• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.213-214
• /
• 2010

An objective of this experimental research is to investigate the diffusion characteristics for chloride ion of concrete subjected to sulfate attack. For this purpose, concretes with three types of cement such as ordinary portland cement(OPC), binary blended cement(BBC), and ternary blended cement(TBC) containing mineral admixtures were made for water-binder ratios of 32% and 43%. The concrete specimens were immersed in sulfate solution for 365 days, and then the resistance against chloride ion penetration of them were estimated by using NT BUILD 492. It was observed from the test results that the resistance to chloride ion penetration of concrete subjected to sulfate attack was greatly decreased than that of standard curing concrete under the same age.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.4A
• /
• pp.347-353
• /
• 2009

The qualitative factors influencing the ingress of chloride ion into concrete are water-binder (W/B) ratio, cement type, age, chloride ion concentration of given environment, wet and dry conditions, etc. Thus, an objective of this experimental research is to investigate the effects of cement types and environmental conditions on the chloride ion diffusion characteristics in concrete through the chloride ion diffusion test. For this purpose, the diffusion coefficients for chloride ion in concrete with three types of cement such as ordinary portland cement (OPC), binary blended cement (BBC), and ternary blended cement (TBC), were measured for the concrete specimens with W/B ratios of 32%, 38%, and 43%, respectively. The diffusion coefficients for chloride ion were also measured for the concrete specimens with W/B ratio of 43%, which were subjected to standard curing and field exposure conditions. It was observed from the test results that the resistance against chloride ion penetration increased with decreasing W/B ratio and those of BBC and TBC concretes were greater than that of OPC concrete. Therefore, it was revealed that the use of these cements containing mineral admixtures is required to extend the service life of RC structures exposed to chloride environment. On the other hand, it was noted that the resistance against chloride ion penetration of field exposure test specimens was slightly lower than that of standard curing test specimens due to the penetration of chloride ion under the irregular ambient temperature, splash of wave, and cycle of wet and dry.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.401-404
• /
• 2008

Crack is a penetration path of harmful material such as chloride ion, and causes a serious deterioration in durability. So, the characteristics of chloride penetration are investigated for the cracked flexural concrete members using high-durable materials. For these, the flexural crack of beam specimen is introduced by transverse loading. And, Rapid Chloride Penetration Test (RCPT) and Long-term chloride penetration test are carried out to compare the chloride penetration depth. From test results when crack is happened, the chloride penetration resistance of the durable member was superior than that of the normal member. Blast furnace slag concrete member has a excellent chloride penetration resistance in long-term chloride penetration test.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.2
• /
• pp.149-156
• /
• 2016

It has been well known that concrete structures exposed to chloride and sulfate attack environments lead to significant deterioration in their durability due to chloride ion and sulfate ion attack. The purpose of this experimental research is to evaluate the long-term durability against chloride ion and sulfate attack of the alkali activated cementless concrete replacing the cement with ground granulated blast furnace slag. For this purpose, the cementless concrete specimens were made for water-binder ratios of 40%, 45%, and 50%, respectively and then this specimens were cured in the water of $20{\pm}3^{\circ}C$ and immersed in fresh water, 10% sodium sulfate solution for 28, 91, 182, and 365 days, respectively. To evaluate the long-term durability to chloride ion and sulfate attack for the cementless concrete specimens, the diffusion coefficient for chloride ion and compressive strength ratio, mass change ratio, and length change ratio were measured according to the NT BUILD 492 and JSTM C 7401, respectively. It was observed from the test results that the resistance against chloride ion and sulfate attack of the cemetntless concrete were comparatively largely increased than those of OPC concrete irrespective of water-binder ratio.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.1
• /
• pp.34-39
• /
• 2014

The purpose of this experimental research is to evaluate the resistance of reinforcement corrosion and chloride ion penetration of high volume fly ash (HVFA) concrete. For this purpose, concrete test specimens were made for various strength level and replacement ratio of fly ash, and then compressive strength and diffusion coefficient for chloride ion of them were measured for 28, 91 and 182 days, respectively. Also, corrosion monitoring by half cell potential method was carried out for the made lollypop concrete test specimens to detect the time of corrosion initiation for reinforcement in concrete. As a result, it was observed from the test results that compressive strength of HVFA concrete was decreased with increasing replacement ratio of fly ash but long-term resistance against reinforcement corrosion and chloride ion penetration of that was increased.

• Journal of the Society of Disaster Information
• /
• v.7 no.1
• /
• pp.21-31
• /
• 2011

The objectives of this study is replaced Silicafume with Metakaolin that is used to lightweight concrete to better performance. So, this study made high-performance lightweight concrete using Metakaolin and characteristics of the fundamental properties and chloride ion diffusion. Consequently, it is compressive strength and chloride ion penetration resistance is lower than lightweight concrete using Silicafume, the performance of compressive strength contrast Silicafume is about 88 to 95%. Also, this study got a content result because the chloride ion penetration resistance showed the performance in around 80 to 90%. As a result, this study insist that replacement ratio of Metakaolin is suitable for 10 to 15%.Silicafume and Metakaolin have similar characteristics. In addition, it is similar to the performance of alternative materials is possible.

• Journal of the Korea Concrete Institute
• /
• v.20 no.4
• /
• pp.469-475
• /
• 2008

It is obvious that chloride penetration through cracks can threaten the durability of concrete substantially, according to the previous studies of author. It was proposed that crack depth corrseponded with critical crack width from the surface is a crucial factor in view of durability design of concrete structures. It is now necessary to deal with chloride penetration through microcracks characterized with the mixing features of concrete. The purpose of this study is examining the effect of mix proportional features of concrete such as coarse aggregate, high strengtherize of concrete and reinforcement of steel fiber on chloride penetration through cracks. Although small size of coarse aggregate can lead to many microcracks in concrete, the cracks should not impact on chloride penetration directly. On the contrary, chloride should penetrate through cracks easily in concrete with a large size of coarse aggregate because mixrocracks are connected to each other. Second, high strength concrete has an excellent performance to resist with chloride penetration. However, for cracked high strength concrete, its performance is reduced upto the level of ordinary concrete. Finally, steel fiber reinforcement is effective to reduce chloride penetration through cracks because steel fiber reinforcement can lead to reduce crack depth significantly.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.151-152
• /
• 2017

This tests examined the effectiveness of bacteria slime on the chloride ion penetration resistance of cement mortar. Test results exhibited that the chloride ion penetration depth of mortars including 5% expanded vermiculite immobilizing bacteria was 17% smaller than that of the control mortar without expanded vermiculite.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.4
• /
• pp.349-358
• /
• 2023

This research aimed to enhance the initial strength of concrete that is mixed with ground granulated blast furnace slag, as well as to fortify its resistance to carbonation and chloride ion permeation. To achieve this, alkaline aqueous, produced through the electrolysis of potassium carbonate, was employed as the mixing water in the preparation of concrete. To substantiate the increment in initial strength, compressive strength measurements of the concrete were executed. Additionally, an accelerated carbonation test and a chloride ion permeation resistance test were undertaken. The results confirmed that the initial strength of the concrete, which utilized electrolysis alkaline aqueous as mixing water, exhibited an improvement in comparison to concrete mixed with conventional water. It was also verified that both carbonation resistance and chloride ion permeation resistance showed enhancements.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.1
• /
• pp.1-9
• /
• 2020

Chloride ion, which penetrates into the cement composites from the outside, generally diffuses by the concentration gradient. Chloride ions are adsorbed by the chemical reaction with cement hydrates. Recent studies have shown that anion exchange resin (AER) powder can effectively adsorb the chloride ion in the cement composites, and thus, the cement composites containing AER have a high chloride adsorption capacity and a good resistance for chloride penetration. In this study, the chloride adsorption ability of the AER powder was investigated under the conditions of distilled water and calcium hydroxide saturated solution to determine if the AER powder is less effective to increase the chloride adsorption ability after grinding process. The chloride adsorption ability of AER powder was compared with the previous research about the chloride adsorption of AER bead. In addition, the compressive strength, chloride diffusion coefficient (using NT Build 492 method), and the chloride profile of cement mortar substituted with AER powder were investigated. There was no decrease in the chloride adsorption capacity of AER powder but increase in the kinetic property for chloride adsorption after the grinding process. The AER powder could absorb the chloride ion in the mortar quickly, and showed better chloride ion adsorption ability than the cement hydrates.