• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.321-330
• /
• 2011

Recently, the effects of high temperature and fiber content on the residual mechnical properties of high-strength concrete were experimentally investigated. In this paper, residual mechanical properties of concrete with water to cement (w/c) ratios of 0.55, 0.42 and 0.35 exposed to high temperature are compared with those obtained in fiber reinforced concrete with similar characteristics ranging from 0.05% to 0.20% polypropylene (PP) fiber volume percentage. Also, factors including pre-load levels of 20% and 40% of the maximum load at room temperature are considered. Outbreak time, thermal strain, length change, and mass loss were tested to determine compressive strength, modulus of elasticity, and energy absorption capacity. From the results, in order to prevent the explosive spalling of 50 MPa grade concretes exposed to high temperature, more than 0.05 vol. % of PP fibers is needed. Also, the cross-sectional area of PP fiber can influence the residual mechanical properties and spalling tendency of fiber reinforced concrete exposed to high temperature. Especially, the external loading increases not only the residual mechanical properties of concrete but also the risk of spalling and brittle failure tendency.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.3
• /
• pp.323-331
• /
• 2012

Since the 1970s, the mechanical properties of concrete at high temperature, such as compressive strength, elastic modulus, thermal strain, etc. have been investigated. Internal and external factors should be effect to concrete elevated temperature. In particular, the thermal properties of aggregate and cooling conditions are most important to estimate residual mechanical properties. This study evaluates the mechanical properties of concrete with aggregate type and cooling methods. We use normal and light aggregate for different thermal properties, and also test mechanical properties to use ${\O}100{\times}200$ mm cylinder specimen according to target temperature, slow cooling and water cooling. We found that normal aggregate concrete that uses is more highly influenced by cooling conditions than concrete that uses light aggregate concrete. In addition, the residual mechanical properties of concrete increase as cooling velocity lowers.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.1
• /
• pp.131-139
• /
• 2012

The lateral reinforcements of concrete such as hoops and spiral bars are known to confine concrete to compensate the strength loss due to fire by reducing explosive spalling and improving the capacity of ductility. In this context, a study was conducted to investigate the residual mechanical properties of confined and unconfined concrete($f_{ck}$=60MPa) after a single thermal cycle at 300, 600, $800^{\circ}C$. The main parameters required to establish the stress-strain relationship are the peak stress, the elastic modulus, and the strain at peak stress. The knowledge of the residual mechanical properties of concrete is necessary whenever the thermally damaged structure is required to bear a significant share of the loads, even after a severe thermal accident. Based on the results obtained in this study, the residual stress of confined concrete under thermal damage is higher according to the level of confinement and the larger strain made it to have better ductility. The decreasing ratio of elastic modulus from the relationship of stress and strain was also smaller than that of unconfined concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.311-318
• /
• 2018

When reinforced concrete structures are exposed to fire, their mechanical properties such as compressive strength, elasticity coefficient and rebar yield strength, are degraded. Therefore, the structure's damage assessment is essential in determining whether to dismantle or augment the structure after a fire. In this study, the confinement effect of lateral reinforcement of RC column according to the numbers of fire exposure face and stirrup was verified by fire resistant test with the heating temperatures of $400^{\circ}C$, $600^{\circ}C$ and $800^{\circ}C$. The test results showed that the peak stress decreases and peak strain increases as the temperature is getting higher, also transverse ties are helpful in improving the compressive resistance of concrete subjected to high temperature. Based on the results of this study, the residual stress of confined concrete under thermal damage is higher at the condition of more lateral reinforcement ratio and less fire exposure faces. The decreasing ratio of elastic modulus of more confined and less exposure faces from the relationship of load and displacement was also smaller than that of opposite conditions.

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.431-440
• /
• 2011

Concrete structures exposed to fire produce changes in their internal structure, resulting in their service life reduction due to the deterioration of its strength and performance capacity. The deterioration level are dependent on the temperature, exposure time, concrete mix proportions, aggregate property, and material properties. This study was performed to evaluate the thermal behavior of ultra-high strength concrete for the parameters of water to cement ratio (compressive strength), fine to total aggregate ratio, and maximum coarse aggregate size. At room temperature and $500^{\circ}C$, tests of ultrasonic pulse velocity, resonance frequency, static modulus of elasticity, and compressive strength are performed using ${\varnothing}100{\times}200\;mm$ cylindrical concrete specimens. The results showed that the residual mechanical properties of ultra-high strength concrete heated to $500^{\circ}C$ is influenced by variation of a water to binder ratio, fine to total aggregate ratio, and maximum coarse aggregate size.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.11a
• /
• pp.99-100
• /
• 2012

Aggregate thermal properties and cooling methods are most important to evaluate the residual mechanical properties of concrete. In this study, we evaluate the residual mechanical properties of concrete according to the aggregate type and cooling method. We use the normal weight aggregate and light weight aggregate which have different thermal properties. After heating to the target temperature, we evaluate the mechanical properties according to the slow and fast cooling condition. As a result, normal weight aggregate concrete has higher effectiveness of cooling conditions than light weight aggregate concrete.

• Journal of the Korea Concrete Institute
• /
• v.25 no.6
• /
• pp.613-620
• /
• 2013

Concrete has been recognized as a material which is resistant to high temperatures, but chemicophysical property of concrete is changed by the high temperature. So, mechanical properties of concrete may be reduced. Because of this, standards and researches on the degradation of the mechanical properties of concrete at high temperatures have been presented. However, research data about the state that considering the loading condition and high-strength concrete is not much. Therefore, this study evaluated the high-temperature properties of high-strength concrete by loading condition and elevated temperature. The stress-strain, strain at peak stress, compressive strength, elastic modulus, thermal strain and the transient creep are evaluated under the non-loading and $0.25f_{cu}$ loading conditions on high strength concrete of W/B 12.5%, 14.5% and 20%. Result of the experiment, decrease in compressive strength due to high temperature becomes larger as the compressive strength increases, and residual rate of elastic modulus and compressive strength is high by the shrinkage caused by loading and thermal expansion due to high temperature are offset from each other, at a temperature above $500^{\circ}C$.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.211-212
• /
• 2011

It was very important to evaluate concrete experimentally at elevated temperature because concrete was filled with aggregate of concrete volume about 70 percent. Concrete exposure to high temperatures produces changes in its internal structure, for instance loss of its strength and deformation capacity, in extreme cases risking the service life of the structure. The work of this paper is performed to evaluate the thermal behavior of ultra-high strength concrete having different water to cement ratio (strength), fine aggregate to aggregate ratio and maximum size of coarse aggregate. For exposure to 500℃ during 1 hour, residual mechanical properties of the ultra-high strength concrete decreased as the s/a ratio decreases and the maximum size of coarse aggregate increases.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.05a
• /
• pp.63-64
• /
• 2012

In case of concrete, it should be deformed by many factors, such as explosive spalling, thermal strain and creep at high temperature. Structural fire design has been proposed to predict fire damage as national standard. It is general safer to use values obtained from tests of unstressed residual test in stead of stressed test. But most of thermal properties on concrete were conducted with normal aggregate. In this study, it evaluated mechanical properties of concrete with aggregate type and loading condition. we use normal and light aggregate to have different thermal properties. Also, we test mechanical properties to use Ø100×200 mm cylinder specimen according to target temperature and 0%, 20%, 40% loading.

• Journal of the Korea Concrete Institute
• /
• v.24 no.1
• /
• pp.53-60
• /
• 2012

The main object of this paper is to investigate the effects of high temperatures on the physical and mechanical properties of natural sand concrete(NSC) and crushed sand concrete(CSC). Test samples were exposed to high temperature ranging from $200^{\circ}C$ to $800^{\circ}C$. After exposure, various tests were conducted. Color image analysis and weight losses were determined and compressive strength test and splitting tensile strength test were conducted. The results indicated that weight losses increased as exposure temperature increased with comparable decreasing rate. The results also showed that compressive strength and splitting tensile strength and modulus of elasticity decreased as exposure temperature increased. The results also showed that residual compressive strength of NSC decreased more drastically than that of CSC at $200^{\circ}C$ and $400^{\circ}C$. Residual splitting tensile strength of NSC decreased more than that of CSC at $200^{\circ}C$, while NSC and CSC showed comparable residual strength ratio at $800^{\circ}C$.