• Journal of Korean Society of Coastal and Ocean Engineers
• /
• v.22 no.4
• /
• pp.241-247
• /
• 2010

Corrosion of steel embedded in concrete is one of the foremost factors that affect the durability of concrete structures in marine environments. This paper presents an application technique of anode-ladder-system to evaluate corrosion behaviours of marine concrete structure. In order to investigate the behaviours quantitatively, the measurement of potential and current was performed on the concrete elements subjected to the penetration and diffusion of chloride ions. The main variable was the heights from seawater level; namely 3.7, 6.0 and 8.2 m. As a result of the monitoring, it was found that the corrosion characteristics differently behaved with the increasing height. Additionally, through migration test, the relationship between compressive strength of concrete and diffusivity of chloride ions was observed. It is suggested, ultimately, that in order to reduce or mitigate steel corrosion, both appropriate concrete cover depth and high-quality of concrete in early ages should be done.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.263-264
• /
• 2009

This paper presents the example of corrosion monitoring sensor that is applied to massive RC structure exposed to marine environments. Corrosion monitoring sensor is used as an early warning system to predict the initial stage of corrosion in concrete structures. So, it can be a good method to verify the design life and prepare measures for concrete deterioration in advance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.3
• /
• pp.37-46
• /
• 2024

This study investigates the evolution of concrete damage due to chloride-induced steel corrosion through Impact-echo (IE) testing. Three reinforced concrete specimens, each measuring 1500 mm in length, 400 mm in width, and 200 mm in thickness, were fabricated using three concrete mixture proportions of blended cement types: ordinary Portland cement, ground granulated blast-furnace slag and fly ash. Steel corrosion in the concrete was accelerated by impressing a 0.5 A current following a 35-day cycle of wet-and-dry saturation in a 3% NaCl solution. Initial IE data collected during the saturation phase showed no significant changes, indicating that moisture had a minimal impact on IE signals and highlighting the slow progress of corrosion under natural conditions. Post-application of current, however, there was a noticeable decline in both IE peak frequency and the P-wave velocity in the concrete as the duration of the impressed current increased. Remarkably, progressive monitoring of IE proves highly effective in capturing the critical features of steel-corrosion induced concrete deterioration, such as the onset of internal damages and the rate of damage propagation. These results demonstrate the potential of progressive IE data monitoring to enhance the reliability of diagnosing and prognosticating the evolution of concrete damage in marine environment.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.258-259
• /
• 2019

Corrosion of rebar in RC structures, which results in premature deterioration of reinforced concrete structures, is a very serious problem. Most corrosion monitoring and sensing technologies require some type of wired or wireless connection between the sensor and monitoring electronics. This causes significant problems in their installation and long-term use. In this paper we describe a corrosion monitoring technology of rebar in reinforced concrete structures. Especially, it is emphasize that the development of sensors and monitoring system not only occurrence of rebar corrosion but also penetration of deterioration factor such like chloride ion and carbon dioxite etc..

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.4
• /
• pp.307-313
• /
• 2014

Recent interest in the increased structural performance and durability evaluation of this concrete structure in a salt damage environment is increasing. The most secure and reliable method of accelerated corrosion test is a method to carry out the rebar corrosion monitoring can be exposed directly to the marine test site exposure. However, long-term exposure testinghas the disadvantage that a long period is necessary. So, a lot of research on RC of salt damage environment have beenpromoted as alternatives to replace this. However, accelerated corrosion test, in the short term only is appropriate and is but an accelerated test method to evaluate the critical chlorine concentration, there is a difficult problem that you still get the answer. It is one of the correlation problems accelerated test correspond to a certain period of exposure environment. Therefore, in this study, to clarify the differences rebar corrosion beginning, through the actual corrosion accelerated test in corrosion time and laboratory test chamber of the structure of the marine environment results in both environments, it is an object of correlation coefficient derived.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.1
• /
• pp.117-125
• /
• 2017

The role of fly ash in concrete become impotent with finding the characteristics of fly ash in which it is used as cement replacement material. In this paper, corrosion test results obtained by two test methods such as the long-term exposure corrosion test and the accelerated corrosion test method, were compared to investigated the corrosion resistance between fly ash concrete and normal concrete. Corrosion initiation time was measured in two types of concrete, i.e., one mixed with fly ash(FA) and the other without admixture(OPC). The accelerated corrosion test was carried out by four case, i.e., two samples is a cyclic drying-wetting method combined without carbonation(case 1) and combined with carbonation(case 2), and the other two samples is a artificial seawater ponding test method combined without carbonation(case 3) and combined with carbonation(case 4). Whether corrosion occurs, it was measures using half-cell potential method. The ponding test combined without carbonation was most effective in accelerating corrosion time of steel bars. The results indicated that the corrosion of rebar embedded in concrete occurred according to the order of OPC, FA. The delay relative ratio of corrosion obtained by corrosion initiation time between FA and OPC is 1.04 to 1.27. Consequently, fly ash concrete as the age increases its corrosion resistance was improved compared with OPC concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.262-263
• /
• 2019

In this study, a sensor for detecting corrosion of rebar embedded in reinforced concrete structures was fabricated and its performance was verified. In order to monitor the open circuit potential(OCP) of the rebar embedded in reinforced concrete, a concrete embedded solid electrode was constructed as a sensor using MnO2. The OCP of the rebar could be observed using a sensor and a data logger. The decrease of the OCP to -510mV (vs.MnO2) or less was judged to be corrosion of the rebar. Since it is a solid-mediated sensor, it is more stable and durable than an electrode using an aqueous solution, and it is considered that the corrosion state of the rebar can be monitored for a long period of time.

• Magazine of the Korea Concrete Institute
• /
• v.12 no.3
• /
• pp.45-52
• /
• 2000

• Magazine of the Korea Institute for Structural Maintenance and Inspection
• /
• v.16 no.3
• /
• pp.10-18
• /
• 2012

• Journal of the Korea Institute of Building Construction
• /
• v.22 no.6
• /
• pp.651-662
• /
• 2022

The electrochemical impedance spectroscopy(EIS) method was used to evaluate the concrete deterioration process related to chloride-induced steel corrosion with various corrosion levels(initiation, rust propagation and acceleration periods). The impressed current technique, with four total current levels of 0C, 13C, 65C and 130C, was used to accelerate steel corrosion in concrete cylinder samples with w/c ratio of 0.4, 0.5, and 0.6, immersed in a 0.5M NaCl solution. A series of EIS measurements was performed to monitor concrete deterioration during the accelerated corrosion test in this study. Some critical parameters of the equivalent circuit were obtained through the EIS analysis. It was observed that the charge transfer resistance(R_c) dropped sharply as the impressed current increased from 0C to 13C, indicating a value of approximately 10kΩcm². However, the sensitivity of R_c significantly decreased when the impressed current was further increased from 13C to 130C after corrosion of steel had been initiated. Meanwhile, the double-layer capacitance value(C_dl) linearly increased from 50×10^-6μF/cm² to 250×10^-6μF/cm² as the impressed current in creased from 0C to 130C. The results in this study showed that monitoring C_dl is an effective measurement parameter for evaluating the progress of internal concrete damages(de-bonding between steel and concrete, micro-cracks, and surface-breaking cracks) induced by steel corrosion. The findings of this study provide a fundamental basis for developing an embedded sensor and signal interpretation method for monitoring concrete deterioration due to steel corrosion at various corrosion levels.