• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.04a
• /
• pp.118-119
• /
• 2007

오스테나이트계 스테인리스 AISI304L강을 저온 플라즈마 분위기에서 표면에 C와 N을 주입하면 내식성의 저하 없이 표면경도를 증가 시킬 수 있다. 이 공정에서 온도에 따른 영향을 조사하기위해 $380^{\circ}C{\sim}430^{\circ}C$의 온도 범위에서 20시간 동안 실시하였다. 경화층의 두께는 $7{\sim}16\;{\mu}m$정도였으며, N의 농도가 높은 영역과 C의 농도가 높은 영역으로 나뉘어 형성되었고, N이 풍부한 영역이 표면층에 형성되고 그 아래에 C의 농도 높은 영역이 형성되었다. 표면층은 질소에 의해 확장된 오스테나이트(${\gamma}_N$)상을 가지며 고온에서 처리한 경우 석출물이 형성되었다. 표면경도는 약 $900\;HV_{0.01}{\sim}1200\;HV_{0.01}$로 측정되었다.

• Journal of Bio-Environment Control
• /
• v.6 no.3
• /
• pp.216-224
• /
• 1997

In the recent 10 years the protected cultivation area in Korea has been increased rapidly, and now it is very important issue to develop the heating and cooling system using the renewable energy, because the greenhouse heating and cooling cost is increased with the fossil fuel price rises. Actually the development of the cooling system is more difficult than that of the heating system, since the cooling load of greenhouse in the summer season is 2―3 times larger than the heating load in the winter season. In this study low temperature phase change materials (LTPCM) for the cold storage system were selected and developed. The theoretical and experimental analysis of thermal characteristics of LTPCM makes it possible to control the phase change temperature and stabilize the thermo-physical properties. LTPCM developed in this study has good advantages to be used as the cold storage not only for the house and working space in factory but also for the cold storage of agricultural and live-stock products.

• Analytical Science and Technology
• /
• v.24 no.3
• /
• pp.200-211
• /
• 2011

In this study, 13 compounds including four volatile fatty acids (VFA) and nine volatile organic compounds (VOC) were analyzed by cryogenic trapping-thermal desorption technique. In order to evaluate the analytical method for VFA, calibration experiments were performed using five different sorbent materials. When the calibration results are compared between different sorbents, sampling tube filled with Carbopack X showed the highest response factor (RF) for both VFA and VOC. To validate this new analytical method for VFA using cryogenic trapping-thermal desorption technique, this method was compared with alkali absorption method recommended by the odor prevention law of the Korea Ministry of Environment (KMOE). For this purpose, unknown samples were analyzed by two different methods, i.e., cryogenic trapping-thermal desorption (TD) and alkali absorption with solid phase microextraction (SPME). When the results of two different methods were compared, ratios of concentrations determined by the two analytical methods (TD/SPME) was found as 0.46 (valeric acid) ~ 0.71 (isovaleric acid). Therefore, additional study is required to properly establish and find stable analytical conditions for VFA analysis. Furthermore, comparison between two different methods should be made with more reliable calibration approaches.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.3
• /
• pp.133-137
• /
• 2002

$ZnWO_4$ nano-powders were successfully synthesized at low temperature by polymerized complex method using zinc acetate and tungstic acid as starting materials. The polymeric precursors were heat-treated at temperatures from 300 to $600^{\circ}C$ for 3 h. The precursors and heat-treated powders were evaluated for crystallization process, thermal decomposition, surface morphology and crystallite size. Crystallization of the $ZnWO_4$ powders were detected at $400^{\circ}C$ and entirely completed at a temperature of $600^{\circ}C$. The particles heat-treated at $400^{\circ}C$ showed primarily co-mixed morphology with spherical and silk-worm-like forms, while the particles heat-treated at $500^{\circ}C$ showed more homogeneous morphology. The average crystalline sizes were 17.62~24.71 nm showing an ordinary tendency to increase with the temperatures from 400 to $600^{\circ}C$.

• Journal of the Korean Vacuum Society
• /
• v.5 no.4
• /
• pp.377-386
• /
• 1996

Austenitic stainless steel type 304L has been nitrided under the low pressure of high nitrogen environment for 5 hours by the square-wave-pulse-d.c. plasma as a function of temperature 400~$600^{\circ}C$ and of pulsation. At the temperature range lower than $500^{\circ}C$ and at the relatively high ratio of pulse duration to pulse period, nonstoichiometric stainless steel nitride has been developed in the form of a thin layer which has many cracks. At the temperature range higher than $500^{\circ}C$, with the increasing temperature or with the increasing ratio of the pulse duration to pulse period up to 50s/100s, the nitrided layer was composed mainly of CrN and Fe4N phases and became thick, uniform, columnar and nearly crack-free. The nitrided layer at $500^{\circ}C$ was mixed with the low-temperature layer and the high temperature layer and was very brittle.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.10 no.4
• /
• pp.695-701
• /
• 2009

Vortex tube is the device that can separate small particles from the compressed gas, as well as compressed gas into hot and cold flow. In this study, computational approach has been performed to analyze the characteristics of the vortex tube. Energy separation characteristics of the vortex tube has been tested for various geometric design parameters. For the given conditions, it is found that as the tube is lengthened, hot end temperature is reduced but cold end temperature does not influenced much. As the orifice diameter decreases, cold end temperature decreases. Also, as hot gas fraction increases, hot end temperature decreases. The results from this study can be used for the basic design parameter of the $CO_2$ reduction device.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.30-30
• /
• 2010

고강도강의 용접성은 저온균열 저항성으로 대변되는데, TMCP강과 HSLA강 등이 개발되면서 고강도강의 저온균열저항성이 크게 향상되어 무예열 용접성이 확보되었다. 그러나 용접재료 측면에서는 그에 상응하는 재료의 개발이 지연되어 강재 개발로 인한 우수한 성능을 충분히 발휘하지 못하고 있으며 용접부의 건전성 문제가 심각하게 인식되고 있다. 이로 인해 고강도강에 적용시킬 수 있는 무예열 용접재료의 필요성이 대두되어 개발이 진행되고 있으며 상용화를 앞두고 있다. 이러한 용접재료의 개발단계에서 합금설계는 가장 중요한 항목으로 합금 조성에 따라 용착금속의 강도 및 인성에 상당한 변화를 가져오기 때문이다. 합금원소 중 Al은 강재의 탈산을 돕기 때문에 가능한 많은 양의 첨가를 요구하지만 적정량 이상을 초과하게 되면 오히려 용착금속의 저온인성 특성에 부정적인 영향을 미치게 된다. 본 연구에서는 고강도 GMA 용착금속의 Al함량을 단계적으로 변화시켜 용착금속 내 최적의 Al의 함량을 찾고자 하였다. 또한 높은 비용 및 많은 시간을 필요로 하는 와이어로드를 제작하지 않고도 Al함량을 조절 할 수 있는 방법을 고안하고자 하였다. 실험의 모재는 HSLA-100강을 사용하였으며 용접재료는 ER120S-G급의 GMA용접 재료를 사용하였다. 모재 성분과의 희석을 방지하기 위해 V-Groove 가공 후 6패스 Buttering 용접을 실시하였고, 다시 Buttering용접부에 V-Groove 가공을 하여 최종 용접을 실시하였다. 이 때 Al함량을 조절하기 위해 최종 용접 개선부 밑면에 홈을 판 후 Al fiber(직경 0.3mm)를 깔고 용접(입열량 20kJ/cm)하여 Al함유량을 총 3가지(0.003~0.04% Al)로 제어하였다. 용접 후 각각의 시편에 대해 미세조직, 충격시험, O/N분석, 성분분석 등의 시험을 수행하여 저온인성과의 상관관계를 알아보았다.

• Korean Journal of Materials Research
• /
• v.9 no.6
• /
• pp.599-603
• /
• 1999

We have investigated the growth characteristics of thick GaN on Sim substrate with AlN and low temperature GaN buffer layer. The vertical hydride vapor phase epitaxy system with $GaCl_3$ precursor was used for growth of GaN. AlN and GaN buffer layer were deposited on Si substrate to reduce the lattice mismatch and the thermal expansion coefficient mismatch between si and GaN. Optimization of deposition condition for AlN and low temperature GaN buffer layers were carried out. We studied the effects of growth temperature, V/III ratio on the properties of thick GaN. Surface morphology, growth rate and crystallinity of thick GaN were measured using Atomic Force Microscopy (AFM), $\alpha-step$-, Scanning Electron Microscopy (SEM) and X-Ray Diffractometer(XRD).

• Korean Journal of Materials Research
• /
• v.5 no.4
• /
• pp.405-411
• /
• 1995

급냉응고된 Al-3.51wt%Li-0.34wt%Zr 합금의 시효거동을 시차주사열량계(DSC)에 의한 열분석 방법으로 조사하였다. DSC에 의한 비열측정 결과 $\delta$’의 석출에 의한 발열반응과 $\delta$, $\beta$ 및 복합석출상의 석출에 의한 발열반응을 확인하였으며 $\delta$’ 및 $\delta$의 재고용에 의한 2개의 흡열반응을 확인하였다. 7$0^{\circ}C$ 저온시효시 $\delta$’의 석출에 의한 발열반응 이전에 흡열반응이 나타났으며 이것은 $\delta$’ 석출 이전에 $\delta$’ 전구생성물이 형성되었음을 의미한다. DSC 곡선상에 나타난 발열과 흡열곡선을 해석하여 얻은 $\delta$’상 석출과 재고용의 활성화에너지값은 각각 83KJ/mol과 98KJ/mol로서 Al-Li 2원계 및 Al-Li-Mg에 비해 높은 값을 나타내엇으며, 시효에 의한 강화가 일어나 DSC에 의한 비열변화 조사결과 나타난 $\delta$’상 석출 완료 시효조건점 (21$0^{\circ}C$, 1시간)에서 최고경도값(Hv 160)을 나타내었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.32-32
• /
• 2003

최근 환경오염에 대한 문제가 심각해지면서 인체에 유해한 유기물질의 분해에 대한 관심이 높아지고 있으며 따라서 뛰어난 광촉매 특성을 보이는 타이태니아(TiO$_2$)에 대한 많은 연구가 수행되고있다. 타이태니아가 보이는 결정상 중에는 brookite, anatse, rutile이 있는데 이 중에서 anatse 상이 가장 우수한 광촉매 특성을 나타내는 것으로 알려져 있다. 그러나 anatse 상을 얻기 위해서는 $600^{\circ}C$ 이상의 온도로 열처리를 해야 한다는 문제점이 있으며 광촉매 특성을 향상시키기 위해서는 anantase 나노결정을 제조하여 표면적을 극대화시 키는 것이 요구되고 있다. 본 연구에서는 이러 한 두 가지 문제점을 해결하기 위하여 Polyethylen oxide(PEO)-TiO$_2$ 나노하이브리드를 Sol-Gel공정을 이용하여 합성하였으며 이들에 대한 hot-water treatment를 통하여 10$0^{\circ}C$ 이하의 저온에서 anatase 나노결정상의 분말을 합성하는데 성공하였다. 이는 SiO$_2$-TiO$_2$계 하이브리드에서만 hot-water treatment를 통하여 anatase로 결정화가 가능하다는 기존의 연구결과와 상반되는 결과로서 무기질 성분으로서 TiO$_2$만 존재하는 하이브리드에 대한 hoi-water treatment를 통하여 anatase결정상이 형성될 수 있었다.