• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.1-5
• /
• 2008

The effect of $BaCeO_3$ doping on the critical current density of YBCO film by TFA-MOD method was studied. $BaCeO_3$ doping was made by two method; one is direct addition of $BaCeO_3$ nano-sized powder prepared by citrate process followed by grinding with planetary ball mill for 10 hours. Another is addition of Ba-Ce precursor solution prepared with Ba-acetate and Ce acetate dissolved in TFA to the YBCO-TFA precursor solution. The film was made by standard dip coating and heat treatment process with conversion temperature of $790^{\circ}C$ in 1000 ppm oxygen containing moisturized Ar gas atmosphere. The direct addition of $BaCeO_3$ powder resulted in YBCO film with good epitaxial growth and no evidence of second phase formation. The addition through precursor solution resulted in the increase of critical current density upto 30 at% doping and uniform dispersion of $BaCeO_3$ fine inclusion was confirmed by SEM-EDX.

• Progress in Superconductivity
• /
• v.13 no.2
• /
• pp.90-96
• /
• 2011

We investigated the properties of artificial pinning centers of YBCO multilayer films in which $Y_2O_3$ and ZnO nanoparticles are uniformly introduced by using the pulsed laser deposition (PLD) technique. $Y_2O_3$ and ZnO nanoparticles were deposited on top of YBCO buffer layer and the density of nanoparticles was controlled by varying the number of nanoparticle layers. YBCO superconducting layers with total thickness of 250 nm were deposited on top of $Y_2O_3$ and ZnO nanoparticles. Based on analyses of the surface morphology, the transition temperature $T_c$, and the critical current density $J_c$, we discussed the difference between the two kinds of nanoparticles as flux pinning centers.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.75-82
• /
• 1999

TE$_{01\;{\delta}}$ mode Cavity Resonators with a low loss dielectric rod and YBa$_2Cu_3O_{7-{\delta}}$ (YBCO) endplates were prepared and their microwave properties were studied at temperatures above 30 K. Both sapphire and rutile were used as the dielectrics. The TE$_{01\;{\delta}}$ mode Q$_0$ of the resonator, designed to work as a tunable resonator with variations in the gap distance (s) between the dielectric rod and the top YBCO, was more than 1000000 at s = 0 mm and at 30 K and .the resonant frequency of 19.56GHz when a sapphire rod was used for the dielectric. The TE$_2Cu_3O_{7-{\delta}}$ mode resonant frequency (f$_0$) appeared to decrease as the temperature is raised. Meanwhile, the temperature dependence of the TE$_2Cu_3O_{7-{\delta}}$ mode f$_0$ of the rutile-loaded resonator appeared different with f$_0$ increasing according to the temperature and Q$_0$ more than 300000 at 30 K and f$_0$ = 8.56 CHz. Comparisons were made between the microwave properties of the sapphire-loaded and the rutile-loaded resonators. Also, applications of the TE$_2Cu_3O_{7-{\delta}}$ mode cavity resonator for a tunable resonator with a very high Q$_0$ as · well as a characterization tool for surface resistance measurements of HTS films are described.

• Progress in Superconductivity
• /
• v.11 no.1
• /
• pp.62-66
• /
• 2009

Introduction of proper impurity into $YBa_2Cu_3O_{7-x}$ (YBCO) thin films is an effective way to enhance its flux-pinning properties. We investigate effect of $Y_2O_3$ nanoparticles on the critical current density $J_c$ of the YBCO thin films. The $Y_2O_3$ nanoparticles were created perpendicular to the film surface (parallel with the c-axis) either between YBCO and substrate or on top of YBCO, YBCO/$Y_2O_3$/LAO or $Y_2O_3$/YBCO/STO, by pulsed laser deposition. The deposition temperature of the YBCO films were varied ($780^{\circ}C$ and $800^{\circ}C$) to modify surface morphology of the YBCO films. Surface morphology characterization revealed that the lower deposition temperature of $780^{\circ}C$ created nano-sized holes on the YBCO film surface which may behave as intrinsic pinning centers, while the higher deposition temperature produced much denser and smoother surface. $J_c$ values of the YBCO films with $Y_2O_3$ particles were either remained nearly the same or decreased for the samples in which YBCO is grown at $780^{\circ}C$. On the other hand, $J_c$ values were enhanced for the samples in which YBCO is grown at higher temperature of $800^{\circ}C$. The difference in the effect of $Y_2O_3$ can be explained by the fact that the higher deposition temperature of $800^{\circ}C$ reduces intrinsic pinning centers and $J_c$ is enhanced by introduction of artificial pinning centers in the form of $Y_2O_3$ nanoparticles.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.3
• /
• pp.12-15
• /
• 2004

There are two major approaches to obtain texture template for HTS coated conductor (CC) ---IBAD and RABiTS. CC's with IBAD template showed both longer and higher Ic results so far. IBAD for CC began with YSZ, the processing of which is very slow compared to other processings needed for the fabrication of CC. Because of this very slow processing speed, IBAD with other materials such as Gd$_2$Zr$_2$O$_{7}$(GZO) and MgO have been developed. The processings of IBAD-GZO and IBAD-MgO are known to be up to 3times and 100 times. respectively, as fast as the processing of IBAD-YSZ. IBAD-MgO is very attractive in that the processing is very fast. IBAD-MgO also needs additional buffer layer(s). Many materials are being investigated to be used as a buffer layer on top of the MgO. BaZrO$_3$ (BZO) is a good candidate as the buffer layer on top of the IBAD-MgO because it is chemically stable and does not react with YBCO at high temperatures. It also has good lattice match with MgO. The BZO film has been deposited on single crystal MgO, and YBCO film was deposited on BZO/MgO to investigate the possibility of using BZO as both the buffer and capping layer of the CC.C.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.3
• /
• pp.21-26
• /
• 2004

Deposition condition of YBa$_2$Cu$_3$$O_{7-x}$ (YBCO) films on moving IBAD templates (CeO$_2$/IBAD-YSZ/SS) was studied in a hot-wall type metal organic chemical vapor deposition (MOCVD) process using single liquid source. The reel velocity was 40 cm/hr and the source mole ratios of Y(tmhd)$_3$:Ba(tmhd)$_2$:Cu(tmhd)$_2$ were 1:2.3:3.1 and 1:2.1:2,9, Two different types of IBAD templates with thin CeO$_2$ and thick CeO$_2$ layers were used, The YBCO films were successfully deposited at the deposition temperatures of 780~89$0^{\circ}C$ ; the a-axis growth was observed together with the c-axis growth up to 83$0^{\circ}C$. while the c-axis growth became dominant above 83$0^{\circ}C$. The top surface of the c-axis film was fairly dense and included a small amount of the a-axis growth, although the peaks of the a-axis grains were not observed in XRD pattern, The YBCO film deposited on IBAD template with thin CeO$_2$ layer showed low critical current of 2.5 A/cm-width. while the YBCO film deposited on IBAD template with thick CeO$_2$ layer showed higher critical current of 50 A/cm-width. This result indicates that thick CeO$_2$ layer is thermally more stable than thin CeO$_2$ layer at the high deposition temperature of the MOCVD process.s.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.119-125
• /
• 2007

We investigated recovery in $Au/YBa_2Cu_3O_7$ (YBCO) thin film meander lines on sapphire substrates. The meander lines were fabricated by patterning YBCO films coated with gold layers. The lines were subjected to simulated AC fault current and then small current was applied for recovery measurements. The samples were immersed in liquid nitrogen during the experiment. After the fault, the resistance decreased linearly, first slowly and then fast to zero. The initial slow decrease was due to the decrease of the meander line temperature, whereas the fast decrease was originated from the transition from the normal state to the superconducting state. The recovery speed depended on the size of samples, and was faster in the smaller samples during the whole period of recovery. The experimental results were analyzed quantitatively with the concept of heat transfer within the sample and to the surrounding liquid nitrogen. A heat balance equation was solved for the initial phase of recovery, and an expression for the time dependence of resistance was obtained. The result agreed with data well.

• Progress in Superconductivity
• /
• v.5 no.2
• /
• pp.118-123
• /
• 2004

We investigated quench distribution in AU/YBCO thin film meander lines with a heater. Quench distribution during faults is important for superconducting fault current limter applications, because uniform quench allows application of higher voltages across the meander lines. AU/YBCO thin films grown on sapphire substrates were patterned into meander lines by photolithography. Gold films grown on the rear sides of the substrates were also patterned into meander lines, and used as heaters. Meander lines on the front and the rear sides were connected in parallel. The meander lines were subjected to simulated AC fault currents for quench measurements during faults. They were immersed in liquid nitrogen during the experiment for effective cooling. Resistance of the AU/YBCO meander lines initially increased more rapidly with the rear heater than without, and consequently the fault current was limited more. The resistance subsequently became similar, The resistance distribution was more uniform with the heater, especially during the initial quench. Quench was completed more uniformly and significantly earlier. This resulted in uniform distribution of dissipated power. These results could be explained with the concept of quench propagation, which was accelerated by heat transfer across the substrate from the rear heater.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1288-1289
• /
• 2011

세계가 점차적으로 "전화(電化)"됨에 따라 전기 에너지의 효과적인 분배와 사용이 급격히 중요하게 되었다. 일반 도체를 통한 전류의 흐름은 도체의 저항에 의해 줄열을 발생시켜 전기 에너지의 손실을 일으키고 결국은 에너지와 경제적 자원의 낭비를 초래하게 된다. 초전도체의 저항은 직류 전류에서는 0, 교류 전류에서는 거의 0이기 때문에 초전도체를 이용하면 전력 소자 및 기기의 부피와 무게를 현저히 줄일 수 있는 반면에 모든 전기 시스템의 효율을 향상시킬 수 있고, 에너지 사용의 절감에 따라 환경 문제에 도움을 줄 수 있다. 사고 전류 제한기의 설계에 있어서, 권선형태에 따른 솔레노이드 마그네트와 팬케이크 마그네트를 설계, 제작하여 자장 특성 및 한류 특성을 비교 하였다. 2세대 고온 초전도 선재로 불리는 YBCO 박막형 초전도 선재를 이용하여 동작 전류 증대를 위한 다병렬 솔레노이드 마그네트와 다병렬 팬케이크 마그네트를 제작하였다. 이를 이용하여 440 V/ 630 A급 초전도 사고 전류 제한기와 2 kA 급 대전류 통전 사고 전류 제한 모듈을 설계, 제작하여 단락 특성 시험을 수행하였다. 한편, 자장 응용 기기에 적용 가능한 더블 팬케이크 마그네트를 제 2 세대 초전도선재를 이용하여 설계, 시작하였다. 2세대 선재는 1세대 선재에 비하여 20 T 이상의 외부 자장에 대한 특성이 우수하여 고자장 마그네트 시스템에 더욱 적합하다. 이에 초전도 마그네트 보호를 위한 상전도 영역 전파 실험을 수행하여 CC 선재의 안정도를 측정하였다. 또한 영구전류모드 운전과 플럭스 펌프를 통한 전류 충전에 대한 연구도 병행하였다.

• Progress in Superconductivity
• /
• v.6 no.2
• /
• pp.118-123
• /
• 2005

A low cost YBCO oxide powder was employed as a starting precursor for MOD process. YBCO oxide is advantageous over metal acetates or TFA salts which are popular starting precursors for conventional MOD-TFA process because that YBCO oxide precursor is cheap and easy to control molar ratio. YBCO thin films were prepared by this oxide-precursor-based MOD process and annealing condition was optimized. The YBCO thin film annealed at below $780^{\circ}C$ shows no transport $I_c$ and poor microstructure. Raman spectroscopic study of YBCO thin film indicates that YBCO thin film prepared at below $780^{\circ}C$ contains a number of imperfections such as non-superconducting $BaCuO_2$ phase, cation disorder, etc. However, the YBCO thin film treated at above $800^{\circ}C$ shows improvement in microstructure and current transport properties. This research was supported by a grant from Center for Applied Superconductivity Technology of the 21st Century Frontier R&D Program funded by the Ministry of Science and Technology, Republic of Korea.