• Polymer(Korea)
• /
• v.30 no.2
• /
• pp.162-167
• /
• 2006

Polyamic acid (PAA) was prepared from cyclobutane-1,2,3,4-tetracarboxylic dianhydride (CBDA) and 4,4'-fiaminodiphenyl ether (DDE). In order to impart a photosensitivity to the PAA, diazonaphthoquinone (DNQ) derivative (DI) was added. However, the addition of the DI was not enough to inhibit the dissolution of the PAA for a aqueous alkal solution. Therefore, we had synthesized poly(amic acid ester)s by an adding 1,2-epoxy-3-phenoxypropane to the PAA. That is, an acidity of the PAA could be controlled by an esterification reaction of 1,2-epoxy-3-phenoxypropane with the PAA. Significant difference of a dissolution rate of the poly(amic acid ester) between an o(posed and unexposed area was observed at an acid content of 60% and less. Resolution of the positively patterned film showed about $25{\mu}m$ at the exposure dose of $200mJ/cm^2$.

• Polymer(Korea)
• /
• v.30 no.2
• /
• pp.97-107
• /
• 2006

In spite of excellent thermomechanical performance the majority of aromatic polyimides are so poor in processability due to their high backbone rigidity that their applications are greatly limited. The introduction of long side chains not only enhances their processiblity but also makes useful contribution to discovering new application fields. In this article, a variety of novel aromatic polyimides with flexible side chains were prepared either from new dimines or new dianhydrides to measure the influence of the side chains on structure and properties of the polymers and their new applications as liquid crystal alignment layers, photosensitive polymers, alternating multilayer nano-films and photoluminescent materials are discussed.

• Polymer(Korea)
• /
• v.32 no.1
• /
• pp.38-42
• /
• 2008

Ultrathin films were coated on low density Polyethylene (LDPE) food packaging films by plasma polymerization of methane, acetylene, hexamethyldisiloxane (HMDSO), and HMDSO+oxygen to improve the barrier property of the LDPE films. The film coated in HMDSO +oxygen (flow rate: 0.6+ 9.0 SCCM) plasma at 40 W for 10 min showed the highest improvement in the barrier property against oxygen, reducing the permeability of oxygen as much as 18.6 times. The film coated in acetylene (flow rate 0.75 SCCM) plasma at 10 W for 10 min showed the highest improvement in the barrier property against carbon dioxide and moisture, reducing the permeability of carbon dioxide and moisture as much as 12.0 and 3.0 times, respectively. In addition, cherry tomato, cucumber, and mushroom (Flammulina velutipes) wrapped with the coated films were kept fresh $1.5{\sim}3.0$ times longer than those wrapped with an LDPE film.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.5
• /
• pp.206-209
• /
• 2006

Indium tin oxide (ITO) films were synthesized on polymer (PES, polyethersulfone) at room temperature by pulsed DC magnetron sputtering. By the control of introducing hydrogen to argon atmosphere, the resistivity of ITO films was obtained at $5.27\;{\times}\;10^{-4}\;{\Omega}{\cdot}cm$ without substrate heating in comparison with $2.65\;{\times}\;10{-3}\;{\Omega}{\cdot}cm$ under hydrogen free condition. ITO film synthesized at Ar condition was changed from amorphous to crystalline. These result from the enhancement of electron temperature in $Ar\;+\;H_2$ plasma, which induces the increase of ionization of target materials and argon. The dominant increase of ions such as In II and O II and neutral Sn I was monitored by optical emission spectroscopy (OES). Thermal energy required for the crystalline film formation is compensated by kinetic energy transfer through ion bombardments to substrate.

• Polymer(Korea)
• /
• v.38 no.3
• /
• pp.397-405
• /
• 2014

To manufacture of high-performance semi-structural double-sided adhesive tape, 2-ethylhexyl acrylate (2-EHA) and acrylic acid (AAC) were used, and the syrup was prepared by UV irradiation in this study. The effects of the thickness, various inorganic filler contents, and filler types on the semi-structural properties of acrylic double-sided adhesive tape were investigated. The peel strength increased with increasing thickness and wetting time. In case of the thin thickness (under $250{\mu}m$) with decreasing true density of inorganic filler, the peel strength increased with increasing wetting time. The initial peel strength showed a higher value at a big size of inorganic filler, and the filler's size in adhesive tapes was confirmed by SEM images. The peel strength and dynamic shear strength increased as a proportional relationship with various inorganic fillers and contents, and these inorganic fillers in $0.1{\mu}m$ thickness indicated more effect on the dynamic shear strength of double-sided adhesive tape. From these results the thin acrylic double-sided adhesive tape determined to be use for applications as a high-performance semi-structural.

• Polymer(Korea)
• /
• v.38 no.6
• /
• pp.801-808
• /
• 2014

Ion diffusion and chemical binding to acrylic polymer were investigated in a solid film. The composition of acrylic monomers containing amino group and carboxylic acid was adjusted for rapid ion migration in the film. p-Methylred (PMR) and phenolphthalein derivatives were optically sensitive to the concentration of proton and hydroxyl anion, respectively and verified the ion migration through the film layers. A rapid proton migration was observed in the film of a high amino content. On the other hand, $OH^-$ migration occurred rapidly in a high content of carboxylic acid group. The proton migration occurred through the internal layer as well as surface layer of a film and was reversible during 50 repetition examination. Copper(II) ion migration was examined with a Rhodamine-containing polymer film. The light absorption and emission spectra of a Rhodamine-Cu complex showed the key contribution of carboxylic acid group to the Cu(II) migration in a film.

• Korean Journal of Materials Research
• /
• v.25 no.1
• /
• pp.54-59
• /
• 2015

Glancing angle deposition (GLAD) is a powerful technique to control the morphology and microstructure of thin film prepared by physical vapor deposition. Chromium (Cr) thin films were deposited on a polymer substrate by a sputtering technique using GLAD. The change in thickness and Vickers microhardness for the samples was observed with a change in the glancing angle. The adhesion properties of the critical load (Lc) by a scratch tester for the samples were also measured with varying the glancing angle. The critical load, thickness and Vickers microhardness for the samples decreased with an increase in the glancing angle. However, the thickness of the Cr thin film prepared at a $90^{\circ}$ glancing angle showed a relatively large value of 50 % compared to that of the sample prepared at $0^{\circ}$. The results of X-ray diffraction and scanning electron microscopy demonstrated that the effect of GLAD on the microstructure of samples prepared by sputter technique was not as remarkable as the samples prepared by evaporation technique. The relatively small change in thickness and microstructure of the Cr thin film is due to the superior step-coverage properties of the sputter technique.

• Polymer(Korea)
• /
• v.28 no.5
• /
• pp.433-443
• /
• 2004

The membranes of the blends of chitosan and polycaprolactarn (PA6) were prepared in formic acid. FT-IR data revealed that hydrogen bonding between amide and hydroxyl groups of chitosan and PA6, respectively, was formed. Thermogravimetric analysis demonstrated that the blend samples contain water. DMA results showed that the dissipation of water in the samples significantly reduced the storage modulus (E'). The mechanical loss tangent (tan $\delta$) data of the blend samples showed the $\beta$d loss peak around $0^{\circ}C$. The blend samples were completely dried in a vacuum and then exposed to high moisture to absorb water which would cause, so called, w-bridges between the molecules. The E' data of these regained samples increased abnormally and additional loss peak appeared on the shoulder of the peak around $50^{\circ}C$. Under dry condition, the samples with a blend ratio of 40/60 for chitosan/PA6 displayed a better miscibility between two components.

• Applied Chemistry for Engineering
• /
• v.32 no.4
• /
• pp.403-408
• /
• 2021

In this study, a thin and flexible planar supercapacitor (PSC) was fabricated by coating polyaniline (PANI) on a screen-printed carbon electrode. Carbon ink was coated onto the flexible polyethylene terephthalate using a screen-printing method; subsequently, a thin film of PANI was coated onto the carbon surface using a dilute polymerization method. A thin flexible PANI electrode in an interdigitated structure was assembled with a polymer gel electrolyte that resulted in planar-shaped supercapacitor (PSC) devices. The as-obtained PANI/PSC was very thin and flexible, exhibiting a high areal capacitance of 409 µF/cm was obtained at a rate of 10 mV/s. This capacitance retains 46% of its original value at 500 mV/s. The flexible PANI/PSC exhibited an excellent capacitance retention of 82% even under bent states of 180° and 100 repetitive bent cycles.

• Membrane Journal
• /
• v.32 no.6
• /
• pp.390-400
• /
• 2022

Nanofiltration (NF) membranes are more popular than reverse osmosis (RO) membranes as they can be operated at much lower pressures for applications in treatment of wastewater from industries like food processing and pharmaceutical as well as municipal sewage water. The separation mechanism in case of NF membranes is based on solution diffusion as well as sieving, for which the crosslinking density of the thin film of the composite membrane is less then RO membrane. Unlike ceramic membranes, membrane fouling is one of the chronic problems that occur during the nanofiltration process in polymeric membranes. Membrane cleaning is done to get rid of reversible as well as irreversible fouling by treatment with sodium hypochlorite. Compared to polymeric membranes, ceramic membranes show higher stability against these agents. In this review different types of ceramic membrane applied wastewater treatment by NF process are discussed.