• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.3
• /
• pp.1671-1676
• /
• 2015

A unique crystallization behavior of poly(L-lactide)(PLLA)/poly(D-lactide)(PDLA) stereocomplex(SC) was observed when a PLLA/PDLA blend was subjected to the specific melting conditions. Therefore, we tried to blend PLLA and PDLA at overall composition to form PLA stereocomplexes. Moreover, impact modifier and reinforcement materials such as talc and glass fiber added to enhance the mechanical and thermal properties such as impact strength and heat distortion temperature(HDT). As a result, we got one representative result, one composite recipe with HDT $115^{\circ}C$. For more economic technology, we tried to blend PLLA and Polypropylene at overall composition and we got another representative result which could be applied to current PP/talc composites and ABS materials. The core technology of this might be the well dispersion of glass fibers into the matrix resin such as PP, PLLA and impact strength modifier.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1995.10a
• /
• pp.89-92
• /
• 1995

For the development of lilght weight cement concrete with high durability, this study used perlite and paper sludge ash by the light weight material, and polypropylene fiber by the reinforcment, and poly-acrylic ester emulsion by the matrix improvement. According to the increasing mixture ratio of fiber and use of polymer, the light weight polypropylene fiber reinforced polymer cement ratio of fiber and use of polymer, the light weight polypropylene fiber reinforced polymer cement concrete were showed high resistance for frost damage.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.108-111
• /
• 2004

The polypropylene(PP) fiber is poised as a low cost alternative for reinforcement in structural applications in comparison with other high performance fibers, such as the polyvinyl-alcohol(PVA), polyethylene, carbon and aramid fiber. The mechanical properties of the composite are strongly determined by the interfacial behavior of fiber and cementitious matrix. The crack bridging mechanism contribute to composite toughness from activation of the fiber-matrix interface where energy is dissipated through debonding of the interface and fiber pullout. In this study, therefore, the pullout behavior of PP fibers is investigated. Experimental work includes the investigation of the interfacial properties, and the composite property. The quantification of interfacial properties, the frictional bond is achieved through single fiber pullout test. A study on the effect of inclination angle on fiber pullout behavior is also conducted.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.407-415
• /
• 2023

In this study, a carbonation test was conducted on cementitious composites reinforced with recycled waste rope fibers (W series) according to EN 12390-12 standards. The test results were compared to those of commercially available polypropylene fibers (P series). In the carbonation test, both the carbonation depth and area were significantly influenced by the water-to-cement ratio. Notably, the carbonation resistance performance of cementitious composites containing waste rope fibers surpassed that of commercially available PP fibers under equivalent conditions. Throughout the 250-day test period, the W series exhibited higher compressive strength values than the P series, while both series displayed a similar trend of strength increase during the same duration. During the initial stage, the W series exhibited flexural strength levels similar to those of the P series. However, in the later stages, the P series showed a higher mean flexural strength by 1.0 MPa.

• Journal of Adhesion and Interface
• /
• v.9 no.2
• /
• pp.16-23
• /
• 2008

In this study, novel waste wool/polypropylene NFRPs (natural fiber reinforced polymer composites), which are constituted with waste wool discarded as industrial scrap during manufacturing processes of woven fabrics and general purpose thermoplastic polypropylene (PP), were fabricated by means of compressionmolding and their mechanical and thermal properties were characterized. The mechanical properties of PP resin were significantly improved by an introduction of waste wool to PP. In particular, as the loading of waste wool was 50 vol% in the NFRP, the flexural strength of the NFRP was increased about 20%, the flexural modulus about 143%, the tensile strength about 76%, and the tensile modulus about 90% in comparison with each of PP control. In addition, the maximum value of the heat deflection temperature (HDT) obtained with the NFRP was $138^{\circ}C$ at a 50 vol% loading of waste wool. This is $21^{\circ}C$ higher than the HDT of PP control. The result here suggests that waste wool be a potential candidate for a reinforcing material of thermoplastic matrix resins.

• Journal of the Korea Concrete Institute
• /
• v.21 no.2
• /
• pp.179-186
• /
• 2009

The peculiarity pointed out for high strength concrete is the occurrence of spalling during a fire. Recently, there are many efforts such as development of all types of spalling reducing materials and other innovative materials in various fields. Need is now to examine the adequate mixing proportions of these materials. This study intended to derive experimentally and statistically mix proportions that can represent the basic quality requirements as well as the optimal effects on the fire-resistance for 4 types of functional materials that are metakaolin, waste tire chip, polypropylene fiber and steel fiber. Here, the tests were planned through an optimal test method using an orthogonal array table with 4 parameters and 3 levels. The statistical analysis adopted the response surface analysis method. Results verified mutual complementary contribution between the materials when using a combination of the functional materials selected as parameters for the strengthening of the fire-resistance of 80 MPa-class high strength concrete. Besides, the optimal conditions of the fire-resistance strengthening materials derived through response surface analysis were a volumetric replacement of silica fume by 80% of metakaolin, a volumetric replacement of fine aggregates by 3% of tire waste chip, and an addition of 0.2% of the whole volume by polypropylene fiber without mixing of steel fiber. In such cases, the basic characteristics as well as the fire-resistant characteristics of high strength concrete were also satisfied.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.5
• /
• pp.79-85
• /
• 2004

This study was performed to evalute mechanical and drying shrinkage properties of polypropylene fiber reinforced high flow concrete. The compressive strength and drying shrinkage ratio were increased with increasing the binder volume ratio and decreased with increasing the content of polypropylene fiber. The splitting tensile strength was increased with increasing the binder volume ratio and the content of polypropylene fiber. The flexural strength was increased with increasing the binder volume ratio and increased by the polypropylene fiber content 0.4%, but above the polypropylene fiber content 0.6% was decreased. This concrete can be used for high flow concrete.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.4
• /
• pp.57-63
• /
• 2004

This study was performed to evaluate flow properties of polypropylene fiber reinforced high flow concrete. Test results were showed that the slump, slump flow and L-type compacting were decreased with increasing the content of polypropylene fiber. But, the Box-type passing and air content were increased with increasing the content of polypropylene fiber. The slump was $25.5{\sim}27.5cm$, the slump flow was $60{\sim}65cm$, the Box-type passing was $2{\sim}6cm$, the L-type compacting was excellent and air content was $2.7{\sim}3.2cm%$ by the polypropylene fiber content 0.2%, respectively. This concrete can be used for high flow concrete.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.48 no.2
• /
• pp.59-66
• /
• 2006

This study is performed to evaluate freezing and thawing properties of polypropylene fiber reinforced eco-concrete using soil, natural coarse aggregate, soil compound and polypropylene fiber. The mass loss ratio is decreased with increasing the content of natural coarse aggregate and soil compound, but it is increased with increasing the content of polypropylene fiber. The ultrasonic pulse velocity, dynamic modulus of elasticity and durability factor are increased with increasing the content of natural coarse aggregate and soil compound, but it is decreased with increasing the content of polypropylene fiber. The mass loss ratio, ultrasonic pulse velocity, dynamic modulus of elasticity and durability factor are $1.49{\sim}3.32%,\;1,870{\sim}2,465\;m/s,\;77X10^2{\sim}225X10^2\;MPa\;and\;84.6{\sim}92.8$ after freezing and thawing 300 cycles, respectively. These eco-concrete can be used for environment-friendly side walk and farm road.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.04a
• /
• pp.146-152
• /
• 1996

Polypropylene fiber reinforced mortar and concrete as civil material or architectural material have been used in America and British etc, and have been researched. Polypropylene fibers have many advantages in many points ; in economical costs, chemical stability and durability. It has been reported that polypropylene fiber can control restrained tensile stresses and cracks and increase toughness, resistance to impact, corrosion, fatigue and durability. This study has been performed to obtain the properties of polypropylene fiber reinforced concrete such as compressive strength, flexural strength, toughness, slump, drying shrinkage crack and drying shrinkage characteristics. The test variables are fiber contents, fiber length, fiber types, and so on. From the results of this study, we can expect the effects of the admixtures of polypropylene fiber about strength and drying shrinkage properties in concrete and mortar.