• International Journal of Highway Engineering
• /
• 제13권1호
• /
• pp.139-148
• /
• 2011

Asphalt concrete overlay method is used by general maintenance and rehabilitation of construction for aged concrete pavement in Korea. However, in case of the AC overlay method to extend service life of the existing concrete pavements, various distresses of reflection crack, pothole and rutting are the typical problems of the asphalt overlay on existing concrete pavement since it has different physical characteristics between asphalt overlay and existing concrete pavement. To achieve this, application of concrete overlay method is required instead of AC overlay method. Concrete overlay method has advantages that can reduce maintenance cycle and costs since it has excellent bearing value for heavy vehicles and no rutting. However, technical problems of detour road construction, traffic control and other disadvantages happened by long curing time. Thus, in this study and experimental research were launched to evaluate the workability, durability and resistance against environmental loading of Very Rapid Hardening Acrylic Polymer Modified Concrete(VRH-APMC) for application of bonded concrete overlay method. Test results showed that the compressive and bond strength were exceed 21MPa and 1.4MPa of target strength after four hours for rapid traffic opening properties. And tests of resistance against environmental loading results showed that VRH-APMC secured excellent durability. Thus, it was known that VRH-APMC was suitable material for large scale bonded concrete overlay method, and it was possible to use maintenance and rehabilitation method which needs enough workability and rapid traffic opening.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 한국건축시공학회 2018년도 춘계 학술논문 발표대회
• /
• pp.236-237
• /
• 2018

The aim of the research is evaluating a fundamental properties of mortar with atomized molten slag to develop a hardener for dry soil paving concrete. According to the analyzing results, comparing OPC, more favorable strength characteristics were obtained, while it showed rapid setting when the mixture contained more than 10 %. Therefore, when the atomized molten slag is used as a hardener, appropriate retarding process is needed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• 제22권6호
• /
• pp.176-181
• /
• 2018

Concrete structures are degraded physically and chemically due to various reasons after construction. Because the deterioration of concrete structure reduces the service life, reasonable repair and maintenance techniques are needed. Recently, in order to efficiently repair concrete structures, many researches on hybrid repair materials having improved adhesion performance have been carried out actively. In this study, we developed a hybrid repair material containing rapid hardening cement, PVA powder, nylon fiber, and latex to improve adhesion and water-tightness of existing concrete. The compressive strength, drying shrinkage and the adhesion strength test were carried out to evaluate the performance of the repair material. In addition, the flexure bond performance was evaluated before and after repair. From the results, the bending strength was 110% ~ 150% in all specimens except for the specimen containing only the rapid hardening cement, and all the specimens behaved with the existing concrete in the crack pattern generated by the bending strength.

• International Journal of Highway Engineering
• /
• 제13권1호
• /
• pp.169-175
• /
• 2011

Strength is one of the very important factors to evaluate the physical properties of concrete. Aggregate forms the most parts in concrete. Cement as a binder in concrete is also closely related to strength. This experiment was tested to understand the effect of the characteristics of aggregate and cement on the relationship between concrete compressive strength and Shear Wave velocity. It was experimented by the different types of cement and maximum coarse aggregate sizes. Type I cement and rapid setting cement was used. Aggregates from three different regions were used. Aggregate of 19mm and 13mm maximum coarse aggregate sizes was used for grading. The relationship between compressive strength and Shear Wave velocity was tested under the condition of same mixture. LA wear test was used to quantify the characteristics of aggregate. As a result, the relationship between concrete compressive strength and Shear Wave velocity was affected by the types of cement, but regular relationship was appeared regardless of types of aggregate, grading and abrasion ratio.

• Journal of the Korean Recycled Construction Resources Institute
• /
• 제6권3호
• /
• pp.102-109
• /
• 2011

In this study, in order to develop ultra rapid hardening mortar(URHM) for tunnel repairs using bottom ash of low recycle ratio and Admixture as Eco concept, watertightness and durability properties of URHM on temperature condition of construction field were performed. Test result, seepage quantity and water absorption coefficient regarding watertightness of URHM were as in the following : series II > series I. Seepage quantity for the standard condition were smaller than low temperatures. all specimens were satisfied below 20g as standards of seepage quantity on KS F 4042. Because of the decrease of unit cement content by to replacement of blast furnace slag, the neutrlization resistance for durability properties was reduced. The result of alkali resistance and acide resistance, compressive strengths for specimens soaked in calcium hydroxide solution of seriesI were lower than compressive strengths for specimens not soaked. On the other hand, the case of series II show that the deterioration of compressive strengths for specimens was not almost showed. Compressive strengths of specimens soaked were similar with specimens not soaked except series II-C in $5^{\circ}C$. Therefore, specimens using both blast furnace slag and bottom ash were good in alkali resistance and acide resistance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• 제16권6호
• /
• pp.163-170
• /
• 2012

With the advantage of a rapid exothermic reaction property, jet set concrete may be used as a cold weather concrete because it can reach the required strength before being damaged by cold weathers. And it can be hardened more quickly if the field temperature is properly compensated by heating. Because ordinary concrete cannot be hardened well under sub-zero temperatures, anti-freeze agents are typically added to prevent the frost damage and to ensure the proper hardening of concrete. While the addition of a large amount of anti-freeze agent is effective to prevent concrete from freezing and accelerates cement hydration resulting in shortening the setting time and enhancing the initial strength, it induces problems in long-term strength growth. Also, it is not economically feasible because most anti-freeze agents are mainly composed of chlorides. Recent studies reported that magnesia-phosphate composites can be hardened very quickly and hydrated even in low temperatures, which can be used as an alternative of cold weather concrete for cold weathers and very cold places. As a preliminary study, to obtain the material properties, mortar specimens with different mixture proportions of magnesia-phosphate composites were manufactured and series of experiments were conducted varying the curing temperature. From the experimental results, an appropriate mixture design for cold weathers and very cold places is suggested.

• Proceedings of the Korea Concrete Institute Conference
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.153-158
• /
• 2001

The effects of polymer-cement ratio and shrinkage-reducing agent content on the durability characteristics of ultrarapid-hardening polymer-modified mortars using redispersible polymer powder are examined. As a result, the flexural and tensile strengths of the ultrarapid-hardening polymer-modified mortars using redispersible polymer powder tend to increase with increasing polymer-cement ratio, and tend to decrease with increasing shrinkage-reducing agent content. However, the compressive strength of the ultrarapid-hardening polymer-modified mortars using redispersible polymer powder decrease with increasing polymer-cement ratio and shrinkage-reducing agent content. And, water absorption and mass change of chemicals resistance of ultrarapid-hardening polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio.

• Proceedings of the Korea Concrete Institute Conference
• /
• 한국콘크리트학회 2002년도 봄 학술발표회 논문집
• /
• pp.93-98
• /
• 2002

The effects of polymer-cement ratio, antifoamer content and shrinkage-reducing agent content on the air content, setting time and drying shrinkage of polymer-modified mortars using redispersible polymer powder are examined. As a result the air content of the polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio and antifoamer agent content. Regardless of the antifoamer content, the setting time of the polymer-modified mortars using redispersible polymer powder tend to delayed with increasing polymer-cement ratio. Irrespective of the antifoamer content, the drying shrinkage of the polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio and shrinkage-reducing agent content.

• Proceedings of the Korea Concrete Institute Conference
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.413-416
• /
• 2005

The super early hardening cement is widely used for reducing construction period. But there are some problems with handling the cement because the loss of workability is so big to control. In this study, the fluidity properties of super early hardening cement paste was evaluated at early age of hydration by using gel-time determination method. 4 types of set controlling agent were selected and combinations of them were used for gel-time test. As a result, the gel-time of super early hardening cement paste was extended up to 20 minutes by using the combinations of several types set controlling agent.

• Journal of the Korea institute for structural maintenance and inspection
• /
• 제11권5호
• /
• pp.71-80
• /
• 2007

Because of the characteristics relating to high tensile ductility, High Performance Fiber Reinforced Cementitious Composites (HPFRCC) are studied to be adopted in repair and retrofit of buildings. A series of three shear wall specimens was tested under constant axial stress and reversed cyclic lateral loading in order to evaluate the seismic retrofit that had been proposed for the shear wall with the opening. The retrofit involved the use of newly developed ECC and MDF(Macro Defect Free), both of which are sprayed through the high pressure pump, over the entire face of the wall. The results indicate that two difference types of retrofitting strategy make the different effects of a rise in the strength and ductility of each specimen.