• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.4
• /
• pp.61-64
• /
• 2003

The fractography was used to observe the stress profile on a single ion-exchanged glass. In the processing, the temperature was varied during the ion exchange, and then the stress profile on the single ion-exchanged glass was shifted from glass surface to slightly below the glass surface. The hackle mark and mirror surface were varied according to process conditions, and the glass strength was increased with increasing the number of hackle markers. In case of breaking the stress profile by using indenter, the breaking property was similar to the annealed glass.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.22 no.6
• /
• pp.565-572
• /
• 2009

This work intends to establish the reliability and fracture toughness $K_{IC}$ criterion of welded joints by EGW for high strength EH36-TMCP ultra thick plate. For this, firstly thermo elasto-plastic analysis has been carried out on two pass X-groove butt joint model to clarify the thermal and mechanical behaviour(residual stress, plastic strain, magnitude of stress and their distribution and production mechanism). Moreover, to establish fracture criterion, analysis of fracture toughness $K_{IC}$ has been performed under the notch machined and residual stress with the load condition on EGW welded joints. A quantitative fracture criterion for EGW welded joints is suggested by using $K_{IC}$.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.15 no.6
• /
• pp.547-557
• /
• 2013

The mode II fracture toughness and strength due to shear stress are important parameters in the stability of caprock and injection zone with application to geological sequestration of carbon dioxide. In this research, a short beam compression test has been used to determine the shear strength and the mode II fracture toughness for Coconino sandstone. The average value of the shear strength and mode II fracture toughness are estimated to be 23.53 MPa and 1.58 MPa${\surd}$m respectively. The stress intensity factor is suggested by finite element analysis using the displacement extrapolation method. The effect of biaxial stress and water saturation on the fracture toughness has also been investigated. The fracture toughness increases with confining stresses, but decreases by 11.4% in fully saturated condition.

• Tunnel and Underground Space
• /
• v.22 no.1
• /
• pp.12-21
• /
• 2012

Although the Mohr-Coulomb and Hoek-Brown failure criteria have been adopted widely in rock mechanics, they neglect the ${\sigma}_2$ effect. The result of true triaxial tests on rock samples, however, reveals that the ${\sigma}_2$ effect on strength of rocks is considerable, so that rock failure criteria taking into account the influence of ${\sigma}_2$ are necessary for the precise stability evaluation of rock structures. In this study, a new nonlinear 3-D failure criterion has been suggested by combining the Hoek-Brown criterion with the smooth octahedral shape function taken from Jiang & Pietruszczak (1988). The performance of the new criterion was assessed by comparing the strength predictions from both the suggested criterion and the corresponding linear 3-D criterion. The resulting fit of the new criterion to the true triaxial test data for six rock types taken from the literature shows that the criterion fits the experimental data very well. Furthermore, for the data sets having data taken in the low ${\sigma}_3$ range, the nonlinear failure criterion works better than the linear criterion.

• Journal of the Korean Geotechnical Society
• /
• v.33 no.1
• /
• pp.79-91
• /
• 2017

An experimental study has been conducted by using the Cyclic Direct Simple Shear apparatus to evaluate the influence of average and cyclic shear stresses on the undrained shear failure behavior of marine silty sand considering various relative densities. The obtained results show that despite using different relative densities, similar trends were gained in the cyclic shear deformation. Moreover, the cyclic shear deformation is affected mainly by the average and cyclic shear stresses. The number of cyclic loads for failure is significantly affected by the cyclic shear stress ratio and relative density, and is less affected by the average shear stress ratio. The proposed three-dimensional stress-dependent failure contour can be used effectively to assess the soil shear strength considering various relative densities in the design of foundation used for offshore structures.

• Tunnel and Underground Space
• /
• v.21 no.2
• /
• pp.93-102
• /
• 2011

In spite of being unable to take into the effect of intermediate principal stress, Mohr-Coulomb and Hoek-Brown criteria are very popular as rock failure criteria. The recent researches reveal that the influence of intermediate principal stress on the failure strength of rock is substantial, so that 3-D failure criteria in which the intermediate principal stress could be considered is necessary for the safe design of the important rock structures. In this study, the likely application of the 3-D failure criterion proposed by Jiang & Pietruszczak (1988) to the prediction of the true triaxial strength of rock materials is discussed. The failure condition is linear in the meridian plane of principal stress space and it is represented by the smooth surface contacting the corners of the Mohr-Coulomb surface. The performance of the Jiang & Pietruszczak's criterion is demonstrated by simulating the actual true triaxial tests on the rock samples of three different rock types.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.17 no.4
• /
• pp.423-431
• /
• 2004

For the fracture mechanics analysis of cracks in welds of dissimilar steels, residual stress analysis and fracture analysis must be performed simultaneously. The standard definition of the J -integral leads to a path dependent value in the presence of a residual stress field. And unlike cracks in homogeneous materials, a bimaterial interface crack always induces both opening and shearing modes of stress in the vicinity of the crack tip. Therefore, it is necessary to develope a path independent J-integral definition for a crack in a residual stress field generated by welding of dissimilar steels. This paper addresses the modification of the Rice-J-integral to produce a path independent J -integral when residual stresses due to welding of dissimilar steels and external forces are present. The residual stress problem is treated as an initial strain problem and the J-integral proposed for this class of problems is used. And a program which can evaluate the J -integral for a crack in a weld of dissimialr steels is developed using proposed J integral definition.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.87-100
• /
• 1989

해양구조물의 원통형 조인트에 대한 파괴역학적 피로수명 산출방법이 개발되었다. 개발된 방법을 이용해서 2평면 K형 조인트에 대한 피로수명을 구체적인 파괴역학적 방법으로 산출 하였다. 이 분석을 위해 용접부위 표면균열의 응력확대 계수를 3차원 유한요소법에 의해 계산하였다. 계산된 결과에 의하면 용접부위 표면균열 첨단은 단순한 Mode I형태를 보이지 않고 Mode I, II, III이 복합된 형태임이 입증되었다. 계산된 응력확대 계수를 사용해서 16개의 용접부위균열 성장형태를 일반적인 피로균열 성장법칙을 적용해서 계산하였고, 균열성장의 안정분석을 통해 각 균열의 최종 파괴상태를 파괴해석도면(failure assessment diagram)법을 이용해서 계산하였다.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.6
• /
• pp.165-174
• /
• 1997

고강도 및 보통강도 콘크리트의 압축파괴 거동에 영향을 미치는 요소들 (재료의 강도, 시편의 세장비, 전단구속, 실험장치의 강성, 피드백 신호)에 관한 연구가 수행되었다. 피드백 신호로 자동 조절되는 유압 실험기계항에서 원주변형 피드백 신호를 사용하여 연화곡선을 구했다. 재하장치로부터의 단부 전단 구속을 줄이면 제한된 영역 안에서 재하방향 균형이 형성되고, 또한 연화곡선의 경사가 급해지고 파괴에너지도 작아진다. 이때 길이가 큰 시편에서 파괴에너지가 커지는 것은 안장과는 달리 단순균열이 형성되는 것이 아니고 , 파괴가 용적을 가진다는 것을 의미한다. 압축응력하의 국부 파괴는 재료특성이 아니므로, 단부 전단구속이 없더라도 재료적 특성으로서의 응력-변형도 곡선은 정하기 어렵다.

• Journal of the KSME
• /
• v.16 no.4
• /
• pp.41-48
• /
• 1976

재료의 피로문제에 대해서는 꽤 오래 전부터 많은 연구가 이루어져왔고, 피로의 현상파악에서부 터 피로이론의 구명, 나아가서는 실제문제로서의 피로설계, 피로수명예측 등에 기여한 업적은 아 주 크다 하겠다. 그러나 종래의 피로문제연구의 방향이, S-N 곡선에서 얻어지는 피로한계강도 (더 정확한 표현으론 피로파괴한계강동)에 바탕을 두고, 정력확적인 설계관례인 안전계수의 도입 을 빌려, 피로강도를 실용화할려는 선에서 이루어져 왔다고 보겠다. 재료의 피로한계강도란, 그 정의로 미루어, 다분히 정적으로는 극한강도 또는 피로강도의 개념에 견주어 질 수 있는 공칭응 력으로써 탄성학적으로 해석될 수도 없고, 다만 탄역성이론의 개념을 바탕으로 근사해석례만이 허용되고 있을 뿐이다. 재료에는 소위 평활재이건 절결재이건 간에 또 검출여부에 관계없이, 내외 부에 대소각종의 결함이나 역학적 불연속부가 잠재해있음은 이미 공지의 사실이며, 이들 결합, 불 연속부등이 외하중하에서 응분의 응력집중원이 되어 재료를 전반적인 파괴로 몰고 갈 수 있다 함 도, 또한 이러한 역학적거동이 피로파괴에 까지 확장해석될 수 있을 것이란 것도 이미 잘 알려져 있는 터이라 하겠다. 재료내외부의 제결합을 응력집중이 극대인 crack로 대체해서 외하중하에서 의 응력장거동을 해석한 선형탄성파괴역학(LEFM)은, 바로 이러한 실제재료의 강도설계에 보다 큰 정확성을 부여한 방법론적 학문이라 하겠고, 나아가서는 재료의 파괴기구를 파헤치는데 진일 보적인 역학적인 수법이라 하겠다. 취성파괴, 연성파괴에 바탕을 둔 파괴역학(LEFM)을 피로파괴 에 적용시키는 데는 상당한 문제점들을 수반할 것임은 충분히 인지되나, 제한된 경계조건하에서 의 적용 예는 종래의 어떤 방법에 의한 것 보다도 피로강도설계, 안전사용 피로수명예측 등에 획기적인 진전을 보여주고 있다. 파괴역학은 crack 재의 강도학이고, 더 구체적으로 음력학대계수 (stress intensity factor) K 또는 이와 연연되는 parameter 인 strain energy release rate(G), crack-tip plactic zone size r$_{p}$,.rho., crack-tip opening displacement .phi., strain intensity 등을 쓰는 재료강도학이기 때문에, 이 수법을 피로파괴에 적용시킴은, 종래의 공칭응력으로 피로 문제를 다루던 방법과는 판이하다 하겠다. 본고에선 파괴역학의 관점에서 피로구열의 안정성장을 논하고, 과거 10여년간의 피로 crack문제에 대한 연구방법, 실험방법 등을 소개하는 방향으로 고 를 진행시켜 나가겠다.