• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2015년도 춘계 학술논문 발표대회
• /
• pp.166-167
• /
• 2015

The purpose of this study is to examine the effect on drying shrinkage of self-healing epoxy-modified mortars(EPMMs) using expansive admixtures. The EPMMs are prepared with polymer-binder ratios of 0 and 10%, and tested for drying shrinkage and pore structure analysis. As a result, regardless of the expansion and swelling agent content, the drying shrinkage of the EPMMs is remarkably decreased than that of unmodified mortars. Also, the pore size distribution of the EPMMs is moved to smaller size in comparison with unmodified mortars. In this study, the EPMM with expansive agent 7.5% and swelling agent 2.5% is recommended as a optimal mix proportion for reduction of drying shrinkage.

• 한국구조물진단유지관리공학회 논문집
• /
• 제25권1호
• /
• pp.85-92
• /
• 2021

본 연구는 액상폴리머인 에폭시수지를 이용한 고내구성 폴리머 시멘트계 재료를 개발할 목적으로 고로슬래그미분말 치환율을 20%로 고정하고, 4종류의 알칼리 활성화제를 이용한 경화제 무첨가 에폭시수지 혼입 폴리머 시멘트 모르타르를 제작하여, 강도 특성, 에폭시수지 경화도, 흡수율, 내황산성, 중성화 및 염화물이온 침투저항성을 검토한 것이다. 그 결과, 알칼리 자극제의 종류에 관계없이, 고로슬래그 미분말 20%를 사용한 경화제 무첨가 EMM의 압축강도는 폴리머 결합재비 10%에서 최댓값을 나타냈으며, 폴리머 결합재비 20%에서는 에폭시수지의 경화도 감소와 함께 압축강도 또한 감소하는 것으로 나타냈다. 휨강도는 압축강도와 마찬가지로 수산화칼슘을 첨가한 것이 가장 우수하게 나타났으며, 폴리머 결합재비의 증가와 함께 증가하였으며, 모두 9.0 MPa 이상의 휨강도를 발현하였다. 알칼리 자극제의 종류에 관계없이, 경화제 무첨가 EMM의 방수성, 중성화 및 염화물이온 침투저항성은 폴리머 결합재비의 증가와 함께 현저히 개선되었으며, 4종류의 알칼리 자극제 가운데 수산화칼슘을 첨가한 모르타르가 가장 우수한 것으로 나타났다. 한편, 알칼리 자극제의 종류에 관계없이, 경화제 무첨가 EMM의 내황산성은 폴리머 결합재비의 증가와 함께 떨어졌는데, 이것은 폴리머 결합재비의 증가에 따른 에폭시수지의 미경화 에폭시수지의 증가에 기인한 것으로 판단된다. 4가지 알칼리 자극제의 종류에 대하여 물성 및 내구성을 비교 검토한 결과, 수산화칼슘을 첨가한 것이 가장 우수한 것으로 확인되었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 춘계 학술논문 발표대회
• /
• pp.22-23
• /
• 2017

The purpose of this study is to ascertain self-healing function on microcracks in bisphenol F-type epoxy-modified mortars using expansive admixtures. The specimens are prepared with various polymer-binder ratios of 0, 5, 10, 20%, expansive admixture contents of 0% and 10%, a sodium carbonate content of 0.25%, and subjected to exposure conditions of CR1, CR2, CR3 and CR4. The specimens are tested for self-healing effect, porosity and FE-SEM analysis. As a result, self-healing effects of bisphenol F-type EPMMs with expansive admixtures are visible in all of the outdoor exposure conditions. In particular, exposure conditions of CR3 and CR4 are most noticeable. And the porosity of EPMMs is reduced with an increase in the polymer-binder ratio, and is considerably smaller than that of unmodified mortar.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 춘계 학술논문 발표대회
• /
• pp.288-289
• /
• 2014

The purpose of this research is to examine strength properties of epoxy-modified mortar with expansive and swelling agent contents. The polymer-modified mortars (PMMs) using epoxy resin are prepared with various polymer-binder ratios, expansive and swelling agent contents. The PMMs using epoxy resin are tested for compressive, flexural and tensile strengths. As a result, the strength properties of the PMMs using epoxy resin are depending on the polymer-binder ratio rather than expansive and swelling agent content, and are remarkably improved over unmodified mortar (UMM).

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2011년도 추계 학술논문 발표대회
• /
• pp.107-108
• /
• 2011

The purpose of present study is to examine the application of effective curing to hardener-free epoxy-modified mortars. The epoxy-modified mortars are prepared with polymer-cement ratios, subjected to two types of curing conditions, and tested for compressive, flexural and tensile strengths. As a result, hardener-free epoxy-modified mortars with steam curing is markedly improved with increasing air-dry curing period. High strength development of the epoxy-modified mortars may be achieved by the dense microstructure by cement and the hardener of the epoxy resin in the mortars.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 춘계 학술논문 발표대회
• /
• pp.263-264
• /
• 2012

The purpose of present study is to examine the long-term strength improvement of hardener-free epoxy-modified mortars with steam curing. As a result, strength improvement of hardener-free epoxy-modified mortars is markedly improved with increasing of air-dry curing period. This is improved by markedly increase the degree of hardening of the hardener-free epoxy resin in the epoxy-modified mortars with additional air-dry curing period.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 추계 학술논문 발표대회
• /
• pp.21-22
• /
• 2014

The purpose of this study is to ascertain strengths and hardening rate of epoxy-modified mortar with wood-tar contents. The polymer-modified mortars (PMMs) using epoxy resin with wood-tar are prepared with various polymer-binder ratios of 1, 3, 5% and wood-tar contents of 0, 5, 10, 15 and 20%. The PMMs using epoxy resin are tested for compressive, flexural and tensile strengths and hardening rate of epoxy resin. As a result, the strengths and hardening rate under polymer-binder ratio 1% and wood-tar content of 5% are more excellent than those of other specimens.

• 한국구조물진단유지관리공학회 논문집
• /
• 제24권1호
• /
• pp.80-87
• /
• 2020

본 연구는 고성능 폴리머 시멘트계 프리캐스트 제품의 개발 및 미세균열 발생 시 자기치유기능을 확보할 목적으로 경화제 무첨가 EMM의 물리적 성질을 검토하고, 그 물성에 영향을 끼치는 시멘트 매트릭스 내의 에폭시수지 경화도와 현미경을 통한 조직구조의 관찰과 함께 자기치유효과를 검토하였다. 그 결과, 경화제 무첨가 EMM의 폴리머 혼입에 의한 강도 개선 효과는 인장강도, 휨강도, 압축강도의 순으로 나타났다. 접착성은 콘크리트 피착체의 모세관 공극에 폴리머 필름의 형성에 기인한 투묘효과에 기인하여 크게 향상되었다. 투수저항성은 폴리머 결합재비 20% 및 고로슬래그 미분말 치환율 30%를 병용한 EMM에서 보통시멘트 모르타르 대비 97%의 감소율을 나타내 매우 우수하였다. 고로슬래그미분말, 팽창재 및 황산나트륨을 병용한 EMM의 균열 폭은 고로슬래그 치환율이 증가함에 따라 미미하게 감소하였으나, 고로슬래그미분말 치환율 20%에서 수중침지기간의 증가와 함께 서서히 균열부 자기폐색 효과를 관찰할 수 있었다.

• 콘크리트학회논문집
• /
• 제26권4호
• /
• pp.517-524
• /
• 2014

이 연구는 해양환경이나, 방사선 폐기물 및 가스 저장 시설과 같은 고내구성을 요하는 철근콘크리트 구조물의 내구성 향상 기법 및 장수명화 기술의 개발을 목적으로, 우수한 성능을 갖는 비스페놀 A형 및 F형 에폭시수지와 염화물 이온 흡착제인 아질산형 하이드로칼루마이트를 병용한 폴리머 시멘트 모르타르의 염화물이온 침투 저항성, 탄산화 저항성, 건조수축 및 철근부식 촉진시험을 통하여 내구성과 방청성을 비교 검토하는 것이다. 그 결과, 폴리머 결합재비에 관계없이 칼루마이트 치환에 의해 폴리머 시멘트 모르타르의 내구성이 일부 저하하는 경향을 보였으나, 이는 폴리머 결합재비의 증가와 함께 크게 개선되었다. 방청성의 경우 비스페놀 A형 및 F형 에폭시수지 사용으로 시멘트 매트릭스 내 생성된 폴리머 필름에 의한 이온 및 가스투과 저항성이 증대하였으며, 칼루마이트의 염화물이온 흡착과 아질산이온 방출에 의해 우수한 방청효과를 보였다. 이상의 연구 결과로부터 철근콘크리트의 고성능 다기능 폴리머 혼입 시멘트 모르타르 제품의 개발이 가능할 것으로 판단된다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2009년도 추계 학술논문 발표대회
• /
• pp.55-59
• /
• 2009

The epoxy resin without hardener can harden by a ring-opening reaction in the presence of the alkalies produced by the hydration of cement in epoxy-modified mortars and concretes. This paper investigates the effect of curing conditions on the strength improvement of polymer-modified mortars using bisphenol A-type epoxy resin without hardener. The polymer-modified mortars using epoxy resin are prepared with various polymer-cement ratios, and subjected to ideal, water, dry and heat cures. In the heat cure, the epoxy-modified mortars are sealed or unsealed with a PVDC (polyvinylidene chloride) film. The epoxy-modified mortars are tested for flexural and compressive strengths at desired curing methods. The microstructures of the epoxy-modified mortars are also observed by scanning electron microscope. The effects of curing conditions on the strength development of the epoxy-modified mortars are examined. From the test results, the marked effectiveness of the heat cure under the PVDC film sealing against the development of the strength of the epoxy-modified mortar without the hardener is recognized. The flexural and compressive strengths of 7-day-90℃ heat-cured, PVDC film-sealed epoxy-modified mortars without hardener reach 7 to 17MPa and 24 to 44MPa respectively, and are two to three times of Unmodified mortar. Such high strength development of the epoxy-modified mortars may be achieved by the dense microstructure formation by cement hydrates and the hardening of the epoxy resin in the mortars.