• Conservation Science in Museum
• /
• v.11
• /
• pp.49-52
• /
• 2010

A wooden Comb excavated at Shinchang-dong wetland site was treated with cetylalcohol as a reinforcing agent. The conservation process was done by freeze drying the wooden artifact after substituting it with no.3 butyl alcohol and impregnating with 40wt% cetylalcohol solution. Consequently there was no noticeable surface damage. Also it showed 54% of remaining weight and a shrinkage of length 3.3%, width 2.1% and thickness 3.1%. Therefore using cetylalcohol for conservation of waterlogged archeological wood was effective dimensional stability and remaining weight.

• Conservation Science in Museum
• /
• v.26
• /
• pp.13-24
• /
• 2021

Two wooden fish excavated from Wiryeseong Fortress on Seonggeosan Mountain in Cheonan-si, Chungcheongnam-do Province were frail due to their deterioration within the burial environment. To prevent further deformation, conservation treatment was conducted on them to strengthen the wooden materials and stabilize the dimensions. Prior to the conservation treatment, the species of wood was determined to be pine and infrared Irradiation on the patterns remaining on the wooden fish revealed that they were depictions of carp. For conservation treatment, the wooden fish were impregnated with PEG #3, 350 in a water solution with a 40% concentration, followed by freeze-drying.

• 한국문화재보존과학회:학술대회논문집
• /
• 2005.11a
• /
• pp.246-251
• /
• 2005

경산 임당유적에서 출토된 목제 갑옷틀은 수침된 상태로 출토된 목제유물로 재질이 매우 취약하여, 대기 중에 노출되면 급속도로 건조가 진행되어 곧바로 수축 변형이 일어나 유물로써 가치를 잃어버리게 된다. 특히 목제 갑옷틀은 오랜 매장기간동안 목질부의 분해가 많이 진행되어 재질이 취약할 뿐 아니라 원통목을 가공한 것이어서 건조 과정에서 수축변형이 발생우려가 높다. 따라서 목제 갑옷틀은 건조변형이 적고 치수안정화가 우수한 처리법을 적용하여야 한다. 따라서 목제 갑옷틀은 t-butanol 용액을 용제로 PEG#4000 40%로 함침 전처리 후 진공 동결건조법으로 보존처리 하였다.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1982-1984
• /
• 2004

Stator coil of rotating machinery has shown different characteristics according to impregnated with coil or not. And this is major determinant of equipment's life. In this paper, PD characteristics is studied as a classification scheme between two specimens. Processing of the coil impregnation is very important thing because that influences on thermal and electrical characteristics of the coil. And then PD is occurring at the coil and causing insulation degradation. For processing statistical processing, PD data acquired from PD detector using PDASDA(partial discharge acquisition, storage and display system). And also these statistical distribution and parameter are applied to classify PD sources by neural networks. As a result of, Neural Networks have a good discrimination rate for classification PD sources.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.59 no.3
• /
• pp.311-316
• /
• 2010

According to increase of combined cycle power generation, the manufacturing market of gas turbine generator has become more competitive, so there is high pressure on the manufacturer to reduce generator price. Global VPI(vacuum pressure impregnation) method is effective to save the production cost and time for manufacturing stator windings, but it has an abrasion problem by vibration between stator windings and slots. This paper presents the insulation breakdown case, which is for VPI type generator during high voltage insulation tests, and also shows the cause analysis, repair works as well as reliability test. the purpose of this paper is to understand the insulation properties of VPI type generator and to know prevention of insulation weakness.

• Journal of Conservation Science
• /
• v.32 no.2
• /
• pp.155-165
• /
• 2016

This study aimed at verifying the effect of hydroxypropyl cellulose(HPC) treatment on polyethylene glycol(PEG)-treated waterlogged wood for surface stabilizing. This research investigated macroscopic and microscopic appearance, color change, weight change, and dimensional change. And effect of HPC was verified through variance analysis (ANOVA) and least significant difference test(LSD). HPC formed thin layer on the surface of wood specimen, and blocked the pore of tracheid and the gap between the crack. Specimens without deterioration showed no invisible change except HPC 1,000,000 treatment group. Whitening was appeared at the sound surface of HPC 1,000,000 treated wood. Specimens with deterioration showed a little color difference change by external moisture adsorption. Thin layer of HPC on the surface of wood specimen was maintained after the deterioration, and this HPC layer significantly suppressed the weight and dimensional change by moisture adsorption.

• Journal of Conservation Science
• /
• v.36 no.3
• /
• pp.225-235
• /
• 2020

The present study aimed to monitor changes in the amount of PEG free-flowing back from PEG-treated woods and compressive strength changes with change in relative humidity from 90% to 30%. The change in the relative humidity was done 3 times. For the current study, water-logged wood (Prinus group) was used and the wooden blocks cut out of it were subjected to 3 different impregnation methods combined with different drying conditions as follows: 1) impregnating with 80% PEG#4000 followed by drying in nature (hereafter PEG80), 2) impregnating with 40% PEG#4000 and then drying in vacuum freeze drying equipment (hereafter PEG40), and 3) impregnating with 40% PEG#4000 in t-butanol, followed by drying in the vacuum freeze drying equipment (hereafter TB40). It was verified that most of the PEG was free-flowing back from the PEG-treated woods; however, a small amount of left PEG was observed on the lumen surface. The amount of PEG free-flowing back from the PEG-treated woods increased whenever the relative humidity changes from 90% to 30%. The compressive strengths of PEG80 and TB40 were increased whenever the relative humidity changed from 90% to 30%, whereas PEG40 decreased. The current study showed how to control the relative humidity to effectively manage PEG-treated waterlogged woods.

• Fire Science and Engineering
• /
• v.24 no.3
• /
• pp.52-57
• /
• 2010

Fire protection countermeasure were considered on the straw thatched roof and wooden structure. For the fire resistant treatment, rice straw was soaked in the fire resistant liquid with different soaking time. After treatment, some rice straw sample was washed with water then the rice straws were tested to check the fire resistance performance. And the wood was soaked in the fire resistant liquid at an atmospheric pressure, vacuum-pressure condition and painted with brush on the surface. To analyse the fire resistant performance of rice straw, ignition delay time was measured under the radiant heat flux of cone heater. And the fire resistant performance of wood samples were tested with 45 degree fire resistant test apparatus and cone heater. Based on the cone heater test, the rice straw which most easily ignitable material shows the longer ignition delay time than not treated ones and even in the water washed straw show a longer ignition delay time than not treated ones. And fire resistant treated woods of vacuum-pressure treated sample showed the most excellent performance on fire resistance. And the fire resistant treated by brush and soaking showed a longer ignition delay time than not treated ones. From this experiment, it was found that a fire resistant treatment of rice straw and wood of the house can be protected from the fire spread.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.229-229
• /
• 2007

나노결정 합금재료를 전력선 통신 커플러용 자심재료로 응용하기 위해서는 고주파 대역에서의 손실 특성이 제어되어야 한다. 즉 고속 전력선 통신을 위한 자심재료의 투자율 및 완화 주파수 등의 전자기적 특성은 30MHz까지 우수하고 안정적으로 유지되어야 하며, 높은 투자율 및 자속밀도, 공진주파수뿐만 아니라 낮은 전력손실 값을 가져야 한다. 따라서 본 연구에서는 나노결점 합금 리본 표면에 딥 코팅, 졸-겔법, 진공함침 등의 방법을 이용하여 PZT, $TiO_2$ 및 $SiO_2$ 등의 산화물 고저항층을 형성시켜 자기적 성질을 유지하면서 고주파 대역의 와전류 손실을 감소시켜 통신용 자심재료로의 응용성을 향상시키고자 하였다. PZT 슬러리의 제타전위 조절을 통해 최적의 분산조건을 얻을 수 있었고, 평균 150nm인 PZT 입자의 초미립자와 가소제, 분산제, 결합제의 첨가조건을 확립할 수 있었다. 딥-코팅은 슬러리 내 유지시간 10초, 인상속도 5mm/min로 30회 반복되었을 때 가정 우수한 특성을 나타내었으며, 고주파 대역에서의 손실 감소효과를 나타내었다. 그리고 졸-겔법에 의해 제조된 슬러리를 이용한 $TiO_2$와 $SiO_2$ 산화물 저항층 코팅을 통해 금속 알콕사이드의 혼합조건 및 저항층 형성용 슬러리의 제조조건을 확립하였고, 합금 리본표면에 균일하고 우수한 점착력을 가지는 저항층을 형성시킬 수 있었으며, 이에 따른 코어손실의 감소효과를 나타낼 수 있었다. 또한 진공 함침법을 통한 저항층 형성에서, $TiO_2$ 나노분말을 표면 저항층으로 코팅했을 때, 가장 높은 코어손실 감소효과를 나타내었다. 한편, 표면 저항층이 형성된 나노결정 합금으로 제조한 자심재료를 이용하여 전력선 통신용 비접촉식 커플러에의 적용과 시험을 통해 고주파 손실 감소효과에 의한 신호전송 특성과 전류특성을 향상시킬 수 있었다.

• Journal of Conservation Science
• /
• v.37 no.6
• /
• pp.821-830
• /
• 2021

The weapons excavated from the de-militarized zones (DMZ) of Korea are vulnerable to corrosion due to the immediate and drastic environmental change. Especially, the chloride ions (Cl^-) in iron weapons cause active corrosion and require removal. In this study, conservation treatment and de-salination was performed for the discovered weapons from excavation sites of soldiers killed in action during the Korean War. Furthermore, an attempt was made to prepare the most stable plan for conservation treatment through the comparative study of soaking weapons in distilled water without chemicals and in a solution of sodium (SSC) at different temperatures. In the preliminarily experiments, the comparison of the eluted Cl^- ions according to different conditions of de-salination showed that the highest number of ions were detected from the de-salination with SSC at a temperature of 100℃, and its duration was much smaller, i.e., 1~2 weeks. Accordingly, for the parts from the guns and rifles amongst other objects, a six-time de-salination was conducted in the SSC solution for 8 hours at 100℃ and subsequently, for 16 hours at room temperature during which the distilled water and SSC were exchanged every week. However, in the case of a loaded rifle, the de-salination was not conducted, considering the risk that the high temperature and pressure by impregnation in vacuum could cause an explosion