• Resources Recycling
• /
• v.26 no.1
• /
• pp.11-15
• /
• 2017

The amount of the wood chip ash is expected to increase continuously as demand of wood chip-based heat and electricity increase. Thus, there is increased interest in wood chip ash utilization. In this study, as a program of utilization in wood chip ash, the physical and chemical properties of wood chip ashes generated from a combined heat and power plant were investigated. The chemical analysis showed that the main contents of wood chip ash are composed of silica, alumina and alkali. A possibility of reuse as secondary cementitious materials was investigated by the analysis of strength activity index, and compared with coal ash. The highest value for Strength activity index of wood chip fly ash was 78% at 90 days curing time. This result revealed that wood chip fly ash has the potential to be utilized as the admixture for cementitious material.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.57 no.5
• /
• pp.81-88
• /
• 2015

바이오매스는 유망한 신재생 에너지이다. 바이오매스는 액체 및 기체 연료로 전 환 할 수 있고, 다양한 공정을 통해 열 및 전력을 생산시키는데 사용된다. 바이오매스 가스화 공정은 바이오매스를 일산화탄소, 이산화탄소, 수소 및 메탄으로 이루어진 합성 가스로 전환시키는 기술이다. 바이오매스를 이용한 합성 가스 생산 및 활용은 세계적으로 늘어나는 에너지 필요성을 충족시킬 수 있는 대체에너지이다. 현재, 바이오매스 가스화의 주요 원료는 목질계 우드 칩을 주로 사용하고 있지만, 일반적으로 우드칩의 경우 수분을 다량 함유하고 있기 때문에 가스화 공정을 위해서는 별도의 건조처리를 필요로 한다. 우드칩의 건조에는 많은 에너지가 소요되고, 다량의 우드칩 건조에는 시간과 기상 및 공간적인 환경에 영향을 받는다. 본 연구에서는 미건조 우드칩의 가스화 공정을 위하여 미건조 우드칩에 숯을 각각 10, 30, 50 % 비율로 혼합하여 실험을 수행하였고, 실험결과 생산된 합성가스의 CO 농도 는 숯의 비율에 따라 14.9 ~ 25.6 % 증가되는 경향을 나타내었지만, 반대로 $CO_2$ 및 $CH_4$ 농도는 감소하였다. 이에 따라 합성가스 생산을 위한 미건조 우드칩과 숯의 최적혼합비율은 약 30 %로 판단되며, 발열량은 $1285.7kcal/Nm^3$, Gas yield는 $2.3Nm^3/kg$ 로 나타났다. 이에 적절한 숯의 혼합사용은 미건조 우드칩의 직접적인 가스화에 도움이 될 것으로 사료되며, 바이오매스 건조 공정에 필요한 에너지를 절약할 수 있을 것으로 판단된다.

• Journal of Korean Society of Forest Science
• /
• v.98 no.4
• /
• pp.426-434
• /
• 2009

This study was carried out to derive the most optimal production process for the wood fuels(chip and pellet), by collecting cost data on each procedure through the life cycle assessment approach, and to compare between the profitability and efficiency, from the view points of producers and consumers, irrespectively. The costs accounted in this analysis were based on the opportunity cost. The results show that wood chips are cheaper than wood pellets in production costs. In respect to the process with the lowest production cost, while wood chips should be to crush collected residues into pieces on the spot for merchandizing, wood pellets need to be transported to manufactory for pelletizing. The study findings also include that the profits, which is estimated by subtracting expenses from gained sale revenue, were a bit higher for wood chips than wood pellets. Additionally, the price ratio of wood pellets to wood chips for getting the same caloric value appears to be 1.27. Despite of economic benefits of processing wood chips, there are several problems in practice. For producers, there is a possible increase in not only transportation cost for conveying crushers to the dispersed places, but storage cost due to the lack of the marketplaces in the immediate surroundings. For consumers, on the other hand, there are some challenging issues, such as bulky storage facility requirement, additional labor for fuel supplement, frequent ashes disposal, and decomposition in summer and freezing in winter caused by wood chips' own moisture.

• Journal of Wetlands Research
• /
• v.20 no.2
• /
• pp.145-154
• /
• 2018

In this study, three pilot-scale wetland systems were built for treating stormwater runoff from asphalt road. Each of the system consists of a settling tank and a vertical flow wetland packed with 25%, 50%, and 75% woodchip as treatment media. According to the analysis of the distributions of particle size, it was found that solids ranging in size $0.52-30{\mu}m$ were predominant in the stormwater runoff. After 24-hours settling, those coarser than $20{\mu}m$ were significantly detained. Further retention, especially for the finer-sized fraction, occurred in the wetland through internal recirculation during the dry day periods. As a primary media of the wetland, woodchip showed a high filtration and attachment capacity for the particulates in pre-settled stormwater, whereas overall amount of solids in the wetland effluent increased due to the detachment of woody elements from the media. This was observed mainly during the initial 75 days of operation, and the size and detachment rate were found to be strongly related with the woodchip packing ratio. The mechanism involving woody particle detachment was modeled as a first-order form. In addition, water quality factors and operational parameters affecting the detachment were analyzed and discussed.

• Applied Chemistry for Engineering
• /
• v.23 no.5
• /
• pp.440-444
• /
• 2012

In this work, a semi-carbonized wood chip (SC-WC) was prepared by heat-treatment at low carbonization temperature. The pyrolysis characterization and heating value of the SC-WC at different heat-treatment temperature were evaluated. The pyrolysis characterization and heating value of the SC-WC were determined using thermal gravimetric analyzer (TGA) in $N_{2}$ atmosphere and calorimeter, respectively. From the TGA results, the thermal decomposition reaction of the SC-WC treated at by low temperature was similar to pure wood chip and the reaction was most actively occurred in the range of $200^{\circ}C$ to $400^{\circ}C$, whereas the initial thermal decomposition temperature of the SC-WC increased with the increasing heat-treatment temperature. In addition, the heating value of the SC-WC showed a similar trend as to the decamposition temperature behavior. This is probably attributed to increased carbon content of SC-WC by the localized carbonization of the wood chip which consisted of cellulose, hemi-cellulose, and lignin.

• Korean Chemical Engineering Research
• /
• v.54 no.3
• /
• pp.431-435
• /
• 2016

The aim of this study was to investigate the effect of gamma irradiation on the pretreatment of wood chips with NaOH solution. The degree of saccharification was quantified by measuring reducing sugar and glucose concentrations after enzymatic hydrolysis. After pretreatment with 10 g/L NaOH, the wood chips were irradiated at the doses of 0, 50, 100, and 200 kGy, respectively. Among the irradiated samples, wood chips irradiated at the dose of 200 kGy had the highest reducing sugar concentration of 12.2 g/L. Also, to define the effect of irradiation before pretreatment, the wood chips were first gamma-irradiated and then pretreated with NaOH. When the NaOH treatment was conducted after irradiation at 200 kGy, the reducing sugar content was further increased to 13.4 g/L and glucose content of the wood chip was as high as 7.9 g/L. These results suggest that gamma irradiation may be the promising method for pretreatment of cellulose biomass.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.05a
• /
• pp.175.1-175.1
• /
• 2011

우드칩을 포함하는 화석연료대비 발열량이 낮은 바이오매스를 가스화를 통하여 활용하는 경우 타르 및 수트를 포함하는 저열량의 합성가스가 생성된다. 이러한 합성가스를 엔진을 통한 발전, 스팀, 수소 및 화학제품 생산으로 활용하기 위해서는 고효율의 타르 정제 및 제거가 필수적이다. 특히 착화가 어렵고 연소온도 및 연소율이 낮으며, 화염구간이 좁은 저열량의 합성가스를 이용하여 스팀을 생산하기 위해서는 많은 문제점으로 인하여 기술 개발이 필요하다. 본 연구에서는 하향류식 가스화기를 이용하여 우드칩을 연료로 합성가스를 제조하였으며, 합성가스에 포함되어 있는 타르 및 수트와 같은 미반응 물질을 제거할 수 있는 집진, 세정장치를 설계 및 제작하였다. 특히 고효율 타르의 제거를 위하여 두 종류의 산화촉매를 이용한 합성가스 내 타르의 제거 연구를 수행하였다. Ru 촉매를 이용하는 경우 합성가스 내 타르의 농도를 100ppb 정도까지 저감이 가능하였다. 정제된 합성가스는 유류 혼소 버너를 통하여 보일러 연소실에서 혼합연소되어 30만kcal/h의 열을 공급함으로써 스팀을 생산 하였으며, 생성된 스팀은 블록 건조 시설에서 이용하였다.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.3
• /
• pp.323-336
• /
• 2016

This study was carried out to evaluate the physicochemical properties of steam exploded wood chips for peat moss substitute in vegetation media. Also, the mixtures at the different ratios of peat moss and pretreated wood chips (90 : 10, 70 : 30 and 50 : 50 (w/w), respectively) were evaluated by physicochemical and plant growth characteristics. The pretreated wood chips was showed that bulk density, porosity and pH were $0.26g/cm^3$, 93.3% and 5.7, respectively. This result indicates that physicochemical properties was improved when wood chips was apply to steam explosion in the range of optimum physicochemical condition for vegetation media. In particular, the mixture ratio of peat moss and pretreated wood chips to 70 : 30 (w/w) showed higher seed germination, plant height and leaf growth than peat moss. Also, the bulk density, porosity, water holding capacity, pH and C/N ratio were $0.20g/cm^3$, 91.8%, 76.1%, 5.2 and 51.0 in the range of optimum physicochemical condition for vegetation media.

• Journal of Wetlands Research
• /
• v.18 no.2
• /
• pp.183-193
• /
• 2016

In this study, design and performance of infiltration trench using woodchip as media for treating stormwater from highway were examined through field monitoring. Average reduction efficiency for TSS, COD, BOD, TN, and TP was 88%, 94%, 85%, 80%, and 75% respectively, which is similar to values reported by other studies and design manuals even though direct comparison is not possible due to different monitoring and design conditions. Mean field infiltration rate estimated by measuring the change of water depth inside the observation well was about 40mm/hr, and the time taken for complete infiltration was about 0.83days, which corresponds well with design criteria recommended by MOE guidelines in Korea. In addition, according to analysis of infiltration rate and reduction efficiency, effective rainfall depth applied for determining water quality volume(WQv), 5mm was found to be properly established as design criteria. Woodchip must be considered and included as an alternative media together with crushed rock and gravel into the design guidelines because it has more advantages in terms of weight, porosity, cost, and easiness of management than other media materials.

• Korean Journal of Organic Agriculture
• /
• v.28 no.2
• /
• pp.209-221
• /
• 2020

Highbush blueberries (Vaccinium corymbosum), 'Duke', 'Bluecrop', and 'Elliott', were applied with ground cover mulch systems to evaluate bush growth and fruit characteristics. Soil temperature variation was lower in the woodchip mulching plot. Therefore, CEC, soil pH, phosphate, mineral ions were not significantly different among mulching materials. The number of main stem was higher in woodchip > sawdust > rice husk > plastic film mulching plot, respectively. Total shoot number was also higher in organic mulching plots than in plastic film plot. However, total shoot number was not significantly different among the organic mulching plots. Fruit weight was the highest in the woodchip mulching plot of all blueberry cultivars, however, soluble sugar content, organic acidity, fruit firmness were not significantly different in mulching materials. Yield was higher in organic mulching plots than in plastic film plot in all blueberry cultivars. Especially, yield per shrub of woodchip plots was the highest about 3.6 kg in 'Duke', 2.7 kg in 'Bluecrop', and 2.6 kg in 'Elliott'. Furthermore, correlation of main stem number and yield was highly significant (r² = 0.8413). Therefore, woodchip mulching is expected to be an eco-friendly method to increase the number of stems and the yield of blueberries.