• Applied Chemistry for Engineering
• /
• v.32 no.1
• /
• pp.15-19
• /
• 2021

In this study, we studied a facile method for the synthesis of stable and nearly spherical gold nanoparticles using a tyrosine-rich peptide, Tyr-Tyr-Gly-Tyr-Tyr (YYGYY), as both the reducing and capping agent. The peptide coated spherical and polycrystalline gold nanoparticles with diameters from 3 to 15 nm were successfully synthesized by varying the concentration of the peptide and metal precursor under UV irradiation. The nanoparticles were then characterized by transmission electron microscopy (TEM), UV-Vis spectroscopy, scanning transmission electron microscopy-energy dispersive X-ray spectroscopy (STEM-EDS), Fourier transform infrared spectroscopy (FT-IR), and X-ray diffraction (XRD). Furthermore, the catalytic activity of gold nanoparticles was confirmed by the reduction of 4-nitrophenol to 4-aminophenol, in which the catalytic reaction rate constant was 7.3 × 10-3 s-1.

• Applied Chemistry for Engineering
• /
• v.32 no.2
• /
• pp.163-167
• /
• 2021

In the present work, we studied a method for the synthesis of uniform gold-peptide hierarchical superstructures using tyrosine rich peptide, Tyr-Tyr-Leu-Tyr-Tyr (YYLYY). Peptide nanoparticles self-assembled by dityrosine bonds were synthesized through the photo-crosslinking reaction of the peptide, and gold-peptide hybrid nanoparticles were synthesized using biomineralization properties of tyrosine in a green synthetic manner. The synthesized gold-peptide hybrid nanoparticles were then characterized by transmission electron microscopy, scanning electron microscopy, dynamic light scattering, UV-vis spectroscopy, scanning transmission electron microscopy-energy dispersive X-ray spectroscopy, and X-ray diffraction. Furthermore, the catalytic activity of gold-peptide hybrid nanoparticles was confirmed by the reduction reaction of methylene blue where the catalytic reaction rate constant was 13.4 × 10-3 s-1.

• Journal of Oral Medicine and Pain
• /
• v.36 no.3
• /
• pp.161-167
• /
• 2011

Sialolith is one of the most common pathologic conditions found in the salivary glands. The mechanisms responsible for the formation of sialoliths have not been elucidated so far. In this article, the chemical composition and micromorphology of a sialolith of a 58-year old female patient suffering from chronic sialoadenitis of the submandibular gland was analyzed using scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). In a SEM evaluation, the highly mineralized amorphous core surrounded by lamellar and concentric structures was revealed, however no foreign body, organic material, or signs of microorganism were observed in the core of the sialolith. EDX analysis showed the central core was composed of only Ca, O and P, and that a high level of C was detected near the central area as well. These results indicated that the inorganic composition of the sialolith was hydroxyapatite crystals, and that inorganic and organic substances existed around the central cores. This study suggests that the sialolith was composed mainly of hydroxyapatite crystals and the formation of the nucleus of the sialolith in the submandibular gland duct was secondary to sialadenitis, which favors the growth of an inorganic crystalline nucleus.

• Applied Chemistry for Engineering
• /
• v.31 no.2
• /
• pp.220-225
• /
• 2020

Hair is made of proteins containing various amino acids. Ultraviolet (UV) radiation is believed to be responsible for the most damaging effects of sunlight, and also plays an important role in hair aging. The purpose of this study was to investigate the changes in morphological and chemical structures after ultraviolet B (UVB) irradiation of human hair. The UVB-irradiated hair showed characteristic morphological and structural changes, compared to those of the normal hair. The result from a scanning electron microscope (SEM) equipped with an energy dispersive X-ray diffractometer (EDX) showed that the scale of UV-irradiated hair appeared to be rough and the amount of oxygen element was higher than that of the normal hair. Fluorescence and three dimensional (3D) topographical images were obtained by a confocal laser scanning microscope (CLSM). In 3D images, the green emission intensity of normal hair was much higher than that of fluorescing UVB-irradiated hair. The intensity of green emission reflects the intrinsic fluorescence of hair protein. Also, a fluorescent imaging method using fluorescamine reagent was used to identify the free amino groups resulting from a peptide bond breakage in UVB-irradiated hair. Strong blue fluorescence of UVB-irradiated hair, which indicates a very high level of amino groups, was observed by CLSM. Therefore, the fluorescamine as an extrinsic fluorescence could provide a useful tool to identify the peptide bond breakage in UVB-irradiated hair. Infrared image mapping was also employed to assess the cross-sections of normal and UVB-irradiated specimens to examine the oxidation of disulfide bonds. The degree of peak areas with strong absorbance for the disulfide mono-oxide was spread from the outside to the inside of hair. The spectroscopic techniques used alone, or in combination, launch new possibilities in the field of hair cosmetics.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.6
• /
• pp.703-714
• /
• 2023

This research conducts a series of tests to investigate the setting retarding properties and strength development in cement pastes incorporating various types and dosages of sugar-based super retarding agents. Six such agents, including Sucrose, Sugar powder, Saccharin, Aspartame, Stevioside, and Mogroside, commercially available, were selected for evaluation. The study also examines the micro-structural properties of these cement pastes. The test mixtures were prepared using a 27.5% water-to-cement ratio and ordinary Portland cement. Micro-structural analyses were conducted using Scanning Electron Microscopy(SEM), X-Ray Diffraction(XRD), and Energy Dispersive Spectroscopy(EDS). The findings reveal that the incorporation of sucrose, sugar powder, and stevioside significantly retards the setting time. Particularly, adding 0.1% sucrose extended the setting time by approximately two-fold compared to the control(Plain) mixture. Most mixtures, barring those with sugar powder and stevioside, exhibited compressive strength comparable to the Plain mixture. Notably, with 0.2% sucrose, strength measurements were not feasible at 1 day, but at 3 days, the strength gains aligned with the Plain mixture. XRD, SEM, and EDS analyses confirmed the hydration delay(set retarding) of C3S due to sucrose, with further quantitative corroboration provided by EDS. SEM was used to verify the presence or absence of hydration products. The study concludes that sucrose, as a sugar-based retarder, offers effective set retarding capabilities and compressive strength development in concrete.

• Clean Technology
• /
• v.23 no.1
• /
• pp.95-103
• /
• 2017

In this study, $ATiO_3$ (A = Ca, Sr, Ba) perovskite, which is the widely known for non $TiO_2$ photocatalysts, were synthesized using sol-gel method. And Ni was added at the A site of $ATiO_3$ by using that it is easy to incorporate. The physicochemical characteristics of the obtained $ATiO_3$ and Ni-$ATiO_3$ particles were confirmed using the X-ray diffraction (XRD) UV-visible spectroscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), the $N_2$ adsorption-desorption isotherm measurement, and X-ray photoelectron spectroscopy (XPS). The $H_2$ was produced using the photolysis of MeOH. Using the Ni-$ATiO_3$ photocatalysts, $H_2$ production was higher than using the $ATiO_3$ photocatalysts. Especially, $273.84mmolg^{-1}$ $H_2$ was produced after 24 h reaction over the Ni-$SrTiO_3$. Also in the water (0.1 M KOH) with the Ni-$SrTiO_3$, $H_2$ production was $961.51mmolg^{-1}$ after 24 h reaction.

• Applied Chemistry for Engineering
• /
• v.20 no.6
• /
• pp.617-621
• /
• 2009

Zinc oxide (ZnO) nanorods were grown on the pre-oxidized silicon substrate with the assistance of Au and the fluorine-doped tin oxide (FTO) based on the catalysts by vapor-liquid-solid (VLS) synthesis. Two types of ZnO powder particle size, 20nm, $20{\mu}m$, were used as a source material, respectively The properties of the nanorods such as morphological characteristics, chemical composition and crystalline properties were examined by X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX) and field-emission scanning electron microscope (FE-SEM). The particle size of ZnO source strongly affected the growth of ZnO nanostructures as well as the crystallographic structure. All the ZnO nanostructures are hexagonal and single crystal in nature. It is found that $1030^{\circ}C$ is a suitable optimum growth temperature and 20 nm is a optimum ZnO powder particle size. Nanorods were fabricated on the FTO deposition with large electronegativity and we found that the electric potential of nanorods rises as the ratio of current rises, there is direct relationship with the catalysts, Therefore, it was considered that Sn can be the alternative material of Au in the formation of ZnO nanostructures.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.1
• /
• pp.89-96
• /
• 2023

In this paper, a ferrosilicon by-product was evaluated to confirm the feasibility of recycling it as supplementary cementitious material of ordinary Portland cement in concrete. Three different levels of replacement ratio (10 %, 20 % and 30 % of total binder) were applied to find which is the most beneficial to be used as a binder. Ferrosilicon concrete was initially assessed at setting time and compressive strength. Durability was evaluated by the resistance to chloride penetration test(RCPT) and alkali-silica reaction(ASR) with a comparison to silica fume concrete due to their similarity in chemical composition. The porosimetry and X-ray diffraction analysis along with energy dispersive X-ray spectroscopy give information on the microstructural characteristics of the ferrosilicon concrete. It was found that 10 % ferrosilicon concrete has higher strength while 20 %, 30 % have lower strength than OPC concrete. However, chemical resistance to chloride attack is higher when replacement is increased. Compared to silica fume, the durability of ferrosilicon might be less efficient however, it is obviously beneficial than OPC. High SiO₂ content in ferrosilicon results in producing more C-S-H gel which could make denser pore structure. Most of the risk of alkali silica reaction to silicate binders through length change tests was less than 0.2 %, and both mortar using ferrosilicon and silica fume showed better resistance to alkali silica reaction as the substitution rate increased.Reuse of industrial waste rather than producing highly refined additives might reduce environmental load during manufacture and save costs.

• Clean Technology
• /
• v.19 no.3
• /
• pp.320-326
• /
• 2013

Nano-sized PtRu-Ni/VC and PtRu-Sn/VC electrocatalysts were synthesized by a one-step radiation-induced reduction (RIR) (30 kGy) process using distilled water as the solvent and Vulcan XC-72 as the supporting material. The obtained electrocatalysts were characterized by transmission electron microscopy (TEM), scanning electron microscope energy dispersive spectroscopic (SEM-EDS), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), respectively. The catalytic efficiency of electrocatalysts was examined for oxygen reduction, MeOH oxidation and CO stripping decreased in the following order, Hydrogen stripping : PtRu-Sn/VC > PtRu-Ni/VC > PtRu/VC$^{(R)}$ (E-TEK). MeOH oxidation : PtRu-Sn/VC > PtRu-Ni/VC > PtRu/ VC$^{(R)}$ (E-TEK). Unit cell performance : PtRu-Sn/VC > PtRu-Ni/VC > PtRu/VC$^{(R)}$ (E-TEK) catalysts.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.4
• /
• pp.167-172
• /
• 2013

Titanium dioxides nanoparticles coated aluminum oxide powders were fabricated by pulsed laser deposition (PLD) with Nd : YAG laser at 266 nm. The Pulse laser energy is 100 mJ/pulse. During the irradiation of the focused laser on the $TiO_2$ target, Ar gas is supplied into the chamber. The gas pressure is varied in a range of $1{\times}10^{-2}$ to 100 Pa. Titanium dioxides nanoparticles deposited aluminum oxide powders were characterized by using energy dispersive X-ray spectroscopy (EDX), high resolution transmission electron microscopy (HR-TEM), in order to understand the effect of Ar background gas on surface morphology and properties of the powders. The coated $TiO_2$ nanoparticles had nanosized spherical shape and the crystallite sizes of 10~30 nm. The morphology of coated $TiO_2$ nanoparticles is not affected by gas pressure. However, the particle size and crystallinity slightly increased with the increase of gas pressure. According to this technique, the size and crystallinity of nanoparticles can be easily controlled by controlling pressure during the laser irradiation.