Light wavelength is the major factor of fruit body development associated with mushroom cultivation, but its wavelength range in Pleurotus eryngii is poorly understood. Using four kinds of light emitting diode (LED) including blue (475 nm), green (525 nm), yellowed (590 nm) and red (660 nm), we investigated to elucidate suitable light wavelength during primordium formation and fruit body development of P. eryngii on bottle cultivation. Primordia formation did not occur in blue light and red light. The morphological properties of fruit body in fluorescent lamp and blue light irradiation were showed thicker and larger pileus than those in other LEDs. However, length of stipe in fluorescent lamp and blue light was shorter than that of other LEDs. The DPPH radical was high in blue light, green light, and yellow light except for red light, and the polyphenol was high in four kinds of LED sources. And ergosterol was the highest in the green light. Thus, the high-quality mushroom production of P. eryngii is possible to green light condition considering productivity and functional materials.

• Korean Journal of Materials Research
• /
• v.22 no.3
• /
• pp.145-149
• /
• 2012

Red phosphors of $Gd_{1-x}Al_3(BO_3)_4:{Eu_x}^{3+}$ were synthesized by using the solid-state reaction method. The phase structure and morphology of the phosphors were measured using X-ray diffraction (XRD) and field emission-scanning electron microscopy (FE-SEM), respectively. The optical properties of $GdAl_3(BO_3)_4:Eu^{3+}$ phosphors with concentrations of $Eu^{3+}$ ions of 0, 0.05, 0.10, 0.15, and 0.20 mol were investigated at room temperature. The crystals were hexagonal with a rhombohedral lattice. The excitation spectra of all the phosphors, irrespective of the $Eu^{3+}$ concentrations, were composed of a broad band centered at 265 nm and a narrow band having peak at 274 nm. As for the emission spectra, the peak wavelength was 613 nm under a 274 nm ultraviolet excitation. The intensity ratio of the red emission transition ($^5D_0{\rightarrow}^7F_2$) to orange ($^5D_0{\rightarrow}^7F_1$) shows that the $Eu^{3+}$ ions occupy sites of no inversion symmetry in the host. In conclusion, the optimum doping concentration of $Eu^{3+}$ ions for preparing $GdAl_3(BO_3)_4:Eu^{3+}$ phosphors was found to be 0.15 mol.

• Journal of Powder Materials
• /
• v.27 no.2
• /
• pp.146-153
• /
• 2020

The co-doping effect of aliovalent metal ions such as Mg²⁺, Ca²⁺, Sr²⁺, Ba²⁺, and Zn²⁺ on the photoluminescence of the Y₂O₃:Eu³⁺ red phosphor, prepared by spray pyrolysis, is analyzed. Mg²⁺ metal doping is found to be helpful for enhancing the luminescence of Y₂O₃:Eu³⁺. When comparing the luminescence intensity at the optimum doping level of each Mg²⁺ ion, the emission enhancement shows the order of Zn²⁺ ≈ Ba²⁺ > Ca²⁺ > Sr³⁺ > Mg²⁺. The highest emission occurs when doping approximately 1.3% Zn²⁺, which is approximately 127% of the luminescence intensity of pure Y₂O₃:Eu³⁺. The highest emission was about 127% of the luminescence intensity of pure Y₂O₃:Eu³⁺ when doping about 1.3% Zn²⁺. It is determined that the reason (Y, M)₂O₃:Eu³⁺ has improved luminescence compared to that of Y₂O₃:Eu³⁺ is because the crystallinity of the matrix is improved and the non-luminous defects are reduced, even though local lattice strain is formed by the doping of aliovalent metal. Further improvement of the luminescence is achieved while reducing the particle size by using Li₂CO₃ as a flux with organic additives.

• Journal of Satellite, Information and Communications
• /
• v.7 no.3
• /
• pp.145-148
• /
• 2012

In applying LCD to TV application, one of the most significant factors to be improved is image sticking on the moving picture. LCD is different from CRT in the sense that it's continuous passive device, which holds images in entire frame period, while impulse type device generate image in very short time. To reduce image sticking problem related to hold typedisplay mode, we made an experiment to drive TN-LCD like CRT. We made articulate images by turn on-off backlight, and we realized the ratio of Back Light on-off time by counting between on time and off time for video signal input during 1 frame (16.7ms). Conventional CCFL (cold cathode fluorescent lamp) cannot follow fast on-off speed, so we evaluated new fluorescent substances of light source to improve residual light characteristic of CCFL. We realized articulate image generation similar to CRT by CCFL blinking drive and TN-LCD overdriving. As a result, reduced image sticking phenomenon was validated by naked eye and response time measurement.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.4
• /
• pp.298-303
• /
• 2012

$Y_{1-x}VO_4:Eu_x^{3+}$ red phosphors were synthesized with changing the mol ratios of $Eu^{3+}$ ions by using the solid-state reaction method. The crystalline structure of phosphors was found to be a tetragonal system with the maximum diffraction intensity at $25.02^{\circ}$. The grain particles showed the truncated hexagonal patterns with a very homogeneous size distribution at 0.05 mol of $Eu^{3+}$ ion. The excitation spectra of the phosphor ceramics were composed of a broad band centered at 303 nm and weak narrow multilines peaked in the range of 360-420 nm. The dominant emission spectrum was the strong red emission centered at 619 nm due to the $^5D_0{\rightarrow}^7F_2$ electric dipole transition. The experimental results suggest that the optimum doping mol ratio of $Eu^{3+}$ ions for preparing the red phosphors is 0.10 mol with the asymmetry ratio of 5.21.

• Korean Journal of Materials Research
• /
• v.27 no.10
• /
• pp.534-543
• /
• 2017

$Gd_2O_3:Eu^{3+}$ red phosphors were prepared by template method from crystalline cellulose impregnated by metal salt. The crystallite size and photoluminescence(PL) property of $Gd_2O_3:Eu^{3+}$ red phosphors were controlled by varying the calcination temperature and $Eu^{3+}$ mol ratio. The nano dispersion of $Gd_2O_3:Eu^{3+}$ was also conducted with a bead mill wet process. Dependent on the time of bead milling, $Gd_2O_3:Eu^{3+}$ nanosol of around 100 nm (median particle size : $D_{50}$) was produced. As the bead milling process proceeded, the luminescent efficiency decreased due to the low crystallinity of the $Gd_2O_3:Eu^{3+}$ nanoparticles. In spite of the low PL property of $Gd_2O_3:Eu^{3+}$ nanosol, it was observed that the photoluminescent property was recovered after re-calcination. In addition, in the dispersed nanosol treated at $85^{\circ}C$, a self assembly phenomenon between particles appeared, and the particles changed from spherical to rod-shaped. These results indicate that particle growth occurs due to mutual assembly of $Gd(OH)_3$ particles, which is the hydration of $Gd_2O_3$ particles, in aqueous solvent at $85^{\circ}C$.

• Journal of Powder Materials
• /
• v.24 no.6
• /
• pp.457-463
• /
• 2017

Nanosized $Gd_2O_3:Eu^{3+}$ red phosphor is prepared using a template method from metal salt impregnated into a crystalline cellulose and is dispersed using a bead mill wet process. The driving force of the surface coating between $Gd_2O_3:Eu^{3+}$ and mica is induced by the Coulomb force. The red phosphor nanosol is effectively coated on mica flakes by the electrostatic interaction between positively charged $Gd_2O_3:Eu^{3+}$ and negatively charged mica above pH 6. To prepare $Gd_2O_3:Eu^{3+}$-coated mica ($Gd_2O_3:Eu/mica$), the coating conditions are optimized, including the stirring temperature, pH, calcination temperature, and coating amount (wt%) of $Gd_2O_3:Eu^{3+}$. In spite of the low luminescence of the $Gd_2O_3:Eu/mica$, the luminescent property is recovered after calcination above $600^{\circ}C$ and is enhanced by increasing the $Gd_2O_3:Eu^{3+}$ coating amount. The $Gd_2O_3:Eu/mica$ is characterized using X-ray diffraction, field emission scanning electron microscopy, zeta potential measurements, and fluorescence spectrometer analysis.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.3
• /
• pp.194-200
• /
• 2020

Perylene bisimide derivatives are developed for red organic phosphor because of their advantages, such as excellent luminous efficiency and high thermal stability. Despite these advantages, they have poor solubility characteristics in organic solvents and short emission wavelength as red organic phosphor for hybrid light-emitting diodes (LEDs). In this study, we prepared terrylene bisimide using a coupling reaction and swallow-tail imide group, which has excellent solubility. The structures and properties of swallow-tail terrylene bisimide (9C) were analyzed using ¹H-nuclear magnetic resonance (¹H-NMR), Fourier-transform infrared (FT-IR), UV/Vis spectroscopy, and thermal gravimetric analysis (TGA). The maximum absorption wavelength of (9C) in the UV/Vis spectrum was 647 nm, and the maximum emission wavelength was 676 nm. In the TGA, (9C) demonstrated good thermal stability with less than 5 wt% weight loss up to 415℃. In the solubility test, (9C) has a good solubility of more than 5 wt% in chloroform and dichloromethane. When the compounds (9C) were mixed with PMMA (polymethly methacrylate), the films showed peaks at 680 nm in the PL spectra. The results verify the suitability of (9C) as a red organic phosphor for hybrid LEDs.

• Korean Journal of Materials Research
• /
• v.32 no.10
• /
• pp.425-428
• /
• 2022

In this study, Y₃Al₅O₁₂:Eu³⁺ red phosphors were synthesized at different temperatures using a solid state reaction method. The crystal structures, surface and optical properties of the Y₃Al₅O₁₂:Eu³⁺ red phosphors were investigated using X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM), and photoluminescence (PL) analyses. From XRD results, the crystal structure of the Y₃Al₅O₁₂:Eu³⁺ red phosphors was determined to be cubic. The maximum emission spectra were observed for the Y₃Al₅O₁₂:Eu³⁺ red phosphor prepared by annealing for 4h at 1,700 ℃. The 565~590 nm photoluminescent spectra of the Y₃Al₅O₁₂:Eu³⁺ red phosphors is associated with the ⁵D₀ → ⁷F₂ magnetic dipole transition of the Eu³⁺ ions. The intensity of the photoluminescent spectra in the red phosphors is more dominant for the magnetic dipole transition than the electric dipole transition with increasing annealing temperature. The International Commission on Illumination (CIE) coordinates of Y₃Al₅O₁₂:Eu³⁺ red phosphors prepared by 1,700 ℃ annealing temperature are X = 0.5994, Y = 0.3647.

• Journal of the Semiconductor & Display Technology
• /
• v.22 no.1
• /
• pp.83-87
• /
• 2023

Y₂SiO₅ Powder based on silicon and yttrium is well known as powder phosphors due to their excellent sustainability and efficiency. A new electroluminescence device was fabricated with Y₂SiO₅:Eu³⁺ powder phosphors though a simple screen printing method. The powder-dispersed electroluminescence device consisted of the Y₂SiO₅:Eu³⁺ powder-dispersed phosphor layer and BaTiO₃-dispersed dielectric layer. The annealing temperature of the phosphor for the best powder electroluminescence performance was optimized to high temperature in ambient atmosphere though a solid-state reaction. The Eu³⁺ concentration for the best device performance was also investigated and furthermore, the thermal dependence of the electroluminescence intensity was investigated at the operating voltage at 100℃, which is the Curie temperature of the BaTiO₃ layer. And the intensity was exponentially increased with voltage and increased linearly with frequency.