Abstract
The amount of the wood chip ash is expected to increase continuously as demand of wood chip-based heat and electricity increase. Thus, there is increased interest in wood chip ash utilization. In this study, as a program of utilization in wood chip ash, the physical and chemical properties of wood chip ashes generated from a combined heat and power plant were investigated. The chemical analysis showed that the main contents of wood chip ash are composed of silica, alumina and alkali. A possibility of reuse as secondary cementitious materials was investigated by the analysis of strength activity index, and compared with coal ash. The highest value for Strength activity index of wood chip fly ash was 78% at 90 days curing time. This result revealed that wood chip fly ash has the potential to be utilized as the admixture for cementitious material.
우드칩 분진 발생량은 우드칩 기반 난방과 에너지 수요가 증가함에 따라 계속적으로 증가할 것으로 기대된다. 따라서 우드칩 분진의 활용에 대한 관심도 증가하고 있다. 이 연구를 통해 우드칩 분진의 재활용을 위한 일안으로 열병합 발전으로부터 발생한 우드칩 분진에 대한 물리적, 화학적 특성을 분석했다. 화학 분석 결과 우드칩 분진의 주된 구성성분은 실리카, 알루미나, 알칼리로 나타났다. 우드칩 분진에 대한 strength activity index 분석과 석탄재와의 비교를 통해 이차 시멘트계 재료로써 재활용 가능성을 확인했다. 90일 동안 경화한 우드칩 분진에 대한 strength activity index 최대값은 78%였으며 이는 시멘트계 재료에 대한 혼합물로써 재활용할 수 있음을 제시하는 결과이다.