy Engineering
• /
• v.4 no.1
• /
• pp.76-84
• /
• 1995

본 연구에서는 코코넛 껍질로부터 제조한 활성탄을 열 및 산소-암모니아의 혼합가스로 전처리하여 표면의 특성 변화와 이산화황 흡착능에 미치는 영향을 살펴보았다. 전처리한 활성탄으로 이산화황 흡착실험을 수행한 결과, 전처리한 활성탄은 기본 활성탄 시료보다 높은 흡착능력을 보였다. 본 연구의 전처리 실험에서는 산소와 암모니아를 주입하여 활성점을 제공하는 산소와 환원성 분위기를 조성하는 질소관능기를 도입하였다. 전처리 조건은 0∼25%의 암모니아와 473∼1273K의 온도이며 처리조건을 변화시킴으로써 표면 기능의 척도가 되는 세공구조와 원소조성 및 표면 관능기 등에 직접적인 영향을 주었다. 흡착능력은 고정층 반응기에서 전자 비틀림 저울로 이산화황 흡착량을 측정하여 비교하였고, 이 과정 중의 활성탄 표면의 특성변화를 원소분석, 승온탈착법, 산-염기 적정법, 주사현미경법 등의 분석 방법을 통해서 알아보았다. 그 결과, 이산화황의 최대 흡착 능력은 온도조건 973∼1173K에서 나타났다. 또한, 암모니아로 처리하지 않은 활성탄에 비하여 암모니아로 처리한 활성탄은 그 주입농도에 관계없이 이산화황의 흡착제거율을 약 48% 정도 향상시켰다.

• Proceedings of the Korean Environmental Sciences Society Conference
• /
• 2004.05a
• /
• pp.372-374
• /
• 2004

최근들어 비금속광물의 구조적 특성을 이용한 활용분야가 매우 다양해지고 있다. 특히 판상광물은 차폐(은폐)력이 매우 우수하고, 층간특성을 이용한 흡착 및 저장특성이 매우 우수하다. 본 연구에서는 이와 같은 판상광물의 기본의 특성에 또 다른 기능성 물질을 흡착시킴으로써 부가적인 새로운 기능성을 갖는 친환경성 건축소재를 개발하고자 천연산 인상흑연 및 견운모를 기능성 모소재로 사용하고 미립화 및 표면 환경기능화를 위하여 BMK로 흑연입자 표면을 기능화하였다. 제조된 기능성 마감재인 닥터하우스를 모르타르에 도포하여 다양한 기능성을 측정한 결과 78% 이상의 유해가스(포름알데히드) 정화제거효과 및 99.9% 이상의 항균, 항곰팡이 효과를 갖는 것으로 나타났다.

• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.358-365
• /
• 2016

Removing hazardous materials from water resources is very important for efficient utilization of the resources, and adsorptive removal is regarded as a competitive technology when good adsorbents with high capacity/selectivity are available. Metal-organic framework (MOF), composed of both organic and inorganic (metallic) species, have been tried for various adsorptions because of huge surface area/pore volume, well-defined pore structure, and facile functionalization. In this review, we summarized technologies on adsorptive removal of hazardous organics from water mainly using MOFs as adsorbents. Instead of reporting high adsorption capacity or rate, we summarized mechanisms of interaction between adsorbates (organics) and adsorbents (MOFs) and methods to modify or functionalize MOFs for effective adsorptions. We expect for readers of this review to understand needed characteristics of adsorbents for the adsorptive removal, functionalization of MOFs for effective adsorption and so on. Moreover, they might have an idea on storage and delivery of organics via understanding of the mechanism of adsorption and interaction.